CN108751367A - A kind of Arabic gum graphene oxide flocculant aid and the preparation method and application thereof - Google Patents
A kind of Arabic gum graphene oxide flocculant aid and the preparation method and application thereof Download PDFInfo
- Publication number
- CN108751367A CN108751367A CN201810562872.5A CN201810562872A CN108751367A CN 108751367 A CN108751367 A CN 108751367A CN 201810562872 A CN201810562872 A CN 201810562872A CN 108751367 A CN108751367 A CN 108751367A
- Authority
- CN
- China
- Prior art keywords
- graphene oxide
- arabic gum
- microcapsules
- flocculant aid
- flocculant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of Arabic gum graphene oxide flocculant aids and the preparation method and application thereof.The Arabic gum graphene oxide flocculant aid includes following component in parts by weight:75 ~ 85 parts of Arabic gum graphene oxide microcapsules, 15 ~ 25 parts of dispersant;The Arabic gum graphene oxide microcapsules include core material and wrap up the wall material of the core material, and the mass ratio of the wall material and core material is 0.5:1~2:1;The core material is graphene oxide, and the wall material is Arabic gum.Arabic gum graphene oxide flocculant aid of the present invention can improve the purifying rate of unit flocculant while improving flocculation efficiency, maintain or reduce the dosage of flocculant.
Description
Technical field
The present invention relates to the technical fields of water process water purification agent, more particularly, to a kind of Arabic gum graphene oxide
Flocculant aid and the preparation method and application thereof.
Background technology
Flocculation process is indispensable key link in sewage treatment process.During sewage disposal, often need
Flocculant is added, so that the suspended particulates in sewage is gathered and becomes larger to form floc sedimentation, to make the coagulation of particle.Flocculated principle is such as
Under:Positive (negative) electrical group is carried in flocculant, can neutralize in water and electrically be difficult to the particle detached with negative (just), is dropped
Its low potential, and using aggregation property these particles are concentrated, cotton-shaped coagulating sedimentation is formed, and pass through physics or chemistry side
Method is separated.
Conductive agent is added in the meeting having in existing flocculant, and its object is to, to electron transmission, make to flocculate by conductive agent
The charge generated in journey is transmitted to floccule surface by conductive agent, and the charge inside floccule can be also transmitted to by conductive agent
Floccule surface, it is easier to which the balance for breaking sewage system improves flocculated speed (flocculation efficiency).But, it has been found that
Partial flocculation efficiency around flocculant containing conductive agent is to be improved, but the flocculating and purifying of entire sewage disposal system
Rate (i.e. removal rate) is not improved but, or even is declined so that is needed to add more flocculants and be can be only achieved original wadding
Solidifying purifying rate, increases economic cost, loses more than gain instead in this way.
Invention content
The present invention is solves the problems, such as described in the above-mentioned prior art, provides a kind of Arabic gum graphene oxide and flocculates and helps
Agent, the Arabic gum graphene oxide flocculant aid can improve the net of unit flocculant while improving flocculation efficiency
Rate (removal rate) maintains or reduces the dosage of flocculant.
It is a further object of the present invention to provide the preparation methods of the Arabic gum graphene oxide flocculant aid.
In order to solve the above technical problems, the technical solution adopted by the present invention is:
A kind of Arabic gum graphene oxide flocculant aid, including following component in parts by weight:Arabic gum
75~85 parts of graphene oxide microcapsules, 15~25 parts of dispersant;The Arabic gum graphene oxide microcapsules include core material
With the wall material for wrapping up the core material, the mass ratio of the wall material and core material is 0.5:1~2:1;The core material is graphite oxide
Alkene, the wall material are Arabic gum.
Present inventor studies the conductive agent of existing flocculant, is found that while that conductive agent is played in flocculation process
Charge transfer acts on, and improves flocculated speed, but it also accelerates the charge consumption of flocculant simultaneously, flocculant is having enough time expanding
Dissipate before, charge has just been consumed, flocculant can only useful effect in part, this has also been resulted in around flocculant
Partial flocculation it is efficient, but the not high reason of flocculating and purifying rate (i.e. removal rate) of entire sewage disposal system.
In this regard, the present invention is improved the conductive agent of existing flocculant, graphene oxide is chosen as conductive agent, and will
Graphene oxide makes microcapsules, is combined together with dispersant, in flocculation process, the micro- glue of Arabic gum graphene oxide
Capsule can disperse rapidly, and graphene oxide during dispersion in Arabic gum graphene oxide microcapsules can be released gradually
It puts, plays the role of charge transfer to flocculation process, improve flocculated speed.Compared with existing conductive agent, by the application institute
It is gradually to discharge to state Arabic gum graphene oxide microcapsules, the charge of flocculant can before being consumed totally just with oxidation
Graphene is uniformly dispersed together, therefore can improve flocculated speed and whole flocculating and purifying rate.
In order to reach said effect, the dispersion of graphene oxide and release opportunity are crucial, in the present invention, it is preferred to water
Wall material of the Arabic gum of dissolubility as cladding graphene oxide, and the ratio by designing wall material and core material so that Arabic
Graphene oxide in glue graphene oxide microcapsules can effectively play a role in flocculation process.
In order to enable Arabic gum graphene oxide microcapsules efficiently and effectively to disperse, Arabic gum oxidation of the present invention
Graphene flocculant aid also includes dispersant, and studies the proportioning for obtaining Arabic gum graphene oxide microcapsules and dispersant.
Preferably, the Arabic gum graphene oxide flocculant aid includes following component in parts by weight:Arabic gum oxygen
80 parts of graphite alkene microcapsules, 20 parts of dispersant.
Preferably, the dispersant is one or more of polyvinyl alcohol, polyethylene, pyrrolidones.
It is highly preferred that the dispersant is the mixture of polyvinyl alcohol and pyrrolidones;The polyvinyl alcohol and pyrrolidines
The mass ratio of ketone is 1:2.
The release opportunity of graphene oxide is the key that the present invention, very much not with wall material in existing microcapsules and the ratio of core material
Identical, the present invention show that the zone of reasonableness of the mass ratio of wall material and core material is 0.5 by research:1~2:1.Preferably, the wall
The mass ratio of material and core material is 1:1.
Preferably, the preparation method of the Arabic gum graphene oxide microcapsules includes the following steps:
S1. graphene oxide is placed in ultrasonic disperse in pure water, obtains graphene oxide dispersion;
S2. wall material is added to the graphene oxide dispersion, temperature is 30~45 DEG C, pressure is 0.5~2MPa's
Under inert atmosphere, 30~60min is stirred, mixing speed is 800~1500r/min;
S3. after stirring terminates, solid product is collected in filtering, is freeze-dried to get the micro- glue of Arabic gum graphene oxide
Capsule.
Further, in step S1, the ratio of the graphene oxide and pure water is 0.1~0.3g:10ml, preferably
0.1g:10ml。
Further, in step S2, the wall material is made into the solution that mass fraction is 30~40wt%, is added into institute
State graphene oxide dispersion.
Preferably, the grain size of the graphene oxide is 300~1200nm, preferably 500~800nm.Preferably, described
Inert gas is nitrogen.
Preferably, in step S2, wall material is added to the graphene oxide dispersion, temperature is 35 DEG C, pressure is
Under the inert atmosphere of 1MPa, 30min, mixing speed 800r/min are stirred.
The present invention studies the reaction condition of microcapsule coated process, finds the inert gas environment in certain pressure
Under, the surface of graphene oxide can first coat a thin layer of air film, and wall material is coated on outside again, effectively prevent wall material stifled in this way
The aperture of graphene oxide composite material is filled in, and after freeze-drying, wall material and oxidation in Arabic gum graphene oxide microcapsules
Certain gap is still stayed between graphene, is contacted convenient for the release of graphene oxide and with flocculant.
The present invention also provides the preparation methods of the Arabic gum graphene oxide flocculant aid.The preparation method includes
Following steps:
S1. Arabic gum graphene oxide microcapsules are prepared;
S2. Arabic gum graphene oxide microcapsules are mixed with dispersant in proportion.
The present invention further provides the applications of the Arabic gum graphene oxide flocculant aid.The Arabic gum oxidation
Graphene flocculant aid can be applied in sewage disposal.
Further, the application is to improve the flocculation efficiency of flocculant in sewage disposal.Specifically, the application is to incite somebody to action
The Arabic gum graphene oxide flocculant aid is added to flocculant in sewage, is stirred, and is flocculated, sedimentation.The flocculant
Mass ratio with Arabic gum graphene oxide flocculant aid is 8~10:1, preferably 9:1.
The Arabic gum graphene oxide flocculant aid can be efficiently applied to existing flocculant system, further
Ground, the flocculant include but not limited to aluminum sulfate, polyoxygenated aluminium, iron chloride and ferrous sulfate, polyacrylamide.Preferably,
The flocculant is polyacrylamide.
Compared with prior art, the beneficial effects of the invention are as follows:
The present invention is improved the conductive agent of existing flocculant, chooses graphene oxide as conductive agent, and will oxidation
Graphene makes microcapsules, is combined together with dispersant, in flocculation process, the Arabic gum graphene oxide microcapsules energy
Enough rapid dispersions, graphene oxide during dispersion in Arabic gum graphene oxide microcapsules can gradually be discharged,
Play the role of charge transfer to flocculation process, improve flocculated speed, while can also improve the purifying rate (removal of unit flocculant
Rate), maintain or reduce the dosage of flocculant.
Specific implementation mode
By following specific examples, present invention be described in more detail, it should be understood that specific implementation described herein
Example is only used for explaining the present invention, is not intended to limit the present invention, can carry out various change in the range of right of the present invention limits
Become.
Unless otherwise noted, raw material involved in following embodiment are commercially available, equipment used and
Technique is known to those skilled in the art.Wherein, graphene oxide is that the limited public affairs of graphite science and technology are contained by Hunan state
Department's production, grain size is 500~800nm.Polyacrylamide is purchased from Sinopharm Chemical Reagent Co., Ltd., and molecular weight is
3000000.
Examples 1 to 7 and comparative example 1~4
A kind of Arabic gum graphene oxide flocculant aid includes Arabic gum graphene oxide microcapsules and dispersant.Ah
It includes core material and wall material to draw primary glue graphene oxide microcapsules, and core material is graphene oxide, and wall material is Arabic gum.
In each embodiment and comparative example, dosage (A), the dosage of dispersant of Arabic gum graphene oxide microcapsules
(B), the design parameters such as mass ratio (D) of the type (C), wall material of dispersant and core material are as shown in table 1.
The preparation method of Arabic gum graphene oxide flocculant aid includes the following steps:
S1. Arabic gum graphene oxide microcapsules are prepared, are included the following steps:
S11. graphene oxide is placed in ultrasonic disperse in pure water, the ratio of graphene oxide and pure water is 0.1g:
10ml obtains graphene oxide dispersion;
S12. wall material is made into the solution that mass fraction is 30wt%, gained graphene oxide dispersion is added, in temperature
Under the nitrogen atmosphere for being 1MPa for 35 DEG C, pressure, 30min, mixing speed 800r/min are stirred.
S13. after stirring terminates, solid product is collected in filtering, and freeze-drying is micro- to get Arabic gum graphene oxide
Capsule.
S2. Arabic gum graphene oxide microcapsules are mixed with dispersant according to the above ratio.
Table 1
Embodiment 8
As different from Example 1, in the present embodiment the preparation method of Arabic gum graphene oxide microcapsules include with
Lower step:
S11. graphene oxide is placed in ultrasonic disperse in pure water, the ratio of graphene oxide and pure water is 0.1g:
10ml obtains graphene oxide dispersion;
S12. wall material is made into the solution that mass fraction is 30wt%, gained graphene oxide dispersion is added, in temperature
Under the nitrogen atmosphere for being 0.5MPa for 35 DEG C, pressure, 30min is stirred, mixing speed is 800 r/min.
S13. after stirring terminates, solid product is collected in filtering, and freeze-drying is micro- to get Arabic gum graphene oxide
Capsule.
Other Step By Condition parameters are same as Example 1.
Embodiment 9
As different from Example 1, in the present embodiment the preparation method of Arabic gum graphene oxide microcapsules include with
Lower step:
S11. graphene oxide is placed in ultrasonic disperse in pure water, the ratio of graphene oxide and pure water is 0.1g:
10ml obtains graphene oxide dispersion;
S12. wall material is made into the solution that mass fraction is 30wt%, gained graphene oxide dispersion is added, in temperature
Under the nitrogen atmosphere for being 2MPa for 35 DEG C, pressure, 30min, mixing speed 800r/min are stirred.
S13. after stirring terminates, solid product is collected in filtering, and freeze-drying is micro- to get Arabic gum graphene oxide
Capsule.
Other Step By Condition parameters are same as Example 1.
Embodiment 10
As different from Example 1, in the present embodiment the preparation method of Arabic gum graphene oxide microcapsules include with
Lower step:
S11. graphene oxide is placed in ultrasonic disperse in pure water, the ratio of graphene oxide and pure water is 0.1g:
10ml obtains graphene oxide dispersion;
S12. wall material is made into the solution that mass fraction is 30wt%, gained graphene oxide dispersion is added, in temperature
Under the nitrogen atmosphere for being 1MPa for 30 DEG C, pressure, 30min, mixing speed 1500r/min are stirred.
S13. after stirring terminates, solid product is collected in filtering, and freeze-drying is micro- to get Arabic gum graphene oxide
Capsule.
Other Step By Condition parameters are same as Example 1.
Embodiment 11
As different from Example 1, in the present embodiment the preparation method of Arabic gum graphene oxide microcapsules include with
Lower step:
S11. graphene oxide is placed in ultrasonic disperse in pure water, the ratio of graphene oxide and pure water is 0.1g:
10ml obtains graphene oxide dispersion;
S12. wall material is made into the solution that mass fraction is 30wt%, gained graphene oxide dispersion is added, in temperature
Under the nitrogen atmosphere for being 1MPa for 45 DEG C, pressure, 30min, mixing speed 800r/min are stirred.
S13. after stirring terminates, solid product is collected in filtering, and freeze-drying is micro- to get Arabic gum graphene oxide
Capsule.
Other Step By Condition parameters are same as Example 1.
Comparative example 5
As different from Example 1, in the present embodiment the preparation method of Arabic gum graphene oxide microcapsules include with
Lower step:
S11. graphene oxide is placed in ultrasonic disperse in pure water, the ratio of graphene oxide and pure water is 0.1g:
10ml obtains graphene oxide dispersion;
S12. wall material is made into the solution that mass fraction is 30wt%, gained graphene oxide dispersion is added, in temperature
Be for 35 DEG C, pressure normal pressure nitrogen atmosphere under, stir 30min, mixing speed 800r/min.
S13. after stirring terminates, solid product is collected in filtering, and freeze-drying is micro- to get Arabic gum graphene oxide
Capsule.
Other conditional parameters are same as Example 1.
Comparative example 6
As different from Example 1, in the present embodiment the preparation method of Arabic gum graphene oxide microcapsules include with
Lower step:
S11. graphene oxide is placed in ultrasonic disperse in pure water, the ratio of graphene oxide and pure water is 0.1g:
10ml obtains graphene oxide dispersion;
S12. wall material is made into the solution that mass fraction is 30wt%, gained graphene oxide dispersion is added, in temperature
Under the nitrogen atmosphere for being 3MPa for 35 DEG C, pressure, 30min, mixing speed 800r/min are stirred.
S13. after stirring terminates, solid product is collected in filtering, and freeze-drying is micro- to get Arabic gum graphene oxide
Capsule.
Other Step By Condition parameters are same as Example 1.
Test
Water purification performance survey is carried out using Arabic gum graphene oxide flocculant aid obtained by the various embodiments described above and comparative example
Examination, condition are as follows:Take identical outdoor elements polluted-water water sample (abbreviation raw water, the turbidity of raw water is 820NTU after tested,
Turbidity tests foundation《The measurement of GB 13200-1991 water turbidities》), flocculant and the flocculation of Arabic gum graphene oxide are helped
Certain usage ratio is pressed in agent, adds in the water sample of isometric raw water (stirring 5min), is calculated when the turbidity of water sample is down to
The dosage of required flocculant when 1NTU, and record static balance time (stopping the used time to settlement stability after stirring).
Flocculant chooses polyacrylamide, and flocculant is 9 in mass ratio with Arabic gum graphene oxide flocculant aid:1
Ratio add in the water sample of isometric raw water.In addition, using be added without Arabic gum graphene oxide flocculant aid as pair
As usual.Shown in test result table 2:
Table 2
Obviously, the above embodiment of the present invention be only to clearly illustrate example of the present invention, and not be pair
The restriction of embodiments of the present invention.For those of ordinary skill in the art, may be used also on the basis of the above description
To make other variations or changes in different ways.There is no necessity and possibility to exhaust all the enbodiments.It is all this
All any modification, equivalent and improvement etc., should be included in the claims in the present invention made by within the spirit and principle of invention
Protection domain within.
Claims (8)
1. a kind of Arabic gum graphene oxide flocculant aid, which is characterized in that including following component in parts by weight:
75 ~ 85 parts of Arabic gum graphene oxide microcapsules, 15 ~ 25 parts of dispersant;The Arabic gum graphene oxide microcapsules
The mass ratio of wall material including core material and the package core material, the wall material and core material is 0.5:1~2:1;The core material is oxidation
Graphene, the wall material are Arabic gum.
2. Arabic gum graphene oxide flocculant aid according to claim 1, which is characterized in that including it is following by weight
The component that number calculates:80 parts of Arabic gum graphene oxide microcapsules, 20 parts of dispersant.
3. Arabic gum graphene oxide flocculant aid according to claim 1, which is characterized in that the wall material and core material
Mass ratio be 1:1.
4. Arabic gum graphene oxide flocculant aid according to claim 1 or 2, which is characterized in that the dispersant
For one or more of polyvinyl alcohol, polyethylene, pyrrolidones.
5. Arabic gum graphene oxide flocculant aid according to claim 4, which is characterized in that the dispersant is poly-
The mixture of vinyl alcohol and pyrrolidones;The mass ratio of the polyvinyl alcohol and pyrrolidones is 1:2.
6. Arabic gum graphene oxide flocculant aid according to claim 1, which is characterized in that the Arabic gum oxygen
The preparation method of graphite alkene microcapsules includes the following steps:
S1. graphene oxide is placed in ultrasonic disperse in pure water, obtains graphene oxide dispersion;
S2. wall material is added to the graphene oxide dispersion, in the indifferent gas that temperature is 30 ~ 45 DEG C, pressure is 0.5 ~ 2MPa
Under atmosphere, 30 ~ 60 min are stirred, mixing speed is 800 ~ 1500 r/min;
S3. after stirring terminates, solid product is collected in filtering, is freeze-dried to get Arabic gum graphene oxide microcapsules.
7. the preparation method of any one of the claim 1 ~ 6 Arabic gum graphene oxide flocculant aid, which is characterized in that packet
Include following steps:
S1. Arabic gum graphene oxide microcapsules are prepared;
S2. Arabic gum graphene oxide microcapsules are mixed with dispersant in proportion.
8. application of any one of the claim 1 ~ 6 Arabic gum graphene oxide flocculant aid in sewage disposal.