CN108742090A - 一种教室用隔热透光窗帘及制备方法 - Google Patents
一种教室用隔热透光窗帘及制备方法 Download PDFInfo
- Publication number
- CN108742090A CN108742090A CN201810538827.6A CN201810538827A CN108742090A CN 108742090 A CN108742090 A CN 108742090A CN 201810538827 A CN201810538827 A CN 201810538827A CN 108742090 A CN108742090 A CN 108742090A
- Authority
- CN
- China
- Prior art keywords
- parts
- curtain
- fibers
- face layer
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种教室用隔热透光窗帘，包括外层的深色帘和内层的浅色帘，深色帘包括竹炭纤维面层、芬芳面层和负离子释放层，芬芳面层按重量份数包括50~60份棉纤维、20~30份黄柏皮纤维、10~20份楝树皮纤维、10~20份竹纤维；浅色帘包括帘布本体和穿设在帘布本体上的玻璃微珠，帘布本体按重量份数包括45~55份棉纤维、25~35份麻纤维和20~30份调温纤维，制备方法如下：将竹炭纤维面层和芬芳面层的两侧边沿及底边沿缝合，上边沿活动连接，负离子释放层设置在竹炭纤维面层和芬芳面层之间，形成具有夹心结构的深色帘；在玻璃微珠外镀反光隔热涂层，并将其穿设在帘布本体上，形成浅色帘；本发明既不影响教室的光线明亮度，又可以避免强光直射对学生造成干扰，同时还可以净化教室内空气。
Description
技术领域
本发明涉及教学用品领域，更具体地说，涉及一种教室用隔热透光窗帘及制备方法。
背景技术
目前我国窗帘材料比较传统，同时具有良好的隔热保温效果和透光效果的窗帘材料或窗帘比较少见，尤其是在学校的教室内，窗帘的设置至关重要，如果窗帘过于厚重，会遮挡光线，或者影响通风效果，只能通过灯光来辅助照明或者空调辅助换气，如果过于轻薄，又起不到遮挡强光、炎热的作用，室内的酷热和刺眼的强光照射会影响学生的学习效率，白天开着空调和照明，会造成大量的能源消耗，而且日光能提供真正的全光谱光线，是兼顾生理及心理的健康光线，长时间无日光照射，会影响人体正常生理周期，一直依赖空调也会引发空调病发病率，会极大地影响了学生的身体健康；
随着节能环保材料的迅猛发展、新型化纤技术的成熟、纺织技术的提升，近年来功能性的窗帘有了飞跃的发展，为了给学生营造一个良好的学习环境，因此需要窗帘具备以下功能：一是可以隔绝正午的强光直射，减少热量射入教室内，二是可以保证教室内的光线明亮，不会由于厚重窗帘的遮挡影响采光，三是教室内学生众多，特别是处于青春期的青少年，运动量大，室内空气不是很新鲜洁净，因此需要通过窗户这一与外界换气通道进行净化，通过窗帘提高室内的空气质量，营造“绿色、自然、健康”的环境，因此，急需一种可以满足上述功能的教室用隔热透光窗帘及制备方法，为学生营造一个优美的学习环境，提高学生的学习效率。
发明内容
有鉴于此，为解决上述现有技术的不足，本发明的目的在于提供一种教室用隔热透光窗帘及制备方法，既不影响教室的光线明亮度，又可以避免强光直射对学生造成干扰，同时还可以净化教室内空气。
为实现上述目的，本发明所采用的技术方案是：
一种教室用隔热透光窗帘，包括位于外层的深色帘和位于内层的浅色帘，所述深色帘包括竹炭纤维面层、芬芳面层和负离子释放层，所述竹炭纤维面层和芬芳面层的两侧边沿及底边沿缝合，上边沿活动连接，所述负离子释放层设置在所述竹炭纤维面层和芬芳面层之间，形成夹心结构；所述芬芳面层按重量份数包括50~60份棉纤维、20~30份黄柏皮纤维、10~20份楝树皮纤维、10~20份竹纤维；
所述浅色帘包括帘布本体和若干穿设在所述帘布本体上的玻璃微珠，所述玻璃微珠外镀有反光隔热涂层，所述帘布本体按重量份数包括45~55份棉纤维、25~35份麻纤维和20~30份调温纤维，所述反光隔热涂层按重量份数包括30~50份树脂、10~20份氧化钛粉、5~10份氧化锌粉、3~8份电气石、8~15份硅藻土、3~5份纳米银离子、10~20份外加剂。
进一步的，所述帘布本体由纬纱、主经纱和副经纱编织而成，所述玻璃微珠的直径为1~3mm，所述玻璃微珠穿设在所述主经纱上，且两根所述纬纱之间的主经纱上仅穿设一颗玻璃微珠。
进一步的，所述负离子释放层由无纺布袋和蛋白石、电气石颗粒制成。
进一步的，所述外加剂按重量份数包括2~3份分散剂、3~5份消泡剂和5~15份颜料。
一种教室用隔热透光窗帘的制备方法，包括以下步骤：
（1）将竹炭制成纳米竹炭微粉，将纳米竹炭微粉加入涤纶原浆中，通过纺棉工艺制成竹炭纤维面层；
（2）按重量份数，取50~60份棉纤维、20~30份黄柏皮纤维、10~20份楝树皮纤维、10~20份竹纤维，混纺制得织物，即可制得芬芳面层；
（3）将蛋白石、电气石破碎成0.5~2mm的颗粒，将其装入无纺布袋中，并压制成真空薄片状的负离子释放层，备用；
（4）将竹炭纤维面层和芬芳面层裁剪成大小相同的尺寸，并将二者的两个侧边沿及下边沿缝合，在上边沿装上暗扣或拉链，再将真空薄片状的负离子释放层放入竹炭纤维面层和芬芳面层之间，扣上暗扣或者拉链，即可制得具有夹心结构的深色帘；
（5）按重量份数，取45~55份棉纤维、25~35份麻纤维和20~30份调温纤维，分别制成纬纱、主经纱和副经纱；
（6）按重量份数取30~50份树脂、10~20份氧化钛粉、5~10份氧化锌粉、3~8份电气石、8~15份硅藻土、3~5份纳米银离子、2~3份分散剂、3~5份消泡剂和5~15份颜料，放入20~30份水中调配成反光隔热颜料；制备粒径为1~3mm的带孔玻璃微珠，在其表面喷涂反光隔热颜料，形成厚度为50~100μm的反光隔热涂层；
（7）在主经纱上穿设带有反光隔热涂层的玻璃微珠，和纬纱、副经纱纺织成浅色帘，并使浅色帘的纬纱之间的主经纱上仅穿设一颗玻璃微珠；
（8）将深色帘安装在外层，将浅色帘安装在内层，即可制得教室用隔热透光窗帘。
进一步的，涤纶原浆中加入防晒调理液，所述防晒调理液由水性聚氨酯、氧化锌、二氧化钛、光稳定剂、抗氧剂和水合成。
进一步的，所述步骤（2）中，先将棉纤维、黄柏皮纤维、楝树皮纤维、竹纤维放入微波设备，在60~70℃杀虫杀菌处理30~45s，然后放入烘箱烘干；取25~30份棉纤维、10~20份楝树皮纤维、5~10份竹纤维作为经线，取25~30份棉纤维、20~30份黄柏皮纤维、5~10份竹纤维作为纬线，混纺制得织物。
进一步的，所述步骤（6）中，所述颜料为白色。
进一步的，所述步骤（6）中，按重量份数取30~50份树脂、10~20份氧化钛粉、5~10份氧化锌粉、3~8份电气石、8~15份硅藻土、3~5份纳米银离子、2~3份分散剂、3~5份消泡剂，放入20~30份水中调配成混合液，重复调配上述混合液多份，然后分别在各组混合液中加入取不同颜色的颜料5~15份，调配成不同颜色的反光隔热颜料，将玻璃微珠分为多组，每组分别喷涂一种颜色，形成具有多种颜色的玻璃微珠。
本发明的有益效果是：
本发明的教室用隔热透光窗帘，分为外层的深色帘和内层的浅色帘，深色帘又分为竹炭纤维面层、芬芳面层和负离子释放层，竹炭纤维面层位于最外层，芬芳面层设置在里层，负离子释放层设置在中间形成夹心结构；
首先，深色帘中，由于竹炭纤维颜色较深，碳质结构致密、比重大、孔隙多、矿物质含量丰富，具有很强的吸附分解能力，能发挥抑菌功能，设置在最外层，可以阻挡强光，同时还将竹炭纤维面层经过特殊防晒处理，使其具有一定的抗UV功能，既可有效隔离紫外线伤害，又可减缓竹炭纤维面层直面强光照射带来的老化、强度降低的问题；芬芳面层中添加有竹纤维、棉纤维、黄柏皮纤维、楝树皮纤维，既可以延缓窗帘由于清洗和日晒导致的起球及老化，提高窗帘的强度，延长窗帘的使用寿命，又可以通过黄柏皮纤维、楝树皮纤维独特的气味及功效增加窗帘的抑菌性能和植物香味，配合中间层设置的负离子释放层，可以起到清除尘埃、杀灭细菌、净化空气的作用，为学生提供一个健康、清新的学习环境；
其次，浅色帘由帘布本体和若干穿设在帘布本体上的玻璃微珠组成，帘布本体由纬纱、主经纱和副经纱编织而成，玻璃微珠穿设在主经纱上，且两根纬纱之间的主经纱上仅穿设一颗玻璃微珠，形成纱线与玻璃微珠编织的结构；其中，帘布本体中含有一定量的调温纤维，属于相变材料，使窗帘具有对冷、热环境能自主调整，具有双向温度调节和舒适性的功能，可主动、智能的改变温度，可在夏天起到适当的清凉、镇定的效果，冬天起到保温的效果；此外，玻璃微珠外镀有反光隔热涂层，当经过深色帘过滤后的阳光照射在浅色帘上时，一方面可通过玻璃微珠反射部分阳光，另一方面还可通过纱线编织的、具有一定孔隙率的帘布本体透过部分阳光，既可避免强光直射进教室内、将热量反射走保持室内清凉，又可保持教室的光线需求解决了现有的窗帘如果防晒必然遮光、室内昏暗的问题；综上可知，本发明的窗帘通过外层深色帘阻隔强光，内层浅色帘上的玻璃微珠反射部分阳光，通过浅色帘布本体透过部分阳光，既可避免强光直射进教室内，又可保持教室的光亮。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为教室用隔热透光窗帘的双层结构示意图；
图2为负离子释放层的结构示意图；
图3为浅色帘的结构示意图；
附图标记：1、深色帘，2、浅色帘，3、竹炭纤维面层，4、芬芳面层，5、负离子释放层，501、无纺布袋，502、蛋白石、电气石颗粒，6、帘布本体，601、纬纱，602、主经纱，603、副经纱，7、玻璃微珠。
具体实施方式
下面给出具体实施例，对本发明的技术方案作进一步清楚、完整、详细地说明。本实施例是以本发明技术方案为前提的最佳实施例，但本发明的保护范围不限于下述的实施例。
实施例1
一种教室用隔热透光窗帘，包括位于外层的深色帘1和位于内层的浅色帘2，通过外层的深色帘1阻隔强光，内层的浅色帘2上的玻璃微珠反射部分阳光，通过浅色帘布本体透过部分阳光，既可避免强光直射进教室内，又可保持教室的光亮；
所述深色帘1包括竹炭纤维面层3、芬芳面层4和负离子释放层5，所述竹炭纤维面层3和芬芳面层4的两侧边沿及底边沿缝合，上边沿活动连接，所述负离子释放层5由无纺布袋501和蛋白石、电气石颗粒502制成，设置在所述竹炭纤维面层3和芬芳面层4之间，形成夹心结构，由于竹炭纤维颜色较深，碳质结构致密、比重大、孔隙多、矿物质含量丰富，具有很强的吸附分解能力，能发挥抑菌功能，同时还将竹炭纤维面层3经过特殊防晒处理，使其具有一定的抗UV功能，通过深色的竹炭纤维面层3阻隔强光，可有效隔离紫外线伤害；所述芬芳面层4按重量份数包括50份棉纤维、20份黄柏皮纤维、10份楝树皮纤维、10份竹纤维；芬芳面层4中添加的竹纤维、棉纤维、黄柏皮纤维、楝树皮纤维，可以延缓窗帘由于清洗和日晒导致的起球及老化，提高窗帘的强度，延长窗帘的使用寿命，又可以通过黄柏皮纤维、楝树皮纤维独特的气味及功效增加窗帘的抑菌性能和植物香味，配合中间层设置的负离子释放层5，可以起到清除尘埃、杀灭细菌、净化空气的作用，为学生提供一个健康、清新的学习环境；
所述浅色帘2包括帘布本体6和若干穿设在所述帘布本体6上的玻璃微珠7，所述帘布本体6由纬纱601、主经纱602和副经纱603编织而成，所述玻璃微珠7的直径为1mm，所述玻璃微珠7穿设在所述主经纱602上，且两根所述纬纱601之间的主经纱602上仅穿设一颗玻璃微珠7；所述帘布本体6按重量份数包括45份棉纤维、25份麻纤维和20份调温纤维，调温纤维属于相变材料，使窗帘具有对冷、热环境能自主调整，具有双向温度调节和舒适性的功能，可主动、智能的改变温度，可在夏天起到适当的清凉、镇定的效果，冬天起到保温的效果；所述玻璃微珠7外镀有反光隔热涂层，所述隔热涂层按重量份数包括30份树脂、10份氧化钛粉、5份氧化锌粉、3份电气石、8份硅藻土、3份纳米银离子、10份外加剂，所述外加剂按重量份数包括2份分散剂、3份消泡剂和5份颜料；玻璃微珠7外镀有反光隔热涂层，当经过深色帘1过滤后的阳光照射在浅色帘2上时，一方面可通过玻璃微珠7反射部分阳光，另一方面还可通过纱线编织的、具有一定孔隙率的帘布本体6透过部分阳光，既可避免强光直射进教室内、将热量反射走保持室内清凉，又可保持教室的光线需求解决了现有的窗帘如果防晒必然遮光、室内昏暗的问题。
一种教室用隔热透光窗帘的制备方法，包括以下步骤：
（1）将竹炭制成纳米竹炭微粉，制备防晒调理液，将纳米竹炭微粉和防晒调理液加入涤纶原浆中，通过纺棉工艺制成竹炭纤维面层，所述防晒调理液由水性聚氨酯、氧化锌、二氧化钛、光稳定剂、抗氧剂和水合成；将竹炭纤维面层增加防晒处理，既可有效隔离紫外线伤害，又可减缓竹炭纤维面层直面强光照射带来的老化、强度降低的问题，提高使用寿命；
（2）按重量份数，取50份棉纤维、20份黄柏皮纤维、10份楝树皮纤维、10份竹纤维，先将棉纤维、黄柏皮纤维、楝树皮纤维、竹纤维放入微波设备，在60~70℃杀虫杀菌处理30~45s，然后放入烘箱烘干；取25份棉纤维、10份楝树皮纤维、5份竹纤维作为经线，取25份棉纤维、20份黄柏皮纤维、5份竹纤维作为纬线，混纺制得织物，即可制得芬芳面层；植物树皮原料丰富，成本低，一般都会作为废料处理，在本发明中作为原料添加进棉纤维中，经过微波处理后，可杀死纤维上附着的虫卵、细菌，使获得的面层干净、具有特殊清香味，醒脑清新；
（3）将蛋白石、电气石破碎成0.5~2mm的颗粒，将其装入无纺布袋中，并压制成真空薄片状的负离子释放层，备用；该负离子释放层可压制为条状负离子和压线间隔设置的形状，也可压制成块状负离子和压线间隔设置的形状；
（4）将竹炭纤维面层和芬芳面层裁剪成大小相同的尺寸，并将二者的两个侧边沿及下边沿缝合，在上边沿装上暗扣或拉链，再将真空薄片状的负离子释放层放入竹炭纤维面层和芬芳面层之间，扣上暗扣或者拉链，即可制得具有夹心结构的深色帘；由暗扣或者拉链结构将深色帘设置成夹心结构，方便拆卸，进行清洗时可将负离子释放层取出，非常方便；
（5）按重量份数，取45份棉纤维、25份麻纤维和20份调温纤维，分别制成纬纱、主经纱和副经纱；
（6）按重量份数取30份树脂、10份氧化钛粉、5份氧化锌粉、3份电气石、8份硅藻土、3份纳米银离子、2份分散剂、3份消泡剂和5份白色颜料，放入20份水中调配成白色反光隔热颜料；制备粒径为1mm的带孔玻璃微珠，在其表面喷涂反光隔热颜料，形成厚度为50μm的反光隔热涂层；帘布本体为浅色，点缀白色的玻璃微珠，颜色清爽，看起来赏心悦目；
（7）在主经纱上穿设带有反光隔热涂层的玻璃微珠，和纬纱、副经纱纺织成浅色帘，并使浅色帘的纬纱之间的主经纱上仅穿设一颗玻璃微珠、相邻两根主经纱之间间隔设置1根副经纱，形成玻璃微珠穿设较为密集的浅色帘；
（8）将深色帘安装在外层，将浅色帘安装在内层，即可制得教室用隔热透光窗帘。
实施例2
一种教室用隔热透光窗帘，包括位于外层的深色帘1和位于内层的浅色帘2，通过外层的深色帘1阻隔强光，内层的浅色帘2上的玻璃微珠反射部分阳光，通过浅色帘布本体透过部分阳光，既可避免强光直射进教室内，又可保持教室的光亮；
所述深色帘1包括竹炭纤维面层3、芬芳面层4和负离子释放层5，所述竹炭纤维面层3和芬芳面层4的两侧边沿及底边沿缝合，上边沿活动连接，所述负离子释放层5由无纺布袋501和蛋白石、电气石颗粒502制成，设置在所述竹炭纤维面层3和芬芳面层4之间，形成夹心结构，由于竹炭纤维颜色较深，碳质结构致密、比重大、孔隙多、矿物质含量丰富，具有很强的吸附分解能力，能发挥抑菌功能，同时还将竹炭纤维面层3经过特殊防晒处理，使其具有一定的抗UV功能，通过深色的竹炭纤维面层3阻隔强光，可有效隔离紫外线伤害；述芬芳面层4按重量份数包括55份棉纤维、25份黄柏皮纤维、15份楝树皮纤维、15份竹纤维；芬芳面层4中添加的竹纤维、棉纤维、黄柏皮纤维、楝树皮纤维，可以延缓窗帘由于清洗和日晒导致的起球及老化，提高窗帘的强度，延长窗帘的使用寿命，又可以通过黄柏皮纤维、楝树皮纤维独特的气味及功效增加窗帘的抑菌性能和植物香味，配合中间层设置的负离子释放层5，可以起到清除尘埃、杀灭细菌、净化空气的作用，为学生提供一个健康、清新的学习环境；
所述浅色帘2包括帘布本体6和若干穿设在所述帘布本体6上的玻璃微珠7，所述帘布本体6由纬纱601、主经纱602和副经纱603编织而成，所述玻璃微珠7的直径为2mm，所述玻璃微珠7穿设在所述主经纱602上，且两根所述纬纱601之间的主经纱602上仅穿设一颗玻璃微珠7；所述帘布本体6按重量份数包括50份棉纤维、30份麻纤维和25份调温纤维，调温纤维属于相变材料，使窗帘具有对冷、热环境能自主调整，具有双向温度调节和舒适性的功能，可主动、智能的改变温度，可在夏天起到适当的清凉、镇定的效果，冬天起到保温的效果；所述玻璃微珠7外镀有反光隔热涂层，所述隔热涂层按重量份数包括40份树脂、15份氧化钛粉、8份氧化锌粉、5份电气石、12份硅藻土、4份纳米银离子、15份外加剂，所述外加剂按重量份数包括2.5份分散剂、4份消泡剂和10份颜料；玻璃微珠7外镀有反光隔热涂层，当经过深色帘1过滤后的阳光照射在浅色帘2上时，一方面可通过玻璃微珠7反射部分阳光，另一方面还可通过纱线编织的、具有一定孔隙率的帘布本体6透过部分阳光，既可避免强光直射进教室内、将热量反射走保持室内清凉，又可保持教室的光线需求解决了现有的窗帘如果防晒必然遮光、室内昏暗的问题。
一种教室用隔热透光窗帘的制备方法，包括以下步骤：
（1）将竹炭制成纳米竹炭微粉，制备防晒调理液，将纳米竹炭微粉和防晒调理液加入涤纶原浆中，通过纺棉工艺制成竹炭纤维面层，所述防晒调理液由水性聚氨酯、氧化锌、二氧化钛、光稳定剂、抗氧剂和水合成；将竹炭纤维面层增加防晒处理，既可有效隔离紫外线伤害，又可减缓竹炭纤维面层直面强光照射带来的老化、强度降低的问题，提高使用寿命；
（2）按重量份数，取55份棉纤维、25份黄柏皮纤维、15份楝树皮纤维、15份竹纤维，先将棉纤维、黄柏皮纤维、楝树皮纤维、竹纤维放入微波设备，在60~70℃杀虫杀菌处理30~45s，然后放入烘箱烘干；取28份棉纤维、15份楝树皮纤维、8份竹纤维作为经线，取28份棉纤维、25份黄柏皮纤维、8份竹纤维作为纬线，混纺制得织物，即可制得芬芳面层；植物树皮原料丰富，成本低，一般都会作为废料处理，在本发明中作为原料添加进棉纤维中，经过微波处理后，可杀死纤维上附着的虫卵、细菌，使获得的面层干净、具有特殊清香味，醒脑清新；
（3）将蛋白石、电气石破碎成0.5~2mm的颗粒，将其装入无纺布袋中，并压制成真空薄片状的负离子释放层，备用；该负离子释放层可压制为条状负离子和压线间隔设置的形状，也可压制成块状负离子和压线间隔设置的形状；
（4）将竹炭纤维面层和芬芳面层裁剪成大小相同的尺寸，并将二者的两个侧边沿及下边沿缝合，在上边沿装上暗扣或拉链，再将真空薄片状的负离子释放层放入竹炭纤维面层和芬芳面层之间，扣上暗扣或者拉链，即可制得具有夹心结构的深色帘；由暗扣或者拉链结构将深色帘设置成夹心结构，方便拆卸，进行清洗时可将负离子释放层取出，非常方便；
（5）按重量份数，取50份棉纤维、30份麻纤维和25份调温纤维，分别制成纬纱、主经纱和副经纱；按重量份数，取100份水，然后放入15份松香、50份聚氨酯树脂 、8份润滑剂、4份抗静电剂、1份偶联剂，水浴加热至50~60℃，使混合物溶解形成润滑耐磨液，将纬纱、主经纱和副经纱放入润滑耐磨液中浸泡1~2h，取出干燥在表面形成润滑耐磨层，一方面在串设玻璃微珠时，会对主经纱造成摩擦，设置润滑耐磨层可以提高主经纱的平滑性，提高串珠过程的流畅性，另一方面在长期使用过程中，玻璃微珠和主经纱、副经纱及纬纱之间会相互摩擦，设置润滑耐磨层可提高纱线的耐磨性，提高帘布本体的使用寿命；
（6）按重量份数取40份树脂、15份氧化钛粉、8份氧化锌粉、5份电气石、12份硅藻土、4份纳米银离子、2.5份分散剂、4份消泡剂和10份白色颜料，放入25份水中调配成白色反光隔热颜料；制备粒径为2mm的带孔玻璃微珠，在其表面喷涂反光隔热颜料，形成厚度为80μm的反光隔热涂层；帘布本体为浅色，点缀白色的玻璃微珠，颜色清爽，看起来赏心悦目；
（7）在主经纱上穿设带有反光隔热涂层的玻璃微珠，和纬纱、副经纱纺织成浅色帘，并使浅色帘的纬纱之间的主经纱上仅穿设一颗玻璃微珠、相邻两根主经纱之间间隔设置2根以上副经纱，形成玻璃微珠穿设较为稀疏的浅色帘；
（8）将深色帘安装在外层，将浅色帘安装在内层，即可制得教室用隔热透光窗帘。
实施例3
一种教室用隔热透光窗帘，包括位于外层的深色帘1和位于内层的浅色帘2，通过外层的深色帘1阻隔强光，内层的浅色帘2上的玻璃微珠反射部分阳光，通过浅色帘布本体透过部分阳光，既可避免强光直射进教室内，又可保持教室的光亮；
所述深色帘1包括竹炭纤维面层3、芬芳面层4和负离子释放层5，所述竹炭纤维面层3和芬芳面层4的两侧边沿及底边沿缝合，上边沿活动连接，所述负离子释放层5由无纺布袋501和蛋白石、电气石颗粒502制成，设置在所述竹炭纤维面层3和芬芳面层4之间，形成夹心结构，由于竹炭纤维颜色较深，碳质结构致密、比重大、孔隙多、矿物质含量丰富，具有很强的吸附分解能力，能发挥抑菌功能，同时还将竹炭纤维面层3经过特殊防晒处理，使其具有一定的抗UV功能，通过深色的竹炭纤维面层3阻隔强光，可有效隔离紫外线伤害；述芬芳面层4按重量份数包括60份棉纤维、30份黄柏皮纤维、20份楝树皮纤维、20份竹纤维；芬芳面层4中添加的竹纤维、棉纤维、黄柏皮纤维、楝树皮纤维，可以延缓窗帘由于清洗和日晒导致的起球及老化，提高窗帘的强度，延长窗帘的使用寿命，又可以通过黄柏皮纤维、楝树皮纤维独特的气味及功效增加窗帘的抑菌性能和植物香味，配合中间层设置的负离子释放层5，可以起到清除尘埃、杀灭细菌、净化空气的作用，为学生提供一个健康、清新的学习环境；
所述浅色帘2包括帘布本体6和若干穿设在所述帘布本体6上的玻璃微珠7，所述帘布本体6由纬纱601、主经纱602和副经纱603编织而成，所述玻璃微珠7的直径为3mm，所述玻璃微珠7穿设在所述主经纱602上，且两根所述纬纱601之间的主经纱602上仅穿设一颗玻璃微珠7；所述帘布本体6按重量份数包括55份棉纤维、35份麻纤维和30份调温纤维，调温纤维属于相变材料，使窗帘具有对冷、热环境能自主调整，具有双向温度调节和舒适性的功能，可主动、智能的改变温度，可在夏天起到适当的清凉、镇定的效果，冬天起到保温的效果；所述玻璃微珠7外镀有反光隔热涂层，所述隔热涂层按重量份数包括50份树脂、20份氧化钛粉、10份氧化锌粉、8份电气石、15份硅藻土、5份纳米银离子、20份外加剂，所述外加剂按重量份数包括3份分散剂、5份消泡剂和15份颜料；玻璃微珠7外镀有反光隔热涂层，当经过深色帘1过滤后的阳光照射在浅色帘2上时，一方面可通过玻璃微珠7反射部分阳光，另一方面还可通过纱线编织的、具有一定孔隙率的帘布本体6透过部分阳光，既可避免强光直射进教室内、将热量反射走保持室内清凉，又可保持教室的光线需求解决了现有的窗帘如果防晒必然遮光、室内昏暗的问题。
一种教室用隔热透光窗帘的制备方法，包括以下步骤：
（1）将竹炭制成纳米竹炭微粉，制备防晒调理液，将纳米竹炭微粉和防晒调理液加入涤纶原浆中，通过纺棉工艺制成竹炭纤维面层，所述防晒调理液由水性聚氨酯、氧化锌、二氧化钛、光稳定剂、抗氧剂和水合成；将竹炭纤维面层增加防晒处理，既可有效隔离紫外线伤害，又可减缓竹炭纤维面层直面强光照射带来的老化、强度降低的问题，提高使用寿命；
（2）按重量份数，取60份棉纤维、30份黄柏皮纤维、20份楝树皮纤维、20份竹纤维，先将棉纤维、黄柏皮纤维、楝树皮纤维、竹纤维放入微波设备，在60~70℃杀虫杀菌处理30~45s，然后放入烘箱烘干；取30份棉纤维、20份楝树皮纤维、10份竹纤维作为经线，取30份棉纤维、30份黄柏皮纤维、10份竹纤维作为纬线，混纺制得织物，即可制得芬芳面层；植物树皮原料丰富，成本低，一般都会作为废料处理，在本发明中作为原料添加进棉纤维中，经过微波处理后，可杀死纤维上附着的虫卵、细菌，使获得的面层干净、具有特殊清香味，醒脑清新；
（3）将蛋白石、电气石破碎成0.5~2mm的颗粒，将其装入无纺布袋中，并压制成真空薄片状的负离子释放层，备用；该负离子释放层可压制为条状负离子和压线间隔设置的形状，也可压制成块状负离子和压线间隔设置的形状；
（4）将竹炭纤维面层和芬芳面层裁剪成大小相同的尺寸，并将二者的两个侧边沿及下边沿缝合，在上边沿装上暗扣或拉链，再将真空薄片状的负离子释放层放入竹炭纤维面层和芬芳面层之间，扣上暗扣或者拉链，即可制得具有夹心结构的深色帘；由暗扣或者拉链结构将深色帘设置成夹心结构，方便拆卸，进行清洗时可将负离子释放层取出，非常方便；
（5）按重量份数，取55份棉纤维、35份麻纤维和30份调温纤维，分别制成纬纱、主经纱和副经纱；
（6）按重量份数取50份树脂、20份氧化钛粉、10份氧化锌粉、8份电气石、15份硅藻土、5份纳米银离子、3份分散剂、5份消泡剂，放入30份水中调配成混合液，重复调配上述混合液多份，然后分别在各组混合液中加入取不同颜色的颜料15份，调配成不同颜色的反光隔热颜料；制备粒径为3mm的带孔玻璃微珠，将玻璃微珠分为多组，每组分别喷涂一种颜色，形成具有厚度为100μm的反光隔热涂层、多种颜色的玻璃微珠；帘布本体为浅色，点缀不同颜色的玻璃微珠，可以增加窗帘的趣味性；
（7）在主经纱上穿设带有反光隔热涂层的玻璃微珠，和纬纱、副经纱纺织成浅色帘，并使浅色帘的纬纱之间的主经纱上仅穿设一颗玻璃微珠、相邻两根主经纱之间间隔设置1根副经纱，形成玻璃微珠穿设较为密集的浅色帘；
（8）将深色帘安装在外层，将浅色帘安装在内层，即可制得教室用隔热透光窗帘。
将本发明实施例1的窗帘与市面上出售的隔热窗帘A、普通窗帘B相比，其中隔热性以窗外与室内的温差作为测试标准，温差越大，隔热性越好，防晒性以防晒指数UPF为测试标准，UPF越高防晒性越好，具体优点如表1所示：
由上可知，本发明的窗帘一方面由于竹炭纤维面层经过特殊防晒处理，使其具有一定的抗UV功能，既可有效隔离紫外线伤害，另一方面由于帘布本体中含有一定量的调温纤维，属于相变材料，使窗帘具有对冷、热环境能自主调整，具有双向温度调节和舒适性的功能，可主动、智能的改变温度，可在夏天起到适当的清凉、镇定的效果，冬天起到保温的效果，同时玻璃微珠外镀有反光隔热涂层，当经过深色帘过滤后的阳光照射在浅色帘上时，一是可通过玻璃微珠反射部分阳光，二是还可通过纱线编织的、具有一定孔隙率的帘布本体透过部分阳光，既可避免强光直射进教室内、将热量反射走保持室内清凉，又可保持教室的光线需求，解决了现有的窗帘如果隔热必然遮光、室内昏暗的问题，将其用于教室内，既不影响教室的光线明亮度，又可以避免强光直射对学生造成干扰，同时还可以净化教室内空气。
以上显示和描述了本发明的主要特征、基本原理以及本发明的优点。本行业技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会根据实际情况有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (9)
1.一种教室用隔热透光窗帘，其特征在于，包括位于外层的深色帘（1）和位于内层的浅色帘（2），所述深色帘（1）包括竹炭纤维面层（3）、芬芳面层（4）和负离子释放层（5），所述竹炭纤维面层（3）和芬芳面层（4）的两侧边沿及底边沿缝合，上边沿活动连接，所述负离子释放层（5）设置在所述竹炭纤维面层（3）和芬芳面层（4）之间，形成夹心结构；所述芬芳面层（4）按重量份数包括50~60份棉纤维、20~30份黄柏皮纤维、10~20份楝树皮纤维、10~20份竹纤维；
所述浅色帘（2）包括帘布本体（6）和若干穿设在所述帘布本体（6）上的玻璃微珠（7），所述玻璃微珠（7）外镀有反光隔热涂层，所述帘布本体（6）按重量份数包括45~55份棉纤维、25~35份麻纤维和20~30份调温纤维，所述反光隔热涂层按重量份数包括30~50份树脂、10~20份氧化钛粉、5~10份氧化锌粉、3~8份电气石、8~15份硅藻土、3~5份纳米银离子、10~20份外加剂。
2.根据权利要求1所述的一种教室用隔热透光窗帘，其特征在于，所述帘布本体（6）由纬纱（601）、主经纱（602）和副经纱（603）编织而成，所述玻璃微珠（7）的直径为1~3mm，所述玻璃微珠（7）穿设在所述主经纱（602）上，且两根所述纬纱（601）之间的主经纱（602）上仅穿设一颗玻璃微珠（7）。
3.根据权利要求1所述的一种教室用隔热透光窗帘，其特征在于，所述负离子释放层（5）由无纺布袋（501）和蛋白石、电气石颗粒（502）制成。
4.根据权利要求1所述的一种教室用隔热透光窗帘，其特征在于，所述外加剂按重量份数包括2~3份分散剂、3~5份消泡剂和5~15份颜料。
5.根据权利要求1所述的一种教室用隔热透光窗帘的制备方法，其特征在于，包括以下步骤：
（1）将竹炭制成纳米竹炭微粉，将纳米竹炭微粉加入涤纶原浆中，通过纺棉工艺制成竹炭纤维面层；
（2）按重量份数，取50~60份棉纤维、20~30份黄柏皮纤维、10~20份楝树皮纤维、10~20份竹纤维，混纺制得织物，即可制得芬芳面层；
（3）将蛋白石、电气石破碎成0.5~2mm的颗粒，将其装入无纺布袋中，并压制成真空薄片状的负离子释放层，备用；
（4）将竹炭纤维面层和芬芳面层裁剪成大小相同的尺寸，并将二者的两个侧边沿及下边沿缝合，在上边沿装上暗扣或拉链，再将真空薄片状的负离子释放层放入竹炭纤维面层和芬芳面层之间，扣上暗扣或者拉链，即可制得具有夹心结构的深色帘；
（5）按重量份数，取45~55份棉纤维、25~35份麻纤维和20~30份调温纤维，分别制成纬纱、主经纱和副经纱；
（6）按重量份数取30~50份树脂、10~20份氧化钛粉、5~10份氧化锌粉、3~8份电气石、8~15份硅藻土、3~5份纳米银离子、2~3份分散剂、3~5份消泡剂和5~15份颜料，放入20~30份水中调配成反光隔热颜料；制备粒径为1~3mm的带孔玻璃微珠，在其表面喷涂反光隔热颜料，形成厚度为50~100μm的反光隔热涂层；
（7）在主经纱上穿设带有反光隔热涂层的玻璃微珠，和纬纱、副经纱纺织成浅色帘，并使浅色帘的纬纱之间的主经纱上仅穿设一颗玻璃微珠；
（8）将深色帘安装在外层，将浅色帘安装在内层，即可制得教室用隔热透光窗帘。
6.根据权利要求5所述的一种教室用隔热透光窗帘的制备方法，其特征在于，所述步骤（1）中，涤纶原浆中加入防晒调理液，所述防晒调理液由水性聚氨酯、氧化锌、二氧化钛、光稳定剂、抗氧剂和水合成。
7.根据权利要求1所述的一种教室用隔热透光窗帘的制备方法，其特征在于，所述步骤（2）中，先将棉纤维、黄柏皮纤维、楝树皮纤维、竹纤维放入微波设备，在60~70℃杀虫杀菌处理30~45s，然后放入烘箱烘干；取25~30份棉纤维、10~20份楝树皮纤维、5~10份竹纤维作为经线，取25~30份棉纤维、20~30份黄柏皮纤维、5~10份竹纤维作为纬线，混纺制得织物。
8.根据权利要求5所述的一种教室用隔热透光窗帘的制备方法，其特征在于，所述步骤（6）中，所述颜料为白色。
9.根据权利要求5所述的一种教室用隔热透光窗帘的制备方法，其特征在于，所述步骤（6）中，按重量份数取30~50份树脂、10~20份氧化钛粉、5~10份氧化锌粉、3~8份电气石、8~15份硅藻土、3~5份纳米银离子、2~3份分散剂、3~5份消泡剂，放入20~30份水中调配成混合液，重复调配上述混合液多份，然后分别在各组混合液中加入取不同颜色的颜料5~15份，调配成不同颜色的反光隔热颜料，将玻璃微珠分为多组，每组分别喷涂一种颜色，形成具有多种颜色的玻璃微珠。