CN108741333A - A kind of warmth-retaining clothing material - Google Patents
A kind of warmth-retaining clothing material Download PDFInfo
- Publication number
- CN108741333A CN108741333A CN201810397688.XA CN201810397688A CN108741333A CN 108741333 A CN108741333 A CN 108741333A CN 201810397688 A CN201810397688 A CN 201810397688A CN 108741333 A CN108741333 A CN 108741333A
- Authority
- CN
- China
- Prior art keywords
- copper powder
- warmth
- insulating layer
- clothing material
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of warmth-retaining clothing material, which is made of lining, insulating layer, the copper powder coating of insulating layer upper surface and outer shell fabric successively from inside to outside, and the lining is fleece fabric;The glass fibre cotton that the insulating layer is made of glass fibre and acrylic resin adhesive;The copper powder coating is made of copper powder and ethylene-propylene-diene monomer viscose binder, and room temperature far infrared transmissivity is 0.2~0.4;The outer shell fabric is windproof material.Material thermal conductivity is low in the present invention, has good hydrophobic performance, not absorbing sweat, good permeability, surface copper powder coating has extremely low room temperature far infrared transmissivity, and so strong that inhibit human body by heat loss through radiation, warming effect greatly improves, material overall structure is simple, soft comfortable, and lightweight is practical.
Description
Technical field
The present invention relates to a kind of dress materials more particularly to a kind of warmth-retaining clothing materials.
Background technology
The heat insulating material of warming clothing mainly has the cotton-wool that natural feather, animal skin, wool, cotton-wool and chemical fibre make, natural material
Expect that warming, bulkiness is good, but easy knot tying is blocking by force intolerant to hygroscopicity during damaging by worms, easily growing bacterium, use, makes its heat insulating ability
The shortcomings of variation;Fibers material bulkiness flexibility and heat insulating ability are all preferable, but easily occur boring hair phenomenon after washing.However it navigates
Vacant level ultra-fine fibre glass cotton just has intensity high in the case where adhesive is uniformly wrapped in fiber surface, and flexibility is good, heat conduction
Coefficient is low, can meet the warming demand of needed by human body, and the heat exchange between human body and environment is mainly right with heat transfer, heat in addition
Stream, heat radiation these three forms realize, research find when human body in it is static when heat radiation as main radiating mode to ring
Border discharges a large amount of heat, therefore control clothes can effectively manage human body to the radiance of human-body emitting normal temperature infrared line
Body temperature, therefore can thicken clothes to avoid passing through and protected to realize using inhibiting human body radiation heat dissipation improve warming effect
It is warm, cause thick and heavy clothes to fetter the action of people, dress is uncomfortable, and inaesthetic problem.
Chinese patent CN105150641A disclose it is a kind of be made of surface layer protective layer intermediate insulating layer and inner layer it is super
Insulation garment material, in-between insulating layer are that the multilayer materials such as compound polyimide fabric, warming filling fabric use
Warming filling fabric is senior middle school's empty class fiber, birds down fiber, aerogel material.This more structural thermal insulation materials have reached anti-
The effect of wind, waterproof, moisture-inhibiting, heat preservation, moisture absorption, heat release, but this structure filling causes clothes heavy and too fat to move, influences U.S.
It sees.
Chinese Patent Application No. 2013106529103 its be related to it is a kind of suitable for winter dress Far-infrared shell fabric of bluish dogbane
Insulation garment, including garment body, garment body are provided with solar panel behind, and solar panel and setting are in clothes
The accumulator of body interior connects, and is provided with multiple infrared heat-transfer devices in the interlayer of garment body, infrared heat-transfer device with
Accumulator be connected, the garment body is made of fabric, the fabric from the inside to the outside successively by far infrared layer, bluish dogbane layer and it is pure
Cotton fabric layer is total to three-decker closely compound composition, and far infrared coating is foam coating, may be implemented to reduce winter to clothes
The quantity of dress, and there is insulation effect, but its is complicated, durability is poor, and cleaning wearing is inconvenient.
Invention content
The present invention is directed to overcome the deficiencies of the prior art and provide a kind of warmth-retaining clothing material.
To realize the present invention purpose the technical solution adopted is that:A kind of warmth-retaining clothing material, it is characterised in that the guarantor
Package material is warmly taken to be made of lining, insulating layer, the copper powder coating of insulating layer upper surface and outer shell fabric successively from inside to outside,
The lining is fleece fabric;The insulating layer is the glass fibre and acrylic resin that average diameter is 0.2~1.5 μm
The glass fibre cotton of adhesive composition;The copper powder coating is 1 by mass ratio: the copper powder and ethylene propylene diene rubber of (2~5.5)
Adhesive forms, and room temperature far infrared transmissivity is 0.2~0.4;The outer shell fabric is windproof material.
Further, the insulation layer thickness is 0.8~3cm, and glass fibre cotton is in layered distribution, thickness 100~200
μm, surface density is 150~300g/m2。
Further, it is adhesive that the copper powder, which is coated with epoxidized ethylene-propylene-diene mischpolymer, and copper powder is filler, forms distribution
Uniform low emissivity coatings, copper powder mass fraction are 35%~45%, and coating layer thickness is 130~300 μm.
Further, the ethylene propylene diene rubber is epoxy-modified ethylene propylene diene rubber, and modifier components are:Toluene is (molten
Liquid mass fraction be 7%~9%), hydrogen peroxide (27~30mg/L), acetic acid (19.5~21.5mg/L), settled through absolute ethyl alcohol,
Distilled water cleans, and saturated sodium bicarbonate impregnates, and drying is made.
Further, the adhesive is made through emulsification treatment by epoxy-modified ethylene propylene diene rubber, emulsion group
Divide and weight ratio is:The epoxy-modified ethylene propylene diene rubber toluene solution that mass fraction is 12%: emulsifier Tween60: hydrogen-oxygen
Change potassium: distilled water=50: 2: 1: 65.
The present invention is by the advantageous effect that above technical scheme is obtained:(1) spun-glass insulation cotton thermal coefficient is low,
Layer structure improves material in the heat bridge effect of thickness direction, and there is good warmth retention property, acrylic resin adhesive to have
Good hydrophobic performance, not absorbing sweat.(2) emulsified epoxy-modified ternary answers the bonding of the third rubber soft comfortable and glass fibre cotton
Property is good, and has good gas permeability.(3) copper powder coating in surface has extremely low room temperature far infrared transmissivity, strong to obtain
Inhibit human body by heat loss through radiation, warming effect greatly improves, and material overall structure is simple, and lightweight is practical.
Specific implementation mode
With reference to specific embodiment, the present invention is furture elucidated, it should be understood that these embodiments are merely to illustrate the present invention
Rather than limit the scope of the invention, after having read the present invention, various equivalences of the those skilled in the art to the present invention
It is as defined in the appended claims that the modification of form falls within the application.
Embodiment 1
A kind of warmth-retaining clothing material, from inside to outside successively by lining, insulating layer, insulating layer upper surface copper powder coating, with
And outer shell fabric composition, the lining are fleece fabric;Insulating layer is the glass fibre and acrylic acid tree that average diameter is 1 μm
The glass fibre cotton of fat adhesive composition;The copper powder and ethylene-propylene-diene monomer viscose binder that copper powder coating is 1: 4 by mass ratio form,
Room temperature far infrared transmissivity is 0.3;Outer shell fabric is windproof material.
Insulation layer thickness is 1.5cm, and glass fibre cotton is in layered distribution, 150 μm of thickness, surface density 200g/m2。
It is adhesive that copper powder, which is coated with epoxidized ethylene-propylene-diene mischpolymer, and copper powder is filler, forms the low-launch-rate being evenly distributed
Coating, copper powder mass fraction are 40%, and coating layer thickness is 200 μm.
Ethylene propylene diene rubber is epoxy-modified ethylene propylene diene rubber, and modifier components are:(liquid quality fraction is toluene
8%), hydrogen peroxide (28mg/L), acetic acid (20mg/L), settle through absolute ethyl alcohol, and distilled water cleaning, saturated sodium bicarbonate impregnates,
Drying is made.
Adhesive is made through emulsification treatment by epoxy-modified ethylene propylene diene rubber, and emulsion components and weight ratio are:Matter
Measure the epoxy-modified ethylene propylene diene rubber toluene solution that score is 12%: emulsifier Tween60: potassium hydroxide: distilled water=50:
2∶1∶65。
Embodiment 2
A kind of warmth-retaining clothing material, from inside to outside successively by lining, insulating layer, insulating layer upper surface copper powder coating, with
And outer shell fabric composition, the lining are fleece fabric:Insulating layer is the glass fibre and acrylic acid that average diameter is 1.1 μm
The glass fibre cotton of Resin adhesive composition;Copper powder and ethylene-propylene-diene monomer viscose binder group of the copper powder coating by mass ratio for 1: 3
At room temperature far infrared transmissivity is 0.2;Outer shell fabric is windproof material.
Insulation layer thickness is 02cm, and glass fibre cotton is in layered distribution, 180 μm of thickness, surface density 250g/m2。
It is adhesive that copper powder, which is coated with epoxidized ethylene-propylene-diene mischpolymer, and copper powder is filler, forms the low-launch-rate being evenly distributed
Coating, copper powder mass fraction are 42%, and coating layer thickness is 180 μm.
Ethylene propylene diene rubber is epoxy-modified ethylene propylene diene rubber, and modifier components are:(liquid quality fraction is toluene
9%), hydrogen peroxide (30mg/L), acetic acid (21.5mg/L), settle through absolute ethyl alcohol, distilled water cleaning, saturated sodium bicarbonate leaching
Bubble, drying are made.
Adhesive is made through emulsification treatment by epoxy-modified ethylene propylene diene rubber, and emulsion components and weight ratio are:Matter
Measure the epoxy-modified ethylene propylene diene rubber toluene solution that score is 12%: emulsifier Tween60: potassium hydroxide: distilled water=50:
2∶1∶65。
2 specific implementation modes of the present invention are above are only, but the design concept of the present invention is not limited thereto, all utilizations
This design carries out the present invention change of unsubstantiality, should all belong to the behavior for invading the scope of protection of the invention.In every case it is not
It is detached from the content of technical solution of the present invention, according to the technical essence of the invention to any type of simple made by above example
Modification, equivalent variations and remodeling, still fall within the protection domain of technical solution of the present invention.
Claims (5)
1. a kind of warmth-retaining clothing material, it is characterised in that the warmth-retaining clothing material from inside to outside successively by lining, insulating layer,
The copper powder coating and outer shell fabric of insulating layer upper surface form, and the lining is fleece fabric;The insulating layer is flat
The glass fibre cotton of a diameter of 0.2~1.5 μm of glass fibre and acrylic resin adhesive composition;The copper powder coating
Be 1 by mass ratio: the copper powder and ethylene-propylene-diene monomer viscose binder of (2~5.5) forms, room temperature far infrared transmissivity for 0.2~
0.4;The outer shell fabric is windproof material.
2. a kind of warmth-retaining clothing material according to claim 1, it is characterised in that the insulation layer thickness be 0.8~
3cm, glass fibre cotton are in layered distribution, and 100~200 μm of thickness, surface density is 150~300g/m2。
3. a kind of warmth-retaining clothing material according to claim 1, it is characterised in that the copper powder is coated with epoxidation ternary
EP rubbers is adhesive, and copper powder is filler, forms the low emissivity coatings being evenly distributed, copper powder mass fraction is 35%~
45%, coating layer thickness is 130~300 μm.
4. a kind of warmth-retaining clothing material according to claim 1 and 3, it is characterised in that the ethylene propylene diene rubber is epoxy
Modified EPT rubber, modifier components are:Toluene (liquid quality fraction is 7%~9%), hydrogen peroxide (27~30mg/
L), acetic acid (19.5~21.5mg/L), settles through absolute ethyl alcohol, and distilled water cleaning, saturated sodium bicarbonate impregnates, and drying is made.
5. a kind of warmth-retaining clothing material according to claim 1 and 3, it is characterised in that the adhesive is changed by epoxy
Property ethylene propylene diene rubber through emulsification treatment be made, emulsion components and weight ratio are:Mass fraction is epoxy-modified the three of 12%
First EP rubbers toluene solution: emulsifier Tween60: potassium hydroxide: distilled water=50: 2: 1: 65.