CN108725006A - A kind of false proof process of aluminizer printed form unsealing pull line - Google Patents
A kind of false proof process of aluminizer printed form unsealing pull line Download PDFInfo
- Publication number
- CN108725006A CN108725006A CN201810574313.6A CN201810574313A CN108725006A CN 108725006 A CN108725006 A CN 108725006A CN 201810574313 A CN201810574313 A CN 201810574313A CN 108725006 A CN108725006 A CN 108725006A
- Authority
- CN
- China
- Prior art keywords
- aluminizer
- aluminizing
- pull line
- printing
- face
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of false proof process of aluminizer printed form unsealing pull line, are as follows：Step 1 carries out two-sided sided corona treatment to base membrane layer, then carries out processing of aluminizing on one side to base membrane layer；Printing toner is added in PET varnish and is uniformly mixed, obtained the first product, printed to the face of aluminizing using the first product, obtain printing layer by step 2；Step 3 wash aluminium processing using aluminium washing machine to printing layer, then coats anti-mucus to the non-face of aluminizing of base membrane layer and prints, and to aluminizing, face coats adhesive sticker, is then wound, ageing treatment and cutting.After the present invention opens outer packing, unsealing pull line two kinds of different patterns of inside and outside presentation are anti-fake to achieve the effect that；Using the light-proofness of aluminizer, the Quick Response Code or symbol for having anti-counterfeiting information on packed article can be protected, dismantles rear visible 2 D code information or symbol, under the premise of not increasing other antifalsification labels, tear tape anti-counterfeiting design and combination anti-fake design can be carried out.
Description
Technical field
The present invention relates to aluminizer printed form unsealing pull line field, specifically a kind of aluminizer printed form unsealing pull line is prevented
Pseudo- technique.
Background technology
Aluminizer is by the aluminium wire of high-purity by vacuum aluminium plating process in high temperature（1100-1200 degrees Celsius）Under flash to
Gaseous state, when plastic film is by being evaporated in vacuo room later, gaseous aluminium molecule is deposited to Plastic film surface and the light that is formed
The film of metal color.It is a kind of cheap beautiful, property due to its not only characteristic with plastic film, but also the characteristic with metal
Excellent, the highly practical packaging material of energy.Mainly there is polyester aluminizer using most metallized films at present（VMPET）And CPP
Aluminizer（VMCPP）.The effect that film surface is aluminized is shading, resisting ultraviolet radiation, has not only extended the shelf-life of content, but also
The brightness for improving film, to a certain extent instead of aluminium foil, it may have inexpensive, beautiful and preferable barrier property, therefore,
Application of the aluminizer in composite packaging is very extensive, is mainly used in the drying such as biscuit, dilated food packaging and one at present
In a little medical, cosmetics outer packings.
Aluminizer carries out printing cutting as basement membrane plus man-hour requirement uses unsealing pull line, and existing unsealing pull line is from interior past
Include non-drying glue layer, printing layer, base membrane layer, aluminium coated, printing layer, character layer and adherent layer, the opening of this structure successively outside
The ineffective security of bracing wire, this is just that the producer brings puzzlement.
Invention content
The purpose of the present invention is to provide a kind of false proof process of aluminizer printed form unsealing pull line, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the present invention provides the following technical solutions：
A kind of false proof process of aluminizer printed form unsealing pull line, is as follows：
Step 1 carries out two-sided sided corona treatment to base membrane layer, then carries out processing of aluminizing on one side to base membrane layer；
Printing toner is added in PET varnish and is uniformly mixed, the first product obtained, using the first product to plating by step 2
Aluminium face is printed, and printing layer is obtained, and the mass ratio for printing toner and PET varnish is 1.2-1.6：3.6-4.5；
Step 3 carries out printing layer using aluminium washing machine to wash aluminium processing, then coats anti-mucus simultaneously to the non-face of aluminizing of base membrane layer
And printed, to aluminizing, face coats adhesive sticker, is then wound, ageing treatment and cutting are to get to finished product.
As a further solution of the present invention：The corona value of two-sided sided corona treatment is not less than 42 dynes.
As a further solution of the present invention：Printing toner includes that red-colored organic dyes, yellow organic dyestuff, black are organic
At least three kinds in dyestuff, green organic dyes and golden organic dyestuff.
As a further solution of the present invention：Processing progress membrane pressure processing before of aluminizing is carried out to base membrane layer.
As a further solution of the present invention：To aluminizing, face printing uses colored text printing technology, to non-face print of aluminizing
Brush uses micro laser engraving mask-making technology.
As a further solution of the present invention：Adhesive sticker includes the raw material of following parts by weight：4.6-6.5 parts of cornstarch,
3.5-6 parts of acetone, 1.5-2.2 parts of nano silicon dioxide, 5-7.8 parts of lemon, 0.8-1.3 parts of 3-phoshoglyceric acid and matrimony vine
2-2.7 parts of extracting solution.
As a further solution of the present invention：Fructus lycii extracted solution be 5-6.4 in pH value after matrimony vine is broken and temperature is 32-
Enzymolysis obtains under 45 degrees Celsius.
Compared with prior art, the beneficial effects of the invention are as follows：It is of the invention novel in design, it is simple in structure, open outer packing
Afterwards, two kinds of different patterns of the inside and outside presentation of unsealing pull line, it is anti-fake to achieve the effect that；Using the light-proofness of aluminizer, can protect
The Quick Response Code or symbol for having anti-counterfeiting information on packed article dismantle rear visible 2 D code information or symbol, anti-not increasing other
Under the premise of pseudo label, tear tape anti-counterfeiting design and combination anti-fake design can be carried out, anti-counterfeiting performance is strong.
Specific implementation mode
The technical solution of this patent is described in more detail With reference to embodiment.
Embodiment 1
A kind of false proof process of aluminizer printed form unsealing pull line, is as follows：
Step 1 carries out two-sided sided corona treatment to base membrane layer, and the corona value of two-sided sided corona treatment is not less than 42 dynes, then to base
Film layer carries out processing of aluminizing on one side；
Printing toner is added in PET varnish and is uniformly mixed, the first product obtained, using the first product to plating by step 2
Aluminium face is printed, and printing layer is obtained, and the mass ratio for printing toner and PET varnish is 1.2：3.6, printing toner has including red
The mixture of engine dyeing material, black organic dyestuff and golden organic dyestuff；
Step 3 carries out printing layer using aluminium washing machine to wash aluminium processing, then coats anti-mucus simultaneously to the non-face of aluminizing of base membrane layer
And printed, to aluminizing, face coats adhesive sticker, is then wound, ageing treatment and cutting are to get to finished product.
Embodiment 2
A kind of false proof process of aluminizer printed form unsealing pull line, is as follows：
Step 1 carries out two-sided sided corona treatment to base membrane layer and membrane pressure is handled, then carries out processing of aluminizing on one side to base membrane layer；
Printing toner is added in PET varnish and is uniformly mixed, the first product obtained, using the first product to plating by step 2
Aluminium face is printed, and printing layer is obtained, and the mass ratio for printing toner and PET varnish is 1.35：4.1；
Step 3 carries out printing layer using aluminium washing machine to wash aluminium processing, then coats anti-mucus simultaneously to the non-face of aluminizing of base membrane layer
And printed, to aluminizing, face coats adhesive sticker, and adhesive sticker includes the raw material of following parts by weight：4.6 parts of cornstarch, acetone
2 parts of 3.5 parts, 1.5 parts of nano silicon dioxide, 5 parts of lemon, 0.8 part of 3-phoshoglyceric acid and fructus lycii extracted solution, then carry out
Winding, ageing treatment and cutting are to get to finished product.
Embodiment 3
A kind of false proof process of aluminizer printed form unsealing pull line, is as follows：
Step 1 carries out two-sided sided corona treatment to base membrane layer, then carries out processing of aluminizing on one side to base membrane layer；
Printing toner is added in PET varnish and is uniformly mixed, the first product obtained, using the first product to plating by step 2
Aluminium face carries out colored text printing, obtains printing layer, and the mass ratio for printing toner and PET varnish is 1.5：3.8, print toner packet
Include the mixture of yellow organic dyestuff, black organic dyestuff, green organic dyes and golden organic dyestuff；
Step 3 carries out printing layer using aluminium washing machine to wash aluminium processing, then coats anti-mucus simultaneously to the non-face of aluminizing of base membrane layer
And printed using micro laser engraving mask-making technology, to aluminizing, face coats adhesive sticker, then wound, ageing treatment and
Cutting is to get to finished product.
Embodiment 4
A kind of false proof process of aluminizer printed form unsealing pull line, is as follows：
Step 1 carries out two-sided sided corona treatment to base membrane layer and membrane pressure is handled, then carries out processing of aluminizing on one side to base membrane layer；
Printing toner is added in PET varnish and is uniformly mixed, the first product obtained, using the first product to plating by step 2
Aluminium face is printed, and printing layer is obtained, and the mass ratio for printing toner and PET varnish is 1.42：4.4, printing toner includes red
The mixture of organic dyestuff, yellow organic dyestuff, black organic dyestuff, green organic dyes and golden organic dyestuff；
Step 3 carries out printing layer using aluminium washing machine to wash aluminium processing, then coats anti-mucus simultaneously to the non-face of aluminizing of base membrane layer
And printed, to aluminizing, face coats adhesive sticker, and adhesive sticker includes the raw material of following parts by weight：5.7 parts of cornstarch, acetone
2.6 parts of 5.6 parts, 2.1 parts of nano silicon dioxide, 7.5 parts of lemon, 1.25 parts of 3-phoshoglyceric acid and fructus lycii extracted solution, Chinese holly
Qi extracting solution is to digest to obtain in the case where pH value is 5.9 and temperature is 40 degrees Celsius after matrimony vine is broken, is then wound, at timeliness
It reason and cuts to get to finished product.
Embodiment 5
A kind of false proof process of aluminizer printed form unsealing pull line, is as follows：
Step 1 carries out two-sided sided corona treatment to base membrane layer and membrane pressure is handled, and the corona value of two-sided sided corona treatment is reached not less than 42
Then cause carries out processing of aluminizing on one side to base membrane layer；
Printing toner is added in PET varnish and is uniformly mixed, the first product obtained, using the first product to plating by step 2
Aluminium face carries out colored text printing, obtains printing layer, and the mass ratio for printing toner and PET varnish is 1.6：4.5, print toner packet
Include the mixture of red-colored organic dyes, yellow organic dyestuff, black organic dyestuff, green organic dyes and golden organic dyestuff；
Step 3 carries out printing layer using aluminium washing machine to wash aluminium processing, then coats anti-mucus simultaneously to the non-face of aluminizing of base membrane layer
And printed using micro laser engraving mask-making technology, to aluminizing, face coats adhesive sticker, and adhesive sticker includes following parts by weight
Raw material：6.5 parts of cornstarch, 6 parts of acetone, 2.2 parts of nano silicon dioxide, 7.8 parts of lemon, 1.3 parts of 3-phoshoglyceric acid
With 2.7 parts of fructus lycii extracted solution, fructus lycii extracted solution is to be digested after matrimony vine is broken in the case where pH value is 5.8 and temperature is 42 degrees Celsius
It arrives, is then wound, ageing treatment and cutting are to get to finished product.
The raw material support that non-drying glue layer provides 180 degree stripping for aluminizer printed form bracing wire, holds the technical indicators such as viscosity.Base
The raw material that film layer provides tensile strength, fracture strength, shrinking percentage etc. for aluminizer printed form bracing wire is supported.Printing layer and plating
Aluminium layer provides the original support of printing effect and pattern for aluminizer printed form bracing wire.By traditional one side print brush layer in the present invention
It is adjusted to printed on both sides, is continuing traditional printing processing on one side, another side is printed, washes aluminium processing；To in base membrane layer
Outer two sides carries out corona, membrane pressure, micro printing, coating print, the multiple tracks technique such as wash aluminium, coating.It is positive in manufacturing method
Aluminium technique is washed using colored text printing, the back side uses micro laser engraving plate-making technology, font height 0.01mm printing
Word is secured on face, the whole production technology for using unsealing pull line.After opening outer packing, unsealing pull line is inside and outside to be presented two kinds of differences
Pattern, it is anti-fake to achieve the effect that；Using the light-proofness of aluminizer, the Quick Response Code for having anti-counterfeiting information on packed article can be protected
Or symbol, dismantle rear visible 2 D code information or symbol.Packing material and packed article are combined anti-counterfeiting design, design is skilful
It is wonderful, structural manufacturing process is complicated, high in technological content, anti-counterfeiting performance is strong.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (7)
1. a kind of false proof process of aluminizer printed form unsealing pull line, which is characterized in that be as follows：
Step 1 carries out two-sided sided corona treatment to base membrane layer, then carries out processing of aluminizing on one side to base membrane layer；
Printing toner is added in PET varnish and is uniformly mixed, the first product obtained, using the first product to plating by step 2
Aluminium face is printed, and printing layer is obtained, and the mass ratio for printing toner and PET varnish is 1.2-1.6：3.6-4.5；
Step 3 carries out printing layer using aluminium washing machine to wash aluminium processing, then coats anti-mucus simultaneously to the non-face of aluminizing of base membrane layer
And printed, to aluminizing, face coats adhesive sticker, is then wound, ageing treatment and cutting are to get to finished product.
2. the false proof process of aluminizer printed form unsealing pull line according to claim 1, which is characterized in that the two-sided electricity
The corona value of dizzy processing is not less than 42 dynes.
3. the false proof process of aluminizer printed form unsealing pull line according to claim 1 or 2, which is characterized in that the print
Swabbing powder includes in red-colored organic dyes, yellow organic dyestuff, black organic dyestuff, green organic dyes and golden organic dyestuff
At least three kinds.
4. the false proof process of aluminizer printed form unsealing pull line according to claim 1, which is characterized in that the base membrane layer
Carry out processing progress membrane pressure processing before of aluminizing.
5. the false proof process of aluminizer printed form unsealing pull line according to claim 1, which is characterized in that the face of aluminizing
Printing uses colored text printing technology, and micro laser engraving mask-making technology is used to non-face printing of aluminizing.
6. the false proof process of aluminizer printed form unsealing pull line according to claim 1, which is characterized in that the adhesive sticker
Include the raw material of following parts by weight：4.6-6.5 parts of cornstarch, 3.5-6 parts of acetone, 1.5-2.2 parts of nano silicon dioxide, lemon
2-2.7 parts of 5-7.8 parts of essential oil, 0.8-1.3 parts of 3-phoshoglyceric acid and fructus lycii extracted solution.
7. the false proof process of aluminizer printed form unsealing pull line according to claim 6, which is characterized in that the matrimony vine carries
It is to digest to obtain in the case where pH value is 5-6.4 and temperature is 32-45 degrees Celsius after matrimony vine is broken to take liquid.