CN108713821A - A kind of Degradable environment protection insole that gas permeability is strong - Google Patents
A kind of Degradable environment protection insole that gas permeability is strong Download PDFInfo
- Publication number
- CN108713821A CN108713821A CN201810369950.XA CN201810369950A CN108713821A CN 108713821 A CN108713821 A CN 108713821A CN 201810369950 A CN201810369950 A CN 201810369950A CN 108713821 A CN108713821 A CN 108713821A
- Authority
- CN
- China
- Prior art keywords
- parts
- strong
- gas permeability
- insole
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to novel environment friendly dress ornament shoes and hats material development technical fields,Disclose a kind of Degradable environment protection insole that gas permeability is strong,Using degradable biotic component as primary raw material,Modification is processed to it,Natural macromolecular material is solved in calorifics,Poor mechanical property,The performance requirement problem of engineering material cannot be met,Modified material skin-friendly is good,After absorbing sweat,Hydrophilic radical in molecule forms hydrogen bond with hydrone,It is firmly combined with,Cavity structure being capable of the more sweat of dilatation absorption,At the same time,The ventilative duct on surface makes transmission path be carried out according to minimum resistance,Promote sweat that can distribute as soon as possible,Gas exchanges are carried out with external environment,Prevent the generation of bacterium and the formation of sweat stain,Foot temperature can also be adjusted,Alleviate wet bored sense,Eliminate the discomfort of movement sweat releasing band,Long-time service can relieve fatigue,Solve the problems, such as tinea pedis.
Description
Technical field
The invention belongs to novel environment friendly dress ornament shoes and hats material development technical fields, and in particular to a kind of gas permeability it is strong can
Degradation environment protection insole.
Background technology
Shoes are the necessitys of people's daily life, and the requirement now with consumer to health care, Xie Ye manufacturers open
Gradually to health, comfort aspect develops the shoes product of hair, and an important component of the insole as shoes entirety, good
Moisture absorption, antibacterial, bactericidal property will be to ensureing that the deodorization performance of shoes has vital effect.Relevant information shows：80% people
It is sweaty feet, foot odour causes the serious pollution of public place, dormitory, family's air, it has also become influences people's quality of life
A great problem separately has a large amount of patients to subject the pain of the diseases such as tinea pedis, the ringworm of the foot.Although pedal skin only accounts for human skin surface
Long-pending 7%, but 40% integrated distribution of human sweat glands, in foot, simultaneously as the physiological function feature of foot, sweat gland is each foot
The distribution at position is unbalanced, wherein arch of the foot, toe space and toe joint position density of hesitating are maximum, and heel, instep want slightly smaller.
When temperature is 20 DEG C, sweat steam raising amount of the foot in shoes can reach 20g-5Og per hour, then by 8 hours shoes are worn daily
It can calculate, foot is discharged into the quantity of perspiration about 160g-400g in shoe cavity daily, during the motion, foot and upper of a shoe liner material, sole
The intense attrition of material, have stimulated nerve ending, and sweat secretion speed quickly increases.One foot about 80,000 sweat pores, often
Minute amount of sweat about 0.8g-1.89g, the quantity of perspiration that usually shoe body is accumulated in strenuous exercise is up to 100g.
Current various types of insoles are full of on the market, and the most common are the insoles of EVA materials, have good support
Power, elasticity are good, but poor air permeability, the TPR insoles of same good appearance are welcome by women, but still there are poor air permeability,
The more persons of pin sweat need to avoid using, and latex insole can be soft with deodorization absorbing sweat, moderate, but wears no resistance, service life
Short, degradability is poor after eliminating, and is unfavorable for environmental protection.
Invention content
The purpose of the present invention is for existing problem, providing a kind of Degradable environment protection insole that gas permeability is strong, utilize
Bionics principle, the insole antibacterial, ventilating processed is good and degradable, non-hazardous to human body and environment.
The present invention is achieved by the following technical solutions：
A kind of Degradable environment protection insole that gas permeability is strong, is made of following component in parts by weight：180-190 parts of stalk, bamboo
10-12 parts of fiber, 5.0-6.0 parts of green tea bar, 1.5-2.0 parts of talcum powder, 1.0-1.2 parts of calcium carbonate, tourmaline powder 0.8-1.0
Part, 150-160 parts of stalk treatment fluid, 20-25 parts of starch, 60-70 parts of water；Its processing method includes the following steps：
（1）The stalk of harvesting is cleaned up using the buck of a concentration of 0.2-0.3%, is dried to that water content between 5-8%, is sent
Enter to cut into strip of the length between 0.5-0.6 centimetres in cutting machine, is then placed in stalk treatment fluid and carries out heating stirring
Pretreatment, pretreatment temperature are 80-90 DEG C, and processing time is 40-50 minutes, and pretreatment, which is placed in 140-150 DEG C of baking oven, dries
It discharges within roasting 20-30 minutes；
（2）Starch dissolution is configured to starch emulsion in water, heating stirring 10-15 minutes in 40-50 DEG C of water-bath, is added
Talcum powder, calcium carbonate, tourmaline powder continue stirring 30-40 minutes, are then ultrasonically treated 20-25 minutes, are added to step（1）In
Baking after material in, be added bamboo fibre, green tea bar stirring, be sent into fiberizer in heat defibrination, heating temperature 80-85
DEG C, it is pressed into the sheet of different size thickness by calender, is cut out by mechanical stitch after sizing and is pressed into dimension
Insole.
Further described as to said program, the stalk treatment fluid according to mass percent meter contain it is following at
Point：Zinc oxide accounts for 0.6-0.7%, terpinol accounts for 1.2-1.4%, ethyl cellulose accounts for 0.3-0.4%, sodium metasilicate accounts for 1.0-1.2%, carbon
Sour sodium accounts for 1.5-1.8%, ethyl alcohol accounts for 4-6%, remaining as water.
It is further described as to said program, the tourmaline powder particle size is between 10-20 microns.
It is further described as to said program, step（1）Described in buck be saleratus solution.
It is further described as to said program, step（2）Middle addition bamboo fibre, green tea bar are stirred to slurries water content
Between 20-25%.
The present invention has the following advantages compared with prior art：It is taken into account not with gas permeability to solve existing insole skin-friendly
Foot, and problem difficult to degrade, the present invention provides a kind of Degradable environment protection insole that gas permeability is strong, with degradable biology at
It is divided into primary raw material, modification is processed to it, solves natural macromolecular material in calorifics, poor mechanical property, cannot meet
The performance requirement problem of engineering material, modified material skin-friendly is good, after absorbing sweat, the hydrophilic radical in molecule and hydrone
Form hydrogen bond, be firmly combined with, cavity structure can dilatation absorb more sweat, at the same time, the ventilative duct on surface makes
Transmission path is carried out according to minimum resistance, promotes sweat that can distribute as soon as possible, and gas exchanges are carried out with external environment,
Prevent the generation of bacterium and the formation of sweat stain, additionally it is possible to adjust foot temperature, alleviate wet bored sense, eliminate movement sweat releasing band
Discomfort, long-time service can relieve fatigue, and solve the problems, such as tinea pedis.
Specific implementation mode
The present invention is further explained in the light of specific embodiments.
Embodiment 1
A kind of Degradable environment protection insole that gas permeability is strong, is made of following component in parts by weight：180 parts of stalk, bamboo fibre
10 parts, 5.0 parts of green tea bar, 1.5 parts of talcum powder, 1.0 parts of calcium carbonate, 0.8 part of tourmaline powder, 150 parts of stalk treatment fluid, starch 20
Part, 60 parts of water；Its processing method includes the following steps：
（1）The stalk of harvesting is cleaned up using a concentration of 0.2% buck, is dried to water content between 5-8%, feeding is cut
Strip of the length between 0.5-0.6 centimetres is cut into cutting mill, is then placed in progress heating stirring in stalk treatment fluid and is located in advance
Reason, pretreatment temperature are 80 DEG C, and processing time is 40 minutes, and pretreatment is placed in 140 DEG C of baking ovens to toast 20 minutes and discharge；
（2）Starch dissolution is configured to starch emulsion in water, talcum is added in heating stirring 10 minutes in 40 DEG C of water-baths
Powder, calcium carbonate, tourmaline powder continue stirring 30 minutes, are then ultrasonically treated 20 minutes, are added to step（1）In baking after
In material, bamboo fibre, the stirring of green tea bar is added, is sent into fiberizer and heats defibrination, heating temperature is 80 DEG C, by calender pressure
The sheet of different size thickness is made, cuts out the insole for being pressed into dimension after sizing by mechanical stitch.
Further described as to said program, the stalk treatment fluid according to mass percent meter contain it is following at
Point：Zinc oxide, which accounts for 0.6%, terpinol and accounts for 1.2%, ethyl cellulose and account for 0.3%, sodium metasilicate and account for 1.0%, sodium carbonate, accounts for 1.5%, ethyl alcohol
Account for 4%, remaining as water.
It is further described as to said program, the tourmaline powder particle size is between 10-20 microns.
It is further described as to said program, step（1）Described in buck be saleratus solution.
It is further described as to said program, step（2）Middle addition bamboo fibre, green tea bar are stirred to slurries water content
Between 20-25%.
Embodiment 2
A kind of Degradable environment protection insole that gas permeability is strong, is made of following component in parts by weight：185 parts of stalk, bamboo fibre
11 parts, 5.5 parts of green tea bar, 1.8 parts of talcum powder, 1.1 parts of calcium carbonate, 0.9 part of tourmaline powder, 155 parts of stalk treatment fluid, starch 22
Part, 65 parts of water；Its processing method includes the following steps：
（1）The stalk of harvesting is cleaned up using a concentration of 0.25% buck, is dried to water content between 5-8%, is sent into
Strip of the length between 0.5-0.6 centimetres is cut into cutting machine, and it is pre- to be then placed in progress heating stirring in stalk treatment fluid
Processing, pretreatment temperature are 85 DEG C, and processing time is 45 minutes, and pretreatment is placed in 145 DEG C of baking ovens to toast 25 minutes and discharge；
（2）Starch dissolution is configured to starch emulsion in water, talcum is added in heating stirring 12 minutes in 45 DEG C of water-baths
Powder, calcium carbonate, tourmaline powder continue stirring 35 minutes, are then ultrasonically treated 22 minutes, are added to step（1）In baking after
In material, bamboo fibre, the stirring of green tea bar is added, is sent into fiberizer and heats defibrination, heating temperature is 82 DEG C, by calender pressure
The sheet of different size thickness is made, cuts out the insole for being pressed into dimension after sizing by mechanical stitch.
Further described as to said program, the stalk treatment fluid according to mass percent meter contain it is following at
Point：Zinc oxide, which accounts for 0.65%, terpinol and accounts for 1.3%, ethyl cellulose and account for 0.35%, sodium metasilicate and account for 1.1%, sodium carbonate, accounts for 1.6%, second
Alcohol accounts for 5%, remaining as water.
It is further described as to said program, the tourmaline powder particle size is between 10-20 microns.
It is further described as to said program, step（1）Described in buck be saleratus solution.
It is further described as to said program, step（2）Middle addition bamboo fibre, green tea bar are stirred to slurries water content
Between 20-25%.
Embodiment 3
A kind of Degradable environment protection insole that gas permeability is strong, is made of following component in parts by weight：190 parts of stalk, bamboo fibre
12 parts, 6.0 parts of green tea bar, 2.0 parts of talcum powder, 1.2 parts of calcium carbonate, 1.0 parts of tourmaline powder, 160 parts of stalk treatment fluid, starch 25
Part, 70 parts of water；Its processing method includes the following steps：
（1）The stalk of harvesting is cleaned up using a concentration of 0.3% buck, is dried to water content between 5-8%, feeding is cut
Strip of the length between 0.5-0.6 centimetres is cut into cutting mill, is then placed in progress heating stirring in stalk treatment fluid and is located in advance
Reason, pretreatment temperature are 90 DEG C, and processing time is 50 minutes, and pretreatment is placed in 150 DEG C of baking ovens to toast 30 minutes and discharge；
（2）Starch dissolution is configured to starch emulsion in water, talcum is added in heating stirring 15 minutes in 50 DEG C of water-baths
Powder, calcium carbonate, tourmaline powder continue stirring 40 minutes, are then ultrasonically treated 25 minutes, are added to step（1）In baking after
In material, bamboo fibre, the stirring of green tea bar is added, is sent into fiberizer and heats defibrination, heating temperature is 85 DEG C, by calender pressure
The sheet of different size thickness is made, cuts out the insole for being pressed into dimension after sizing by mechanical stitch.
Further described as to said program, the stalk treatment fluid according to mass percent meter contain it is following at
Point：Zinc oxide, which accounts for 0.7%, terpinol and accounts for 1.4%, ethyl cellulose and account for 0.4%, sodium metasilicate and account for 1.2%, sodium carbonate, accounts for 1.8%, ethyl alcohol
Account for 6%, remaining as water.
It is further described as to said program, the tourmaline powder particle size is between 10-20 microns.
It is further described as to said program, step（1）Described in buck be saleratus solution.
It is further described as to said program, step（2）Middle addition bamboo fibre, green tea bar are stirred to slurries water content
Between 20-25%.
Comparative example 1
With differing only in for embodiment 1, the addition of tourmaline powder is omitted, remaining is consistent.
Comparative example 2
With differing only in for embodiment 2, the addition of stalk treatment fluid is omitted, remaining is consistent.
Comparative example 3
With differing only in for embodiment 3, the addition of starch is omitted, remaining is consistent.
Comparative example 4
With differing only in for embodiment 3, step is omitted（1）In preprocessing process, remaining is consistent.
Comparative example 5
With differing only in for embodiment 3, the addition of sodium silicate solution is omitted in stalk treatment fluid, remaining is consistent.
Contrast experiment
In leather shoes processing, insole is prepared using the method for embodiment 1-3 and comparative example 1-5 respectively, while with existing linen-cotton
Insole as a control group 1, the insole of existing EVA materials as a control group 2, carries out insole material capability test, including mechanics
Performance, moisture absorption, moisture releasing experiment, keeps irrelevant variable consistent, while randomly selecting 100 volunteers and trying on examination in test
It tests, recycling wear trials report carries out wearing feeling and scored, comparison result recorded as shown in the table：
| Project | Fracture strength（N） | Moisture percentage（%） | Moisture releasing percentage（%） | Comfort level scores（Point） |
| Embodiment 1 | 1315 | 35 | 99.6 | 98 |
| Embodiment 2 | 1320 | 38 | 99.9 | 99 |
| Embodiment 3 | 1318 | 36 | 99.7 | 99 |
| Comparative example 1 | 1220 | 33 | 98.5 | 91 |
| Comparative example 2 | 939 | 31 | 91.0 | 89 |
| Comparative example 3 | 946 | 33 | 98.0 | 90 |
| Comparative example 4 | 1050 | 25 | 94.0 | 86 |
| Comparative example 5 | 980 | 32 | 93.6 | 95 |
| Control group 1 | 862 | 29 | 86.5 | 93 |
| Control group 2 | 1150 | 15 | 80.3 | 88 |
Wherein, sucting wet experiment：Selection carries out sucting wet experiment under 30 DEG C, 100% relative humidities, at a certain time interval
It weighs, until balance；Moisture releasing is tested：Each group insole is soaked 20 minutes in normal-temperature water, is started when control is with liquid measure about 100%
Experiment, moisture releasing is carried out in 25 DEG C, 20% relative humidity conditions, is weighed at a certain time interval, until balance.
It can be seen that insole gas permeability prepared by the present invention is more preferable, it is suitble to foot movement, meets the demand of health,
And degradability is good.
Claims (5)
1. a kind of Degradable environment protection insole that gas permeability is strong, which is characterized in that be made in parts by weight of following component：Stalk
180-190 parts, it is 10-12 parts of bamboo fibre, 5.0-6.0 parts of green tea bar, 1.5-2.0 parts of talcum powder, 1.0-1.2 parts of calcium carbonate, electrical
0.8-1.0 parts of mountain flour, 150-160 parts of stalk treatment fluid, 20-25 parts of starch, 60-70 parts of water；Its processing method includes following step
Suddenly：
（1）The stalk of harvesting is cleaned up using the buck of a concentration of 0.2-0.3%, is dried to that water content between 5-8%, is sent
Enter to cut into strip of the length between 0.5-0.6 centimetres in cutting machine, is then placed in stalk treatment fluid and carries out heating stirring
Pretreatment, pretreatment temperature are 80-90 DEG C, and processing time is 40-50 minutes, and pretreatment, which is placed in 140-150 DEG C of baking oven, dries
It discharges within roasting 20-30 minutes；
（2）Starch dissolution is configured to starch emulsion in water, heating stirring 10-15 minutes in 40-50 DEG C of water-bath, is added
Talcum powder, calcium carbonate, tourmaline powder continue stirring 30-40 minutes, are then ultrasonically treated 20-25 minutes, are added to step（1）In
Baking after material in, be added bamboo fibre, green tea bar stirring, be sent into fiberizer in heat defibrination, heating temperature 80-85
DEG C, it is pressed into the sheet of different size thickness by calender, is cut out by mechanical stitch after sizing and is pressed into dimension
Insole.
2. a kind of Degradable environment protection insole that gas permeability is strong as described in claim 1, which is characterized in that the stalk treatment fluid
Contain following component according to mass percent meter：Zinc oxide accounts for 0.6-0.7%, terpinol accounts for 1.2-1.4%, ethyl cellulose accounts for
0.3-0.4%, sodium metasilicate account for 1.0-1.2%, sodium carbonate accounts for 1.5-1.
8%, ethyl alcohol accounts for 4-6%, remaining as water.
3. a kind of Degradable environment protection insole that gas permeability is strong as described in claim 1, which is characterized in that the tourmaline powder
Diameter size is between 10-20 microns.
4. a kind of Degradable environment protection insole that gas permeability is strong as described in claim 1, which is characterized in that step（1）Described in
Buck is saleratus solution.
5. a kind of Degradable environment protection insole that gas permeability is strong as described in claim 1, which is characterized in that step（2）Middle addition bamboo
Fiber, green tea bar are stirred to slurries water content between 20-25%.