CN108691509A - Diamond bit and preparation method thereof for engineering investigation - Google Patents
Diamond bit and preparation method thereof for engineering investigation Download PDFInfo
- Publication number
- CN108691509A CN108691509A CN201810234073.5A CN201810234073A CN108691509A CN 108691509 A CN108691509 A CN 108691509A CN 201810234073 A CN201810234073 A CN 201810234073A CN 108691509 A CN108691509 A CN 108691509A
- Authority
- CN
- China
- Prior art keywords
- fan
- cutting tooth
- shaped
- diamond
- cutting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of diamond bit the present invention provides knot for engineering investigation, it includes drilling bit steel body and the drill bit sector cutting tooth in the drilling bit steel body front end is arranged, it is provided with the mouth of a river between adjacent two fan-shaped cutting tooths, the sector cutting tooth is composed of fan-shaped column cutting tooth and fan-shaped scalariform cutting tooth, the front end cutting face of the sector scalariform cutting tooth is slope, and drill bit annular groove is offered in the sector cutting tooth.The diamond bit it is scientific and reasonable for structure, excellent to wide adaptability, the drilling effect on stratum.Simultaneously the present invention also provides the preparation method of the diamond bit, this method combines pressure sintering with cold-press method, plays the double dominant of hot-press method and cold compaction process, it is ensured that bit performance is stablized, and adaptability of the drill bit to stratum is improved.
Description
Technical field
The present invention relates to Geological Engineering technical field, in particular to a kind of diamond bits and its system for engineering investigation
Preparation Method.
Background technology
Currently, the diamond bit market share of the China for engineering investigation accounts for entire field of drill about 30%.Engineering is surveyed
The characteristics of examining is that drilling is shallow, is usually no more than 150m, but the stratum of the depth and variation of lithological are big.It is frequently moved to adapt to drilling machine
It is dynamic, small portable drilling machine is mostly used, the pressure capacity of portable drilling rig is small and rotary torque is small.And existing normal diamond drill bit table
Reveal drilling timeliness it is low, drilling effect is undesirable, and the service life of drill bit is not also grown.
Existing manufacture diamond bit is frequently with hot-press method or electro-plating method.Due to the drill bit knot of both methods manufacture
Structure is relatively simple and single, and it is bad that effect is but shown for drilling complexation and for engineering investigation.Electro-plating method system
Although the drill bit adaptability made is wider, rate of penetration is higher, is reduced using the longevity since the gauge effect of drill bit is undesirable
Life.
Invention content
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide a kind of adaptation scientific and reasonable for structure, to stratum
The diamond bit for engineering investigation that property is wide, drilling effect is excellent, while the present invention also provides the diamond bits
Preparation method, this method are simple for process, of low cost.
To achieve the above object, the diamond bit for engineering investigation of the invention, including drilling bit steel body and setting exist
The drill bit sector cutting tooth of the drilling bit steel body front end is provided with the mouth of a river between adjacent two fan-shaped cutting tooths, and special character exists
In:The sector cutting tooth is composed of fan-shaped column cutting tooth and fan-shaped scalariform cutting tooth, the sector scalariform cutting tooth
Front end cutting face be slope, it is described sector cutting tooth on offer drill bit annular groove.
Any one of following scheme can be used as the preferred embodiment of diamond bit of the present invention:
The ratio between the column cutting tooth and the projected area of bottom of the tooth labial surface of the scalariform cutting tooth are 0.30~0.45 ︰ 1.
The front end cutting face (5.1) forms the fan-shaped cutting angle of back of tooth (6), the sector cutting tooth with bit cutting plane
The value of relief angle (6) is in 15 °~30 ° ranges.
The quantity of the drill bit annular groove is 1~3.
In the sector column cutting tooth, a concentration of the 80~100% of diamond, granularity is 30/40 purpose in diamond
The 15~35% of diamond weight are accounted for, granularity is that 40/50 purpose accounts for the 65~85% of diamond weight.The concentration of diamond herein
System uses " diamond composition world concentration standard ", i.e., 100% concentration contains 4.39 carats of diamond in indicating per cubic centimeter.
In the sector scalariform cutting tooth, a concentration of the 65~75% of diamond, granularity is that 30/40 purpose accounts in diamond
The 30~50% of diamond weight, granularity are that 40/50 purpose accounts for the 50~70% of diamond weight.
The tyre body hardness of the sector column cutting tooth is HRC12~HRC25, and wearability is between 210~250mg;Institute
The tyre body hardness for stating fan-shaped scalariform cutting tooth is HRC10~HRC18, and wearability is between 270~320mg.Fan-shaped column cutting
The tyre body hardness of tooth and wearability are higher, and the hardness and wear resistance of fan-shaped scalariform cutting tooth is relatively low;And it works in drill bit sector
Annular groove is opened up in the middle part of tooth, such drill bit plays the role of the dual broken rock of compact bit and normal diamond drill bit, from basic
On change the deficiency of normal diamond drill bit, be conducive to the effect for improving fractured rock.
The invention also discloses the preparation methods of the diamond bit for engineering investigation, include the following steps:
1) according to designed formula, respectively by diamond, the carcass of fan-shaped column cutting tooth and fan-shaped scalariform cutting tooth
Powder is uniformly mixed in the ball mill with binder, is respectively charged into the steel of prefabricated fan-shaped column cutting tooth and fan-shaped scalariform cutting tooth
In mould, it is sent into cold-press moulding in forcing press, is prefabricated into fan-shaped column cutting tooth and fan-shaped scalariform cutting tooth;
2) fan-shaped column cutting tooth and fan-shaped scalariform cutting tooth arranged in sequence are assembled in graphite jig, is subsequently filled into guarantor
Diameter layer powder and gauge polycrystalline material, in pressure after drilling bit steel body, hot-pressing processing in feeding intermediate frequency furnace;
3) release is come out of the stove immediately after hot-pressing processing, slowly cools to 30 DEG C hereinafter, mould unloading is surveyed to get to for engineering
The diamond bit examined.
Preferably, in step 1), when the cold pressing, the pressure for being cold-pressed fan-shaped column cutting tooth is 20~24MPa, pressurize
7~10s of time;The pressure of the fan-shaped scalariform cutting tooth of cold pressing is 18~22MPa, 6~7s of dwell time.
It is further preferred that in step 2), when the hot pressing, temperature is 945~955 DEG C, and pressure is 13~16MPa,
2.5~3.5min of soaking time, soaking time pressurize always.
The present invention the diamond bit for engineering investigation, from engineering investigation feature and formation characteristics, pass through by
Drill bit sector cutting tooth is designed as being composed of fan-shaped column cutting tooth and fan-shaped scalariform cutting tooth, and the fan-shaped scalariform
The front end cutting face of cutting tooth is designed as slope;Wherein fan-shaped column cutting tooth is the main body of fractured rock, and fan-shaped scalariform is cut
It cuts tooth and plays the fan-shaped column cutting tooth of support, while playing addi-tional crusher rock;The drill bit of this structure, drill bit fan
Shape cutting tooth and the contact area of bottom hole rock are smaller, the contact area of drill bit and rock can be effectively reduced, in identical bit pressure
Under the conditions of, can significantly improve drill bit than pressure value, be conducive to cut rock, be adapted to prospecting type portable drilling rig drilling;Simultaneously
Again can effectively cooling diamond drill bit and timely cleaning hole bed rock powder, improve the efficiency of fractured rock.It is cut in the drill bit sector
Cut after tooth cutting face opens up drill bit annular groove, which changes the mode of drill bit fractured rock, can device to hole bed rock stone with point
Ring mode is crushed, and increases the scope of freedom of bottom hole rock, improves conformability of the drill bit to rock;Bit operation tooth is
Inhomogeneous structure, diamond concentration height, the tyre body hardness of fan-shaped column cutting tooth are high, and wearability is strong, small with rock contact area,
Thus entire drill bit sector cutting tooth plays the dual broken rock effect of compact bit and normal diamond drill bit;Fundamentally change
Become insufficient existing for normal diamond drill bit.
Meanwhile the preparation method of patent of the present invention devises the manufacturing process for being different from conventional method, pressure sintering with it is cold
Platen press combines, and plays the double dominant of hot-press method and cold compaction process, it is ensured that bit performance is stablized, and improves drill bit to stratum
Adaptability.
Description of the drawings
Fig. 1 is a kind of diamond bit bottom labial surface structural schematic diagram for engineering investigation;
Fig. 2 is the A of Fig. 1 to expanded schematic diagram;
Fig. 3 is fan-shaped cutting tooth structural schematic diagram.
In the figures above, the correspondence of each label and parts is:
1, drilling bit steel body, 2, fan-shaped cutting tooth, 3, the mouth of a river, 4 fan-shaped column cutting tooths, before 5, fan-shaped scalariform cutting tooth, 5.1
Hold cutting face, 6, the fan-shaped cutting angle of back of tooth, 7, drill bit annular groove.
Specific implementation mode
It is used for the diamond bit and its system of engineering investigation to the present invention with specific embodiment with reference to the accompanying drawings of the specification
Preparation Method is described in further detail.
Embodiment 1
A kind of diamond bit for engineering investigation as shown in Figure 1 and Figure 2, including drilling bit steel body 1 and setting are in drill bit
The fan-shaped cutting tooth 2 of 1 front end of steel body is provided with the mouth of a river 3 between adjacent two fan-shaped cutting tooths 2, and mouth of a river number is eight, Mei Geshui
Mouth width 6.5mm, 9 each depth 1.5mm of interior external flume;
As shown in figure 3, fan-shaped cutting tooth 2 is composed of fan-shaped column cutting tooth 4 and fan-shaped scalariform cutting tooth 5, in Fig. 3
Fan-shaped column cutting tooth 4 (polyhedron ABDCGEFH constitute) in Fig. 3, (the polyhedron CDLKJIHG structures of fan-shaped scalariform cutting tooth 5
At);The front end cutting face 5.1 of fan-shaped scalariform cutting tooth 5 is slope (face CKJG compositions);One is offered in fan-shaped cutting tooth 2
Drill bit annular groove 7, drill bit groove depth 2mm, wide 2.5mm.Bottom labial surface (face BDHF compositions) and the sector ladder of fan-shaped column cutting tooth 4
The ratio between projected area of 5 bottom labial surface of shape cutting tooth (face DLIH compositions) is 0.35 ︰ 1.Front end cutting face 5.1 and bit cutting plane
The fan-shaped cutting angle of back of tooth 6 is formed, the sector cutting angle of back of tooth 6 is 18 °, a height of 12mm (Fig. 3 of working lining of fan-shaped column cutting tooth 4
Middle conductor AB length).
In fan-shaped column cutting tooth 4 in the present embodiment, a concentration of the 90% of diamond, granularity is 30/40 in diamond
Purpose accounts for the 35% of diamond weight, and granularity is that 40/50 purpose accounts for the 65% of diamond weight.All using SMD40 grades
Diamond;In fan-shaped scalariform cutting tooth 5, a concentration of the 70% of diamond, granularity is that 30/40 purpose accounts for diamond weight in diamond
The 50% of amount, granularity is that 40/50 purpose accounts for the 50% of diamond weight, all using the diamond of SMD25 grades.
Preparation method includes the following steps:
1) according to designed formula, diamond, carcass powder and the binder of the fan-shaped column cutting tooth of system are existed respectively
It is uniformly mixed in ball mill and mixes the diamond of the fan-shaped scalariform cutting tooth of system, carcass powder in the ball mill with binder
It is even, it is respectively charged into the punching block of prefabricated fan-shaped column cutting tooth 4 and fan-shaped scalariform cutting tooth 5, is sent into forcing press and carries out cold pressing pressure
System is prefabricated into fan-shaped column cutting tooth 4 and fan-shaped scalariform cutting tooth 5;When cold pressing compacting, it is cold-pressed the pressure of fan-shaped column cutting tooth
For 22MPa, dwell time 10s;, the pressure for being cold-pressed fan-shaped scalariform cutting tooth is 20MPa, dwell time 7s;
2) fan-shaped column cutting tooth 4 and fan-shaped 5 arranged in sequence of scalariform cutting tooth are assembled in graphite jig, is subsequently filled into
Gauge layer powder and gauge polycrystalline material, in pressure after drilling bit steel body, hot-pressing processing in feeding intermediate frequency furnace;When hot-pressing processing, temperature
It is 950 DEG C, pressure 14MPa, soaking time 3.5min, soaking time pressurize always;
3) release is come out of the stove immediately after hot-pressing processing, slowly cools to 30 DEG C hereinafter, mould unloading, obtains after machined
Diamond bit for engineering investigation.
After testing, the tyre body hardness of the fan-shaped column cutting tooth 4 of the present embodiment is HRC23, and wearability is in 250mg;It is fan-shaped
The tyre body hardness of scalariform cutting tooth 5 is HRC16, and wearability reaches excellent rank in 320mg.
Embodiment 2
A kind of diamond bit for engineering investigation, including drilling bit steel body 1 and the sector in 1 front end of drilling bit steel body is set
Cutting tooth 2 is provided with the mouth of a river 3 between adjacent two fan-shaped cutting tooths 2, and mouth of a river number is seven, each wide 5mm in the mouth of a river, inside and outside water
9 each depth 1.5mm of slot;
As shown in figure 3, fan-shaped cutting tooth 2 is composed of fan-shaped column cutting tooth 4 and fan-shaped scalariform cutting tooth 5, in Fig. 3
Fan-shaped column cutting tooth 4 (polyhedron ABDCGEFH constitute) in Fig. 3, (the polyhedron CDLKJIHG structures of fan-shaped scalariform cutting tooth 5
At);The front end cutting face 5.1 of fan-shaped scalariform cutting tooth 5 is slope (face CKJG compositions);One is offered in fan-shaped cutting tooth 2
Drill bit annular groove 7, drill bit groove depth 2mm, wide 2mm.The bottom labial surface (face BDKF compositions) of fan-shaped column cutting tooth 4 and fan-shaped scalariform
The ratio between projected area of 5 bottom labial surface of cutting tooth (face DLIH compositions) is 0.45 ︰ 1.Front end cutting face 5.1 and bit cutting planar shaped
The angle of back of tooth 6 is cut at sector, the sector cutting angle of back of tooth 6 is 15 °, and a height of 12mm of working lining of fan-shaped column cutting tooth 4 is (in Fig. 3
Line segment AB length).
In fan-shaped column cutting tooth 4 in the present embodiment, a concentration of the 90% of diamond, granularity is 30/40 in diamond
Purpose accounts for the 25% of diamond weight, and granularity is that 40/50 purpose accounts for the 75% of diamond weight.All using SMD40 grades
Diamond;In fan-shaped scalariform cutting tooth 5, a concentration of the 70% of diamond, granularity is that 30/40 purpose accounts for diamond weight in diamond
The 30% of amount, granularity are that 40/50 purpose accounts for the 70% of diamond weight.
Preparation method includes the following steps:
1) according to designed formula, diamond, carcass powder and the binder of the fan-shaped column cutting tooth of system are existed respectively
It is uniformly mixed in ball mill and mixes the diamond of the fan-shaped scalariform cutting tooth of system, carcass powder in the ball mill with binder
It is even, it is respectively charged into the punching block of prefabricated fan-shaped column cutting tooth 4 and fan-shaped scalariform cutting tooth 5, is sent into forcing press and carries out cold pressing pressure
System is prefabricated into fan-shaped column cutting tooth 4 and fan-shaped scalariform cutting tooth 5;When cold pressing compacting, it is cold-pressed the pressure of fan-shaped column cutting tooth
For 20MPa, dwell time 8s;The pressure of the fan-shaped scalariform cutting tooth of cold pressing is 18MPa, dwell time 6s;
2) fan-shaped column cutting tooth 4 and fan-shaped 5 arranged in sequence of scalariform cutting tooth are assembled in graphite jig, is subsequently filled into
Gauge layer powder and gauge polycrystalline material, in pressure after drilling bit steel body, hot-pressing processing in feeding intermediate frequency furnace;When hot pressing, temperature 945
DEG C, pressure 14MPa, soaking time 3.0min, soaking time pressurize always;
3) release is come out of the stove immediately after hot-pressing processing, slowly cools to 30 DEG C hereinafter, mould unloading, obtains after machined
Diamond bit for engineering investigation.
After testing, the tyre body hardness of the fan-shaped column cutting tooth 4 of the present embodiment is HRC21, and wearability is in 240mg;It is fan-shaped
The tyre body hardness of scalariform cutting tooth 5 is HRC14, and wearability reaches excellent rank in 300mg.
Embodiment 3
A kind of diamond bit for engineering investigation, including drilling bit steel body 1 and be arranged in 1 front end of the drilling bit steel body
Fan-shaped cutting tooth 2 is provided with the mouth of a river 3 between adjacent two fan-shaped cutting tooths 2, and mouth of a river number is eight, each wide 7mm in the mouth of a river, interior,
9 each depth 1.5mm of external flume;
As shown in figure 3, fan-shaped cutting tooth 2 is composed of fan-shaped column cutting tooth 4 and fan-shaped scalariform cutting tooth 5, in Fig. 3
Fan-shaped column cutting tooth 4 (polyhedron ABDCGEFH constitute) in Fig. 3, (the polyhedron CDLKJIHG structures of fan-shaped scalariform cutting tooth 5
At);The front end cutting face 5.1 of fan-shaped scalariform cutting tooth 5 is slope (face CKJG compositions);Two are offered in fan-shaped cutting tooth 2
Drill bit annular groove 7, drill bit groove depth 2mm, wide 2.2mm.Bottom labial surface (face BDHF compositions) and the sector ladder of fan-shaped column cutting tooth 4
The ratio between projected area of 5 bottom labial surface of shape cutting tooth (face DLIH compositions) is 0.40 ︰ 1;Front end cutting face 5.1 and bit cutting plane
The fan-shaped cutting angle of back of tooth 6 is formed, the sector cutting angle of back of tooth 6 is 25 °, a height of 10mm (Fig. 3 of working lining of fan-shaped column cutting tooth 4
Middle conductor AB length).
In fan-shaped column cutting tooth 4 in the present embodiment, a concentration of the 80% of diamond, granularity is 30/40 in diamond
Purpose accounts for the 30% of diamond weight, and granularity is that 40/50 purpose accounts for the 70% of diamond weight.All using SMD40 grades
Diamond;In fan-shaped scalariform cutting tooth 5, the weight percent concentration of diamond is 65%, and granularity is 30/40 purpose in diamond
The 40% of diamond weight is accounted for, granularity is that 40/50 purpose accounts for the 60% of diamond weight.
Preparation method includes the following steps:
1) according to designed formula, diamond, carcass powder and the binder of the fan-shaped column cutting tooth of system are existed respectively
It is uniformly mixed in ball mill and mixes the diamond of the fan-shaped scalariform cutting tooth of system, carcass powder in the ball mill with binder
It is even, it is respectively charged into the punching block of prefabricated fan-shaped column cutting tooth 4 and fan-shaped scalariform cutting tooth 5, is sent into forcing press and carries out cold pressing pressure
System is prefabricated into fan-shaped column cutting tooth 4 and fan-shaped scalariform cutting tooth 5;When cold pressing compacting, it is cold-pressed the pressure of fan-shaped column cutting tooth
For 24MPa, dwell time 7s;The pressure of the fan-shaped scalariform cutting tooth of cold pressing is 18MPa, dwell time 6s;
2) fan-shaped column cutting tooth 4 and fan-shaped 5 arranged in sequence of scalariform cutting tooth are assembled in graphite jig, is subsequently filled into
Gauge layer powder and gauge polycrystalline material, in pressure after drilling bit steel body, hot-pressing processing in feeding intermediate frequency furnace;When hot-pressing processing, temperature
It is 955 DEG C, pressure 12MPa, soaking time 3.0min, soaking time pressurize always;
3) release is come out of the stove immediately after hot-pressing processing, slowly cools to 30 DEG C hereinafter, mould unloading, obtains after machined
Diamond bit for engineering investigation.
After testing, the tyre body hardness of the fan-shaped column cutting tooth 4 of the present embodiment is HRC24, and wearability is in 210mg;It is fan-shaped
The tyre body hardness of scalariform cutting tooth 5 is HRC14, and for wearability in 280mg, performance is excellent.
Claims (10)
1. a kind of diamond bit for engineering investigation, including drilling bit steel body (1) and setting are in the drilling bit steel body (1) front end
Fan-shaped cutting tooth (2), be provided with the mouth of a river (3) between adjacent two fan-shaped cutting tooths (2), it is characterised in that:The fan-shaped cutting
Tooth (2) is composed of fan-shaped column cutting tooth (4) and fan-shaped scalariform cutting tooth (5), before the sector scalariform cutting tooth (5)
It is slope to hold cutting face (5.1), and drill bit annular groove (7) is offered on the sector cutting tooth (2).
2. the diamond bit according to claim 1 for engineering investigation, it is characterised in that:The sector column cutting
The ratio between tooth (4) and the projected area of bottom of the tooth labial surface of fan-shaped scalariform cutting tooth (5) are 0.30~0.45 ︰ 1.
3. the diamond bit according to claim 1 for engineering investigation, it is characterised in that:The front end cutting face
(5.1) form the fan-shaped cutting angle of back of tooth (6) with bit cutting plane, the value of the fan-shaped cutting angle of back of tooth (6) 15 °~
30 ° of ranges.
4. the diamond bit according to claim 1 for engineering investigation, it is characterised in that:The drill bit annular groove
(7) quantity is 1~3.
5. the diamond bit according to claim 1 for engineering investigation, it is characterised in that:The sector column cutting
A concentration of the 80~100% of diamond in tooth (4), granularity is that 30/40 purpose accounts for the 15~35% of diamond weight in diamond,
Granularity is that 40/50 purpose accounts for the 65~85% of diamond weight.
6. the diamond bit according to claim 1 for engineering investigation, it is characterised in that:The sector scalariform cutting
A concentration of the 65~75% of diamond in tooth (5), granularity is that 30/40 purpose accounts for the 30~50% of diamond weight in diamond,
Granularity is that 40/50 purpose accounts for the 50~70% of diamond weight.
7. the diamond bit according to claim 1 for engineering investigation, it is characterised in that:Fan-shaped column cutting tooth
(4) tyre body hardness is HRC12~HRC25, and wearability is between 210~250mg;The tire of the sector scalariform cutting tooth (5)
Body hardness is HRC10~HRC18, and wearability is between 270~320mg.
8. a kind of preparation method of the diamond bit described in claim 1 for engineering investigation, includes the following steps:
1) according to designed formula, respectively by diamond, the tire of fan-shaped column cutting tooth (4) and fan-shaped scalariform cutting tooth (5)
Body powder is uniformly mixed in the ball mill with binder, is then respectively charged into prefabricated fan-shaped column cutting tooth (4) and fan-shaped scalariform
In the punching block of cutting tooth (5), it is sent into forcing press cold pressing compacting, is prefabricated into fan-shaped column cutting tooth (4) and fan-shaped scalariform cutting tooth
(5);
2) fan-shaped column cutting tooth (4) and fan-shaped scalariform cutting tooth (5) arranged in sequence are assembled in graphite jig, is subsequently filled into
Gauge layer powder and gauge polycrystalline material, in pressure after drilling bit steel body, hot pressing in feeding intermediate frequency furnace;
3) release is come out of the stove immediately after hot pressing, slowly cool to 30 DEG C hereinafter, mould unloading to get to the Buddha's warrior attendant for engineering investigation
Aiguille.
9. the preparation method of the diamond bit according to claim 8 for engineering investigation, it is characterised in that:Step 1)
In, when the cold pressing, the pressure for being cold-pressed fan-shaped column cutting tooth is 20~24MPa, 7~10s of dwell time;The fan-shaped ladder of cold pressing
The pressure of shape cutting tooth is 18~22MPa, 6~7s of dwell time.
10. the preparation method of the diamond bit according to claim 8 for engineering investigation, it is characterised in that:Step
2) in, when the hot pressing, temperature is 945~955 DEG C, and pressure is 13~16MPa, 2.5~3.5min of soaking time.