CN108676204A - A kind of bionical shaft tower outer layer material formula - Google Patents
A kind of bionical shaft tower outer layer material formula Download PDFInfo
- Publication number
- CN108676204A CN108676204A CN201810439933.9A CN201810439933A CN108676204A CN 108676204 A CN108676204 A CN 108676204A CN 201810439933 A CN201810439933 A CN 201810439933A CN 108676204 A CN108676204 A CN 108676204A
- Authority
- CN
- China
- Prior art keywords
- parts
- bionical
- outer layer
- layer material
- shaft tower
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to rubber compounding technical fields, specifically disclose a kind of bionical shaft tower outer layer material formula, are made from the following raw materials in parts by weight：800~900 parts of natural rubber, 130~180 parts of butadiene rubber, 230~300 parts of neoprene, 5~10 parts of stearic acid, 30~40 parts of zinc oxide, 2~6 parts of anti-aging agent, 20~40 parts of paraffin, 5~9 parts of sulphur, 12~18 parts of vulcanization accelerator TBT P, 15~20 parts of vulcanization accelerator NS, 3~5 parts of accelerator CZ, 40~60 parts of N phenyl N (trichloromethyl sulphur) benzsulfamide.The present invention overcomes the deficiencies in the prior art, by the way that natural rubber, butadiene rubber and neoprene are reasonably matched, make it have good anti-oxidant, ozone-resistant and fire-retardant ability, it is being aided with other addition costs, the bionical shaft tower outer layer material prepared, it is at low cost, it is functional, it is long with service life, nonflammable effect.
Description
Technical field
The present invention relates to rubber compounding technical fields, particularly belong to a kind of bionical shaft tower outer layer material formula.
Background technology
Shaft tower is one of the basic equipment in overhead distribution, can be divided into rod, cement pole and metal by material used
Three kinds of bar.Cement pole has many advantages, such as that service life is long, and maintenance workload is small, and use is relatively broad.Using most in cement pole
Be dial tip bar, taper is generally 1/75, is divided into regular reinforcement mixed mud bar and prestressing force steel bar mixed mud bar.
Electric force pole tower can be seldom wherein seen in urban district or dense population areas with the development of the city, is mostly used greatly
Underfloor cabling, but underfloor cabling is of high cost, it is difficult in maintenance, it is therefore desirable to which that a kind of novel shaft tower adapts to new demand.
Invention content
The object of the present invention is to provide a kind of bionical shaft tower outer layer material formulas, overcome the deficiencies in the prior art, lead to
It crosses and reasonably matches natural rubber, butadiene rubber and neoprene, make it have good anti-oxidant, ozone-resistant and fire-retardant
Ability is being aided with other addition costs, and the bionical shaft tower outer layer material of preparation is at low cost, functional, has service life
It is long, nonflammable effect.
To solve the above problems, the technical solution used in the present invention is as follows：
A kind of bionical shaft tower outer layer material formula, is made from the following raw materials in parts by weight：800~900 parts of natural rubber, suitable fourth rubber
130~180 parts of glue, 230~300 parts of neoprene, 5~10 parts of stearic acid, 30~40 parts of zinc oxide, 2~6 parts of anti-aging agent, stone
20~40 parts of wax, 5~9 parts of sulphur, 12~18 parts of vulcanization accelerator TBT-P, 15~20 parts of vulcanization accelerator NS, vulcanization promote
3~5 parts of agent CZ, 40~60 parts of N- phenyl-N (trichloromethyl sulphur) benzsulfamide.
Further, described to be made from the following raw materials in parts by weight：850 parts of natural rubber, 150 parts of butadiene rubber, neoprene
250 parts of rubber, 8 parts of stearic acid, 35 parts of zinc oxide, 4 parts of anti-aging agent, 30 parts of paraffin, 7 parts of sulphur, vulcanization accelerator TBT-P 15
Part, 18 parts of vulcanization accelerator NS, 4 parts of accelerator CZ, N- phenyl-N（Trichloromethyl sulphur）50 parts of benzsulfamide.
Further, the anti-aging agent includes anti-aging agent RD and anti-aging agent 6C, the anti-aging agent RD and anti-aging agent 6C
Mass ratio is 1:2.7.
Further, further include it is fire-retardant fill out, it is described it is fire-retardant fill out parts by weight be 100~120 parts.
Further, the flame retardant filler includes aluminium hydroxide, magnesium hydroxide and antioxidant.
Further, aluminium hydroxide, magnesium hydroxide and antioxidant weight ratio are 1~3 in the flame retardant filler：1~2：2
~6.
Compared with prior art, implementation result of the invention is as follows by the present invention：
A kind of bionical shaft tower outer layer material formula of the present invention, by the way that natural rubber, butadiene rubber and neoprene is reasonable
Proportioning, make it have good anti-oxidant, ozone-resistant and fire-retardant ability, be aided with other addition cost, preparation it is bionical
Shaft tower outer layer material, it is at low cost, it is functional, have service life long, nonflammable effect.
Specific implementation mode
With reference to embodiment, the invention will be further described, but the present invention is not limited to these instances, and is being de-
Under the premise of from present inventive concept, carried out by it is any improvement be within the scope of the present invention.
Embodiment 1
A kind of bionical shaft tower outer layer material formula of the present invention, is made from the following raw materials in parts by weight：Natural rubber 800~
900 parts, it is 130~180 parts of butadiene rubber, 230~300 parts of neoprene, 5~10 parts of stearic acid, 30~40 parts of zinc oxide, anti-old
2~6 parts of agent, 20~40 parts of paraffin, 5~9 parts of sulphur, 12~18 parts of vulcanization accelerator TBT-P, vulcanization accelerator NS 15~20
Part, 3~5 parts of accelerator CZ, 40~60 parts of N- phenyl-N (trichloromethyl sulphur) benzsulfamide.
Embodiment 2
A kind of bionical shaft tower outer layer material formula of the present invention, is made from the following raw materials in parts by weight：Natural rubber 850
Part, 150 parts of butadiene rubber, 250 parts of neoprene, 8 parts of stearic acid, 35 parts of zinc oxide, 4 parts of anti-aging agent, 30 parts of paraffin, sulphur 7
Part, 15 parts of vulcanization accelerator TBT-P, 18 parts of vulcanization accelerator NS, 4 parts of accelerator CZ, N- phenyl-N（Trichloromethyl
Sulphur）50 parts of benzsulfamide.
Further, the anti-aging agent includes anti-aging agent RD and anti-aging agent 6C, the anti-aging agent RD and anti-aging agent 6C
Mass ratio is 1:2.7.
Embodiment 3
A kind of bionical shaft tower outer layer material formula of the present invention, is made from the following raw materials in parts by weight：Natural rubber 800~
900 parts, it is 130~180 parts of butadiene rubber, 230~300 parts of neoprene, 5~10 parts of stearic acid, 30~40 parts of zinc oxide, anti-old
2~6 parts of agent, 20~40 parts of paraffin, 5~9 parts of sulphur, 12~18 parts of vulcanization accelerator TBT-P, vulcanization accelerator NS 15~20
Part, 40~60 parts of N- phenyl-N (trichloromethyl sulphur) benzsulfamide, fire-retardant fills out 100~120 at 3~5 parts of accelerator CZ
Part.
Further, the flame retardant filler includes aluminium hydroxide, magnesium hydroxide and antioxidant.
Further, aluminium hydroxide, magnesium hydroxide and antioxidant weight ratio are 1~3 in the flame retardant filler：1~2：2
~6.
Above content is only to present inventive concept example and explanation, affiliated those skilled in the art couple
Described specific embodiment does various modifications or additions or substitutes by a similar method, without departing from invention
Conceive or beyond the scope defined by this claim, is within the scope of protection of the invention.
Claims (6)
1. a kind of bionical shaft tower outer layer material formula, it is characterised in that：It is made from the following raw materials in parts by weight：Natural rubber 800
~900 parts, it is 130~180 parts of butadiene rubber, 230~300 parts of neoprene, 5~10 parts of stearic acid, 30~40 parts of zinc oxide, anti-
2~6 parts of old agent, 20~40 parts of paraffin, 5~9 parts of sulphur, 12~18 parts of vulcanization accelerator TBT-P, vulcanization accelerator NS 15~
20 parts, 3~5 parts of accelerator CZ, 40~60 parts of N- phenyl-N (trichloromethyl sulphur) benzsulfamide.
2. a kind of bionical shaft tower outer layer material formula according to claim 1, it is characterised in that：It is described by following weight
The raw material of part is made：850 parts of natural rubber, 150 parts of butadiene rubber, 250 parts of neoprene, 8 parts of stearic acid, 35 parts of zinc oxide,
4 parts of anti-aging agent, 30 parts of paraffin, 7 parts of sulphur, 15 parts of vulcanization accelerator TBT-P, 18 parts of vulcanization accelerator NS, vulcanization accelerator
4 parts of CZ, N- phenyl-N（Trichloromethyl sulphur）50 parts of benzsulfamide.
3. according to a kind of bionical shaft tower outer layer material formula of claims 1 or 2 any one of them, it is characterised in that：Described
The anti-aging agent includes anti-aging agent RD and anti-aging agent 6C, and the anti-aging agent RD and anti-aging agent 6C mass ratioes are 1:2.7.
4. according to a kind of bionical shaft tower outer layer material formula of claims 1 or 2 any one of them, it is characterised in that：Further include
Fire-retardant to fill out, the fire-retardant parts by weight of filling out are 100~120 parts.
5. according to a kind of bionical shaft tower outer layer material formula of claim 4 any one of them, it is characterised in that：Described is fire-retardant
Filler includes aluminium hydroxide, magnesium hydroxide and antioxidant.
6. according to a kind of bionical shaft tower outer layer material formula of claim 5 any one of them, it is characterised in that：Described is fire-retardant
Aluminium hydroxide, magnesium hydroxide and antioxidant weight ratio are 1~3 in filler：1~2：2~6.