A kind of white glass cleaning agent and preparation method thereof
Technical field
The present invention relates to glass cleaner technical fields, are to be related to a kind of white glass cleaning agent and its system more specifically
Preparation Method.
Background technology
Cleaning agent can probably be divided into inorganic cleaning and organic washing two major classes, and organic washing agent is exactly to contain carbon compound
Manufactured cleaning agent, inorganic cleaning agent are exactly cleaning agent made of carbon-free compound.The specific sorting technique of cleaning agent has
Very much, each state is all not quite similar, and China generally falls into water system, half water system and non-water system cleaning agent three categories.However, existing glass
The cleaning performance of glass cleaning agent is still to be improved, and flushing repeatedly is needed after use, can not preferably be suitable for the clear of white glass
It washes, is easy to damage white glass, dirt is easy redeposition.
Invention content
It is an object of the invention to overcome drawbacks described above in the prior art, provide one kind clean up, do not hinder white glass,
It can prevent the white glass cleaning agent and preparation method thereof of soil redeposition.
To achieve the above object, the first aspect of the present invention provides a kind of white glass cleaning agent, and the cleaning agent is by following
The group of weight percent is grouped as:
As preferred embodiment, the alcohol ethers solvent includes propylene glycol monomethyl ether, propandiol butyl ether or diethylene glycol
Ether.
As preferred embodiment, the anion surfactant includes lauryl sodium sulfate.
As preferred embodiment, the nonionic surfactant includes alkyl polyglycoside (APG).
As preferred embodiment, the auxiliary agent includes Sodium Polyacrylate.
As preferred embodiment, the complexing agent includes ethylenediamine tetra-acetic acid (EDTA), tetrasodium ethylenediamine tetraacetate
(EDTA-4Na), disodium ethylene diamine tetraacetate (EDTA-2Na), sodium citrate or sodium gluconate.
As preferred embodiment, the anti redeposition agent includes hydroxymethyl cellulose.
Second aspect of the present invention provides a kind of method of the white glass cleaning agent prepared as described in above-mentioned technical proposal, packet
Include following steps:
By KOH 1%~10%, alcohol ethers solvent 2%~5%, anion surfactant 0.1%~2%, nonionic
Surfactant 0.1%~3%, auxiliary agent 0.05%~1%, complexing agent 0.1%~2%, anti redeposition agent 1%~3% and remaining
The water of amount is added to uniform stirring in reaction vessel by corresponding weight percent and can be prepared by.
Compared with prior art, the beneficial effects of the present invention are:
1, KOH of the invention is capable of providing alkalinity, and alcohol ethers solvent chooses suitable two kinds of surface-actives as solubilizer
Agent compounds, synergistic, the effects that wetting, infiltration, emulsification, dispersion, solubilising can be improved, and has good biological degradability, helps
Agent has chelation to metal ion, plays alkaline buffer, and dirt disperses into water and prevent redeposition, complexing agent can be complexed
Metal ion (Ca2+, Mg2+ etc.) forms white point, anti redeposition agent in order to avoid the deposition again of metal ion, remains on glass
Redeposition can be prevented, the present invention has compared with simple glass cleaning agent and cleans up, do not hinder white glass, can prevent
Only the advantages of soil redeposition.
2, preparation process of the invention is simple, and manufacturing cost is low.
Specific implementation mode
It in order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below will be in the embodiment of the present invention
Technical solution be clearly and completely described, it is clear that described embodiments are some of the embodiments of the present invention, rather than
Whole embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making creative work premise
Lower obtained every other embodiment, shall fall within the protection scope of the present invention.
A kind of white glass cleaning agent, the cleaning agent consist of the following components in percentage by weight:KOH 1%~10%;Alcohol
Ether solvent 2%~5%;Anion surfactant 0.1%~2%;Nonionic surfactant 0.1%~3%;Auxiliary agent
0.05%~1%;Complexing agent 0.1%~2%;Anti redeposition agent 1%~3%;Water surplus.
A method of the white glass cleaning agent described in above-mentioned technical proposal is prepared, is included the following steps:
By KOH, alcohol ethers solvent, anion surfactant, nonionic surfactant, auxiliary agent, complexing agent, resists and sink again
The water of product agent and surplus is added to uniform stirring in reaction vessel by corresponding weight percent and can be prepared by.
The alcohol ethers solvent includes propylene glycol monomethyl ether, propandiol butyl ether or diethylene glycol ether.
The anion surfactant includes lauryl sodium sulfate.
The nonionic surfactant includes alkyl polyglycoside (APG).
The auxiliary agent includes Sodium Polyacrylate.
The complexing agent includes ethylenediamine tetra-acetic acid (EDTA), tetrasodium ethylenediamine tetraacetate (EDTA-4Na), ethylenediamine tetraacetic
Acetic acid disodium (EDTA-2Na), sodium citrate or sodium gluconate.
The anti redeposition agent includes hydroxymethyl cellulose.
Wherein, KOH is capable of providing alkalinity, and alcohol ethers solvent is as solubilizer.
Single surfactant respectively has its shortcoming, if ionic surfactant stablizes temperature, but hydrophily
Too strong, nonionic is good synergist, but has the limitation of certain temperature range again, chooses suitable two kinds of surfaces and lives
Property agent compounding, synergistic, the effects that wetting, infiltration, emulsification, dispersion, solubilising can be improved.
Existing simple glass cleaning agent includes often alkyl phenol polyoxyethylene ether (APEO), with it is good wetting,
Infiltration, emulsification, dispersion, solubilising and cleaning function, be widely used in detergent, the daily-use chemical industry of personal nursing, weaving, papermaking,
The industries such as oil, metallurgy, pesticide, pharmacy, printing, synthetic rubber, synthetic resin, plastics, but biological degradability is poor, therefore can
To be replaced using alkyl polyglycoside (APG), APG is minimum in nonionic surfactant to the irritation of skin and eyes, is had
Good biological degradability, biological degradation rate is 80% in 5 days;Ultimate biodegradation rate is up to 99.3%.
Sodium Polyacrylate replaces the sodium polyphosphate in existing simple glass cleaning agent, has chelation to metal ion,
Play alkaline buffer, dirt disperses into water and prevent redeposition.
Complexing agent can complexation of metal ions (Ca2+, Mg2+ etc.), in order to avoid the deposition again of metal ion, remains in glass
On, form white point.Anti redeposition agent can prevent redeposition.
Embodiment
Embodiment 1:KOH 3%, propylene glycol monomethyl ether 2%, lauryl sodium sulfate 0.5%, APG 0.8%, polyacrylic acid
Sodium 0.1%, EDTA-4Na 1.0%, hydroxymethyl cellulose 1%, water surplus.
Embodiment 2:KOH 3%, propylene glycol monomethyl ether 2%, lauryl sodium sulfate 0.5%, APG 0.8%, polyacrylic acid
Sodium 0.3%, EDTA-2Na 1.0%, hydroxymethyl cellulose 1%, water surplus.
Embodiment 3:KOH 3%, propylene glycol monomethyl ether 3%, lauryl sodium sulfate 0.5%, APG 0.8%, polyacrylic acid
Sodium 0.1%, EDTA-4Na 1.0%, hydroxymethyl cellulose 1%, water surplus.
Embodiment 4:KOH 3%, propylene glycol monomethyl ether 3%, lauryl sodium sulfate 0.5%, APG 1.0%, polyacrylic acid
Sodium 0.1%, sodium citrate 1.0%, hydroxymethyl cellulose 1%, water surplus.
Embodiment 5:KOH 4%, propylene glycol monomethyl ether 2%, lauryl sodium sulfate 0.5%, APG 0.5%, polyacrylic acid
Sodium 0.3%, EDTA-4Na 1.0%, hydroxymethyl cellulose 1%, water surplus.
Embodiment 6:KOH 1%, propylene glycol monomethyl ether 2%, lauryl sodium sulfate 0.1%, APG 0.1%, polyacrylic acid
Sodium 0.05%, EDTA-4Na 0.1%, hydroxymethyl cellulose 1%, water surplus.
Embodiment 7:KOH 1%, propandiol butyl ether 3%, lauryl sodium sulfate 0.1%, APG 0.1%, polyacrylic acid
Sodium 0.05%, EDTA-4Na 0.1%, hydroxymethyl cellulose 1%, water surplus.
Embodiment 8:KOH 8%, diethylene glycol ether 4%, lauryl sodium sulfate 1.5%, APG 2%, polyacrylic acid
Sodium 0.5%, sodium gluconate 1.5%, hydroxymethyl cellulose 2%, water surplus.
Embodiment 9:KOH 10%, propylene glycol monomethyl ether 5%, lauryl sodium sulfate 2%, APG 3%, Sodium Polyacrylate
1%, EDTA2%, hydroxymethyl cellulose 3%, water surplus.
In conclusion the present invention compared with simple glass cleaning agent, has and cleans up, do not hinder white glass, can prevent dirt
Dirty redeposited advantage.
The above embodiment is a preferred embodiment of the present invention, but embodiments of the present invention are not by above-described embodiment
Limitation, it is other it is any without departing from the spirit and principles of the present invention made by changes, modifications, substitutions, combinations, simplifications,
Equivalent substitute mode is should be, is included within the scope of the present invention.