CN108659937A - Water base clay lubricant - Google Patents

Water base clay lubricant Download PDF

Info

Publication number
CN108659937A
CN108659937A CN201810406408.7A CN201810406408A CN108659937A CN 108659937 A CN108659937 A CN 108659937A CN 201810406408 A CN201810406408 A CN 201810406408A CN 108659937 A CN108659937 A CN 108659937A
Authority
CN
China
Prior art keywords
lubricant
water
water base
clay
present
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810406408.7A
Other languages
Chinese (zh)
Inventor
黄继生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810406408.7A priority Critical patent/CN108659937A/en
Publication of CN108659937A publication Critical patent/CN108659937A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses water base clay lubricants, are prepared by following weight percent raw material：Talcum powder 31%, sodium carboxymethylcellulose 0.3%, diatomite 0.6%, sodium pyrophosphate 5%, aluminum stearate 1%, borax 5%, polyethylene glycol 9%, glyceryl monostearate 0.8%, surplus are water, the present invention improves without the high problem of friction coefficient of graphite lubricant, provides one kind for the water base lubricant of hot rolled seamless steel tube and is uniformly dispersed, sprays easy, high temperature resistant, high lubricating effect, the free of contamination environmentally-friendly water-based clay lubricant of easy cleaning.

Description

Water base clay lubricant
Technical field
The present invention relates to water base clay lubricants.
Background technology
Mandrel lubrication is an important link of Metal Forming process in hot rolled seamless steel tube, hot finished steel pipe by with When plug is perforated, it can improve tube rolling lengthening coefficient, surface smoothness, extend plug service life, reduce draught pressure with And energy consumption, rolling accident is reduced or avoided, thus each state of our times is all continuously improving core rod lubricant agent technology.Current heat gold The processing of metal surface is mainly by colloidal graphite mixed with water, but many hidden danger are (such as conductive, difficult cleaning, pollution caused by it Weight) it is increasingly subject to everybody concern.There is a series of no graphitic lubricant research approach in succession, still, opposite greasy property is also There is a problem of certain.
Invention content
The purpose of the present invention is overcoming the shortcomings of in existing product, water base clay lubricant is provided.
In order to achieve the above object, the present invention is achieved by the following technical solutions：
Water base clay lubricant is prepared by following weight percent raw material：Talcum powder 31%, sodium carboxymethylcellulose 0.3%, diatomite 0.6%, sodium pyrophosphate 5%, aluminum stearate 1%, borax 5%, polyethylene glycol 9%, glyceryl monostearate 0.8%, surplus is water.
Beneficial effects of the present invention are as follows：The present invention improves without the high problem of friction coefficient of graphite lubricant, be hot rolling without The water base lubricant of seam steel pipe provides that one kind is uniformly dispersed, spray easy, high temperature resistant, high lubricating effect, easy cleaning free of contamination Environmentally-friendly water-based clay lubricant.
Specific implementation mode
Technical scheme of the present invention is described further below：
Embodiment 1：
Water base clay lubricant is prepared by following weight percent raw material：Talcum powder 31%, sodium carboxymethylcellulose 0.3%, diatomite 0.6%, sodium pyrophosphate 5%, aluminum stearate 1%, borax 5%, polyethylene glycol 9%, glyceryl monostearate 0.8%, surplus is water.
The present invention improves without the high problem of friction coefficient of graphite lubricant, is provided for the water base lubricant of hot rolled seamless steel tube One kind is uniformly dispersed, spraying is easy, high temperature resistant, high lubricating effect, the free of contamination environmentally-friendly water-based clay lubricant of easy cleaning.
It should be noted that listed above is only a kind of specific embodiment of the present invention.It is clear that the invention is not restricted to Upper embodiment, can also be there are many deforming, in short, those skilled in the art can directly lead from present disclosure All deformations for going out or associating, are considered as protection scope of the present invention.

Claims (1)

1. water base clay lubricant, which is characterized in that be prepared by following weight percent raw material：Talcum powder 31%, carboxylic first Base sodium cellulosate 0.3%, diatomite 0.6%, sodium pyrophosphate 5%, aluminum stearate 1%, borax 5%, polyethylene glycol 9% are stearic Sour monoglyceride 0.8%, surplus are water.
CN201810406408.7A 2018-04-30 2018-04-30 Water base clay lubricant Withdrawn CN108659937A (en)