CN108641525A - A kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating - Google Patents
A kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating Download PDFInfo
- Publication number
- CN108641525A CN108641525A CN201810425451.8A CN201810425451A CN108641525A CN 108641525 A CN108641525 A CN 108641525A CN 201810425451 A CN201810425451 A CN 201810425451A CN 108641525 A CN108641525 A CN 108641525A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- heat dissipating
- special heat
- dissipating coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods reducing palm of the hand perspiration mouse Special heat dissipating coating, include the following steps：It is spare to weigh following corresponding raw material for step 1：32 34 parts of acrylic resin, 12 16 parts of water-absorbing resin, 12 14 parts of phosphate, 10 16 parts of blend of foaming, 8 14 parts of negative ion powder, 48 parts of resistance sweat intensive, 10 20 parts of organic solvent.The object of the present invention is to provide a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating, which can make hand be not easy to perspire, and improve user's usage comfort, while having higher use value and good application prospect.
Description
Technical field
The present invention relates to heat radiation coating technical fields, and in particular to one kind can reduce palm of the hand perspiration mouse Special heat dissipating coating
Preparation method.
Background technology
In today of information age, the utilization of computer is very universal, and in addition to the operation of touch screen, general we can pass through
It clicks mouse to be operated, mouse is a kind of input equipment and the calculator display organization coordinate setting in length and breadth of computer
Indicator is gained the name because being similar to mouse, and it is quick that the use of mouse is that the operation is more convenient in order to make computer, to replace keyboard
That cumbersome instruction, mouse can be divided into mechanical mouse and optical mouse by the difference of its operation principle, mechanical mouse mainly by
Spin, roller and grating signal sensor composition drive ball turns, spin that roller is driven to rotate again when you drag mouse,
The photoelectric pulse signal that grating signal sensor mounted in roller end generates reflects Genius mouse vertically and horizontally
Change in displacement, then the movement of onscreen cursor arrow is controlled by the processing of computer program and conversion, and summer exists for a long time
When using mouse, hand is in direct contact with mouse, is easy to cause palm of the hand perspiration, is caused user uncomfortable, it is therefore desirable to design
A kind of mouse surface coating can reduce palm of the hand perspiration, and user is easy to use, comfortably.
Existing mouse coating can only make to reach heat sinking function inside mouse, extension mouse service life, and hand and mouse
It is contacted between long-term, is easy to perspire, cause user to use uncomfortable.
Invention content
In view of the drawbacks of the prior art, palm of the hand perspiration mouse Special heat dissipating can be reduced the object of the present invention is to provide one kind to apply
The preparation method of material, the coating can make hand be not easy to perspire, and improve user's usage comfort.
The present invention solves technical problem and adopts the following technical scheme that：
The present invention provides a kind of preparation methods reducing palm of the hand perspiration mouse Special heat dissipating coating, including following step
Suddenly：
It is spare to weigh following corresponding raw material for step 1：32-34 parts of acrylic resin, 12-16 parts of water-absorbing resin,
12-14 parts of phosphate, 10-16 parts of blend of foaming, 8-14 parts of negative ion powder, 4-8 parts of sweat intensive of resistance, organic solvent 10-20
Part；
Acrylic resin, organic solvent, water-absorbing resin, phosphate in step 1 is sent in reaction kettle by step 2,
Reaction temperature is 120-140 DEG C, keeps the temperature 15-25min, obtains mixture A, then by mixture A, foaming blend, anion
Powder, resistance sweat intensive be sent into homogenizer in, speed of agitator 525-625r/min, mixing time be 25-35min to get
The heat radiation coating of the present invention.
Preferably, in the step 1 foaming mixture preparation method alumina powder, glass powder, zeolite powder are sent to plus
In hot stove, temperature is first risen to 125-135 DEG C, reacts 25-35min, then rises to 755-855 DEG C, keeps the temperature 35-45min, then
Heating is re-sintered, finally takes out and is cooled to room temperature to get foaming mixture.
Preferably, the foaming mixture specific surface area is 4-6m2/ g, gap 0.01-0.11mm.
Preferably, negative ion powder is tourmaline powder in the step 1.
Preferably, the tourmaline powder grain size is 100-200 mesh.
Preferably, resistance sweat intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 2 in the step 1:(5-9)
The mixture of composition.
Preferably, resistance sweat intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 2 in the step 1:7 compositions
Mixture.
Preferably, the interlayer cation of the al bentonite is aluminium ion.
Preferably, organic solvent is ethylene glycol ether in the step 1.
Compared with prior art, the present invention has following advantageous effect：
(1) a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating of the invention, acrylic resin are made
For the body material of the present invention, so that mouse surface is protected, light colour retention is good, and the chlorination hydroxyl aluminium of addition, al bentonite can be very
Secretion sweat is prevented in big degree, foam blend large specific surface area, and porosity is high, can absorb moisture, in foaming blend association
It helps down, volatilization is greatly absorbed by the sweat that water-absorbing resin goes out the palm of the hand, cooperative effect is played between raw material, then reduces
Sweat on the palm of the hand.
(2) a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating of the invention, resistance sweat of the invention
Intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 2:The chlorination hydroxyl aluminium of (5-9), addition can inhibit sweat gland secretion,
Al bentonite is set to expand when the sweat of sweat gland secretion acts on al bentonite simultaneously, active area increases, and aluminium base is swollen in addition
Profit soil release aluminium ion, collaboration chlorination hydroxyl aluminium collective effect sweat gland further inhibit sweat gland secretion, the two to play cooperative effect,
Then the palm of the hand is reduced to perspire.
(3) a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating of the invention, the coating can make
Hand is not easy to perspire, and improves user's usage comfort, while having higher use value and good application prospect.
Specific implementation mode
With reference to specific embodiment, technical scheme in the embodiment of the invention is clearly and completely described, shows
So, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the reality in the present invention
Example is applied, every other embodiment obtained by those of ordinary skill in the art without making creative efforts all belongs to
In the scope of protection of the invention.
Embodiment 1.
A kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating of the present embodiment, includes the following steps：
It is spare to weigh following corresponding raw material for step 1：32 parts of acrylic resin, 12 parts of water-absorbing resin, phosphate
12 parts, 10 parts of blend of foaming, 8 parts of negative ion powder, 4 parts of resistance sweat intensive, 10 parts of organic solvent；
Acrylic resin, organic solvent, water-absorbing resin, phosphate in step 1 is sent in reaction kettle by step 2,
Reaction temperature is 120 DEG C, keeps the temperature 15min, obtains mixture A, then by mixture A, foaming blend, negative ion powder, resistance sweat
Intensive is sent into homogenizer, speed of agitator 525r/min, and mixing time is heat-radiation coatings of the 25min to get the present invention
Material.
Preferably, in the step 1 foaming mixture preparation method alumina powder, glass powder, zeolite powder are sent to plus
In hot stove, temperature is first risen to 125 DEG C, reacts 25min, then rises to 755 DEG C, 35min is kept the temperature, then re-sinters heating, most
It takes out and is cooled to room temperature to get foaming mixture afterwards.
The foaming mixture specific surface area of the present embodiment is 4m2/ g, gap 0.01mm.
Negative ion powder is tourmaline powder in the step of the present embodiment one.
The tourmaline powder grain size of the present embodiment is 100 mesh.
Resistance sweat intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 2 in the step of the present embodiment one:5 compositions
Mixture.
The interlayer cation of the al bentonite of the present embodiment is aluminium ion.
Organic solvent is ethylene glycol ether in the step of the present embodiment one.
Embodiment 2.
A kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating of the present embodiment, includes the following steps：
It is spare to weigh following corresponding raw material for step 1：34 parts of acrylic resin, 16 parts of water-absorbing resin, phosphate
14 parts, 16 parts of blend of foaming, 14 parts of negative ion powder, 8 parts of resistance sweat intensive, 20 parts of organic solvent；
Acrylic resin, organic solvent, water-absorbing resin, phosphate in step 1 is sent in reaction kettle by step 2,
Reaction temperature is 140 DEG C, keeps the temperature 25min, obtains mixture A, then by mixture A, foaming blend, negative ion powder, resistance sweat
Intensive is sent into homogenizer, speed of agitator 625r/min, and mixing time is heat-radiation coatings of the 35min to get the present invention
Material.
Preferably, in the step 1 foaming mixture preparation method alumina powder, glass powder, zeolite powder are sent to plus
In hot stove, temperature is first risen to 135 DEG C, reacts 35min, then rises to 855 DEG C, 45min is kept the temperature, then re-sinters heating, most
It takes out and is cooled to room temperature to get foaming mixture afterwards.
The foaming mixture specific surface area of the present embodiment is 6m2/ g, gap 0.11mm.
Negative ion powder is tourmaline powder in the step of the present embodiment one.
The tourmaline powder grain size of the present embodiment is 200 mesh.
Resistance sweat intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 2 in the step of the present embodiment one:9 compositions
Mixture.
The interlayer cation of the al bentonite of the present embodiment is aluminium ion.
Organic solvent is ethylene glycol ether in the step of the present embodiment one.
Embodiment 3.
A kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating of the present embodiment, includes the following steps：
It is spare to weigh following corresponding raw material for step 1：33 parts of acrylic resin, 14 parts of water-absorbing resin, phosphate
13 parts, 13 parts of blend of foaming, 11 parts of negative ion powder, 6 parts of resistance sweat intensive, 15 parts of organic solvent；
Acrylic resin, organic solvent, water-absorbing resin, phosphate in step 1 is sent in reaction kettle by step 2,
Reaction temperature is 130 DEG C, keeps the temperature 20min, obtains mixture A, then by mixture A, foaming blend, negative ion powder, resistance sweat
Intensive is sent into homogenizer, speed of agitator 600r/min, and mixing time is heat-radiation coatings of the 30min to get the present invention
Material.
Preferably, in the step 1 foaming mixture preparation method alumina powder, glass powder, zeolite powder are sent to plus
In hot stove, temperature is first risen to 130 DEG C, reacts 30min, then rises to 800 DEG C, 40min is kept the temperature, then re-sinters heating, most
It takes out and is cooled to room temperature to get foaming mixture afterwards.
The foaming mixture specific surface area of the present embodiment is 5m2/ g, gap 0.06mm.
Negative ion powder is tourmaline powder in the step of the present embodiment one.
The tourmaline powder grain size of the present embodiment is 150 mesh.
Resistance sweat intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 2 in the step of the present embodiment one:7 compositions
Mixture.
The interlayer cation of the al bentonite of the present embodiment is aluminium ion.
Organic solvent is ethylene glycol ether in the step of the present embodiment one.
Embodiment 4.
A kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating of the present embodiment, includes the following steps：
It is spare to weigh following corresponding raw material for step 1：32.5 parts of acrylic resin, 13 parts of water-absorbing resin, phosphoric acid
12.5 parts of ester, 12 parts of blend of foaming, 10 parts of negative ion powder, 5 parts of resistance sweat intensive, 14 parts of organic solvent；
Acrylic resin, organic solvent, water-absorbing resin, phosphate in step 1 is sent in reaction kettle by step 2,
Reaction temperature is 125 DEG C, keeps the temperature 18min, obtains mixture A, then by mixture A, foaming blend, negative ion powder, resistance sweat
Intensive is sent into homogenizer, speed of agitator 550r/min, and mixing time is heat-radiation coatings of the 28min to get the present invention
Material.
Preferably, in the step 1 foaming mixture preparation method alumina powder, glass powder, zeolite powder are sent to plus
In hot stove, temperature is first risen to 132 DEG C, reacts 32min, then rises to 800 DEG C, 34min is kept the temperature, then re-sinters heating, most
It takes out and is cooled to room temperature to get foaming mixture afterwards.
The foaming mixture specific surface area of the present embodiment is 4.5m2/ g, gap 0.06mm.
Negative ion powder is tourmaline powder in the step of the present embodiment one.
The tourmaline powder grain size of the present embodiment is 140 mesh.
Resistance sweat intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 1 in the step of the present embodiment one:3 compositions
Mixture.
The interlayer cation of the al bentonite of the present embodiment is aluminium ion.
Organic solvent is ethylene glycol ether in the step of the present embodiment one.
Embodiment 5.
A kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating of the present embodiment, includes the following steps：
It is spare to weigh following corresponding raw material for step 1：33.5 parts of acrylic resin, 15 parts of water-absorbing resin, phosphoric acid
13.5 parts of ester, 15 parts of blend of foaming, 13 parts of negative ion powder, 7 parts of resistance sweat intensive, 18 parts of organic solvent；
Acrylic resin, organic solvent, water-absorbing resin, phosphate in step 1 is sent in reaction kettle by step 2,
Reaction temperature is 135 DEG C, keeps the temperature 20min, obtains mixture A, then by mixture A, foaming blend, negative ion powder, resistance sweat
Intensive is sent into homogenizer, speed of agitator 580r/min, and mixing time is heat-radiation coatings of the 32min to get the present invention
Material.
Preferably, in the step 1 foaming mixture preparation method alumina powder, glass powder, zeolite powder are sent to plus
In hot stove, temperature is first risen to 132 DEG C, reacts 32min, then rises to 820 DEG C, 42min is kept the temperature, then re-sinters heating, most
It takes out and is cooled to room temperature to get foaming mixture afterwards.
The foaming mixture specific surface area of the present embodiment is 5.5m2/ g, gap 0.08mm.
Negative ion powder is tourmaline powder in the step of the present embodiment one.
The tourmaline powder grain size of the present embodiment is 160 mesh.
Resistance sweat intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 1 in the step of the present embodiment one:4 compositions
Mixture.
The interlayer cation of the al bentonite of the present embodiment is aluminium ion.
Organic solvent is ethylene glycol ether in the step of the present embodiment one.
It draws a conclusion by many experiments and performance test, in embodiment 1-3, one kind of the invention can reduce the palm of the hand and go out
The preparation method of sweat mouse Special heat dissipating coating, the coating can make hand be not easy to perspire, and improve user's usage comfort, together
When have higher use value and good application prospect.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (9)
1. a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating, which is characterized in that include the following steps：
It is spare to weigh following corresponding raw material for step 1：32-34 parts of acrylic resin, 12-16 parts of water-absorbing resin, phosphoric acid
12-14 parts of ester, 10-16 parts of blend of foaming, 8-14 parts of negative ion powder, 4-8 parts of sweat intensive of resistance, 10-20 parts of organic solvent；
Acrylic resin, organic solvent, water-absorbing resin, phosphate in step 1 is sent in reaction kettle by step 2, reaction
Temperature is 120-140 DEG C, keeps the temperature 15-25min, obtains mixture A, then by mixture A, foaming blend, negative ion powder, resistance
Sweat intensive is sent into homogenizer, speed of agitator 525-625r/min, and mixing time is 25-35min to get the present invention
Heat radiation coating.
2. a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating according to claim 1, feature
It is, alumina powder, glass powder, zeolite powder are sent in heating furnace by foaming mixture preparation method in the step 1, first
Temperature is risen to 125-135 DEG C, reacts 25-35min, then rises to 755-855 DEG C, keeps the temperature 35-45min, then re-sinters and adds
Heat is finally taken out and is cooled to room temperature to get foaming mixture.
3. a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating according to claim 2, feature
It is, the foaming mixture specific surface area is 4-6m2/ g, gap 0.01-0.11mm.
4. a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating according to claim 1, feature
It is, negative ion powder is tourmaline powder in the step 1.
5. a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating according to claim 4, feature
It is, the tourmaline powder grain size is 100-200 mesh.
6. a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating according to claim 1, feature
It is, resistance sweat intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 2 in the step 1:（5-9）The mixing of composition
Object.
7. a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating according to claim 6, feature
It is, resistance sweat intensive is chlorination hydroxyl aluminium, al bentonite according to weight ratio 2 in the step 1:The mixture of 7 compositions.
8. a kind of preparation method reducing palm of the hand perspiration mouse Special heat dissipating coating according to claim 6, feature
It is, the interlayer cation of the al bentonite is aluminium ion.
9. a kind of preparation method of the resistance to greasy dirt resistant to dust protective film in vehicle glass surface according to claim 1, feature
It is, organic solvent is ethylene glycol ether in the step 1.