CN108640597A - Method for preparing carbon-fixing pervious concrete by utilizing waste concrete - Google Patents
Method for preparing carbon-fixing pervious concrete by utilizing waste concrete Download PDFInfo
- Publication number
- CN108640597A CN108640597A CN201810467809.3A CN201810467809A CN108640597A CN 108640597 A CN108640597 A CN 108640597A CN 201810467809 A CN201810467809 A CN 201810467809A CN 108640597 A CN108640597 A CN 108640597A
- Authority
- CN
- China
- Prior art keywords
- waste gas
- industrial waste
- pervious concrete
- concrete
- pervious
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a method for preparing carbon-fixing pervious concrete by utilizing waste concrete, which comprises the steps of crushing the waste concrete to obtain required aggregate, simultaneously carrying out dust removal treatment on industrial waste gas, mixing the industrial waste gas with air to control the required temperature, carrying out carbonization reaction on the industrial waste gas and a blended pervious concrete mixture, then, when the pervious concrete mixture enters a prefabrication molding and hardening maintenance stage, mixing the carbonized industrial waste gas with the non-carbonized industrial waste gas after dust removal, injecting the mixed industrial waste gas into a pervious concrete carbon-fixing chamber to carry out carbonization reaction with the pervious concrete, and thus, repeatedly circulating the industrial waste gas to carry out carbonization reaction with the pervious concrete until prefabrication maintenance is finished. Therefore, the method can fix the carbon dioxide in the industrial waste gas in the preparation process of the pervious concrete, can reduce the content of the carbon dioxide in the industrial waste gas, can ensure the applicability of the pervious concrete, and realizes the resource utilization of the waste concrete.
Description
Technical field
It is specifically a kind of saturating using discarded concrete preparation carbon sequestration the present invention relates to a kind of preparation method of pervious concrete
The method of water coagulation soil.
Background technology
Currently, with the exacerbation of problem of environmental pollution, the discharge of greenhouse effects and greenhouse gases is increasingly taken seriously, greatly
Type Industrial Boiler, power plant flue gas in contain a large amount of carbon dioxide gas, if be largely discharged into air, it will to environment
Cause prodigious influence.It is existing research shows that:There is concrete the ability of absorbing carbon dioxide, the carbon of concrete to converge in full life
Can all it occur in period.
With the continuous development of urban modernization construction, each place in city, which can all use, arrives armored concrete, before city
City road surface is mainly waterproof pavement, since the respiratory of waterproof pavement is poor, can not permeate rainwater.And present life and work
Industry with water still based on underground water, excessive exploitation so that level of ground water drastically declines, and earth's surface ecology starts unbalance, environmental problem
It is increasingly severe.For recharge of groundwater resource, therefore more and more road surfaces are laid with using pervious concrete, pervious concrete
It is Eco-friendly concrete, pervious concrete has the characteristics that porous structure, porosity are big, can permeate rainwater, increases city
Groundwater resources improve urban climate, environmental protection.Pervious concrete can be widely used for square, pavement, in park road and
Parking lot etc..The patent No.:ZL201010185569.1, patent name are:" a kind of pervious concrete and preparation method thereof ", the party
Method prepares pervious concrete using Aggregate of recycled concrete and composite gel material, but not yet relates to how solid in preparation process
Determine carbon dioxide.Additionally, due at present there is more discarded concrete to cause to generate more building waste, environment is caused
It influences.Therefore, how to be fixed in pervious concrete preparation process using discarded concrete carbon dioxide in industrial waste gas at
For urgent need to resolve the problem of.
Invention content
It is permeable mixed using discarded concrete preparation carbon sequestration that in view of the above existing problems in the prior art, the present invention provides a kind of
The method for coagulating soil, can consolidate the carbon dioxide in industrial waste gas in pervious concrete preparation process using discarded concrete
It is fixed, to which discarded concrete can not only be utilized to reduce the content of carbon dioxide in industrial waste gas, while it can guarantee that carbon sequestration is permeable mixed
Coagulate the applicable performance of soil.
To achieve the goals above, the technical solution adopted by the present invention is:It is a kind of saturating using discarded concrete preparation carbon sequestration
The method of water coagulation soil, the specific steps are:
A, preliminary broken pretreatment carried out to discarded concrete using crushing plant, milled and screening process, to obtain
Required coarse aggregate and fine aggregate;
B, industrial waste gas is first passed through into dust filter unit and is dusted processing;
C, the industrial waste gas of dedusting is mixed with normal temperature air, make mixed industrial waste gas temperature be 30 DEG C~
40℃;
D, according to the performance parameter reached needed for pervious concrete, which need to meet country's mark of pervious concrete
Standard, and then determine the existing proportioning of the coarse aggregate and fine aggregate that are obtained in used reinforcing agent, cement, water and step A, then
Reinforcing agent, cement, water, coarse aggregate and fine aggregate in mixing vessel be mixed and form pervious concrete mixture,
The mixing time is 10~15min, continues into mixing vessel injection step C in mixed process treated industrial waste gas
Until stopping after being mixed, make pervious concrete mixture that carburizing reagent occur with the carbon dioxide in industrial waste gas,
And the industrial waste gas after carburizing reagent is collected;
E, pervious concrete mixture is placed in prefabricated mould, and ensures the quality of vibrating needed for pervious concrete,
Then prefabricated mould is put into closed pervious concrete carbon sequestration room, then the injection step C into pervious concrete carbon sequestration room
Treated industrial waste gas, while making the indoor humidity of pervious concrete carbon sequestration be 60%~80% by humidifier, make coagulation
Native mixture continues that carburizing reagent occurs with the carbon dioxide in industrial waste gas, and the industrial waste gas after carburizing reagent is received
Collection, curing time of the concrete in prefabricated mould are not less than 15 days;
F, the industrial waste gas after carburizing reagent that step D and step E is collected is replaced normal temperature air in step C and removed
The industrial waste gas of dirt is mixed, and it is 30 DEG C~40 DEG C to make mixed industrial waste gas temperature, and refills pervious concrete
It in carbon sequestration room, moves in circles, final industrial waste gas is discharged after the concrete curing time until reaching, while from prefabricated mould
It is middle to take out Manufactured pervious concrete.
Further, pervious concrete carbon sequestration room is transparent rubber tank body, and volume is the 3~5 of prefabricated mould volume
Times.
Further, the cement is the Portland cement that compression strength is not less than 42.5 grades.
Compared with prior art, the present invention is used is added pervious concrete preparation process by discarded concrete and industrial waste gas
Mode, first discarded concrete is crushed, obtains coarse aggregate and fine aggregate, while processing is dusted to industrial waste gas,
Avoiding the dust that it is rich in influences the quality of pervious concrete, then mixes industrial waste gas with air, controlled at 30
DEG C~40 DEG C, the waste heat of industrial waste gas can be made full use of in this way, can accelerate the dioxy in discarded concrete absorption industrial waste gas
Change carbon gas, and can be due to the intensity of discarded concrete carburizing reagent raising pervious concrete in preparation process.Therefore saturating
It is passed through industrial waste gas in water coagulation earth forming and hardening process, the carbon dioxide in industrial waste gas can be fixed, temperature is reduced
The discharge of room gas;Pervious concrete carbon sequestration indoor humidity is controlled 60%~80%, the maintenance of pervious concrete is contributed to
And the fixation carbon dioxide of high-speed, the industrial waste gas being carbonized is mixed with the industrial waste gas after dedusting, and repetitive cycling
Into concrete carbon sequestration room, the purpose is to reduce the carbon dioxide content for being discharged into industrial waste gas in air to greatest extent.Therefore this
Invention can not only reduce the content of carbon dioxide in industrial waste gas, while can guarantee the applicable performance of pervious concrete, in addition real
Show discarded concrete recycling, reduces building waste.
Specific implementation mode
The invention will be further described below.
Embodiment:The present invention the specific steps are:
A, preliminary broken pretreatment carried out to discarded concrete using crushing plant, milled and screening process, to obtain
Required coarse aggregate and fine aggregate;
B, industrial waste gas is first passed through into dust filter unit and is dusted processing;
C, the industrial waste gas of dedusting is mixed with normal temperature air, make mixed industrial waste gas temperature be 30 DEG C~
40℃;
D, according to the performance parameter reached needed for pervious concrete, which need to meet country's mark of pervious concrete
Standard, and then determine the existing proportioning of the coarse aggregate and fine aggregate that are obtained in used reinforcing agent, cement, water and step A, then
Reinforcing agent, cement, water, coarse aggregate and fine aggregate in mixing vessel be mixed and form pervious concrete mixture,
The mixing time is 10~15min, continues into mixing vessel injection step C in mixed process treated industrial waste gas
Until stopping after being mixed, make pervious concrete mixture that carburizing reagent occur with the carbon dioxide in industrial waste gas,
And the industrial waste gas after carburizing reagent is collected;
E, pervious concrete mixture is placed in prefabricated mould, and ensures the quality of vibrating needed for pervious concrete,
Then prefabricated mould is put into closed pervious concrete carbon sequestration room, then the injection step C into pervious concrete carbon sequestration room
Treated industrial waste gas, while making the indoor humidity of pervious concrete carbon sequestration be 60%~80% by humidifier, make coagulation
Native mixture continues that carburizing reagent occurs with the carbon dioxide in industrial waste gas, and the industrial waste gas after carburizing reagent is received
Collection, curing time of the concrete in prefabricated mould are not less than 15 days;
F, the industrial waste gas after carburizing reagent that step D and step E is collected is replaced normal temperature air in step C and removed
The industrial waste gas of dirt is mixed, and it is 30 DEG C~40 DEG C to make mixed industrial waste gas temperature, and refills pervious concrete
It in carbon sequestration room, moves in circles, final industrial waste gas is discharged after the concrete curing time until reaching, while from prefabricated mould
It is middle to take out Manufactured pervious concrete.
Further, concrete carbon sequestration room is transparent rubber tank body, and volume is 3~5 times of prefabricated mould volume;It adopts
With transparent rubber tank body convenient for the maintenance situation of observation pervious concrete, and volume uses 3~5 times of prefabricated mould volume,
Can guarantee in concrete carbon sequestration room, there is enough spaces to carry out carburizing reagent for industrial waste gas and pervious concrete.
Further, Portland cement or other kinds of the compression strength not less than 42.5 grades may be used in the cement
Cement, it is preferred to use compression strength is not less than 42.5 grades of Portland cement, not only can reach required compression strength, and
And its carbonation rate is faster, carbon sequestration effect is more preferable.
Claims (3)
1. a kind of method preparing carbon sequestration pervious concrete using discarded concrete, which is characterized in that the specific steps are:
A, preliminary broken pretreatment carried out to discarded concrete using crushing plant, milled and screening process, needed for obtaining
Coarse aggregate and fine aggregate;
B, industrial waste gas is first passed through into dust filter unit and is dusted processing;
C, the industrial waste gas of dedusting is mixed with normal temperature air, it is 30 DEG C~40 to make mixed industrial waste gas temperature
℃;
D, according to the performance parameter reached needed for pervious concrete, in reinforcing agent, cement, water and step A used by determining
Then the proportioning of the coarse aggregate and fine aggregate that arrive carries out reinforcing agent, cement, water, coarse aggregate and fine aggregate in mixing vessel
Mixing forms pervious concrete mixture, and the mixing time is 10~15min, in mixed process into mixing vessel
Stop after continuing injection step C treated industrial waste gas until being mixed, makes pervious concrete mixture and industry
Carburizing reagent occurs for the carbon dioxide in exhaust gas, and the industrial waste gas after carburizing reagent is collected;
E, pervious concrete mixture is placed in prefabricated mould, and ensures the quality of vibrating needed for pervious concrete, then
Prefabricated mould is put into closed pervious concrete carbon sequestration room, the then injection step C processing into pervious concrete carbon sequestration room
Industrial waste gas afterwards, while making the indoor humidity of pervious concrete carbon sequestration be 60%~80% by humidifier, so that concrete is mixed
It closes object to continue that carburizing reagent occurs with the carbon dioxide in industrial waste gas, and the industrial waste gas after carburizing reagent is collected,
Curing time of the concrete in prefabricated mould is not less than 15 days;
F, the industrial waste gas after the carburizing reagent of step D and step E collections is replaced into the normal temperature air in step C and dedusting
Industrial waste gas is mixed, and it is 30 DEG C~40 DEG C to make mixed industrial waste gas temperature, and refills pervious concrete carbon sequestration
Interior is moved in circles, until final industrial waste gas is discharged after reaching the concrete curing time, while being taken from prefabricated mould
Go out Manufactured pervious concrete.
2. a kind of method preparing carbon sequestration pervious concrete using discarded concrete according to claim 1, feature exist
In pervious concrete carbon sequestration room is transparent rubber tank body, and volume is 3~5 times of prefabricated mould volume.
3. a kind of method preparing carbon sequestration pervious concrete using discarded concrete according to claim 1, feature exist
In the cement is the Portland cement that compression strength is not less than 42.5 grades.