CN108635744A - A kind of special treadbelt of household treadmill and its manufacturing method - Google Patents
A kind of special treadbelt of household treadmill and its manufacturing method Download PDFInfo
- Publication number
- CN108635744A CN108635744A CN201810192744.6A CN201810192744A CN108635744A CN 108635744 A CN108635744 A CN 108635744A CN 201810192744 A CN201810192744 A CN 201810192744A CN 108635744 A CN108635744 A CN 108635744A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- framework material
- treadbelt
- coated
- special
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of special treadbelt of household treadmill and its manufacturing methods, it is made of framework material and the polyvinyl chloride coat coated on framework material side, wherein, framework material is the woven fabric of 3/1 brokentwlllweave structure, warp thread is 1000D lower shrinkage nylon multifilament in above-mentioned woven fabric, and weft yarn is 0.3mm ultralow contractive polyester monofilament；Ensure the adhesive property of framework material and polyvinyl chloride coat, ensure that primer in polyvinyl chloride coat and capstock fully melt by the coating processes of optimization, further increase the adhesion strength of framework material and polyvinyl chloride coat, to reduce the treadbelt lamination problem, its service life is effectively improved.
Description
Technical field
The invention belongs to treadmill accessory technical fields, and in particular to a kind of special treadbelt of household treadmill and its manufacturer
Method.
Background technology
With the continuous improvement of people’s lives level, operating pressure causes sub-health population accounting also growing day by day
Cumulative year after year, therefore, the problem of health problem is increasingly paid close attention to as people, motion exercise is also increasingly by the joyous of people
It meets, wherein movement of being run or hurried up using household treadmill is even more the main means for becoming people's daily exercise and taking exercise.
Household treadmill is usually to be made of board, arm-rest frame, operation panel, race plate and treadmill belt.When person taking exercise exists
When moving above, rub between treadmill belt and race plate.This friction will produce electrostatic, conducts and accumulates in user's body
It can make us uncomfortable on body, when user is in operation and control panel, the electrostatic charge accumulated on body is possible to conduction extremely
Electronic component in control panel, causes the damage of electronic component, and then allows treadmill that can not continue normal function and running,
Or it is easy to cause user injured because of static guiding.Therefore, it is necessary to reduce the friction of household running belt of running machine, to which minimizing electrostatic is asked
Topic.
Invention content
To overcome the defect of the above-mentioned prior art, the purpose of the present invention is to provide a kind of special treadbelts of household treadmill；
In addition, also providing the manufacturing method of the above-mentioned special treadbelt of household treadmill.
The above-mentioned purpose of the present invention is achieved through the following technical solutions：
A kind of special treadbelt of household treadmill is applied by framework material with the polyvinyl chloride coated on the framework material side
Coating forms, wherein the framework material is the woven fabric of 3/1 brokentwlllweave structure；The warp thread of the woven fabric is the low receipts of 1000D
Contracting nylon multifilament, weft yarn are 0.3mm ultralow contractive polyester monofilament.
The polyvinyl chloride coat by coated on the framework material side polyvinyl chloride primer and be coated on institute
State the polyvinyl chloride top material composition on polyvinyl chloride primer.
Further, the thickness of the framework material is 2.4~2.6mm.
The second aspect of the present invention, the manufacturing method of the above-mentioned special treadbelt of household treadmill, specifically, including following step
Suddenly：
S1, framework material drying and shaping；
S2, coating polyvinyl chloride coat；
S3, toe joint connector to get；Wherein,
In step S1, the drying and shaping temperature is 180~200 DEG C；
In step S2, the method for the coating polyvinyl chloride coat is：First one layer is coated on the framework material surface
Polyvinyl chloride primer, then a strata vinyl chloride capstock is coated on the primer, wherein polyvinyl chloride primer glues
Degree is 2000~3000mPa.s, and coated weight is 150~180g/mm2, coating speed is 6~8m/min；The polyvinyl chloride face
The viscosity of layered material is 2500~3000mPa.s, and coated weight is 200~300g/mm2, coating speed is 8~10m/min.
Compared with prior art, the beneficial effects of the present invention are：
One, warp thread uses lower shrinkage nylon multifilament in framework material of the invention, it is ensured that framework material is applied with polyvinyl chloride
The adhesive property of coating effectively improves its service life to reduce the treadbelt lamination problem.
Two, by the coating processes of optimization ensure polyvinyl chloride coat in primer and capstock fully melt, into
One step improves the adhesion strength of framework material and polyvinyl chloride coat.
Description of the drawings
Fig. 1 is the partial schematic diagram of the special treadbelt of present inventor's treadmill.
Specific implementation mode
Present pre-ferred embodiments are provided below in conjunction with the accompanying drawings, with the technical solution that the present invention will be described in detail, but the present invention
Protection domain be not limited to following embodiments.
Embodiment 1
The manufacturing method of the special treadbelt of household treadmill specifically includes the following steps：
The first step, framework material drying and shaping：Framework material is put into closed drying in oven and roll-in to surface is put down
Whole, bubble-free, it is 180 DEG C to control the drying temperature in closed baking oven.Wherein, framework material is the machine of 3/1 brokentwlllweave structure
Fabric, wherein warp thread is 1000D lower shrinkage nylon multifilament, and weft yarn is 0.3mm ultralow contractive polyester monofilament, the thickness of framework material
Degree is 2.4mm.
Second step, coating polyvinyl chloride coat：A strata vinyl chloride primer first is coated on the framework material surface,
A strata vinyl chloride capstock is coated on the primer again, wherein the viscosity of polyvinyl chloride primer is 2000mPa.s,
Coated weight is 150g/mm2, coating speed 6m/min；The viscosity of polyvinyl chloride top material is 2500mPa.s, and coated weight is
200g/mm2, coating speed 8m/min.
Third step, is beaten after tooth, hot pressing and finishing up to the special treadbelt of household treadmill at positioning.
Embodiment 2
The manufacturing method of the special treadbelt of household treadmill specifically includes the following steps：
The first step, framework material drying and shaping：Framework material is put into closed drying in oven and roll-in to surface is put down
Whole, bubble-free, it is 190 DEG C to control the drying temperature in closed baking oven.Wherein, framework material is the machine of 3/1 brokentwlllweave structure
Fabric, wherein warp thread is 1000D lower shrinkage nylon multifilament, and weft yarn is 0.3mm ultralow contractive polyester monofilament, the thickness of framework material
Degree is 2.5mm.
Second step, coating polyvinyl chloride coat：A strata vinyl chloride primer first is coated on the framework material surface,
A strata vinyl chloride capstock is coated on the primer again, wherein the viscosity of polyvinyl chloride primer is 2500mPa.s,
Coated weight is 170g/mm2, coating speed 7m/min；The viscosity of polyvinyl chloride top material is 2800mPa.s, and coated weight is
250g/mm2, coating speed 9m/min.
Third step, is beaten after tooth, hot pressing and finishing up to the special treadbelt of household treadmill at positioning.
Embodiment 3
The manufacturing method of the special treadbelt of household treadmill specifically includes the following steps：
The first step, framework material drying and shaping：Framework material is put into closed drying in oven and roll-in to surface is put down
Whole, bubble-free, it is 200 DEG C to control the drying temperature in closed baking oven.Wherein, framework material is the machine of 3/1 brokentwlllweave structure
Fabric, wherein warp thread is 1000D lower shrinkage nylon multifilament, and weft yarn is 0.3mm ultralow contractive polyester monofilament, the thickness of framework material
Degree is 2.6mm.
Second step, coating polyvinyl chloride coat：A strata vinyl chloride primer first is coated on the framework material surface,
A strata vinyl chloride capstock is coated on the primer again, wherein the viscosity of polyvinyl chloride primer is 3000mPa.s,
Coated weight is 180g/mm2, coating speed 8m/min；The viscosity of polyvinyl chloride top material is 3000mPa.s, and coated weight is
300g/mm2, coating speed 10m/min.
Third step, is beaten after tooth, hot pressing and finishing up to the special treadbelt of household treadmill at positioning.
By the special treadbelt of household treadmill prepared in above-described embodiment 3 and commercially available conventional treadbelt according to《GB/T23677-
2017 light-type conveyer belts》、《GB/T10006 films move static friction coefficient with sheet material》、《GB/T3648 conveyer belt electric conductivity specifications
And test method》It is tested for the property, the results are shown in Table 1.
The special treadbelt performance test of household treadmill of table 1 conventional treadbelt and the present invention
As it can be seen from table 1 the peel strength and antistatic surface (Ω) of present inventor's special treadbelt of treadmill are excellent
In conventional treadbelt, this is because warp thread is 1000D lower shrinkage nylon in the special treadbelt framework material of household treadmill of the present invention
Multifilament, weft yarn be 0.3mm ultralow contractive polyester monofilament, the high lubrication property having by itself can reduce treadbelt with run plate it
Between rub, greatly reduce the generation of noise and electrostatic, improve security performance；And, it is ensured that framework material is coated with polyvinyl chloride
The adhesive property of layer effectively improves its service life to reduce the treadbelt lamination problem；On the other hand pass through the painting of optimization
Primer and capstock in coating process guarantee polyvinyl chloride coat fully melt, and further increase framework material and polychlorostyrene second
The adhesion strength of alkene coat.
The above is presently preferred embodiments of the present invention, but the present invention should not be limited to disclosed in the embodiment
Content.So every do not depart from the lower equivalent or modification completed of spirit disclosed in this invention, the model that the present invention protects is both fallen within
It encloses.
Claims (4)
1. a kind of special treadbelt of household treadmill, which is characterized in that by framework material and coated on the framework material side
Polyvinyl chloride coat forms, wherein the framework material is the woven fabric of 3/1 brokentwlllweave structure；Warp thread in the woven fabric
For 1000D lower shrinkage nylon multifilament, weft yarn is 0.3mm ultralow contractive polyester monofilament.
2. a kind of special treadbelt of household treadmill as described in claim 1, which is characterized in that the polyvinyl chloride coat by
Polyvinyl chloride primer coated on the framework material side and coated on the polyvinyl chloride on the polyvinyl chloride primer
Capstock forms.
3. a kind of special treadbelt of household treadmill as described in claim 1, which is characterized in that the thickness of the framework material is
2.4~2.6mm.
4. a kind of manufacturing method of the special treadbelt of household treadmill as described in any one of claims 1 to 3, which is characterized in that packet
Include following steps：
S1, framework material drying and shaping；
S2, coating polyvinyl chloride coat；
S3, toe joint connector to get；Wherein,
In step S1, the drying and shaping temperature is 180~200 DEG C；
In step S2, the method for the coating polyvinyl chloride coat is：First a strata chlorine is coated on the framework material surface
Ethylene primer, a then strata vinyl chloride capstock is coated on the primer, wherein the viscosity of polyvinyl chloride primer is
2000~3000mPa.s, coated weight are 150~180g/mm2, coating speed is 6~8m/min；The polyvinyl chloride top material
Viscosity be 2500~3000mPa.s, coated weight be 200~300g/mm2, coating speed is 8~10m/min.