CN108624208A - A kind of method that nano-titanium dioxide-nano antimony tin oxide prepares water transparent heat insulation paint - Google Patents
A kind of method that nano-titanium dioxide-nano antimony tin oxide prepares water transparent heat insulation paint Download PDFInfo
- Publication number
- CN108624208A CN108624208A CN201810487092.9A CN201810487092A CN108624208A CN 108624208 A CN108624208 A CN 108624208A CN 201810487092 A CN201810487092 A CN 201810487092A CN 108624208 A CN108624208 A CN 108624208A
- Authority
- CN
- China
- Prior art keywords
- nano
- titanium dioxide
- added
- water
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of methods that nano-titanium dioxide nano antimony tin oxide prepares water transparent heat insulation paint, it is characterized in that, add deionized water into nano-particle tin-antiomony oxide, add composite dispersing agent under stirring at low speed, adjust pH, ball milling disperses, and filters off mill pearl and pours out slurry, obtains nano antimony tin oxide aqueous slurry;Nano-titanium dioxide powder is dry in vacuum drying oven, it is added in absolute ethyl alcohol, ultrasonic disperse, water bath with thermostatic control stirring adds silane coupling agent, and drying, the finely ground nano-titanium dioxide for obtaining surface and being modified are taken out after reaction;Into modified nano-titanium dioxide plus deionized water, dispersant, wetting agent, antifoaming agent, mechanical dispersion obtain pre-dispersed liquid, anti-settling agent, mechanical dispersion, ultrasonic disperse are added to obtain nanometer titanium dioxide water pulp;Gained nanometer water slurry, hollow glass micropearl, high speed dispersion is added to add silane coupling agent, thickening leveling agent stirring, add organic silicon defoamer to defoam, water transparent heat insulation paint is made in hydrotropism's polyurethane.
Description
Technical field
The present invention relates to paint fields, and in particular to a kind of nano-titanium dioxide-nano antimony tin oxide prepares aqueous transparent
The method of insulating moulding coating.
Background technology
Nano antimony tin oxide(ATO)Be it is a kind of there is more highly selective function powder, it is and right to visible light transmittance height
Infrared light but has preferable shielding properties.It is coated in glass surface, Jiang Nengqi using the ATO transparent heat insulating dopes prepared as filler
To preferable light transmission heat-blocking action.For the present invention using nano antimony tin oxide as thermal insulating filling, aqueous polyurethane is film forming matter, is prepared
Transparent heat insulating dope, and its translucency, heat-proof quality and physical property are studied.
Invention content
The invention mainly solves the technical problem of providing a kind of nano-titanium dioxide-nano antimony tin oxide prepare it is aqueous
The method of bright insulating moulding coating has excellent transparent heat-insulated performance according to coating prepared by the technique.
A kind of method that nano-titanium dioxide-nano antimony tin oxide prepares water transparent heat insulation paint, which is characterized in that press
Following steps carry out:
(1)The preparation of nano antimony tin oxide slurry:
Deionized water is added into 10-20 parts of nano-particle tin-antiomony oxides, composite dispersing agent is added under stirring at low speed, uses hydroxide
It is 9-10 that sodium solution, which adjusts pH, and ball milling disperses 1-2h, filters off mill pearl and pours out slurry, it is the nano oxidized of 8-12% to obtain solid content
Tin antimony aqueous slurry;
(2)The preparation of nano titania slurry:
1-2 parts of nano-titanium dioxide powders are dried into 10-12h in 120-125 DEG C of vacuum drying oven, are added in absolute ethyl alcohol, are surpassed
Sound disperses 10-12min, is stirred in 80-82 DEG C of water bath with thermostatic control, and 0.1-0.2% silane coupling agent KH560 are added, and is taken after reacting 2-3h
Go out drying, the finely ground nano-titanium dioxide for obtaining surface and being modified;
Deionized water is added into modified nano-titanium dioxide, 1-2% dispersants, 0.1-0.2% wetting agents, 0.1-0.2% is added to disappear
Infusion, mechanical dispersion obtain pre-dispersed liquid, add 0.1-0.2% anti-settling agents, mechanical high-speed to disperse 25-30min, ultrasonic wave disperses 10-
Nanometer titanium dioxide water pulp is made in 15min;
(3)The preparation of transparent heat insulating dope:
It is added into 70-80 parts of aqueous polyurethanes(1)Middle gained thermal insulating filling nano antimony tin oxide aqueous slurry,(2)Middle gained
Material and 5-10 parts of hollow glass micropearls, are disperseed with high speed dispersor, and 0.1-0.2% silane coupling agents KH570, thickening stream is added
25-35min is stirred in flat agent, and the defoaming of 0.1-0.2% organic silicon defoamers is added, water transparent heat insulation paint is made.
Wherein, step(1)Middle composite dispersing agent is made of 0.1-0.2% polyacrylic acid sodium salts, 1-2% polyvinyl alcohol, ball milling
Rotating speed is 1000-2000rpm.
Step(2)Middle mechanical high-speed dispersion rotating speed is 4500-5500rpm.
Step(3)Middle aqueous polyurethane solid content is 40-42%, rate of dispersion 2500-3500rpm.
The reaction mechanism of the present invention is as follows:
With composite dispersing agent polyacrylic acid sodium salt and polyvinyl alcohol ball milling dispersing nanoparticles tin-antiomony oxide (ATO), dissociate in water
Polyvinyl alcohol molecule increase the steric hindrance operating distance between being adsorbed with the ATO particles of polyacrylic acid sodium salt, compound point
Powder can enhance the stability of nano pulp;Surface modification is carried out to nano-titanium dioxide with silane coupling agent KH560, can be improved
The dispersibility of titanium dioxide nanoparticle in water, dispersant can significantly improve the dispersibility of nano titania slurry, wetting
Agent can improve the dispersibility of nano particle in water;Addition nano-titanium dioxide can effectively improve the heat-proof quality of coating;With
Nano antimony tin oxide is thermal insulating filling, aqueous polyurethane is film forming matter, adds hollow glass micropearl and nano-titanium dioxide, system
Standby transparent heat insulating dope, hollow glass micropearl can improve the heat-proof quality of coating.
Specific implementation mode
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment
A kind of method that nano-titanium dioxide-nano antimony tin oxide prepares water transparent heat insulation paint, which is characterized in that press
Following steps carry out:
(1)The preparation of nano antimony tin oxide slurry:
Deionized water is added into 10kg nano-particle tin-antiomony oxides, composite dispersing agent is added under stirring at low speed, uses sodium hydroxide
It is 9-10 that solution, which adjusts pH, and ball milling disperses 2h, filters off mill pearl and pours out slurry, it is aqueous to obtain the nano antimony tin oxide that solid content is 8%
Slurry;
(2)The preparation of nano titania slurry:
1kg nano-titanium dioxide powders are dried into 10h in 120-125 DEG C of vacuum drying oven, are added in absolute ethyl alcohol, ultrasonic disperse
12min is stirred in 80-82 DEG C of water bath with thermostatic control, and 0.1% silane coupling agent KH560 is added, and drying is taken out after reacting 2h, finely ground to obtain table
The nano-titanium dioxide that face is modified;
Deionized water is added into modified nano-titanium dioxide, adds 1% dispersant, 0.1% wetting agent, 0.1% antifoaming agent, machinery
Disperse to obtain pre-dispersed liquid, adds 0.1% anti-settling agent, mechanical high-speed to disperse 30min, ultrasonic wave disperses 15min, and nanometer titanium dioxide is made
Titanium aqueous slurry;
(3)The preparation of transparent heat insulating dope:
It is added into 70kg aqueous polyurethanes(1)Middle gained thermal insulating filling nano antimony tin oxide aqueous slurry,(2)Middle resulting material
And 5kg hollow glass micropearls, disperseed with high speed dispersor, 0.1% silane coupling agent KH570, thickening leveling agent stirring is added
35min is added the defoaming of 0.1% organic silicon defoamer, water transparent heat insulation paint is made.
Wherein, step(1)Middle composite dispersing agent is made of 0.1% polyacrylic acid sodium salt, 1% polyvinyl alcohol, and rotational speed of ball-mill is
2000rpm。
Step(2)Middle mechanical high-speed dispersion rotating speed is 5500rpm.
Step(3)Middle aqueous polyurethane solid content is 42%, rate of dispersion 2500rpm.
Claims (5)
1. a kind of method that nano-titanium dioxide-nano antimony tin oxide prepares water transparent heat insulation paint, which is characterized in that Xiang Na
Add deionized water in rice corpuscles tin-antiomony oxide, add composite dispersing agent under stirring at low speed, pH, ball milling point are adjusted with sodium hydroxide solution
It dissipates, filters off mill pearl and pour out slurry, obtain nano antimony tin oxide aqueous slurry;Nano-titanium dioxide powder is done in vacuum drying oven
It is dry, it is added in absolute ethyl alcohol, ultrasonic disperse, water bath with thermostatic control stirring adds silane coupling agent, and drying is taken out after reaction, finely ground to obtain table
The nano-titanium dioxide that face is modified;Add deionized water, dispersant, wetting agent, antifoaming agent, machinery into modified nano-titanium dioxide
Disperse to obtain pre-dispersed liquid, anti-settling agent, mechanical dispersion, ultrasonic disperse is added to obtain nanometer titanium dioxide water pulp;Hydrotropism's polyurethane
In plus gained nanometer water slurry, hollow glass micropearl, high speed dispersion, add silane coupling agent, thickening leveling agent stirring, added with machine
Silicon defoaming agent defoams, and water transparent heat insulation paint is made.
2. a kind of nano-titanium dioxide-nano antimony tin oxide according to claim 1 prepares water transparent heat insulation paint
Method, which is characterized in that carry out according to the following steps:
(1)The preparation of nano antimony tin oxide slurry:
Deionized water is added into 10-20 parts of nano-particle tin-antiomony oxides, composite dispersing agent is added under stirring at low speed, uses hydroxide
It is 9-10 that sodium solution, which adjusts pH, and ball milling disperses 1-2h, filters off mill pearl and pours out slurry, it is the nano oxidized of 8-12% to obtain solid content
Tin antimony aqueous slurry;
(2)The preparation of nano titania slurry:
1-2 parts of nano-titanium dioxide powders are dried into 10-12h in 120-125 DEG C of vacuum drying oven, are added in absolute ethyl alcohol, are surpassed
Sound disperses 10-12min, is stirred in 80-82 DEG C of water bath with thermostatic control, and 0.1-0.2% silane coupling agent KH560 are added, and is taken after reacting 2-3h
Go out drying, the finely ground nano-titanium dioxide for obtaining surface and being modified;
Deionized water is added into modified nano-titanium dioxide, 1-2% dispersants, 0.1-0.2% wetting agents, 0.1-0.2% is added to disappear
Infusion, mechanical dispersion obtain pre-dispersed liquid, add 0.1-0.2% anti-settling agents, mechanical high-speed to disperse 25-30min, ultrasonic wave disperses 10-
Nanometer titanium dioxide water pulp is made in 15min;
(3)The preparation of transparent heat insulating dope:
It is added into 70-80 parts of aqueous polyurethanes(1)Middle gained thermal insulating filling nano antimony tin oxide aqueous slurry,(2)Middle gained
Material and 5-10 parts of hollow glass micropearls, are disperseed with high speed dispersor, and 0.1-0.2% silane coupling agents KH570, thickening stream is added
25-35min is stirred in flat agent, and the defoaming of 0.1-0.2% organic silicon defoamers is added, water transparent heat insulation paint is made.
3. a kind of nano-titanium dioxide-nano antimony tin oxide according to claim 2 prepares water transparent heat insulation paint
Method, which is characterized in that step(1)Middle composite dispersing agent is made of 0.1-0.2% polyacrylic acid sodium salts, 1-2% polyvinyl alcohol, ball
Mill rotating speed is 1000-2000rpm.
4. a kind of nano-titanium dioxide-nano antimony tin oxide according to claim 2 prepares water transparent heat insulation paint
Method, which is characterized in that step(2)Middle mechanical high-speed dispersion rotating speed is 4500-5500rpm.
5. a kind of nano-titanium dioxide-nano antimony tin oxide according to claim 2 prepares water transparent heat insulation paint
Method, which is characterized in that step(3)Middle aqueous polyurethane solid content is 40-42%, rate of dispersion 2500-3500rpm.