CN108610934A - Single-component polyurethane water-proof paint and preparation method thereof and the composition for being used to prepare the single-component polyurethane water-proof paint - Google Patents
Single-component polyurethane water-proof paint and preparation method thereof and the composition for being used to prepare the single-component polyurethane water-proof paint Download PDFInfo
- Publication number
- CN108610934A CN108610934A CN201710033029.3A CN201710033029A CN108610934A CN 108610934 A CN108610934 A CN 108610934A CN 201710033029 A CN201710033029 A CN 201710033029A CN 108610934 A CN108610934 A CN 108610934A
- Authority
- CN
- China
- Prior art keywords
- polyurethane water
- proof paint
- component polyurethane
- water
- polyether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the composition for being used to prepare single-component polyurethane water-proof paint, the composition includes:With the mixture of the talcum powder or light calcium carbonate powder or the two that are handled together with rare-earth coupling agent.The invention further relates to the novel environment-friendly single-component polyurethane water-proof paints and preparation method thereof comprising the composition.Method of the present invention is handled the mixture of talcum powder and precipitated calcium carbonate powder including (1) together with rare-earth coupling agent, to obtain A material;(2) polyether polyol is fully reacted under certain condition with methyl diphenylene diisocyanate to obtain B material;(3) A material and B material are mixed at a temperature of 60 to 80 DEG C to obtain the single-component polyurethane water-proof paint together with organic bismuth catalyst and other additives in proportion.Polyurethane water-proof paint provided by the invention is a kind of environmentally friendly one-component environment-friendly solvent-free polyurethane waterproof material.It is not only non-toxic and tasteless, without solvent, be free of TDI, without poisoned catalyst, is also free of suspected carcinogens, the auxiliary materials such as MOCA and is easy to get, and the viscosity of the polyurethane water-proof paint may be in ideal range so that site operation is convenient and efficient, winter construction curing rate is adjustable.
Description
Technical field
The present invention relates to polyurethane water-proof paint fields.In particular it relates to which a kind of monocomponent polyurethane waterproof applies
Material, a kind of method preparing single-component polyurethane water-proof paint and a kind of group being used to prepare the single-component polyurethane water-proof paint
Close object.
Background technology
The proposition of Green Chemistry makes we have seen that the brighter future of the mankind.Green Chemistry is also known as Environmental benign chemistry, ring
The friendly chemistry in border, cleaning chemistry, corresponding technology are also known as green technology.Corresponding product is also known as green product.In China,
The developing direction of architectural chemistry conduct industry is:Water-borne modification, high solid differentiation and Non-toxic.Regardless of a kind of substance be it is toxic,
It, which must only enter in organism, can just work, this is known as bioavilability.Bioavilability is smaller, and harm is smaller.To the greatest extent
Pipe people have also looked for some effective solution methods to the pollution problem of chemical products, but thoroughly to solve chemicals pair
The harm of human health and environment for human survival also needs us constantly to produce the substitute of toxic chemical --- green
Chemical products.
Waterproof material should be sent out in the greenization of product, Non-toxic change certainly as the major class in architectural chemistry product
Wave oneself due effect.For As-Is, although various waterproof materials emerge one after another, wherein most production
Product also greatly differ from each other from greenization.
Polyurethane water-proof paint is a kind of potentially possible Green Chemistry product.Polyurethane water-proof paint has 40 in China
The applicating history in or so year, thus have become a ripe technology in production, design and construction etc..National chemical building material
' 95 ' plans and development planning outlines in 2010 and ' 15 ' plans are all classified as polyurethane water-proof paint and give priority to
Water-repellent paint kind successively promulgates national building material industry standard JC/T500-92《Polyurethane water-proof paint》With standard GB/T/
T19250-2003《Polyurethane water-proof paint》.GB/T19250-2013《Polyurethane water-proof paint》、JC1066-2008《Building is anti-
Limits of harmful substances in water paint》.
Currently, polyurethane waterproof material in the market is divided into one-pack type polyurethane waterproof material and two-component-type polyurethane
Waterproof material.Compared with two-component type polyurethane water-proof paint, one-pack type polyurethane water-proof paint eliminates when in use to be applied
Burden process before work, without metering, proportioning, use is easy to operate;Film coated surface is smooth, bubble-free, pin hole;Applicable time
It is long.Therefore one-pack type polyurethane waterproof material exists than two-component-type polyurethane waterproof material on materials'use apparent excellent
Gesture.
Either one-pack type polyurethane waterproof material or two-component type polyurethane waterproof material, its group in conventional formulation
Point be all by polyethers, toluene di-isocyanate(TDI) (Toluene-2,4-diisocyanate, TDI), plasticizer, solvent, catalyst,
The auxiliary agents such as color stuffing and amine or alcohols curing agent composition.Wherein toluene di-isocyanate(TDI) (TDI) be it is colourless have it is strong pungent
The liquid of taste, boiling point are 251 DEG C, and proportion 1.22 meets light blackening.Since the vapour pressure of TDI is high, so using smell weight when TDI,
Toxicity is big.In addition, there are surface drying times especially to grow when the one-pack type polyurethane waterproof material winter containing TDI constructs, it is certainly real
The dry time is also extremely long, long so as to cause the winter construction duration.And methyl diphenylene diisocyanate (Diphenyl-
Methane-diisocyanate, MDI) at 160 DEG C, steam pressure is only that (steam pressure is just at 120 DEG C by TDI by 0.8mmHg
Reach 10mmHg, 1mmHg=133.322Pa), volatility is minimum during production and use.In addition, MOCA is anti-as polyurethane
The crosslinking agent of water paint has carcinogenesis by strong suspicion.Therefore, requirement of the people based on green product be increasingly
It mostly is considered as using water as the one-pack type polyurethane water-proof paint based on MDI of crosslinking agent.
In addition, the organotin, the organolead catalysts that contain in polyurethane waterproof material currently on the market are more toxic, and
And content is also very high in the formula having.The organic bismuth catalyst developed recently has been obtained in terms of the requirement of green product
Prodigious development.
However, it is generally the case that for the poly- ammonia of one-pack type without solvent and the use MDI more environmentally friendly relative to TDI
The viscosity of ester water-repellent paint, the material is very big, and surface drying time is still longer, this make the material in winter can application property obtain not
To guarantee, so that the application of this preferred water-repellent paint is extremely restricted.
Invention content
Based on problems of the prior art as above, it is based on this, it is necessary to provide a kind of monocomponent polyurethane waterproof painting
Material, a kind of method preparing single-component polyurethane water-proof paint and the combination for being used to prepare the single-component polyurethane water-proof paint
Object.
According to an aspect of the invention, there is provided a kind of preparation method of single-component polyurethane water-proof paint, including such as
Lower step:
(1) by 1: 1 mixture of both 600 mesh talcum powder and 400 mesh precipitated calcium carbonates and rare-earth coupling agent at 72 degree ± 2 degree
Abundant activation process is carried out together, obtains A material;
(2) polyether polyol and methyl diphenylene diisocyanate is fully poly- in predefined conditions by equivalent proportion 1: 2.05
It closes, obtains B material;
(3) ratio and the temperature of organic bismuth catalyst, additive at 60 DEG C -80 DEG C by A material and B material by weight 1: 1
Lower mixing obtains the single-component polyurethane water-proof paint in 3-4 hours.
The organic bismuth catalyst is BICAT8118 in one of the embodiments, and wherein bi content is 18%.
The methyl diphenylene diisocyanate is 4,4 '-diphenylmethane diisocyanates in one of the embodiments,
Ester and 2, the mixture of 4 '-methyl diphenylene diisocyanates.
In one of the embodiments, described 4,4 '-methyl diphenylene diisocyanates and 2,4 '-diphenyl methanes two are different
The molar ratio of cyanate is 1: 1,1: 2 or 2: 1.
The polyether polyol includes that the low-unsaturation-degree that molecular weight is 1000-2000 is poly- in one of the embodiments,
Ether dihydric alcohol and molecular weight are the mixture of the low-unsaturation-degree polyether trihydroxylic alcohol of 3000-5000.
The Low unsaturation polyether and the low-unsaturation-degree polyether trihydroxylic alcohol in one of the embodiments,
Mass ratio be 4: 1;
The Low unsaturation polyether, the low-unsaturation-degree polyether trihydroxylic alcohol degree of unsaturation be no more than
0.007 mole/kilogram.
The additive includes gas absorbent, pigment, antioxidant, ultraviolet radiation absorption in one of the embodiments,
It is one or more in agent.
According to another aspect of the present invention, a kind of combination being used to prepare single-component polyurethane water-proof paint is also provided
Object, the composition include:With the mixture of talcum powder, fine particle calcium carbonate or the two for being handled together with rare-earth coupling agent;Wherein, talcum powder and
Both precipitated calcium carbonates mass ratio is 1: 1.
According to another aspect of the present invention, a kind of single-component polyurethane water-proof paint is also provided, which includes
According to combinations of the above object.
According to another aspect of the present invention, a kind of single-component polyurethane water-proof paint is also provided, which is logical
It crosses and is prepared according to method described in any one of the above embodiments.
By reacting film-forming with the moisture in air, i.e., single-component polyurethane water-proof paint prepared by the present invention is
Using water as crosslinking agent, urea bond is introduced to improve material property, the MOCA as pollution sources has been abandoned, using organo-bismuth
Catalyst so that the environmentally protective performance of material is greatly improved.
Polyurethane water-proof paint provided by the invention is a kind of environmentally friendly one-component environment-friendly solvent-free polyurethane water-proof
Material.It is not only non-toxic and tasteless, without solvent, be free of TDI, be free of poisoned catalyst, be also free of the suspected carcinogens such as MOCA, it is auxiliary
It helps material to be easy to get, and so that the viscosity of the single-component polyurethane water-proof paint can be with by the activation process to powder in system
In ideal range so that site operation is convenient and efficient, winter construction curing rate is adjustable.
Specific implementation mode
In order to make the foregoing objectives, features and advantages of the present invention clearer and more comprehensible, below to the specific reality of the present invention
The mode of applying is described in detail.Many details are elaborated in the following description in order to fully understand the present invention.But
The invention can be embodied in many other ways as described herein, and those skilled in the art can be without prejudice to this hair
Similar improvement is done in the case of bright intension, therefore the present invention is not limited to the specific embodiments disclosed below.
In order to solve the above technical problem, the present invention provides a kind of methods preparing single-component polyurethane water-proof paint.
A kind of preparation method of single-component polyurethane water-proof paint, this method comprises the following steps:
(1) by 600 mesh talcum powder or 400 mesh precipitated calcium carbonates or the mixture of the two 1: 1 and rare-earth coupling agent at 75 degree
Under be stirred until homogeneous, obtain A material.
The talcum powder of the present invention is commercially available 600 mesh talcum powder, and precipitated calcium carbonate of the invention is commercially available 400 mesh
Precipitated calcium carbonate.The particle size and ratio are viscosity, the cost with single-component polyurethane water-proof paint obtained in coating
And there is correlation in storage stability.Use the mixture of the mesh number talcum powder and the mesh number precipitated calcium carbonate, institute
The ratio for stating mixture is 1: 1.
Rare-earth coupling agent chemical general formula is (C3H7O) xRe (OCOR ') m (OCOR2) n (OAB) y.The substance is white or shallow
Yellow solid small particles have the characteristics that color is shallow, tasteless, avirulent.
(2) polyether polyol and methyl diphenylene diisocyanate are fully closed under certain condition by equivalent proportion 1: 2.05
Expect at as B;
(3) by A material and B expect in 1: 1 ratio together with organic bismuth catalyst and the other additives selected 60 DEG C-
3-4 hours are mixed at a temperature of 80 DEG C to obtain the single-component polyurethane water-proof paint.
Wherein, above-mentioned organic bismuth catalyst is 18% using BICAT8118, wherein bi content.
In one embodiment, the methyl diphenylene diisocyanate be include 4,4 '-diphenyl methane, two isocyanide
Acid esters and 2, the mixture of 4 '-methyl diphenylene diisocyanates.
In one embodiment, described 4,4 '-methyl diphenylene diisocyanates and 2,4 '-diphenyl methane, two isocyanide
The weight ratio of acid esters is 1: 1,1: 2 or 2: 1.
In one embodiment, the polyether polyol includes the low-unsaturation-degree polyether that molecular weight is 1000 to 2000
The mixture for the low-unsaturation-degree polyether trihydroxylic alcohol that dihydric alcohol and molecular weight are 3000 to 5000.
Wherein, the mass ratio of the Low unsaturation polyether and the low-unsaturation-degree polyether trihydroxylic alcohol is 4: 1.
The Low unsaturation polyether, the low-unsaturation-degree polyether trihydroxylic alcohol degree of unsaturation be no more than 0.007 mole/
Kilogram.
In one embodiment, wherein above-mentioned additive includes gas absorbent, pigment, antioxidant, ultraviolet light suction
It receives one or more in agent.It can specifically select to be added according to client's specific requirement.For example, the monocomponent polyurethane waterproof applies
The appearance color (such as red or green) of material is all to be customized selected by client.User also requires (ring at specific position
Border inclement condition) it constructs, antioxidant and ultra-violet absorber should be added at this time.
The gas absorbent used in the method for the present invention includes aerosil.
The pigment used in the method for the present invention includes carbon black, iron oxide red and chrome green.
The antioxidant used in the method for the present invention includes antioxidant 1010.
The ultraviolet absorber used in the method for the present invention includes UV327.
The environment-friendly plasticizer used in the method for the present invention includes tributyl citrate.
On the other hand, the present invention provides a kind of single-component polyurethane water-proof paint, which is by institute as above
Prepared by the method for the present invention stated.
On the other hand, the present invention provides a kind of composition being used to prepare single-component polyurethane water-proof paint, the combination
Object includes:With the mixture of the talcum powder or fine particle calcium carbonate or the two that are handled together with rare-earth coupling agent.
On the other hand, the present invention provides a kind of single-component polyurethane water-proof paint, which includes as described above
The present invention composition.
The technique effect of acquirement:
1) composition that the present invention has been used in the method for preparing single-component polyurethane water-proof paint of the present invention, passes through
Using the composition, the viscosity of the water-repellent paint can be arbitrarily controlled, so that the water-repellent paint of the present invention can root
There is widely production and applicability in construction according to needs.
2) surface drying time of single component polyurethane waterproof material of the invention can be according to the ratio of MDI in wider range
It substantially adjusts, so that can construct calmly in winter, significantly improves and control production process and work progress
Duration progress;Meanwhile the storage period of material is completely up to standard.
3) used methyl diphenylene diisocyanate (MDI) in method of the invention, abandoned poisonous and hazardous TDI and
Solvent, therefore significantly improve and control the environmental pollution in production process and work progress.
4) waterproof material property indices of the present invention are outstanding.Its tensile strength, fracture elongation, adverse circumstances
It is had excellent performance in terms of construction.GB/T 19250-2013 are fully achieved《Polyurethane water-proof paint》And JC1066-2008《Building is anti-
Limits of harmful substances in water paint》Standard.Any noxious material is free of in formula.
In order to make the purpose , technical scheme and advantage of the present invention be clearer, by the following examples to the present invention
It is described in detail.It should be appreciated that described herein, specific examples are only used to explain the present invention, is not used to limit this hair
It is bright.
It is illustrated below in conjunction with specific embodiment.
Number in following embodiment is mass fraction.
Embodiment 1
The mixture of the talcum powder of equal proportion and fine particle calcium carbonate is added in reaction kettle and is warming up to 74.C, will be dilute under stirring
Native coupling agent chopping is slowly added in the reaction kettle in stirring, is A material after stirring.
Polyether Glycols and polyether-tribasic alcohol are mixed by 4: 1 weight ratio, the vacuum at 100 DEG C -120 DEG C
(0.095MPa or more) is dehydrated 3 hours, after be down to room temperature, property is added quantitative, fixed than mixing two isocyanide of diphenyl methane again
Acid esters MDI, wherein polyether polyol presses equivalent proportion 1: 2.05 with methyl diphenylene diisocyanate.In this way, obtaining B material.This reality
It applies in example, 4,4 '-methyl diphenylene diisocyanate of methyl diphenylene diisocyanate and 2,4 '-diphenyl methane, two isocyanide
The mixture of acid esters, and the weight ratio of the two is 1: 1.It is started to warm up after stirring evenly, 80 DEG C keep the temperature 3 hours.Then A material are added according to quantity
(A and B according to 1: 1 ratio), continues heat preservation 1 hour;Then 60 DEG C are cooled to, quantitative additive (environment-friendly plasticizer is added
Deng) and organic bismuth catalyst etc., it stirs evenly and discharges after vacuum defoamation.As environment-friendly type single component polyurethane waterproof material.
Every environmental protection index of final polyurethane water-proof paint
Wherein, above table be Institute for Environment Hygiene and Health Related Product Safety, China CDC provide to this
The detection of invention sample.Detection method uses《The drinking water standard method of inspection》GB/T5750-2006;Sample treatment
According to《Drinking Water transmission & distribution wetting system and the safe and healthy evaluating regulation of protective materials》It carries out.Sample uses appendix A 13.1
Section configuration, soaking time are 24 hours, and soaking temperature is 25 ± 5 DEG C.Inspection result show color in soaking water, turbidity, it is smelly and
Taste, naked eyes visible, ph, total dissolved solid, oxygen demand, arsenic, cadmium, chromium (sexavalence), aluminium, lead, mercury, chloroform, volatile phenol
Class, carbon tetrachloride, formaldehyde, epoxychloropropane, styrene, benzene, toluene and dimethylbenzene index meet Drinking Water transmission & distribution water
The hygienic requirements of equipment and protective materials Hygienic safety evaluation specification to protective materials.As it can be seen that the polyurethane water-proof of the present invention applies
Expect environmentally protective health.
Embodiment 2
Difference lies in 4,4 '-MDI and 2 with embodiment 1 for the present embodiment, and the ratio of 4 '-MDI is 2: 1, talcum powder and fine particle calcium carbonate
Mixture be added 72 DEG C of reaction temperature in reaction kettle, A material and B material by weight 1: 1 ratio and organic bismuth catalyst, add
The reaction temperature of agent is 70 DEG C, and A material and B material are by weight 1: 1 ratio and the reaction temperature of organic bismuth catalyst, additive
75 DEG C, other are constant, and (polyether polyol presses equivalent proportion 1: 2.05 with methyl diphenylene diisocyanate, and A material are with the B ratios expected
1∶1)。
Embodiment 3
Difference lies in 4,4 '-MDI and 2 with embodiment 1 for the present embodiment, and the ratio of 4 '-MDI is 1: 2, talcum powder and fine particle calcium carbonate
Mixture be added reaction kettle in 70 DEG C of reaction temperature, other are constant, and (polyether polyol is pressed with methyl diphenylene diisocyanate
Equivalent proportion 1: 2.05, A material and the ratio of B material are 1: 1).
The corresponding adjustment 4 of above-described embodiment 1-3,4 '-MDI and 2,4 '-MDI influence the performance of coating as follows:
4,4 '-MDI and 2, the influence of the match ratio of 4 '-MDI to coating property
4.4’ MDI/2.4’ MDI | Tensile strength/Mpa | Elongation at break/% | Viscosity/centipoise |
2∶1 | 2.84 | 800 | 18000 |
1∶2 | 2.08 | 540 | 7600 |
1∶1 | 2.62 | 750 | 13000 |
The indices of final polyurethane water-proof paint prepared by above three embodiments, such as tensile strength, fracture
Elongation, range of viscosities, surface drying time etc., as follows:
It can be seen that from above table, by adjusting 4,4 '-MDI and 2, it is described anti-can to take into account control for the weight ratio of 4 '-MDI
The viscosity of water paint, and water-repellent paint obtain various physical properties can be up to standard.In addition, the surface drying time of the waterproof material can be with
The change of the ratio of MDI substantially adjusts in wider range, and storage period is also up to standard.
Several embodiments of the invention above described embodiment only expresses, the description thereof is more specific and detailed, but simultaneously
Cannot the limitation to the scope of the claims of the present invention therefore be interpreted as.It should be pointed out that for those of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect range.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (10)
1. a kind of preparation method of single-component polyurethane water-proof paint, includes the following steps:
(1) by 1: 1 mixture of both 600 mesh talcum powder and 400 mesh precipitated calcium carbonates and rare-earth coupling agent at 72 DEG C ± 2 DEG C together
Abundant activation process is carried out, A material are obtained;
(2) polyether polyol is fully polymerize with methyl diphenylene diisocyanate by equivalent proportion 1: 2.05 in predefined conditions,
Obtain B material;
(3) A material and B material is mixed at a temperature of 60 DEG C -80 DEG C by weight 1: 1 ratio and organic bismuth catalyst, additive
It closes 3-4 hours and obtains the single-component polyurethane water-proof paint.
2. according to the method described in claim 1, it is characterized in that, the organic bismuth catalyst is BICAT8118, wherein bismuth contains
Amount is 18%.
3. according to the method described in claim 1, it is characterized in that, the methyl diphenylene diisocyanate is 4,4 '-hexichol
Dicyclohexylmethane diisocyanate and 2, the mixture of 4 '-methyl diphenylene diisocyanates.
4. according to the method described in claim 3, it is characterized in that, described 4,4 '-methyl diphenylene diisocyanates and 2,4 '-
The molar ratio of methyl diphenylene diisocyanate is 1: 1,1: 2 or 2: 1.
5. according to the method described in claim 1, it is characterized in that, it is 1000-2000 that the polyether polyol, which includes molecular weight,
Low unsaturation polyether and molecular weight be 3000-5000 low-unsaturation-degree polyether trihydroxylic alcohol mixture.
6. according to the method described in claim 5, it is characterized in that, the Low unsaturation polyether and the low insatiable hunger
Mass ratio with degree polyether-tribasic alcohol is 4: 1;
The Low unsaturation polyether, the low-unsaturation-degree polyether trihydroxylic alcohol degree of unsaturation be no more than 0.007
Mole/kilogram.
7. according to the method described in claim 1, it is characterized in that, the additive include gas absorbent, it is pigment, anti-oxidant
It is one or more in agent, ultra-violet absorber.
8. a kind of composition being used to prepare single-component polyurethane water-proof paint, which is characterized in that the composition includes:With rare earth
The mixture of talcum powder, fine particle calcium carbonate or the two that coupling agent is handled together;Wherein, both talcum powder and precipitated calcium carbonate mass ratio are
1∶1。
9. a kind of single-component polyurethane water-proof paint, which is characterized in that the water-repellent paint includes combination according to any one of claims 8
Object.
10. a kind of single-component polyurethane water-proof paint, which is characterized in that the water-repellent paint is by according in claim 1-7
Prepared by any one of them method.