CN108610077A - A kind of Mobile phone lighting backboard ultra-thin, with high hardness - Google Patents

A kind of Mobile phone lighting backboard ultra-thin, with high hardness Download PDF

Info

Publication number
CN108610077A
CN108610077A CN201611147046.1A CN201611147046A CN108610077A CN 108610077 A CN108610077 A CN 108610077A CN 201611147046 A CN201611147046 A CN 201611147046A CN 108610077 A CN108610077 A CN 108610077A
Authority
CN
China
Prior art keywords
parts
mobile phone
phone lighting
ultra
thin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611147046.1A
Other languages
Chinese (zh)
Inventor
王庆来
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201611147046.1A priority Critical patent/CN108610077A/en
Publication of CN108610077A publication Critical patent/CN108610077A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of Mobile phone lighting backboard ultra-thin, with high hardness, the Mobile phone lighting backboard is formed using following Machining of Ceramics, which includes the component of following parts by weight：Be carbonized 15 24 parts of chromium powder, 7 10 parts of titanium oxide, 8 13 parts of borax, 6 10 parts of hydroxyethyl cellulose, 10 15 parts of magnesia, 6 18 parts of boron nitride, 69 parts of aluminium nitride, 15 20 parts of iron oxide, 9 13 parts of zirconium dioxide, 35 40 parts of silica, 68 parts of ethyl acetate, 46 parts of silane coupling agent, 57 parts in Carbon Dioxide, 9 13 parts of carbon fiber, 7 10 parts of glass fibre, 79 parts of octyl phenol polyoxyethylene ether, 5 10 parts of polyethylene glycol.Intensity and hardness of the present invention are good, resistance to oxidation, good toughness；Adaptability is very extensive.

Description

A kind of Mobile phone lighting backboard ultra-thin, with high hardness
Technical field
The present invention is to belong to Mobile phone lighting backplane technology field, specifically a kind of ultra-thin, with high hardness Mobile phone lighting back of the body Plate.
Background technology
Mobile phone lighting backboard a great variety in recent years has carried out each improvement, existing Mobile phone lighting according to demand Backboard has intensity height, often pursues intensity height merely, and has ignored the raising of oxidation resistent susceptibility and toughness.
Invention content
To solve the problems of the prior art, patent purpose of the present invention is to provide a kind of Mobile phone lighting ultra-thin, with high hardness Backboard.
In order to achieve the above objectives, the technical solution adopted by the present invention is：
A kind of Mobile phone lighting backboard ultra-thin, with high hardness, the Mobile phone lighting backboard using following Machining of Ceramics and At the ceramic material includes the component of following parts by weight：
Be carbonized 15-24 parts of chromium powder, 7-10 parts of titanium oxide, 8-13 parts of borax, 6-10 parts of hydroxyethyl cellulose, magnesia 10- 15 parts, 6-18 parts of boron nitride, 6-9 parts of aluminium nitride, 15-20 parts of iron oxide, 9-13 parts of zirconium dioxide, 35-40 parts of silica, second 6-8 parts of acetoacetic ester, 4-6 parts of silane coupling agent, 5-7 parts in Carbon Dioxide, 9-13 parts of carbon fiber, 7-10 parts of glass fibre, octyl 7-9 parts of phenol polyethenoxy ether, 5-10 parts of polyethylene glycol.The present invention has the following advantages：
1, the present invention has high intensity and hardness, resistance to oxidation, while having certain toughness；Adaptability is very extensive.
Specific implementation mode
Invention is described further with reference to specific embodiment.
Embodiment 1
A kind of Mobile phone lighting backboard ultra-thin, with high hardness, the Mobile phone lighting backboard using following Machining of Ceramics and At the ceramic material includes the component of following parts by weight：
Be carbonized 15-24 parts of chromium powder, 7-10 parts of titanium oxide, 8-13 parts of borax, 6-10 parts of hydroxyethyl cellulose, magnesia 10- 15 parts, 6-18 parts of boron nitride, 6-9 parts of aluminium nitride, 15-20 parts of iron oxide, 9-13 parts of zirconium dioxide, 35-40 parts of silica, second 6-8 parts of acetoacetic ester, 4-6 parts of silane coupling agent, 5-7 parts in Carbon Dioxide, 9-13 parts of carbon fiber, 7-10 parts of glass fibre, octyl 7-9 parts of phenol polyethenoxy ether, 5-10 parts of polyethylene glycol.

Claims (1)

1. a kind of Mobile phone lighting backboard ultra-thin, with high hardness, it is characterised in that：
The Mobile phone lighting backboard is formed using following Machining of Ceramics, which includes the component of following parts by weight：
Be carbonized 15-24 parts of chromium powder, 7-10 parts of titanium oxide, 8-13 parts of borax, 6-10 parts of hydroxyethyl cellulose, 10-15 parts of magnesia, 6-18 parts of boron nitride, 6-9 parts of aluminium nitride, 15-20 parts of iron oxide, 9-13 parts of zirconium dioxide, 35-40 parts of silica, acetic acid second 6-8 parts of ester, 4-6 parts of silane coupling agent, 5-7 parts in Carbon Dioxide, 9-13 parts of carbon fiber, 7-10 parts of glass fibre, octylphenol polyethylene 7-9 parts of ethylene oxide ether, 5-10 parts of polyethylene glycol.
CN201611147046.1A 2016-12-13 2016-12-13 A kind of Mobile phone lighting backboard ultra-thin, with high hardness Pending CN108610077A (en)