CN108609999A - A kind of tourmaline slurry of stabilization and preparation method thereof - Google Patents
A kind of tourmaline slurry of stabilization and preparation method thereof Download PDFInfo
- Publication number
- CN108609999A CN108609999A CN201810440193.0A CN201810440193A CN108609999A CN 108609999 A CN108609999 A CN 108609999A CN 201810440193 A CN201810440193 A CN 201810440193A CN 108609999 A CN108609999 A CN 108609999A
- Authority
- CN
- China
- Prior art keywords
- parts
- tourmaline
- slurry
- preparation
- stabilization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to scientific and technological environmental technology fields, and in particular to a kind of tourmaline slurry of stabilization and preparation method thereof.The method of the tourmaline slurry includes the following steps：By 12 parts of tourmaline of mass fraction meter, 80 100 parts of alcohol-water mixture, 0.1 1 parts of nano-cellulose, 0.5 1.5 parts of silica, 10 20 parts of menthol solutions, 68 parts of essence solvent, after stirring evenly, it is fitted into planetary ball mill tank, ball milling and the substance being prepared, the substance are exactly a kind of tourmaline slurry of stabilization；The present invention develops stable tourmaline slurry, it can be used for the decorative material for internal wall of building, the shortcomings that overcoming electric negative oxygen ion generator, increase the content of indoor negative oxygen ion using the function of tourmaline emitting negative oxygen ion, it not only constructs very simple, and improves tourmaline itself the efficiency of negative oxygen ion release.
Description
Technical field
The invention belongs to scientific and technological environmental technology fields, and in particular to a kind of tourmaline slurry of stabilization and preparation method thereof.
Background technology
Oneself is accepted by vast medical field for the effect of negative aeroion, in addition to beneficial to other than health, also have sterilization,
Dedusting, deodorization.Under normal circumstances, in the concentration of the closed indoor space negative aeroion in city in 100/cm3, with
Under, street 100-300/cm of greening3, wilderness suburb or park 500-1000/cm3, beach, forest and waterfall etc. are recuperated
10000/the cm in area3Left and right (《Ecological magazine》1998 17(6):56-60).
Indoor negative oxygen ion content is low, is unfavorable for human body health, and the main object of the present invention synthesizes a kind of energy of stabilization
The slurry of enough releasing negative oxygen ions is coated in the air outlet or indoor wall of air-conditioning by way of simply spraying, to improve
The content of indoor negative oxygen ion.
There are mainly two types of the methods for generating negative oxygen ion, and one is point discharge methods.Its major defect：Oxygen is born first, generating
Ozone is generated while ion；Second is that there is decaying in performance；The method of second of generation negative oxygen ion is using with special crystalline substance
The ore of body structure, such as tourmaline.
Tourmaline is the natural minerals of multielement, and tourmaline main component has magnesium, aluminium, iron, boron etc. a variety of advantageous to human body
Trace element.Since it is a kind of polarity crystalline solid that structure is special, electron ion itself can be generated for a long time, and permanently release is empty
Gas anion and far infrared.But tourmaline is applied directly in coating, only most surface layer is worked, and internal efficiency is low, wastes
Greatly, it is not convenient enough to use.And tourmaline density is big, easy tos produce deposition.By the preparation method of this patent, making
There is tourmaline slurry good stability, the efficiency of negative oxygen ion release also obviously to increase.
Invention content
In view of the deficiencies of the prior art, the present invention develops stable tourmaline slurry, can be used for the interior wall dress of building
Exterior material, the shortcomings that overcoming electric negative oxygen ion generator, using the function of tourmaline emitting negative oxygen ion increase indoor negative oxygen from
The content of son is not only constructed very simple, and improves tourmaline itself the efficiency of negative oxygen ion release.
A kind of preparation method of the tourmaline slurry of stabilization is：
By the tourmaline of 1-2 parts of mass fraction meter, 80-100 parts of alcohol-water mixture, 0.1-1 parts of nano-cellulose,
0.5-1.5 parts of silica is added in reaction kettle and carries out mixed at high speed, incorporation time 1-2 hours, agitator speed 300-
10-20 parts of menthol solutions and 6-8 parts of essence solvent are added in reaction kettle after having mixed, then are stirred by 400rpm
After device mixing 4-5 minutes, stop stirring, obtain uniformly mixed slurry, then slurry addition is fitted into planetary ball mill tank,
It is ground, Ball-milling Time was at 10-24 hours, after ball milling, carried out abrading-ball lock out operation, obtained slurry is exactly a kind of steady
Fixed tourmaline slurry.
Further, the nanofiber is put in then beaker, then by the cotton of the high-purity of market purchase
Suitable hydrogen peroxide is added, concentration is carried out in 2-5% after impregnating 1-2 hours, and the water inside cotton, which is carried out agent, to be gone out, and is obtained
More dry cotton, weighs the cotton that mass fraction is 10-20 parts and is put into reaction kettle, and 100-120 parts of copper is then added
The concentration of ammonia solution, copper ammon solution is controlled in 10-20%, and turn on agitator is reacted, and mixing speed is controlled in 500-
600rpm, after cotton all dissolving after, stop stirring, be then taken out it is spare, in a kettle be added 200-300 parts of concentration
For the sulfuric acid solution of 1-3mol/L, reserve liquid is added in constant pressure buret, opens blender, mixing speed is controlled in 400-
600rpm, then opens constant pressure buret, and dropping point hastens control at 1-2 drops/sec, it is to be titrated completely after react 1-2 hours again, so
Stop stirring afterwards, obtained suspension is filtered, obtained filter residue is dried, and the fiber obtained after dry is exactly nanometer
Fiber.
Further, the silica is nano oxidized silicon matter of the silica content 98% or more, and particle is big
Small is 200-1000 nanometers.
Further, the menthol solutions are to carry out mass fraction for 2-5 parts of menthol and 80-100 parts of alcohol
The substance for mixing and being prepared.
Further, the essence solvent is to mix mass fraction for 1-3 parts of essence and 100-120 parts of alcohol
The substance for closing and being prepared.
Further, the tourmaline powder is that particle size is in 300-400 mesh powders.
Further, the ball milling, per 100ml, the dosage of abrading-ball is grinding jar：(1-2) a diameter 16mm is stainless
Steel abrading-ball；(3-5) a diameter 12mm stainless steel abrading-balls；(10-20) a diameter 10mm stainless steel abrading-balls；(30-40) a diameter
8mm stainless steel abrading-balls；(100-300) a diameter 5mm stainless steel abrading-balls.
Further, the alcohol solution is that the mass ratio of ethyl alcohol and deionized water is 2-5：100 ratio is mixed
Mixed liquor.
Beneficial to benefit
1, the present invention develops stable tourmaline slurry, can be used for the decorative material for internal wall of building, overcomes the negative oxygen of electricity
The shortcomings that ion generator, increases the content of indoor negative oxygen ion using the function of tourmaline emitting negative oxygen ion；
2, the electrical slurry that prepared by this method is very easy to use, and it is enough quickly and effectively improve in room air bear oxygen from
The content of son；
3, the tourmaline slurry of preparation method of the present invention, making has good stability, is stood by long-time, slurry
It is always maintained at stable dispersity, is not deposited, service efficiency obviously increases.
Description of the drawings
Fig. 1 is that the tourmaline slurry that the present invention makes places 72 hours Stability of Slurry result figures.
In figure：1- embodiments 1,2- embodiments 2,3- embodiments 3,4- embodiments 4,5- embodiments 5,6- embodiments 6.
Specific implementation mode
In order to keep the purpose of the present invention, technical solution and advantageous effect clearer, below in conjunction with experimental data, to this
The preferred embodiment of invention is described in detail, to facilitate the technical staff to understand.
Embodiment 1
A kind of preparation method of the tourmaline slurry of stabilization is：
The cotton of the high-purity of market purchase put in then beaker, suitable hydrogen peroxide, concentration is then added
It in 2-5%, carries out after impregnating 1-2 hours, the water inside cotton, which is carried out agent, to be gone out, and the cotton more dried weighs quality
Number is that 10-20 parts of cotton is put into reaction kettle, and 120 parts of copper ammon solution is then added, and the concentration control of copper ammon solution exists
10%, turn on agitator is reacted, and mixing speed control stops stirring, then in 500rpm after cotton all dissolving
Be drawn off it is spare, in a kettle be added 300 parts of a concentration of 3mol/L sulfuric acid solution, by reserve liquid be added constant pressure buret
In, open blender, then mixing speed control opens constant pressure buret in 600rpm, dropping point hasten control 1-2 drops/
Second, it is to be titrated completely after react 1-2 hour again, then stop stirring, obtained suspension be filtered, obtained filter residue into
Row drying, the fiber obtained after dry is exactly nanofiber.
2 parts of tourmaline of mass fraction meter, 80 alcohol-water mixture are entered and carry out mixed at high speed in reaction kettle, when mixing
Between 1-2 hours, agitator speed 300-400rpm, the essence solvent of 20 parts of menthol solutions and 8 parts is added after having mixed
In reaction kettle, then after being stirred device mixing 4-5 minutes, stops stirring, obtain uniformly mixed slurry, then add the slurry
Entering to be fitted into planetary ball mill tank, be ground, Ball-milling Time was at 10-24 hours, after ball milling, carried out abrading-ball lock out operation,
Obtained slurry is exactly a kind of tourmaline slurry of stabilization.
Embodiment 2
A kind of preparation method of the tourmaline slurry of stabilization is：
The cotton of the high-purity of market purchase put in then beaker, suitable hydrogen peroxide, concentration is then added
It 5%, carries out after impregnating 1-2 hours, the water inside cotton, which is carried out agent, to be gone out, and the cotton more dried weighs mass parts
Number is put into for 10 parts of cotton in reaction kettle, is then added 100 parts of copper ammon solution, the concentration control of copper ammon solution 10%,
Turn on agitator is reacted, and mixing speed control stops stirring, then in 500-600rpm after cotton all dissolving
Be drawn off it is spare, in a kettle be added 200-300 part a concentration of 3mol/L sulfuric acid solution, by reserve liquid be added constant pressure drip
In fixed tube, blender is opened, then mixing speed control opens constant pressure buret in 400-600rpm, dropping point hastens to control
At 1-2 drops/sec, it is to be titrated completely after react 1-2 hour again, then stop stirring, obtained suspension be filtered, is obtained
Filter residue be dried, the fiber obtained after dry is exactly nanofiber.
By 1 part of tourmaline of mass fraction meter, 100 parts of alcohol-water mixture, 0.1 part of nano-cellulose, 0.5 part
Silica be added reaction kettle in carry out mixed at high speed, incorporation time 1-2 hours, agitator speed 300-400rpm has been mixed
The essence solvent of 10 parts of menthol solutions and 6 parts is added in reaction kettle afterwards, then after being stirred device mixing 4-5 minutes, is stopped
It only stirs, obtains uniformly mixed slurry, then slurry addition is fitted into planetary ball mill tank, is ground, Ball-milling Time
At 10-24 hours, after ball milling, abrading-ball lock out operation is carried out, obtained slurry is exactly a kind of tourmaline slurry of stabilization.
Embodiment 3
A kind of preparation method of the tourmaline slurry of stabilization is：
The cotton of the high-purity of market purchase put in then beaker, suitable hydrogen peroxide, concentration is then added
It 5%, carries out after impregnating 1-2 hours, the water inside cotton, which is carried out agent, to be gone out, and the cotton more dried weighs mass parts
Number is put into for 20 parts of cotton in reaction kettle, is then added 120 parts of copper ammon solution, the concentration control of copper ammon solution 10%,
Turn on agitator is reacted, and mixing speed control stops stirring, then by it in 600rpm after cotton all dissolving
Take out it is spare, in a kettle be added 300 parts of a concentration of 3mol/L sulfuric acid solution, by reserve liquid be added constant pressure buret in,
Blender is opened, then mixing speed control opens constant pressure buret in 500rpm, dropping point hastens to control at 1-2 drops/sec,
It is to be titrated completely after react 1-2 hour again, then stop stirring, obtained suspension be filtered, obtained filter residue progress
Dry, the fiber obtained after dry is exactly nanofiber.
By 1.5 parts of tourmaline of mass fraction meter, 100 parts of alcohol-water mixture, 0.8 part of nano-cellulose, 1 part
Silica is added in reaction kettle and carries out mixed at high speed, incorporation time 1-2 hours, agitator speed 300-400rpm, after having mixed
The essence solvent of 20 parts of menthol solutions and 8 parts is added in reaction kettle, then after being stirred device mixing 4-5 minutes, stopping
Stirring, obtains uniformly mixed slurry, and then slurry addition is fitted into planetary ball mill tank, is ground, Ball-milling Time exists
10-24 hours, after ball milling, abrading-ball lock out operation is carried out, obtained slurry is exactly a kind of tourmaline slurry of stabilization.
Embodiment 4
A kind of preparation method of the tourmaline slurry of stabilization is：
The cotton of the high-purity of market purchase put in then beaker, suitable hydrogen peroxide, concentration is then added
It 5%, carries out after impregnating 1-2 hours, the water inside cotton, which is carried out agent, to be gone out, and the cotton more dried weighs mass parts
Number is put into for 20 parts of cotton in reaction kettle, is then added 120 parts of copper ammon solution, the concentration control of copper ammon solution 20%,
Turn on agitator is reacted, and mixing speed control stops stirring, then in 500-600rpm after cotton all dissolving
Be drawn off it is spare, in a kettle be added 300 parts of a concentration of 3mol/L sulfuric acid solution, by reserve liquid be added constant pressure buret
In, open blender, then mixing speed control opens constant pressure buret in 600rpm, dropping point hasten control 1-2 drops/
Second, it is to be titrated completely after react 1-2 hour again, then stop stirring, obtained suspension be filtered, obtained filter residue into
Row drying, the fiber obtained after dry is exactly nanofiber.
By 1.5 parts of tourmaline of mass fraction meter, 100 parts of alcohol-water mixture, 0.8 part of nano-cellulose, 1.5 parts
Silica be added reaction kettle in carry out mixed at high speed, incorporation time 1-2 hours, agitator speed 300-400rpm has been mixed
The essence solvent of 20 parts of menthol solutions and 6 parts is added in reaction kettle afterwards, then after being stirred device mixing 4-5 minutes, is stopped
It only stirs, obtains uniformly mixed slurry, then slurry addition is fitted into planetary ball mill tank, is ground, Ball-milling Time
At 10-24 hours, after ball milling, abrading-ball lock out operation is carried out, obtained slurry is exactly a kind of tourmaline slurry of stabilization.
Embodiment 5
A kind of preparation method of the tourmaline slurry of stabilization is：
The cotton of the high-purity of market purchase put in then beaker, suitable hydrogen peroxide, concentration is then added
It 2%, carries out after impregnating 1-2 hours, the water inside cotton, which is carried out agent, to be gone out, and the cotton more dried weighs mass parts
Number is put into for 10 parts of cotton in reaction kettle, is then added 100 parts of copper ammon solution, the concentration control of copper ammon solution 10%,
Turn on agitator is reacted, and mixing speed control stops stirring, then by it in 500rpm after cotton all dissolving
Take out it is spare, in a kettle be added 200 parts of a concentration of 3mol/L sulfuric acid solution, by reserve liquid be added constant pressure buret in,
Open blender, then mixing speed control opens constant pressure buret in 400-600rpm, dropping point hasten control 1-2 drops/
Second, it is to be titrated completely after react 1-2 hour again, then stop stirring, obtained suspension be filtered, obtained filter residue into
Row drying, the fiber obtained after dry is exactly nanofiber.
By 2 parts of tourmaline of mass fraction meter, 100 parts of alcohol-water mixture, 0.8 part of nano-cellulose, 1.5 parts
Silica be added reaction kettle in carry out mixed at high speed, incorporation time 1-2 hours, agitator speed 300-400rpm has been mixed
The essence solvent of 20 parts of menthol solutions and 8 parts is added in reaction kettle afterwards, then after being stirred device mixing 4-5 minutes, is stopped
It only stirs, obtains uniformly mixed slurry, then slurry addition is fitted into planetary ball mill tank, is ground, Ball-milling Time
At 10-24 hours, after ball milling, abrading-ball lock out operation is carried out, obtained slurry is exactly a kind of tourmaline slurry of stabilization.
Embodiment 6
A kind of preparation method of the tourmaline slurry of stabilization is：
The cotton of the high-purity of market purchase put in then beaker, suitable hydrogen peroxide, concentration is then added
It 5%, carries out after impregnating 1-2 hours, the water inside cotton, which is carried out agent, to be gone out, and the cotton more dried weighs mass parts
Number is put into for 20 parts of cotton in reaction kettle, and 100-120 parts of copper ammon solution is then added, and the concentration control of copper ammon solution exists
20%, turn on agitator is reacted, and mixing speed control stops stirring, so in 600rpm after cotton all dissolving
After be drawn off it is spare, in a kettle be added 300 parts of a concentration of 3mol/L sulfuric acid solution, by reserve liquid be added constant pressure drop
In fixed tube, blender is opened, then mixing speed control opens constant pressure buret in 600rpm, dropping point hastens control in 1-2
Drop/sec, it is to be titrated completely after react 1-2 hour again, then stop stirring, obtained suspension is filtered, obtained filter
Slag is dried, and the fiber obtained after dry is exactly nanofiber.
By 2 parts of tourmaline of mass fraction meter, 100 parts of alcohol-water mixture, 1 part of nano-cellulose, 1.5 parts of oxygen
SiClx, which is added in reaction kettle, carries out mixed at high speed, and incorporation time 1-2 hours, agitator speed 300-400rpm will after having mixed
The essence solvent of 20 parts of menthol solutions and 8 parts is added in reaction kettle, then after being stirred device mixing 4-5 minutes, stops stirring
It mixes, obtains uniformly mixed slurry, then slurry addition is fitted into planetary ball mill tank, is ground, Ball-milling Time is in 10-
24 hours, after ball milling, abrading-ball lock out operation is carried out, obtained slurry is exactly a kind of tourmaline slurry of stabilization.
Experimental analysis：
1, oxygen particle release efficiency test method is born
Suspension prepared by embodiment 1-6 sprays air-conditioner air outlet, wherein the space 60m in room3.It is outstanding not spraying
When supernatant liquid, the content of negative oxygen ion in measuring chamber, after measured, it is 200-250/cm to measure negative oxygen ion in air3；And it passes through
After crossing place's spraying reason, it is as follows to measure negative oxygen ion result in air after measured for the content of negative oxygen ion in measuring chamber.
By upper table we can be found that the invention prepare spray can effectively raising air negative oxgyen ion content,
By comparative example 1 it can be found that if negative oxygen ion when being not added with nano-cellulose and silica in tourmaline cannot
Effective release is accessed, the burst size that negative oxygen ion in nano-cellulose and silica air is only added just has reached effect
Fruit.
2, Stability of Slurry
Suspension prepared by embodiment 1-6 place 72 hours after stability, as Fig. 1 is shown：Implement 1 as seen from the figure
Stablizing effect be worst, the embodiment 2-6 that nano-cellulose and silica is only added could effectively improve slurry
Stability.
Finally illustrate, preferred embodiment above is only used to illustrate the technical scheme of the present invention and unrestricted, although logical
It crosses above preferred embodiment the present invention is described in detail, however, those skilled in the art should understand that, can be
Various changes are made to it in form and in details, defined by claims of the present invention.
Claims (9)
1. tourmaline slurry of a kind of stabilization and preparation method thereof, which is characterized in that a kind of tourmaline slurry of stabilization
For：By the tourmaline, 80-100 parts of alcohol-water mixture, 0.1-1 parts of nano-cellulose, 0.5- of 1-2 parts of mass fraction meter
1.5 parts of silica, 10-20 parts of menthol solutions, 6-8 parts of essence solvent after stirring evenly, is packed into planetary ball mill tank
In, ball milling and the substance that is prepared, the substance are exactly a kind of tourmaline slurry of stabilization.
2. a kind of tourmaline slurry and preparation method thereof of stabilization according to claim 1, which is characterized in that described one
The preparation method of kind of stable tourmaline slurry is：The tourmaline of 1-2 parts of mass fraction meter, 80-100 parts of alcohol water are mixed
Liquid, 0.1-1 parts of nano-cellulose, 0.5-1.5 parts of silica, which are added in reaction kettle, carries out mixed at high speed, incorporation time 1-2
Hour, 10-20 parts of menthol solutions and 6-8 parts of essence solvent are added after having mixed by agitator speed 300-400rpm
In reaction kettle, then after being stirred device mixing 4-5 minutes, stops stirring, obtain uniformly mixed slurry, then add the slurry
Entering to be fitted into planetary ball mill tank, be ground, Ball-milling Time was at 10-24 hours, after ball milling, carried out abrading-ball lock out operation,
Obtained slurry is exactly a kind of tourmaline slurry of stabilization.
3. a kind of tourmaline slurry and preparation method thereof of stabilization according to claim 1, which is characterized in that described receives
Rice fiber is put in then beaker by the cotton of the high-purity of market purchase, suitable hydrogen peroxide, concentration is then added
It in 2-5%, carries out after impregnating 1-2 hours, the water inside cotton, which is carried out agent, to be gone out, and the cotton more dried weighs quality
Number is that 10-20 parts of cotton is put into reaction kettle, and 100-120 parts of copper ammon solution, the concentration control of copper ammon solution is then added
System in 10-20%, reacted by turn on agitator, and mixing speed control stops in 500-600rpm after cotton all dissolving
Only stir, be then taken out it is spare, in a kettle be added 200-300 parts of a concentration of 1-3mol/L sulfuric acid solution, will be standby
It is added in constant pressure buret with liquid, opens blender, then mixing speed control opens constant pressure titration in 400-600rpm
Pipe, dropping point hasten control at 1-2 drops/sec, it is to be titrated completely after react 1-2 hour again, then stop stirring, the suspension that will be obtained
Liquid is filtered, and obtained filter residue is dried, and the fiber obtained after dry is exactly nanofiber.
4. a kind of tourmaline slurry and preparation method thereof of stabilization according to claim 1, which is characterized in that the oxygen
SiClx is nano oxidized silicon matter of the silica content 98% or more, and granular size is 200-1000 nanometers.
5. a kind of tourmaline slurry and preparation method thereof of stabilization according to claim 1, which is characterized in that described is thin
Lotus alcoholic solution is that mass fraction is mixed the substance being prepared for 2-5 parts of menthol and 80-100 part alcohol.
6. a kind of tourmaline slurry and preparation method thereof of stabilization according to claim 1, which is characterized in that the perfume (or spice)
Smart solvent is that mass fraction is mixed the substance being prepared for 1-3 parts of essence and 100-120 part alcohol.
7. a kind of tourmaline slurry and preparation method thereof of stabilization according to claim 1, which is characterized in that the electricity
Gas stone powder is that particle size is in 300-400 mesh powders.
8. a kind of tourmaline slurry and preparation method thereof of stabilization according to claim 1, which is characterized in that the institute
The ball milling stated, per 100ml, the dosage of abrading-ball is grinding jar：(1-2) a diameter 16mm stainless steel abrading-balls；(3-5) a diameter 12mm is not
Become rusty steel abrading-ball；(10-20) a diameter 10mm stainless steel abrading-balls；(30-40) a diameter 8mm stainless steel abrading-balls；(100-300) is a straight
Diameter 5mm stainless steel abrading-balls.
9. a kind of tourmaline slurry and preparation method thereof of stabilization according to claim 2, which is characterized in that the alcohol
Aqueous solution is that the mass ratio of ethyl alcohol and deionized water is 2-5：The mixed liquor that 100 ratio is mixed.