CN108608532A - A kind of bamboo barrel open-and-flat type bamboo recombination board material production method - Google Patents
A kind of bamboo barrel open-and-flat type bamboo recombination board material production method Download PDFInfo
- Publication number
- CN108608532A CN108608532A CN201810491469.8A CN201810491469A CN108608532A CN 108608532 A CN108608532 A CN 108608532A CN 201810491469 A CN201810491469 A CN 201810491469A CN 108608532 A CN108608532 A CN 108608532A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- thick bamboo
- bamboo tube
- tube
- laying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of bamboo barrel open-and-flat type bamboo recombination board material production methods, including broken bamboo, gluing, drying, stacking plate-laying, hot forming in hot press mould, broken bamboo mode are with step：1. by thick bamboo tube, specification is blocked on demand, and prunes the ring of thick bamboo tube convex outer surfaces；2. the bamboo blueness thin layer of thick bamboo tube outer circumference surface is pruned 1mm；3. removing the interlayer ring in thick bamboo tube inner circle；4. stretching into thick bamboo tube inner circle with cutter, along the circumferentially-spaced 3~10mm in bamboo fibre direction, inner circle taeniae seam is cut in drawing；5. thick bamboo tube high temperature carbonization is handled；6. the thick bamboo tube after charing is radially splitted into a mouth, and from groove by thick bamboo tube using hot pressing, weight is open and flat opens, form plane bamboo clappers；7. plane bamboo clappers bamboo strip, yellow bamboo face are planished with thicknessing machine；Then enter gluing program, enters baking step afterwards；Enter after baking step and plate-laying is laminated in hot press mould, enters hot forming after plate-laying is laminated.
Description
Technical field
The present invention relates to bamboo recombination board production method, especially a kind of bamboo barrel open-and-flat type bamboo recombination board material production method.
Background technology
Bamboo recombination board production process is：Broken bamboo, film-making, drying, gluing, drying, the interior stacking plate-laying of hot press mould, hot pressing
Forming.Described broken bamboo is that will justify bamboo to break the bamboo band that bamboo is cut into rectangular cross-section, then by bamboo band through subsequent handling at
Reason, then stratiform that bamboo band tile in moulding press overlap implementation hot forming, and some processes must be by bamboo band rope system
After bamboo curtain splint or bamboo mat shape, the tiling of ability upper mold.
Since bamboo band needs are cutd open, dug, bamboo band can be just made in the bottom left right side thereon, and heavy workload, rim charge waste is also big,
It is thus of high cost.Impregnation glue quantity is big simultaneously, not only improves cost, nor meets environmental requirement.
Invention content
It is an object of the invention to overcome drawbacks described above, a kind of bamboo barrel open-and-flat type bamboo recombination board material production method is provided.
To achieve the above object, the present invention is implemented by the following technical solutions：
A kind of bamboo barrel open-and-flat type bamboo recombination board material production method, including broken bamboo, gluing, drying, the row of stacking in hot press mould
Plate, hot forming, it is characterised in that：Break bamboo mode is with step：
1. by thick bamboo tube, specification is blocked on demand, and prunes the ring of thick bamboo tube convex outer surfaces；
2. the bamboo blueness thin layer of thick bamboo tube outer circumference surface is pruned 1mm；
3. removing the interlayer ring in thick bamboo tube inner circle；
4. stretching into thick bamboo tube inner circle with cutter, along the circumferentially-spaced 3~10mm in bamboo fibre direction, inner circle taeniae seam is cut in drawing；
5. thick bamboo tube high temperature carbonization is handled, thick bamboo tube is put into the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon
Degree is 160-190 DEG C, 2-4 hours heating times, thick bamboo tube carbonization, and carbonizing degree is 5%-30%；
6. the thick bamboo tube after charing is radially splitted into a mouth, and from groove by thick bamboo tube using hot pressing, weight is open and flat opens, shape
At plane bamboo clappers；
7. plane bamboo clappers bamboo strip, yellow bamboo face are planished with thicknessing machine；
Then enter gluing program, gluing program be each plane bamboo clappers gluing or impregnation, but it is to be formed after bamboo recombination plates
The outer surface of the two plate plane bamboo clappers up and down of material does not glue；Enter baking step after the gluing of plane bamboo clappers；Enter after baking step
Be laminated plate-laying in hot press mould, stacking plate-laying require it is to be formed after the outer surface that two plate plane bamboo clappers do not glue up and down in upper
Top layer and lower bottom outerplanar；Enter hot forming step after plate-laying is laminated.
The beneficial effects of the invention are as follows：
Preferably solve stock utilization existing in the prior art is low, presentation quality is poor and manufacturing procedure is complicated etc.
Problem.The present invention uses internal layer gluing, and the bamboo clappers surface processed is without glue, and particularly suitable for Furniture manufacture, building decoration is various
Craftwork and Bamboo cutting board, the bamboo board produced is beautiful and generous, not only environmentally friendly but also hygienic, durable.
Specific implementation mode
Embodiments of the present invention are further described with reference to embodiment, but are not limitation of the invention.
The production stage of the present invention includes broken bamboo, gluing, drying, the interior stacking plate-laying of hot press mould, hot forming, breaks bamboo side
Formula is with step：
1. by thick bamboo tube, specification is blocked on demand, and prunes the ring of thick bamboo tube convex outer surfaces；
2. the bamboo blueness thin layer of thick bamboo tube outer circumference surface is pruned 1mm；
3. removing the interlayer ring in thick bamboo tube inner circle；
4. stretching into thick bamboo tube inner circle with cutter, along the circumferentially-spaced 3~10mm in bamboo fibre direction, inner circle taeniae seam is cut in drawing；
5. thick bamboo tube high temperature carbonization is handled, thick bamboo tube is put into the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon
Degree is 160 DEG C, 2 hours heating times, thick bamboo tube carbonization, carbonizing degree 15%；
6. the thick bamboo tube after charing is radially splitted into a mouth, and from groove by thick bamboo tube using hot pressing, weight is open and flat opens, shape
At plane bamboo clappers；
7. plane bamboo clappers bamboo strip, yellow bamboo face are planished with thicknessing machine；
Then enter gluing program, gluing program be each plane bamboo clappers gluing or impregnation, but it is to be formed after bamboo recombination plates
The outer surface of the two plate plane bamboo clappers up and down of material does not glue；Enter baking step after the gluing of plane bamboo clappers；Enter after baking step
Be laminated plate-laying in hot press mould, stacking plate-laying require it is to be formed after the outer surface that two plate plane bamboo clappers do not glue up and down in upper
Top layer and lower bottom outerplanar；Enter hot forming step after plate-laying is laminated.
The circle thick bamboo tube of interception is subjected to external cutting, the bamboo blueness thin layer about 1mm on removal thick bamboo tube surface, it is therefore an objective to reduce its table
Layer flintiness, makes it reduce cracking when stretching expansion.
It is circumferentially cut open, is made at interval of between 3~10mm of distance along bamboo fibre direction with yellow bamboo face of the cutter in thick bamboo tube
Several taeniaes that cuts open is formed in thick bamboo tube to stitch；
The cutter be on the iron staff of cone, load onto it is several cutter, when thick bamboo tube is sent into conical iron staff,
Tabasheer surface is cut in tabasheer meat from tabasheer surface between about 1~2mm, it is therefore an objective to destroy bamboo under the cutting of several cutteves
The flintiness in yellow face makes circular thick bamboo tube not crack seriously because of the hard of tabasheer when stretching expansion.
By the circle thick bamboo tube high temperature carbonization, make thick bamboo tube softening, Anti-moth-eating；
The high temperature carbonization refers to that Mao bamboo tube is packed into high-temperature sterilization pot, carries out high-temperature process, Mao bamboo tube is made to soften,
It is easy to Mao bamboo tube flattening, it is easy to process.
It is that circular thick bamboo tube is rived a mouth along bamboo fibre direction that a mouth is splitted in the longitudinal direction, by circular thick bamboo tube
Expansion is stretched as possible, in order to which it is flattened.
The moso bamboo that drawn is unfolded is shaped by blank bamboo clappers using hot pressing, weight；
The hot pressing is the concora crush hydraulic press with heating platen using high tonnage, and the Mao bamboo tube of expansion is flattened sizing.
Bamboo strip and yellow bamboo face are planished with thicknessing machine, convenient for compound；
Bamboo clappers longitudinally need to can carry out gluing through two layers or more gluing with bamboo clappers after processing, can also be glued or vertical in length and breadth
Transverse and longitudinal etc. carries out glued.Glued bamboo clappers is that internal layer gluing, the bamboo clappers surface processed is used to be suitable for Furniture manufacture without glue,
Building decoration, various craftworks etc., especially Bamboo cutting board, the Bamboo cutting board produced is beautiful and generous, not only environmentally friendly but also hygienic, prolonged resistance to
With.
The above described is only a preferred embodiment of the present invention, not making any form to technical scheme of the present invention
On limitation.Every essence according to the present invention is to any simple modification, equivalent change and modification made by above example,
It falls within the scope of protection of the present invention.
Claims (1)
1. a kind of bamboo barrel open-and-flat type bamboo recombination board material production method, including broken bamboo, gluing, drying, stacking plate-laying in hot press mould,
Hot forming, it is characterised in that：Break bamboo mode is with step：
1. by thick bamboo tube, specification is blocked on demand, and prunes the ring of thick bamboo tube convex outer surfaces；
2. the bamboo blueness thin layer of thick bamboo tube outer circumference surface is pruned 1mm；
3. removing the interlayer ring in thick bamboo tube inner circle；
4. stretching into thick bamboo tube inner circle with cutter, along the circumferentially-spaced 3~10mm in bamboo fibre direction, inner circle taeniae seam is cut in drawing；
5. thick bamboo tube high temperature carbonization is handled, thick bamboo tube is put into the dry machine of dried disinfecting carbon, the temperature of the dry machine heating of dried disinfecting carbon is
160-190 DEG C, 2-4 hours heating times, thick bamboo tube carbonization, carbonizing degree is 5%-30%；
6. the thick bamboo tube after charing is radially splitted into a mouth, and from groove by thick bamboo tube using hot pressing, weight is open and flat opens, formed flat
Face bamboo board；
7. plane bamboo clappers bamboo strip, yellow bamboo face are planished with thicknessing machine；
Then enter gluing program, gluing program is each plane bamboo clappers gluing or impregnation, but it is to be formed after bamboo recombination board
The outer surface of upper and lower two plate planes bamboo clappers does not glue；Enter baking step after the gluing of plane bamboo clappers；Enter hot pressing after baking step
Be laminated plate-laying in machine mould, stacking plate-laying require it is to be formed after the outer surface that two plate plane bamboo clappers do not glue up and down in upper top layer
With lower bottom outerplanar；Enter hot forming step after plate-laying is laminated.