CN108589400A - Silk wallpaper or wall cloth coating composition and Silk wallpaper or wall cloth - Google Patents
Silk wallpaper or wall cloth coating composition and Silk wallpaper or wall cloth Download PDFInfo
- Publication number
- CN108589400A CN108589400A CN201810498212.5A CN201810498212A CN108589400A CN 108589400 A CN108589400 A CN 108589400A CN 201810498212 A CN201810498212 A CN 201810498212A CN 108589400 A CN108589400 A CN 108589400A
- Authority
- CN
- China
- Prior art keywords
- parts
- areas
- silk
- wall cloth
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to decorative materials technologies, and in particular to a kind of Silk wallpaper or wall cloth coating composition and Silk wallpaper or wall cloth.Composition includes the component of following parts by weight meter:14 parts of 18 20 parts of PVC paste resin P450, plasticizer DINP12,1.2 1.4 parts of titanium dioxide, 68 parts of Paris white, 0.8 1.2 parts of stabilizer, 0.8 1.0 parts of aliphatic wetting dispersing agent, 0.4 0.6 parts of macromolecule polar acid ester wetting dispersing agent, 23 parts of thinner.The Silk wallpaper or wall cloth are to obtain coating semi-finished product by the way that the composition to be coated on non-woven fabrics or non-woven paper, then carried out again with non-woven fabrics or Silk it is compound obtain compound semi-finished product, finished product is obtained after printing.The product of the present invention is not necessarily to glue or binder, and more environmentally-friendly, the product caking property of preparation is strong, and durability is good.
Description
Technical field
The present invention relates to decorative materials technologies, and in particular to a kind of Silk wallpaper or wall cloth coating composition and
Silk wallpaper or wall cloth.
Background technology
Wallpaper is also referred to as wallpaper, is a kind of for papering the indoor hardware fitting of metope, be widely used in house, office,
The interior decoration etc. of hotel.Material is not limited to paper, also includes other materials.
Because with color is various, pattern is abundant, luxurious style, safety and environmental protection, easy for construction, affordable etc. it is a variety of its
The incomparable feature of its house decorative material, therefore obtained in developed countries and regions such as America and Europe, Japan considerable degree of general
And.
Current wallpaper has the following disadvantages or insufficient, first, it needs to be especially by glue in the recombination process of wallpaper
Industrial glue is adhered, not environmentally friendly enough;Second, color saturation is inadequate, and color is not true bright-coloured enough.
Invention content
The purpose of the present invention is to solve the above problem, a kind of Silk wallpaper or wall cloth coating composition are provided,
Also provide a kind of PVC Silk wallpapers using the composition as face coat simultaneously.
In order to reach foregoing invention purpose, the present invention uses following technical scheme:
A kind of Silk wallpaper or wall cloth coating composition, include the component of following parts by weight meter:
18-20 parts of PVC paste resin P450,
DINP12-14 parts of plasticizer,
1.2-1.4 parts of titanium dioxide,
6-8 parts of Paris white,
0.8-1.2 parts of stabilizer,
0.8-1.0 parts of aliphatic wetting dispersing agent,
0.4-0.6 parts of macromolecule polar acid ester wetting dispersing agent,
Thinner 2-3.
The viscosity of scheme as a further preference, composition is controlled in 1200-1500CPS.
Using above-mentioned Silk wallpaper or the Silk wallpaper or wall cloth of wall cloth coating composition, using following steps system
It is standby to form:
(1)Coating composition is coated on non-woven paper or non-woven fabrics, cooling and shaping is carried out after drying, obtain coated semi at
Product;
(2)Coating semi-finished product and non-woven fabrics or Silk heating are carried out it is compound, then pass through cooling and shaping obtain it is compound partly at
Product;
(3)Compound semi-finished product are printed using intaglio printing, and scraper is operated without wiping in printing process.
Scheme as a further preference, the step(1)For:By coating composition using coating machine in 65-100 g/
m2Non-woven paper on be coated, after coating the grammes per square metre of non-woven paper be 250-280 g/m2;About 155-180 DEG C of long baking oven
Hot wind cures, production speed 30-50m/min;Then cooling and shaping obtains coating semi-finished product;Cooling temperature is 25-30 DEG C.
Scheme as a further preference, the step(1)In long baking oven be ten head of district's baking ovens, the temperature of ten area's baking ovens
Distribution is as follows:One 160-165 DEG C of area, two 160-165 DEG C of areas, three 165-170 DEG C of areas, four 170-175 DEG C of areas, five area 175-180
DEG C, six 170-175 DEG C of areas, seven 165-170 DEG C of areas, eight 160-165 DEG C of areas, nine 160-165 DEG C of areas, ten 155-160 DEG C of areas.
Scheme as a further preference, the step(2)For:By coating semi-finished product and 10-50 g/m2Non-woven fabrics or
Silk heating is compound, and concrete technology is:After being preheated at 150-170 DEG C, by coating softening and non-woven fabrics at 230-250 DEG C
Or Silk is compound;Obtain compound semi-finished product.
Scheme as a further preference, the step(2)Middle heating is compound compound using pressure roller and runner pressing progress,
The pressure of pressure roller is 20-35kg, and runner temperature is 230-250 DEG C, and non-woven fabrics or Silk are located at runner side, coating semi-finished product position
In pressure roller side.
Scheme as a further preference, the step(2)Middle recombination velocity is 10-15m/min.
Scheme as a further preference, the step(3)For:It is washed and is printed using intaglio plate, using laser intaglio plate by color
After ink is fully filled with the entire space of a whole page, then stock and intaglio plate are rolled using pressure and are squeezed without wiping operation processing by scraper
Pressure, finally passes through 180-220 DEG C of the drying air-dried with 165-180 DEG C, and production speed is 10-15m/min.
Scheme as a further preference, the step(3)In baking oven be long baking oven, specifically include five baking zones;
Temperature Distribution is:One 165-170 DEG C of area, two 170-175 DEG C of areas, three 170-175 DEG C of areas, four 175-180 DEG C of areas, five area 165-
170℃。
Compared with prior art, the present invention advantageous effect is:Since new combination process may be used, so as to reality
Now quick continuous production, to further solve the seamed splicing during wallpaper use, material technology compound tense is cancelled
Industrial glue bonding squeezes embedded fusion completely, compound fastness is high, and properties of product are more environmentally-friendly using physical characteristics of materials.
Developing and printing coloring process using the present invention, product color plumpness is high, and the three-dimensional sense of no spinning or Silk protrudes.
Specific implementation mode
Explanation is further described to technical scheme of the present invention below by specific embodiment.
If without specified otherwise, the raw material employed in the embodiment of the present invention is raw material commonly used in the art, is implemented
Method employed in example, is the conventional method of this field.
Embodiment 1:
A kind of Silk wallpaper or wall cloth coating composition, include the component of following parts by weight meter:
18 parts of PVC paste resin P450,
DINP14 parts of plasticizer,
1.2 parts of titanium dioxide,
8 parts of Paris white,
0.8 part of stabilizer,
1.0 parts of aliphatic wetting dispersing agent,
0.4 part of macromolecule polar acid ester wetting dispersing agent,
3 parts of thinner.
Above-mentioned component is mixed, then controls the viscosity of mixed composition in 1200CPS.
Wherein,
Stabilizer is potassium zinc stabilizer;
Aliphatic wetting dispersing agent is Aliphatic and wetting agent, KD CHEM CO., LTD.Korean company is purchased
It buys;
Macromolecule polar acid ester wetting dispersing agent is polar acidic ester of a high molecular weight
Polymer and wetting agent derivative, KD CHEM CO., LTD.Korean company is bought.
Using above-mentioned Silk wallpaper or the Silk wallpaper or wall cloth of wall cloth coating composition, using following steps system
It is standby to form:
(1)Coating composition is coated on non-woven paper or non-woven fabrics, cooling and shaping is carried out after drying, obtain coated semi at
Product;
By coating composition using coating machine in 65-100 g/m2Non-woven paper on be coated, the grammes per square metre of non-woven paper after coating
For 250-280 g/m2;Using the 155-180 DEG C of up-and-down hot wind solidification of long baking oven, production speed 30-50m/min;Then cooling fixed
Type obtains coating semi-finished product;Cooling temperature is 25-30 DEG C.
Long baking oven is ten head of district's baking ovens, and the Temperature Distribution of ten area's baking ovens is as follows:One 160-165 DEG C of area, two area 160-165
DEG C, three 165-170 DEG C of areas, four 170-175 DEG C of areas, five 175-180 DEG C of areas, six 170-175 DEG C of areas, seven 165-170 DEG C of areas, 8th area
160-165 DEG C, nine 160-165 DEG C of areas, ten 155-160 DEG C of areas.The temperature of ten area's baking ovens to the quality of coating semi-finished product play to
Important influence is closed, the control of temperature directly affects the last quality of product.Also, the temperature can using multi-region control
Reach institute's standard to be achieved;The length of baking oven adopted in this step is 5m, by controlling throughput rate to control heating
Time;Following embodiment all same;
(2)Coating semi-finished product and non-woven fabrics or Silk heating are carried out it is compound, then pass through cooling and shaping obtain it is compound partly at
Product;
By coating semi-finished product and 10-50 g/m2Non-woven fabrics or Silk heating it is compound, concrete technology is:At 150-170 DEG C
It is at 230-250 DEG C that coating softening is compound with non-woven fabrics or Silk after preheating;Obtain compound semi-finished product.
Heat it is compound carried out using the pressing of pressure roller and runner compound, the pressure of pressure roller is 20-35kg, and runner temperature is 230-
250 DEG C, non-woven fabrics or Silk are located at runner side, and coating semi-finished product are located at pressure roller side.Recombination velocity is 10-15m/min.
(3)Compound semi-finished product are printed using intaglio printing, and scraper is operated without wiping in printing process.
It is washed and is printed using intaglio plate, after color ink is fully filled with the entire space of a whole page using laser intaglio plate, scraper is without wiping
Then stock and intaglio plate are utilized pressure rolling extrusion by operation processing, finally pass through 180-220 DEG C of air-dried and 165-180
DEG C drying, production speed be 10-15m/min;Baking oven herein is long baking oven, specifically includes five baking zones;Temperature Distribution
For:One 165-170 DEG C of area, two 170-175 DEG C of areas, three 170-175 DEG C of areas, four 175-180 DEG C of areas, five 165-170 DEG C of areas.Specifically
According to production speed adjust drying time.The length of baking oven adopted in this step is 15-20m, by controlling production speed
Rate is to control heating time;Following embodiment all same;
Two kinds of materials are substantially bonded by the making of current Artificial Silk using adhesive or glue, this side
Formula not only complex process, and due to the limitation of adhesive and glue, cost is very high, and the organic matter that adhesive and glue water tape come is dirty
Dye is also very serious, this all reduces the quality of product, limits the application of product.In addition, using current adhesion technique system
The durability of Artificial Silk made of standby is poor, after the time is longer, is easy to happen and falls off, this is all by current technique institute
Limitation, causes the quality of product that cannot be guaranteed.
And using being first coated PVC on non-woven fabrics or non-woven paper in the present invention, to form coating,
Then reach the characteristic melted after fusing point using PVC itself, coating semi-finished product and non-woven fabrics or Silk heating progress are compound,
After what this process utilized is polyvinyl chloride resin layer hot mastication, the products such as non-woven fabrics or Silk are squeezed under physical external force effect
It is pressed onto in resin layer, embedded compound, such fastness is strong, and durability is good, and does not use glue and binder, more environmentally-friendly,
Also more durable, improves the quality of product.
It after compound, is printed, current common printing technology is as follows:Color ink is filled into using laser intaglio plate
In mesh, then the extra color ink of the space of a whole page is wiped off with scraper, recycles pressure by stock and intaglio plate rolling extrusion, allows mesh
In the color ink of 60%-70% be transferred on stock.The disadvantage is that the color ink amount of transfer is few, color ink is only transferred to the highest of stock
Point, cannot reach the minimum point on stock surface, and color saturation is poor.And in the present invention, although equally using intaglio printing,
But washing printing is after color ink is fully filled with the entire space of a whole page using laser intaglio plate in the present invention, and grasped without scraper wiping
Make, stock and intaglio plate directly utilized into pressure rolling extrusion, the color ink of the entire space of a whole page is allowed to completely penetrate stock object surface,
Whether highs and lows, so color saturation is very high.The mode of operation of the present invention changes traditional operation mode
It sticks to the established practice, uses the non routine operation of current those skilled in the art, to obtain the preferable product of printing effect.
The product of the present invention is in print color, by using above-mentioned technique, so that developing and printing inking amount is more than recessed
4-5 times of impact transfer printing, so color is very full.
Embodiment 2:
A kind of Silk wallpaper or wall cloth coating composition, include the component of following parts by weight meter:
20 parts of PVC paste resin P450,
DINP12 parts of plasticizer,
1.4 parts of titanium dioxide,
6 parts of Paris white,
1.2 parts of stabilizer,
0.8 part of aliphatic wetting dispersing agent,
0.6 part of macromolecule polar acid ester wetting dispersing agent,
2 parts of thinner.
Above-mentioned component is mixed, then controls the viscosity of mixed composition in 1500CPS.
Wherein,
Stabilizer is potassium zinc stabilizer;
Aliphatic wetting dispersing agent is Aliphatic and wetting agent, KD CHEM CO., LTD.Korean company is purchased
It buys;
Macromolecule polar acid ester wetting dispersing agent is polar acidic ester of a high molecular weight
Polymer and wetting agent derivative, KD CHEM CO., LTD.Korean company is bought.
Using above-mentioned Silk wallpaper or the Silk wallpaper or wall cloth of wall cloth coating composition, using following steps system
It is standby to form:
(1)Coating composition is coated on non-woven paper, cooling and shaping is carried out after drying, obtains coating semi-finished product;
By coating composition using coating machine in 65-100 g/m2Non-woven paper on be coated, the grammes per square metre of non-woven paper after coating
For 250-280 g/m2;Using the 155-180 DEG C of up-and-down hot wind solidification of long baking oven, production speed 30-50m/min;Then cooling fixed
Type obtains coating semi-finished product;Cooling temperature is 25-30 DEG C.
Long baking oven is ten head of district's baking ovens, and the Temperature Distribution of ten area's baking ovens is as follows:One 160-165 DEG C of area, two area 160-165
DEG C, three 165-170 DEG C of areas, four 170-175 DEG C of areas, five 175-180 DEG C of areas, six 170-175 DEG C of areas, seven 165-170 DEG C of areas, 8th area
160-165 DEG C, nine 160-165 DEG C of areas, ten 155-160 DEG C of areas.
(2)Coating semi-finished product and non-woven fabrics or Silk heating progress are compound, it is then obtained by cooling and shaping compound
Semi-finished product;
By coating semi-finished product and 10-50 g/m2Non-woven fabrics or Silk heating it is compound, concrete technology is:At 150-170 DEG C
It is at 230-250 DEG C that coating softening is compound with non-woven fabrics or Silk after preheating;Obtain compound semi-finished product.
Heat it is compound carried out using the pressing of pressure roller and runner compound, the pressure of pressure roller is 20-35kg, and runner temperature is 230-
250 DEG C, non-woven fabrics or Silk are located at runner side, and coating semi-finished product are located at pressure roller side.Recombination velocity is 10-15m/min.
(3)Compound semi-finished product are printed using intaglio printing, and scraper is operated without wiping in printing process.
It is washed and is printed using intaglio plate, after color ink is fully filled with the entire space of a whole page using laser intaglio plate, scraper is without wiping
Then stock and intaglio plate are utilized pressure rolling extrusion by operation processing, finally pass through 180-220 DEG C of air-dried and 165-180
DEG C drying, production speed be 10-15m/min;Baking oven herein is long baking oven, specifically includes five baking zones;Temperature Distribution
For:One 165-170 DEG C of area, two 170-175 DEG C of areas, three 170-175 DEG C of areas, four 175-180 DEG C of areas, five 165-170 DEG C of areas.Specifically
According to production speed adjust drying time.
Embodiment 3:
A kind of Silk wallpaper or wall cloth coating composition, include the component of following parts by weight meter:
20 parts of PVC paste resin P450,
DINP14 parts of plasticizer,
1.2 parts of titanium dioxide,
7 parts of Paris white,
1 part of stabilizer,
0.9 part of aliphatic wetting dispersing agent,
0.5 part of macromolecule polar acid ester wetting dispersing agent,
2-3 parts of thinner.
Above-mentioned component is mixed, then controls the viscosity of mixed composition in 1200-1500CPS.
Wherein,
Stabilizer is potassium zinc stabilizer;
Aliphatic wetting dispersing agent is Aliphatic and wetting agent, KD CHEM CO., LTD.Korean company is purchased
It buys;
Macromolecule polar acid ester wetting dispersing agent is polar acidic ester of a high molecular weight
Polymer and wetting agent derivative, KD CHEM CO., LTD.Korean company is bought.
Using above-mentioned Silk wallpaper or the Silk wallpaper or wall cloth of wall cloth coating composition, using following steps system
It is standby to form:
(1)Coating composition is coated on non-woven paper, cooling and shaping is carried out after drying, obtains coating semi-finished product;
By coating composition using coating machine in 65-100 g/m2Non-woven paper on be coated, the grammes per square metre of non-woven paper after coating
For 250-280 g/m2;Using the 155-180 DEG C of up-and-down hot wind solidification of long baking oven, production speed 30-50m/min;Then cooling fixed
Type obtains coating semi-finished product;Cooling temperature is 25-30 DEG C.
Long baking oven is ten head of district's baking ovens, and the Temperature Distribution of ten area's baking ovens is as follows:One 160-165 DEG C of area, two area 160-165
DEG C, three 165-170 DEG C of areas, four 170-175 DEG C of areas, five 175-180 DEG C of areas, six 170-175 DEG C of areas, seven 165-170 DEG C of areas, 8th area
160-165 DEG C, nine 160-165 DEG C of areas, ten 155-160 DEG C of areas.
(2)Coating semi-finished product and non-woven fabrics or Silk heating progress are compound, it is then obtained by cooling and shaping compound
Semi-finished product;
By coating semi-finished product and 10-50 g/m2Non-woven fabrics or Silk heating it is compound, concrete technology is:At 150-170 DEG C
It is at 230-250 DEG C that coating softening is compound with non-woven fabrics or Silk after preheating;Obtain compound semi-finished product.
Heat it is compound carried out using the pressing of pressure roller and runner compound, the pressure of pressure roller is 20-35kg, and runner temperature is 230-
250 DEG C, non-woven fabrics or Silk are located at runner side, and coating semi-finished product are located at pressure roller side.Recombination velocity is 10-15m/min.
(3)Compound semi-finished product are printed using intaglio printing, and scraper is operated without wiping in printing process.
It is washed and is printed using intaglio plate, after color ink is fully filled with the entire space of a whole page using laser intaglio plate, scraper is without wiping
Then stock and intaglio plate are utilized pressure rolling extrusion by operation processing, finally pass through 180-220 DEG C of air-dried and 165-180
DEG C drying, production speed be 10-15m/min;Baking oven herein is long baking oven, specifically includes five baking zones;Temperature Distribution
For:One 165-170 DEG C of area, two 170-175 DEG C of areas, three 170-175 DEG C of areas, four 175-180 DEG C of areas, five 165-170 DEG C of areas.Specifically
According to production speed adjust drying time.
Embodiment 4:
It is improved on the basis of embodiment 1,2 or 3, improved is matching for Silk wallpaper or wall cloth coating composition
Than the component of following parts by weight is added on the basis of embodiment 1 or 2 or 3:0.8 part of ethylenediamine tetra-acetic acid, bisphenol-A 0.2
Part.By adding ethylenediamine tetra-acetic acid and bisphenol-A in the composition, the adhesion strength after cladding melts is improved, and then can have
The dosage of compound tense is heated after the cladding melts of effect reduction coating semi-finished product with non-woven fabrics or Silk, the dosage of coating is reduced,
Mean that the flexibility of wallpaper or wall paper is more excellent, is conducive to be bonded with wall of different shapes.Also for raising
The competitiveness of product.
Embodiment 5:
It is improved on the basis of embodiment 1,2 or 3, improved is matching for Silk wallpaper or wall cloth coating composition
Than the component of following parts by weight is added on the basis of embodiment 1 or 2 or 3:0.5 part of ethylenediamine tetra-acetic acid, bisphenol-A 0.5
Part.By adding ethylenediamine tetra-acetic acid and bisphenol-A in the composition, the adhesion strength after cladding melts is improved, and then can have
The dosage of compound tense is heated after the cladding melts of effect reduction coating semi-finished product with non-woven fabrics or Silk, the dosage of coating is reduced,
Mean that the flexibility of wallpaper or wall paper is more excellent, is conducive to be bonded with wall of different shapes.Also for raising
The competitiveness of product.
Embodiment 6:
It is improved on the basis of embodiment 1,2,3,4 or 5, improved is Silk wallpaper or wall cloth coating composition
0.2 part of sodium carboxymethylcellulose, 0.1 part of potassium pyrophosphate is particularly added in proportioning on the basis of before this.
Embodiment 7:
It is improved on the basis of embodiment 1,2,3,4 or 5, sodium carboxymethylcellulose particularly is added on the basis of before this
0.3 part, 0.05 part of potassium pyrophosphate.
Sodium carboxymethylcellulose, potassium pyrophosphate is added, further improves the toughness of coating, caused by avoiding coating embrittlement
The problem of wallpaper is easily broken off.
The wallpaper or wall cloth toughness of the present invention is preferable, and fastness is higher, can substantially width produce, during fitting, hold
Bending change is easily carried out according to the structure of wall, reduces handing-over seam during fitting, high comprehensive performance.
Claims (10)
1. a kind of Silk wallpaper or wall cloth coating composition, which is characterized in that include the component of following parts by weight meter:
18-20 parts of PVC paste resin P450,
DINP12-14 parts of plasticizer,
1.2-1.4 parts of titanium dioxide,
6-8 parts of Paris white,
0.8-1.2 parts of stabilizer,
0.8-1.0 parts of aliphatic wetting dispersing agent,
0.4-0.6 parts of macromolecule polar acid ester wetting dispersing agent,
2-3 parts of thinner.
2. composition according to claim 1, which is characterized in that the viscosity of composition is controlled in 1200-1500CPS.
3. using the Silk wallpaper or wall of Silk wallpaper or wall cloth coating composition described in any of the above-described claim
Cloth, which is characterized in that be prepared using following steps:
(1)Coating composition is coated on non-woven paper or non-woven fabrics, cooling and shaping is carried out after drying, obtain coated semi at
Product;
(2)Coating semi-finished product and non-woven fabrics or Silk heating are carried out it is compound, then pass through cooling and shaping obtain it is compound partly at
Product;
(3)Compound semi-finished product are printed using intaglio printing, and scraper is operated without wiping in printing process.
4. Silk wallpaper according to claim 3 or wall cloth, which is characterized in that the step(1)For:By coatings combine
Object is using coating machine in 65-100g/m2Non-woven paper on be coated, after coating the grammes per square metre of non-woven paper be 250-280 g/m2;It adopts
With the 155-180 DEG C of up-and-down hot wind solidification of long baking oven, production speed 40-50m/min;Then cooling and shaping obtains coating semi-finished product;
Cooling temperature is 25-30 DEG C.
5. Silk wallpaper according to claim 4 or wall cloth, which is characterized in that the step(1)In long baking oven be
The Temperature Distribution of ten head of district's baking ovens, ten area's baking ovens is as follows:One 160-165 DEG C of area, two 160-165 DEG C of areas, three 165-170 DEG C of areas,
Four 170-175 DEG C of areas, five 175-180 DEG C of areas, six 170-175 DEG C of areas, seven 165-170 DEG C of areas, eight 160-165 DEG C of areas, 9th area
160-165 DEG C, ten 155-160 DEG C of areas.
6. Silk wallpaper according to claim 3 or wall cloth, which is characterized in that the step(2)For:By coated semi at
Product and 10-50 g/m2Non-woven fabrics or Silk heating it is compound, concrete technology is:After being preheated at 150-170 DEG C, in 230-
It is at 250 DEG C that coating softening is compound with non-woven fabrics or Silk;Obtain compound semi-finished product.
7. Silk wallpaper according to claim 6 or wall cloth, which is characterized in that the step(2)Middle heating Combined Mining
Is carried out with the pressing of pressure roller and runner compound, the pressure of pressure roller is 20-35kg, and runner temperature is 230-250 DEG C, non-woven fabrics or emulation
Silk is located at runner side, and coating semi-finished product are located at pressure roller side.
8. Silk wallpaper according to claim 6 or wall cloth, which is characterized in that the step(2)Middle recombination velocity is
10-15m/min。
9. Silk wallpaper according to claim 1 or wall cloth, which is characterized in that the step(3)For:Using intaglio plate water
Developing and printing brush, after color ink is fully filled with the entire space of a whole page using laser intaglio plate, scraper is without wiping operation processing, then by printing
Object and intaglio plate utilize pressure rolling extrusion, finally pass through 180-220 DEG C of the drying air-dried with 165-180 DEG C, and production speed is
10-15m/min。
10. Silk wallpaper according to claim 1 or wall cloth, which is characterized in that the step(3)In baking oven be length
Baking oven specifically includes five baking zones;Temperature Distribution is:One 165-170 DEG C of area, two 170-175 DEG C of areas, three 170-175 DEG C of areas,
Four 175-180 DEG C of areas, five 165-170 DEG C of areas.