CN108576983A - A kind of high-elastic, anti-sweat composite material - Google Patents
A kind of high-elastic, anti-sweat composite material Download PDFInfo
- Publication number
- CN108576983A CN108576983A CN201810231674.0A CN201810231674A CN108576983A CN 108576983 A CN108576983 A CN 108576983A CN 201810231674 A CN201810231674 A CN 201810231674A CN 108576983 A CN108576983 A CN 108576983A
- Authority
- CN
- China
- Prior art keywords
- composite material
- parts
- sweat
- elastic
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of high-elastic, anti-sweat composite material, the composite material includes by quality component:25 32 parts of viscose rayon, 15 22 parts of polyester fiber, 8 15 parts of spandex fibre, 48 parts of polyamide fibre, 20 28 parts of natural fiber, 0.4 0.9 parts of antistatic agent, 13 parts of lubricant.High-elastic, the anti-sweat composite material of one kind of the present invention, this fabric have very excellent resilience, and as dress ornament, fitting is physical strong, and warmth retention property is good, meanwhile, gas permeability is more prominent, can be greatly improved to prevent sweat, adaptive.
Description
Technical field
The present invention relates to garment material fields, more particularly to a kind of high-elastic, anti-sweat composite material.
Background technology
It with people's living standard is continuously improved, to can moderately requiring for the various daily necessities in daily life
Constantly enhancing.
Clothing, food, lodging and transportion -- basic necessities of life, it is exactly clothing to come first, also reflects the critical role of clothes in daily life from side.With
The development of society, the aesthetic change of people and the impression of comfort, all pursues the close-fitting vest of clothes now, it in this way can be convex
Beautiful stature is showed, while pursuing height and breathing freely, can improve human body comfort to prevent sweat in this way.
But present fabric cannot but combine the advantages of high-elastic and anti-sweat, and more excellent, comprehensive performance is made
Excellent garment material so that people are whether pursuing beauty, or prodigious difficulty is all encountered on the road of comfort.
Invention content
In view of this, the present invention provides a kind of high-elastic, anti-sweat composite materials.
A kind of high-elastic, anti-sweat composite material, the composite material include by quality component:
Preferably, the component includes:
Preferably, the component includes:
Preferably, the natural fiber is at least one of cotton, wool, jute and silk.
Preferably, the natural fiber is the mixing of silk and wool, mass ratio 1:1.
Preferably, the antistatic agent is one kind in sodium alkyl sulfonate, quaternary ammonium salt and polyethylene glycol.
Preferably, the antistatic agent is sodium alkyl sulfonate.
Preferably, the lubricant is stearic acid or organic silicone oil.
High-elastic, the anti-sweat composite material of one kind of the present invention, this fabric have very excellent resilience, as dress ornament, fitting
Physical strong, warmth retention property is good, meanwhile, gas permeability is more prominent, can be greatly improved to prevent sweat, adaptive.
Specific implementation mode
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are some of the embodiments of the present invention, instead of all the embodiments.Based on the implementation in the present invention
Example, every other embodiment obtained by those of ordinary skill in the art without making creative efforts belong to
The scope of protection of the invention.
It should be appreciated that ought use in this specification and in the appended claims, term " comprising " and "comprising" instruction
Described feature, entirety, step, operation, the presence of element and/or component, but one or more of the other feature, whole is not precluded
Body, step, operation, element, component and/or its presence or addition gathered.
It will be further appreciated that the term "and/or" used in description of the invention and the appended claims is
Refer to any combinations and all possible combinations of one or more of associated item listed, and includes these combinations.
Embodiment 1
High-elastic, anti-sweat composite material includes by quality component:
Preparation method is:
Weigh viscose rayon, polyester fiber, spandex fibre, polyamide fibre, cotton, sodium alkyl sulfonate and the organosilicon of component amount
Oil;
Viscose rayon, polyester fiber, spandex fibre, polyamide fibre and cotton are dried, after drying 6h, stand 30min;
Viscose rayon, polyester fiber, spandex fibre, polyamide fibre and cotton after standing is added into mixing willow, is worked
After 30min, sodium alkyl sulfonate and organic silicone oil is added, mixes 3h;
It adds into porcupine opener, cleans, then shredding and mixing, mix 50min, obtain batch mixing;
Mixed batch mixing is added into lapper, spinning is carried out;
The line of hair is woven into fabric, is 50 DEG C of dry 30min in drying temperature;
40 DEG C of water are crossed, is taken out, is carried out shaping at a temperature of 80 DEG C, obtain clothing fabric.
Embodiment 2
High-elastic, anti-sweat composite material includes by quality component:
Preparation method is:
Weigh viscose rayon, polyester fiber, spandex fibre, polyamide fibre, natural fiber, quaternary ammonium salt and the tristearin of component amount
Acid;
Viscose rayon, polyester fiber, spandex fibre, polyamide fibre and natural fiber are dried, after drying 4h, stood
60min;
Viscose rayon, polyester fiber, spandex fibre, polyamide fibre and natural fiber after standing is added into mixing willow,
It works after 28min, quaternary ammonium salt and stearic acid is added, mix 2.2h;
It adds into porcupine opener, cleans, then shredding and mixing, mix 55min, obtain batch mixing;
Mixed batch mixing is added into lapper, spinning is carried out;
The line of hair is woven into fabric, is 58 DEG C of dry 17min in drying temperature;
47 DEG C of water are crossed, is taken out, is carried out shaping at a temperature of 72 DEG C, obtain clothing fabric.
Embodiment 3
High-elastic, anti-sweat composite material includes by quality component:
Preparation method is:
Weigh viscose rayon, polyester fiber, spandex fibre, polyamide fibre, silk, polyethylene glycol and the stearic acid of component amount;
Viscose rayon, polyester fiber, spandex fibre, polyamide fibre and silk are dried, after drying 3h, stand 70min;
Viscose rayon, polyester fiber, spandex fibre, polyamide fibre and silk after standing is added into mixing willow, is worked
After 20min, polyethylene glycol and stearic acid is added, mixes 2h;
It adds into porcupine opener, cleans, then shredding and mixing, mix 80min, obtain batch mixing;
Mixed batch mixing is added into lapper, spinning is carried out;
The line of hair is woven into fabric, is 60 DEG C of dry 15min in drying temperature;
50 DEG C of water are crossed, is taken out, is carried out shaping at a temperature of 70 DEG C, obtain clothing fabric.
Embodiment 4
High-elastic, anti-sweat composite material includes by quality component:
Preparation method is:
Weigh viscose rayon, polyester fiber, spandex fibre, polyamide fibre, silk and wool, quaternary ammonium salt and the tristearin of component amount
Acid;
Viscose rayon, polyester fiber, spandex fibre, polyamide fibre and silk and wool are dried, after drying 5h, stood
40min;
By after standing viscose rayon, polyester fiber, spandex fibre, polyamide fibre and silk and wool be added to mixing willow
In, after the 22min that works, quaternary ammonium salt and stearic acid is added, mixes 2.7h;
It adds into porcupine opener, cleans, then shredding and mixing, mix 75min, obtain batch mixing;
Mixed batch mixing is added into lapper, spinning is carried out;
The line of hair is woven into fabric, is 53 DEG C of dry 26min in drying temperature;
43 DEG C of water are crossed, is taken out, is carried out shaping at a temperature of 77 DEG C, obtain clothing fabric.
Embodiment 5
High-elastic, anti-sweat composite material includes by quality component:
Preparation method is:
Weigh viscose rayon, polyester fiber, spandex fibre, polyamide fibre, silk, sodium alkyl sulfonate and the organosilicon of component amount
Oil;
Viscose rayon, polyester fiber, spandex fibre, polyamide fibre and silk are dried, after drying 5h, stand 50min;
Viscose rayon, polyester fiber, spandex fibre, polyamide fibre and silk after standing is added into mixing willow, is worked
After 26min, sodium alkyl sulfonate and organic silicone oil is added, mixes 2.4h;
It adds into porcupine opener, cleans, then shredding and mixing, mix 70min, obtain batch mixing;
Mixed batch mixing is added into lapper, spinning is carried out;
The line of hair is woven into fabric, is 56 DEG C of dry 22min in drying temperature;
45 DEG C of water are crossed, is taken out, is carried out shaping at a temperature of 74 DEG C, obtain clothing fabric.
The composite material of embodiment 1 to 5, according to GB/T 5453-1997 (100Pa) standard testing permeability, according to
FZ/T50006-94 carries out testing elastic performance, and test result is as follows:
Air permenbility (mm/s) | Elongation (%) | Rebound degree (%) | |
Embodiment 1 | 6055.2 | 610.3 | 97.8 |
Embodiment 2 | 6142.5 | 604.8 | 98.4 |
Embodiment 3 | 5855.8 | 601.3 | 99.1 |
Embodiment 4 | 5985.8 | 598.3 | 98.9 |
Embodiment 5 | 62.34.5 | 62.6 | 99.2 |
By counting table above, it can be seen that the gas permeability of this composite material is average in 6000mm/s or more, and elongation can reach
To 600% or more, rebound degree can reach 98% or more.That is composite material Air permenbility is big, can wear and very relax to prevent sweat
It is suitable, and elongation is long, elasticity is good, this deformation ratio is small, and adaptive greatly improves.
The steps in the embodiment of the present invention can be sequentially adjusted, merged and deleted according to actual needs.
It is described in detail herein, applies specific case and the principle of the present invention and embodiment are explained
It states, above example is merely used to help understand the method and its core concept of the present invention;Meanwhile for the general skill of this field
Art personnel, according to the thought of the present invention, there will be changes in the specific implementation manner and application range, in conclusion this
Description should not be construed as limiting the invention.
Claims (8)
1. a kind of high-elastic, anti-sweat composite material, which is characterized in that the composite material includes by quality component:
2. composite material according to claim 1, which is characterized in that the component includes:
3. composite material according to claim 2, which is characterized in that the component includes:
4. according to any composite materials of claim 1-3, it is characterised in that:The natural fiber is cotton, wool, Huang
At least one of fiber crops and silk.
5. composite material according to claim 4, it is characterised in that:The natural fiber is the mixing of silk and wool,
Its mass ratio is 1:1.
6. according to any composite materials of claim 1-3, it is characterised in that:The antistatic agent be sodium alkyl sulfonate,
One kind in quaternary ammonium salt and polyethylene glycol.
7. composite material according to claim 6, it is characterised in that:The antistatic agent is sodium alkyl sulfonate.
8. according to any composite materials of claim 1-3, it is characterised in that:The lubricant is stearic acid or organic
Silicone oil.