CN108569866A - 一种由建筑垃圾构成的包芯土砌块及其制作方法 - Google Patents
一种由建筑垃圾构成的包芯土砌块及其制作方法 Download PDFInfo
- Publication number
- CN108569866A CN108569866A CN201810450883.4A CN201810450883A CN108569866A CN 108569866 A CN108569866 A CN 108569866A CN 201810450883 A CN201810450883 A CN 201810450883A CN 108569866 A CN108569866 A CN 108569866A
- Authority
- CN
- China
- Prior art keywords
- waste
- clay
- construction waste
- cored
- inorganic hard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种由建筑垃圾构成的包芯土砌块及其制作方法，本发明创新性地以黏土作为粘合剂把建筑垃圾制成的内芯包裹在传统土坯砌块之中，在现场制成各种特色建筑土砌块后可直接用于新建筑的隔墙或景观装饰，既传承了土坯砖的优良传统又可解决建筑垃圾排放问题。特别适用于建筑垃圾中黏土量大且难以回收利用的沿海地区，可实现建筑垃圾原地再生与变废为宝之目的，是建筑垃圾零排放、无污染、资源化、效益最大化的一种有效途径。
Description
技术领域
本发明属于建筑材料技术领域，具体涉及一种由建筑垃圾构成的包芯土砌块及其制作方法。
背景技术
建筑垃圾是建筑生命周期的一环，现今填埋处理、露天堆放、少量回收的方式引发了围城之患；占用土地、污染环境令市容不堪其忧。近年来，我国开始重视建筑垃圾减量化和资源化处理问题，但仍处于简单的回填处理以及将少部分硬质垃圾破碎后作为骨料回收使用的初级阶段，存在回收利用率很低、成本较高、需要转运到异地处理等各种问题。
针对此类现象，尤其是东南沿海地区建筑垃圾中黏土量大且难以回收利用的难题，本发明借鉴传统夯土技术与工艺，将废弃建筑垃圾简单分类后全部就地加工处理，制作成绿色环保土砌块，可全部回收利用于新建筑的建造当中，争取实现零排放。
发明内容
本发明的目的是针对沿海地区建筑垃圾中黏土量大且难以回收利用的特点，提供一种由建筑垃圾构成的包芯土砌块及其制作方法。
为实现上述目的，本发明采用如下技术方案：
本发明创新性地以黏土作为粘合剂把建筑垃圾制成的内芯包裹在传统土坯砌块之中，在现场制成各种特色建筑土砌块后可直接用于新建筑的隔墙或景观装饰，既传承了土坯砖的优良传统又可解决建筑垃圾排放问题。
所述由建筑垃圾构成的包芯土砌块，其包芯土砌块具体为传统土坯砌块包裹自制内芯；所述自制内芯组成包括黏土、无机类硬质垃圾颗粒和有机类杂质纤维。
进一步的，所述黏土包含建筑垃圾中的各种地表泥土与地底深层粘土；所述无机类硬质垃圾颗粒为建筑垃圾中的水泥砂浆、混凝土、石材、砖瓦、陶瓷、玻璃中的一种或几种破碎后制得；所述有机类杂质纤维由建筑垃圾中的竹、木、纸、草梗、布料、塑料中的一种或几种加工后制成。
进一步的，所述无机类硬质垃圾颗粒尺寸控制在30mm以下，所述有机类杂质纤维的长度方向控制在10mm以下、宽度方向（或直径）控制在2mm以内。
进一步的，混制土砌块包容性强，其中黏土、无机类硬质垃圾颗粒和有机类杂质纤维按质量百分数计为黏土30-50%，无机类硬质垃圾颗20-50%，有机类软质纤维0-10%。
所述由建筑垃圾构成的包芯土砌块的制作方法，包括以下步骤：
（1）先将建筑垃圾按照黏土、无机硬质垃圾颗粒、有机软质垃圾进行简单分类；
（2）将无机类硬质垃圾破碎成不大于30mm的硬质垃圾颗粒；
（3）将有机类软质材料，加工制成长度方向控制在10mm以下、宽度方向（或直径）控制在2mm以内的软质纤维；
（4）按照上述黏土、无机硬质垃圾颗粒、有机软质垃圾按配比混合均匀，并根据夯土工艺的技术要求添加相当于混合土料质量15-25wt%的水后，搅匀制成“手捏成团、落地开花”的混合土料；按夯土工艺要求另将黄土单独配制成可夯土料。
（5）在木制模框底部与四周先用黄土夯制一层20mm厚的黄土饰面层，再将混合土料放入模具中间夯实，顶层再用20mm的黄土层夯实，经脱模、修整、固化定型后即制作完成。
进一步的，可添加适量水泥适当提高土砌块的强度和耐水性。
与现有技术相比，本发明具有以下有益效果：结构简单，包容性强，成本低廉、环境友好，可以实现建筑垃圾零排放。
附图说明
图1为一种由建筑垃圾构成的包芯土砌块结构示意图。图中：1-土坯表层；2-垃圾颗粒内芯；3-硬质垃圾颗粒；4-软质垃圾纤维；5-黏土。
具体实施方式
下面结合附图和具体实施方式对本发明进一步说明。
实施例1
一种由建筑垃圾构成的包芯土砌块，包括建筑垃圾中的黏土、硬质颗粒和软质纤维。
所述黏土是福州市内建筑地面以下10米深处的灰色沉积粘土，所述硬质垃圾颗粒由当地建筑垃圾中的水泥砂浆、混凝土、石材、砖瓦、陶瓷、玻璃硬质材料破碎后制得，最大颗粒不超过30mm；所述有机类软质纤维由建筑垃圾中的木模板、编织袋加工后制成，长度方向控制在10mm以下、宽度方向（或直径）控制在2mm以内。
包芯土砌块在本实施例中，土砌块内芯的的内芯配料比例（按质量百分数计）为：水泥15%，粘土32%，硬质垃圾颗粒50%，软质纤维质3 %。
其中包芯土砌块的表层用传统的黄土为原料。
包芯土砌块的外形尺寸为200mm×200mm×300mm，表面黄土层的厚度在20mm。
一种由建筑垃圾构成的包芯土砌块的制作方法，包括以下步骤：
（1）先将建筑垃圾按照黏土、无机硬质垃圾、有机软质垃圾进行简单分类；
（2）将水泥及其它无机硬质垃圾破碎成不大于30mm的硬质垃圾颗粒；
（3）将建筑垃圾中的木模板、编织袋等各种有机类软质材料，加工制成长度方向控制在10mm以下、宽度方向（或直径）控制在2mm以内的软质纤维；
（4）按照上述水泥15wt%、粘土32wt%、硬质垃圾颗粒50wt%、软质纤维质3 wt%的配比混合均匀，并根据夯土工艺的技术要求相当于混合土料质量15wt%的水后搅匀制成“手捏成团、落地开花”的混合土料；按夯土工艺要求另将黄土单独配制成可夯土料。
（5）在木制模框底部与四周先用黄土夯制一层20mm厚的黄土饰面层，再将混合土料放入模具中间夯实，顶层再用20mm的黄土层夯实，经脱模、修整、固化定型后即制作完成。
测得土砌块密度1.72kg/cm3；抗压强度2.78Mpa。
实施例2
在本实施例中土砌块内芯的配料比例为（质量百分数）：水泥5%，黏土45%，硬质垃圾颗粒46%，杂质纤维质4%。其余与实施例1相同。
测得土砌块密度1.62kg/cm3；抗压强度2.53Mpa。
实施例3
在本实施例中土砌块的内芯配料比例为（质量百分数）：黏土50%，硬质垃圾颗粒45%，杂质纤维质5%。其余与实施例1相同。
测得土砌块密度1.60kg/cm3；抗压强度2.1Mpa。
上列较佳实施例，对本发明专利的目的、技术方案和优点进行了进一步详细说明，所应理解的是，以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明专利的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (5)
1.一种由建筑垃圾构成的包芯土砌块，其特征在于：所述包芯土砌块为传统土坯砌块包裹自制内芯；所述自制内芯组成包括黏土、无机类硬质垃圾颗粒和有机类杂质纤维。
2.根据权利要求1所述的一种由建筑垃圾构成的包芯土砌块，其特征在于：其中黏土、无机类硬质垃圾颗粒和有机类杂质纤维按质量百分数计为：黏土30-50%，无机类硬质垃圾颗20-50%，有机类软质纤维0-10%。
3.根据权利要求1所述的一种由建筑垃圾构成的包芯土砌块，其特征在于：所述黏土包括建筑垃圾中的各种地表泥土与地底深层粘土；所述无机类硬质垃圾颗粒为建筑垃圾中的水泥砂浆、混凝土、石材、砖瓦、陶瓷、玻璃中的一种或几种破碎后制得；所述有机类杂质纤维为建筑垃圾中的竹、木、纸、草梗、布料、塑料中的一种或几种加工后制成。
4.根据权利要求1所述的一种由建筑垃圾构成的包芯土砌块,其特征在于：所述无机类硬质垃圾颗粒尺寸控制在30mm以下；所述有机类杂质纤维的长度方向控制在10mm以下、宽度方向或直径控制在2mm以内。
5.一种制作如权利要求1所述的一种由建筑垃圾构成的包芯土砌块的方法，其特征在于：包括以下步骤：
（1）先将建筑垃圾按照黏土、无机类硬质垃圾颗粒、有机类杂质纤维进行简单分类；
（2）将无机类硬质垃圾破碎成不大于30mm的硬质垃圾颗粒；
（3）将有机类杂质纤维，加工制成长度方向控制在10mm以下、宽度方向或直径控制在2mm以内的软质纤维；
（4）按照上述黏土、无机类硬质垃圾颗粒、有机类杂质纤维按配比混合均匀，并根据夯土工艺的技术要求添加相当于混合土料质量15-25wt%的水，搅匀制成“手捏成团、落地开花”的混合土料；按夯土工艺要求另将黄土单独配制成可夯土料；
（5）在木制模框底部与四周先用黄土夯制一层20mm厚的黄土饰面层，再将混合土料放入模具中间夯实，顶层再用20mm的黄土层夯实，经脱模、修整、固化定型后即制作完成。