CN108559198A - A kind of polyvinyl chloride heat proof cable material and preparation method thereof - Google Patents
A kind of polyvinyl chloride heat proof cable material and preparation method thereof Download PDFInfo
- Publication number
- CN108559198A CN108559198A CN201711447823.9A CN201711447823A CN108559198A CN 108559198 A CN108559198 A CN 108559198A CN 201711447823 A CN201711447823 A CN 201711447823A CN 108559198 A CN108559198 A CN 108559198A
- Authority
- CN
- China
- Prior art keywords
- totm
- bisphenol
- corvic
- polyvinyl chloride
- heat proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of polyvinyl chloride heat proof cable material of the present invention and preparation method thereof, is grouped as by the group of following parts by weight：Corvic 80 110；Trioctyl trimellitate (TOTM) 30 40；Lead stearate 0.7 1.2；Bisphenol-A 0.2 0.8；Calcinated argil 27.The present invention have the characteristics that it is wear-resisting, be not easy to flatten, good insulation preformance.The present invention is heat-resist, non-aging, fall off, and avoids the generation of fire, meanwhile, it has been also convenient for the normal operation that outdoor construction is laid with cable.
Description
Technical field
The invention belongs to technical field of polymer materials, and in particular to a kind of polyvinyl chloride heat proof cable material and its preparation side
Method.
Background technology
Wire cable insulating and sheath are commonly called as CABLE MATERIALS with plastics, and which includes a variety of product such as rubber, plastics, nylon
Kind.CABLE MATERIALS manufacturing enterprise is with cable manufacturing enterprise for user, there is the market of CABLE MATERIALS as long as live wire cabling requirements.Electricity
In line cable product insulating layer mouth is almost required in addition to the bare wires product such as steel-cored aluminium strand, electromagnetic wire.But due to China
Edge is vast, and the north and south temperature difference is big, if cable poor heat resistance, is easy for aging, falls off, and not only causes the difficulty of repair in this way, disappears
More resources are consumed, can also cause cable work abnormal, easily cause fire, meanwhile, if easy to aging also bring shadow to construction operation
It rings, is unfavorable for the improvement of people's living standards.
Invention content
The purpose of the present invention is overcoming the deficiencies of existing technologies, provide it is a kind of it is wear-resisting, be not easy to flatten, good insulation preformance it is poly-
Vinyl chloride heat proof cable material and preparation method thereof.
For this purpose, the present invention provides a kind of polyvinyl chloride heat proof cable material, its main feature is that, it is grouped by the group of following parts by weight
At：Corvic 80-110；Trioctyl trimellitate (TOTM) 30-40；Lead stearate 0.7-1.2；Bisphenol-A 0.2-0.8；It forges
Burn clay 2-7；Preparation method includes the following steps：
（1）Prepare slurry：Trioctyl trimellitate (TOTM), lead stearate, bisphenol-A and calcinated argil are mixed into slurry, slurry is made；
（2）Slurry obtained by step is mediated with Corvic, is refined through open type plastic purificating set, enters pelleter afterwards into granulating
Material, you can be made.
Preferably, being grouped as by the group of following parts by weight：Corvic 80；Trioctyl trimellitate (TOTM) 30；Firmly
Resin acid lead 0.7；Bisphenol-A 0.2；Calcinated argil 2.
Preferably, being grouped as by the group of following parts by weight：Corvic 110；Trioctyl trimellitate (TOTM) 40；Firmly
Resin acid lead 1.2；Bisphenol-A 0.8；Calcinated argil 7.
Preferably, being grouped as by the group of following parts by weight：Corvic 100；Trioctyl trimellitate (TOTM) 38；Firmly
Resin acid lead 1.1；Bisphenol-A 0.6；Calcinated argil 6.
Beneficial effects of the present invention：The present invention have the characteristics that it is wear-resisting, be not easy to flatten, good insulation preformance.The present invention is heat-resisting
Property it is good, it is non-aging, fall off, avoid the generation of fire, meanwhile, be also convenient for the normal operation that outdoor construction is laid with cable.
Specific implementation mode
With reference to embodiment, the present invention is furture elucidated.
Embodiment 1：
A kind of polyvinyl chloride heat proof cable material is present embodiments provided, is grouped as by the group of following parts by weight：Corvic
80-110；Trioctyl trimellitate (TOTM) 30-40；Lead stearate 0.7-1.2；Bisphenol-A 0.2-0.8；Calcinated argil 2-7；It is made
Preparation Method includes the following steps：
（1）Prepare slurry：Trioctyl trimellitate (TOTM), lead stearate, bisphenol-A and calcinated argil are mixed into slurry, slurry is made；
（2）Slurry obtained by step is mediated with Corvic, is refined through open type plastic purificating set, enters pelleter afterwards into granulating
Material, you can be made.
The trioctyl trimellitate (TOTM) can be used as plasticizer；Lead stearate can be used as stabilizer so that product has good
Lubricity；Add bisphenol-A, it is ensured that CABLE MATERIALS inner core-body is not easy to be corroded.
Embodiment 2：
A kind of polyvinyl chloride heat proof cable material is present embodiments provided, is grouped as by the group of following parts by weight：Corvic
80；Trioctyl trimellitate (TOTM) 30；Lead stearate 0.7；Bisphenol-A 0.2；Calcinated argil 2；Preparation method, including walk as follows
Suddenly：
（1）Prepare slurry：Trioctyl trimellitate (TOTM), lead stearate, bisphenol-A and calcinated argil are mixed into slurry, slurry is made；
（2）Slurry obtained by step is mediated with Corvic, is refined through open type plastic purificating set, enters pelleter afterwards into granulating
Material, you can be made.
Embodiment 3：
A kind of polyvinyl chloride heat proof cable material is present embodiments provided, is grouped as by the group of following parts by weight：Corvic
110；Trioctyl trimellitate (TOTM) 40；Lead stearate 1.2；Bisphenol-A 0.8；Calcinated argil 7；Preparation method, including walk as follows
Suddenly：
（1）Prepare slurry：Trioctyl trimellitate (TOTM), lead stearate, bisphenol-A and calcinated argil are mixed into slurry, slurry is made；
（2）Slurry obtained by step is mediated with Corvic, is refined through open type plastic purificating set, enters pelleter afterwards into granulating
Material, you can be made.
Embodiment 4：
A kind of polyvinyl chloride heat proof cable material is present embodiments provided, is grouped as by the group of following parts by weight：Corvic
100；Trioctyl trimellitate (TOTM) 38；Lead stearate 1.1；Bisphenol-A 0.6；Calcinated argil 6；Preparation method, including walk as follows
Suddenly：
（1）Prepare slurry：Trioctyl trimellitate (TOTM), lead stearate, bisphenol-A and calcinated argil are mixed into slurry, slurry is made；
（2）Slurry obtained by step is mediated with Corvic, is refined through open type plastic purificating set, enters pelleter afterwards into granulating
Material, you can be made.
The foregoing examples are only illustrative of the present invention, does not constitute the limitation to protection scope of the present invention, all
Be with the present invention it is same or analogous design all belong to the scope of protection of the present invention within.
Claims (4)
1. a kind of polyvinyl chloride heat proof cable material, which is characterized in that be grouped as by the group of following parts by weight：
Corvic 80-110；Trioctyl trimellitate (TOTM) 30-40；Lead stearate 0.7-1.2；Bisphenol-A 0.2-0.8；
Calcinated argil 2-7；
Preparation method includes the following steps：
（1）Prepare slurry：Trioctyl trimellitate (TOTM), lead stearate, bisphenol-A and calcinated argil are mixed into slurry, slurry is made；
（2）Slurry obtained by step is mediated with Corvic, is refined through open type plastic purificating set, enters pelleter afterwards into granulating
Material, you can be made.
2. a kind of polyvinyl chloride heat proof cable material as described in claim 1, which is characterized in that be grouped by the group of following parts by weight
At：Corvic 80；Trioctyl trimellitate (TOTM) 30；Lead stearate 0.7；Bisphenol-A 0.2；Calcinated argil 2.
3. a kind of polyvinyl chloride heat proof cable material as described in claim 1, which is characterized in that be grouped by the group of following parts by weight
At：Corvic 110；Trioctyl trimellitate (TOTM) 40；Lead stearate 1.2；Bisphenol-A 0.8；Calcinated argil 7.
4. a kind of polyvinyl chloride heat proof cable material as described in claim 1, which is characterized in that be grouped by the group of following parts by weight
At：Corvic 100；Trioctyl trimellitate (TOTM) 38；Lead stearate 1.1；Bisphenol-A 0.6；Calcinated argil 6.