CN108546399A - A kind of noctilucence mouse case material and preparation method thereof - Google Patents
A kind of noctilucence mouse case material and preparation method thereof Download PDFInfo
- Publication number
- CN108546399A CN108546399A CN201810382338.6A CN201810382338A CN108546399A CN 108546399 A CN108546399 A CN 108546399A CN 201810382338 A CN201810382338 A CN 201810382338A CN 108546399 A CN108546399 A CN 108546399A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- noctilucence
- mouse case
- tossa
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of noctilucence mouse case materials and preparation method thereof, are related to mouse Material Field, include the raw material of following parts by weight meter:1.5 2.5 parts of 30 40 parts of makrolon, 20 30 parts of fluorine silicone rubber, 8 15 parts of polycaprolactone, 36 parts of tributyl citrate, 5 10 parts of tossa, 5 10 parts of diatomite, 48 parts of glass fibre, 5 10 parts of profound spar powder, 48 parts of luminescent powder, 36 parts of nanometer silicon carbide, 24 parts of β phenylacrylic acids methyl esters, 24 parts of tea seed cake powder, 36 parts of silicone oil, 1.2 2.4 parts of silane coupling agent, 1.2 1.8 parts of antiseptic and antioxidant;Mouse quality of materials of the present invention is light, intensity is high, excellent anti-corrosion performance, has self light emission function, the position of mouse can be clearly distinguished in dark, facility is brought to people and life.
Description
Technical field
The present invention relates to mouse Material Fields, and in particular to a kind of Luminous casing mouse material and preparation method thereof
Background technology
Mouse is a kind of very common and common computer input apparatus, it can carry out quota to the vernier on current screen
Day, and operated by the screen elements that button and roller devices pass through vernier.Most of mouse material is No. seven modelings
Expect that polycarbonate resin is a kind of thermoplastic engineering plastic of function admirable, there is excellent impact resistance, heat-resisting and cold resistance,
Creep resistant and dimensional stability, and be the material uniquely in five large-engineering plastics with good transparency, due to poly- carbonic acid
Particularity on ester structure has become the general engineering plastic that growth rate is most fast in five large-engineering plastics.
In recent years, occurring many Noctilucent plastic products in succession, such as luminous switch, luminous plastics measurer, luminous plastics
Optical fiber, luminous plastics toy, luminous plastics ornament materials etc..Luminous plastics natural light or energy after the irradiation of other artificial light sources
Enough energy of storage light irradiation, then slowly discharge the energy of storage in the form of visible light again in the dark.Noctilucence at present
The adusk illumination indicative function of plastics has brought great convenience, while also having the work of energy saving beautification life
With.But the field of mouse that Noctilucent material is applied in the prior art is seldom, is the project that current mouse Material Field can be studied
One of.
Invention content
For problems of the prior art, the present invention provides a kind of Luminous casing mouse material and its preparation sides
Method, mouse quality of materials of the present invention is light, intensity is high, excellent anti-corrosion performance, has self light emission function, can be clearly in dark
The position for distinguishing mouse brings facility to people and life.
In order to achieve the above object, the present invention is achieved through the following technical solutions:
A kind of Luminous casing mouse material includes the raw material of following parts by weight meter:
30-40 parts of makrolon, 20-30 parts of fluorine silicone rubber, 8-15 parts of polycaprolactone, 3-6 parts of tributyl citrate, jute
5-10 parts of fiber, 5-10 parts of diatomite, 4-8 parts of glass fibre, 5-10 parts of profound spar powder, 4-8 parts of luminescent powder, nanometer silicon carbide 3-
6 parts, 2-4 parts of beta-phenyl methyl acrylate, 2-4 parts of tea seed cake powder, 3-6 parts of silicone oil, 1.2-2.4 parts of silane coupling agent, antiseptic
1.2-1.8 1.5-2.5 parts of part and antioxidant.
Preferably, include the raw material of following parts by weight meter:33-37 parts of makrolon, gathers in oneself 24-26 parts of fluorine silicone rubber
10-13 parts of fat, 4-5 parts of tributyl citrate, 7-9 parts of tossa, 7-9 parts of diatomite, 5-7 parts of glass fibre, profound spar powder
7-9 parts, 5-7 parts of luminescent powder, 4-5 parts of nanometer silicon carbide, 2.5-3.5 parts of beta-phenyl methyl acrylate, 2.5-3.5 parts of tea seed cake powder,
1.8-2.2 parts of 4-5 parts of silicone oil, 1.8-2.1 parts of silane coupling agent, 1.4-1.6 parts of antiseptic and antioxidant.
Preferably, include the raw material of following parts by weight meter:35 parts of makrolon, 25 parts of fluorine silicone rubber, 12 parts of polycaprolactone,
4.5 parts of tributyl citrate, 8 parts of diatomite, 6 parts of glass fibre, 8 parts of profound spar powder, 6 parts of luminescent powder, is received 8 parts of tossa
4.5 parts of silicon carbide of rice, 3 parts of beta-phenyl methyl acrylate, 3 parts of tea seed cake powder, 4.5 parts of silicone oil, 2.0 parts of silane coupling agent, antiseptic
1.5 parts and 2.1 parts of antioxidant.
Preferably, the luminescent powder is alkali earth metal aluminate or manosil AS strontium.
Preferably, the silane coupling agent is gamma-aminopropyl-triethoxy-silane, γ-glycidyl ether oxygen propyl front three
Oxysilane, N- (β-aminoethyl)-γ-aminopropyltrimethoxysilanes and N- (β-aminoethyl)-gamma-aminopropyl-triethoxy silicon
One or more of alkane combines.
Preferably, the antiseptic is zinc oxide, ammonium dihydrogen phosphate and lithium carbonate according to mass ratio 1:2:2 mixing compositions.
Preferably, the antioxidant is N, N- diphenyl-para-phenylene diamines, N, bis- (2, the 4- diaminodiphenyl ether) imines of N-
It is combined with one or more of bis- (2,4- diiminos diphenyl ether) imines of N-.
A kind of preparation method of above-mentioned noctilucence mouse case material is also disclosed in the present invention, specifically, including following step
Suddenly:
(1) each raw material is weighed according to the raw material weight number of noctilucence mouse case material;
(2) tossa is put into sodium hydroxide solution, after impregnating 10-15 hours, after being rinsed well repeatedly with clear water,
It is placed in 80-90 degrees Celsius of vacuum drying oven dry ester moisture and is less than 1%, be placed in pulverizer and crush, mistake
200-500 mesh sieves, and obtains tossa powder;
(3) diatomite, glass fibre, profound spar powder, luminescent powder, nanometer silicon carbide are respectively put into vacuum drying oven,
It is dried in the environment of 100-120 degrees Celsius after being less than 1% to moisture, it is uniform to be put into stirrer for mixing, obtains mixed material
1;
(4) tossa powder and mixed material 1 are added in high-speed mixer, temperature control is to 60-70 degrees Celsius, 3-5 points
Silane coupling agent is added in Zhong Hou, and makrolon, fluorine silicone rubber, polycaprolactone, citric acid is added after 5-10 minutes in mixed at high speed
Tributyl, beta-phenyl methyl acrylate, tea seed cake powder, silicone oil, antiseptic and antioxidant, mixed at high speed obtain mixed after 10-20 minutes
Close material 2;
(5) mixed material 2 is put into double screw extruder and carries out extruding pelletization, 180-190 degrees Celsius of extrusion temperature, spiral shell
80-100 revs/min of bar rotating speed, pellet are cooled to room temperature to get the noctilucence mouse case material.
The present invention has following advantageous effect:
(1) mouse quality of materials of the present invention is light, intensity is high, excellent anti-corrosion performance, has self light emission function, can in dark
Clearly to distinguish the position of mouse, facility is brought to people and life.
(2) present invention is using makrolon, fluorine silicone rubber and three kinds of polymer of polycaprolactone are co-melting prepares material, fluorine silicon rubber
Glue can make up the shortcomings that makrolon is intolerant to highly basic strong acid, the performance of polycarbafil, and polycaprolactone has good life
Object compatibility and good biological degradability, can promote the compatibility between polymer and amalgamation, be material character and knot
Structure is more stablized.
(3) profound spar powder is added in raw material of the present invention, profound spar powder is a kind of mineral drug gypsum crystal, containing abundant
Medical substance, be added in material, can be with antibacterial, the bactericidal property of reinforcing material, be beneficial to man health.
(4) tributyl citrate is added in raw material of the present invention, it is heat-resisting fast light water-fast, have with resin good compatible
Property, to be plasticized the preferable plasticizer of efficiency;Antibacterium of also having does not grow bacterium, nonirritant, anti-flammability and degradability again.
(5) it is added with beta-phenyl methyl acrylate and tea seed cake powder in raw material of the present invention, has the function of essence, material can be made
Material releases faint scent.
Specific implementation mode
The specific implementation mode of the present invention is further described with reference to embodiment, following embodiment is only used for more
Technical scheme of the present invention is clearly demonstrated, and not intended to limit the protection scope of the present invention.
Embodiment 1
A kind of Luminous casing mouse material includes the raw material of following parts by weight meter:
30 parts of makrolon, 20 parts of fluorine silicone rubber, 8 parts of polycaprolactone, 3 parts of tributyl citrate, 5 parts of tossa, silicon
5 parts of diatomaceous earth, 4 parts of glass fibre, 5 parts of profound spar powder, 4 parts of luminescent powder, 3 parts of nanometer silicon carbide, 2 parts of beta-phenyl methyl acrylate,
1.5 parts of 2 parts of tea seed cake powder, 3 parts of silicone oil, 1.2 parts of silane coupling agent, 1.2 parts of antiseptic and antioxidant.
Luminescent powder is alkali earth metal aluminate.
Silane coupling agent is gamma-aminopropyl-triethoxy-silane.
Antiseptic is zinc oxide, ammonium dihydrogen phosphate and lithium carbonate according to mass ratio 1:2:2 mixing compositions.
Antioxidant is N, N- diphenyl-para-phenylene diamines.
A kind of preparation method of above-mentioned noctilucence mouse case material is also disclosed in the present embodiment, specifically, including it is following
Step:
(1) each raw material is weighed according to the raw material weight number of noctilucence mouse case material;
(2) tossa is put into sodium hydroxide solution, after impregnating 10 hours, after being rinsed well repeatedly with clear water, is set
Dry ester moisture is less than 1% in 80 degrees Celsius of vacuum drying oven, is placed in pulverizer and crushes, and crosses 200 mesh sieve,
Obtain tossa powder;
(3) diatomite, glass fibre, profound spar powder, luminescent powder, nanometer silicon carbide are respectively put into vacuum drying oven,
It is dried in the environment of 100 degrees Celsius after being less than 1% to moisture, it is uniform to be put into stirrer for mixing, obtains mixed material 1;
(4) tossa powder and mixed material 1 are added in high-speed mixer, temperature control to after 60 degrees Celsius, 3 minutes,
Silane coupling agent is added, after five minutes, makrolon, fluorine silicone rubber, polycaprolactone, tributyl citrate, β-is added in mixed at high speed
Phenylacrylic acid methyl esters, tea seed cake powder, silicone oil, antiseptic and antioxidant, mixed at high speed after ten minutes, obtain mixed material 2;
(5) mixed material 2 is put into double screw extruder and carries out extruding pelletization, 180 degrees Celsius of extrusion temperature, screw rod turns
80 revs/min of speed, pellet is cooled to room temperature to get the noctilucence mouse case material.
Embodiment 2
A kind of Luminous casing mouse material includes the raw material of following parts by weight meter:
40 parts of makrolon, 30 parts of fluorine silicone rubber, 15 parts of polycaprolactone, 6 parts of tributyl citrate, 10 parts of tossa,
10 parts of diatomite, 8 parts of glass fibre, 10 parts of profound spar powder, 8 parts of luminescent powder, 6 parts of nanometer silicon carbide, beta-phenyl methyl acrylate 4
Part, 4 parts of tea seed cake powder, 6 parts of silicone oil, 2.4 parts of silane coupling agent, 1.8 parts of antiseptic and 2.5 parts of antioxidant.
Luminescent powder is manosil AS strontium.
Silane coupling agent is γ-glycidyl ether oxygen propyl trimethoxy silicane.
Antiseptic is zinc oxide, ammonium dihydrogen phosphate and lithium carbonate according to mass ratio 1:2:2 mixing compositions.
Antioxidant is N, bis- (2,4- diaminodiphenyl ethers) imines of N-.
A kind of preparation method of above-mentioned noctilucence mouse case material is also disclosed in the present embodiment, specifically, including it is following
Step:
(1) each raw material is weighed according to the raw material weight number of noctilucence mouse case material;
(2) tossa is put into sodium hydroxide solution, after impregnating 15 hours, after being rinsed well repeatedly with clear water, is set
Dry ester moisture is less than 1% in 90 degrees Celsius of vacuum drying oven, is placed in pulverizer and crushes, and crosses 500 mesh sieve,
Obtain tossa powder;
(3) diatomite, glass fibre, profound spar powder, luminescent powder, nanometer silicon carbide are respectively put into vacuum drying oven,
It is dried in the environment of 120 degrees Celsius after being less than 1% to moisture, it is uniform to be put into stirrer for mixing, obtains mixed material 1;
(4) tossa powder and mixed material 1 being added in high-speed mixer, temperature control is to 70 degrees Celsius, after five minutes,
Be added silane coupling agent, mixed at high speed after ten minutes, be added makrolon, fluorine silicone rubber, polycaprolactone, tributyl citrate,
Beta-phenyl methyl acrylate, tea seed cake powder, silicone oil, antiseptic and antioxidant, mixed at high speed after twenty minutes, obtain mixed material 2;
(5) mixed material 2 is put into double screw extruder and carries out extruding pelletization, 190 degrees Celsius of extrusion temperature, screw rod turns
100 revs/min of speed, pellet is cooled to room temperature to get the noctilucence mouse case material.
Embodiment 3
A kind of Luminous casing mouse material includes the raw material of following parts by weight meter:
33 parts of makrolon, 24 parts of fluorine silicone rubber, 10 parts of polycaprolactone, 4 parts of tributyl citrate, 7 parts of tossa, silicon
7 parts of diatomaceous earth, 5 parts of glass fibre, 7 parts of profound spar powder, 5 parts of luminescent powder, 4 parts of nanometer silicon carbide, beta-phenyl methyl acrylate 2.5
Part, 2.5 parts of tea seed cake powder, 4 parts of silicone oil, 1.8 parts of silane coupling agent, 1.4 parts of antiseptic and 1.8 parts of antioxidant.
Luminescent powder is alkali earth metal aluminate.
Silane coupling agent is N- (β-aminoethyl)-γ-aminopropyltrimethoxysilane.
Antiseptic is zinc oxide, ammonium dihydrogen phosphate and lithium carbonate according to mass ratio 1:2:2 mixing compositions.
Antioxidant is bis- (the 2,4- diiminos diphenyl ether) imines of N-.
A kind of preparation method of above-mentioned noctilucence mouse case material is also disclosed in the present embodiment, specifically, including it is following
Step:
(1) each raw material is weighed according to the raw material weight number of noctilucence mouse case material;
(2) tossa is put into sodium hydroxide solution, after impregnating 12 hours, after being rinsed well repeatedly with clear water, is set
Dry ester moisture is less than 1% in 85 degrees Celsius of vacuum drying oven, is placed in pulverizer and crushes, and crosses 300 mesh sieve,
Obtain tossa powder;
(3) diatomite, glass fibre, profound spar powder, luminescent powder, nanometer silicon carbide are respectively put into vacuum drying oven,
It is dried in the environment of 108 degrees Celsius after being less than 1% to moisture, it is uniform to be put into stirrer for mixing, obtains mixed material 1;
(4) tossa powder and mixed material 1 are added in high-speed mixer, temperature control to after 65 degrees Celsius, 4 minutes,
Silane coupling agent is added, makrolon, fluorine silicone rubber, polycaprolactone, tributyl citrate, β-is added after 8 minutes in mixed at high speed
Phenylacrylic acid methyl esters, tea seed cake powder, silicone oil, antiseptic and antioxidant, mixed at high speed obtain mixed material 2 after 15 minutes;
(5) mixed material 2 is put into double screw extruder and carries out extruding pelletization, 185 degrees Celsius of extrusion temperature, screw rod turns
90 revs/min of speed, pellet is cooled to room temperature to get the noctilucence mouse case material.
Embodiment 4
A kind of Luminous casing mouse material includes the raw material of following parts by weight meter:
37 parts of makrolon, 26 parts of fluorine silicone rubber, 13 parts of polycaprolactone, 5 parts of tributyl citrate, 9 parts of tossa, silicon
9 parts of diatomaceous earth, 7 parts of glass fibre, 9 parts of profound spar powder, 7 parts of luminescent powder, 5 parts of nanometer silicon carbide, beta-phenyl methyl acrylate 3.5
Part, 3.5 parts of tea seed cake powder, 5 parts of silicone oil, 2.1 parts of silane coupling agent, 1.6 parts of antiseptic and 2.2 parts of antioxidant.
Luminescent powder is alkali earth metal aluminate.
Silane coupling agent is N- (β-aminoethyl)-gamma-aminopropyl-triethoxy-silane.
State antiseptic be zinc oxide, ammonium dihydrogen phosphate and lithium carbonate according to mass ratio 1:2:2 mixing compositions.
Antioxidant is bis- (the 2,4- diiminos diphenyl ether) imines of N-.
A kind of preparation method of above-mentioned noctilucence mouse case material is also disclosed in the present embodiment, specifically, including it is following
Step:
(1) each raw material is weighed according to the raw material weight number of noctilucence mouse case material;
(2) tossa is put into sodium hydroxide solution, after impregnating 14 hours, after being rinsed well repeatedly with clear water, is set
Dry ester moisture is less than 1% in 88 degrees Celsius of vacuum drying oven, is placed in pulverizer and crushes, and crosses 300 mesh sieve,
Obtain tossa powder;
(3) diatomite, glass fibre, profound spar powder, luminescent powder, nanometer silicon carbide are respectively put into vacuum drying oven,
It is dried in the environment of 115 degrees Celsius after being less than 1% to moisture, it is uniform to be put into stirrer for mixing, obtains mixed material 1;
(4) tossa powder and mixed material 1 being added in high-speed mixer, temperature control is to 68 degrees Celsius, after five minutes,
Silane coupling agent is added, makrolon, fluorine silicone rubber, polycaprolactone, tributyl citrate, β-is added after 8 minutes in mixed at high speed
Phenylacrylic acid methyl esters, tea seed cake powder, silicone oil, antiseptic and antioxidant, mixed at high speed obtain mixed material 2 after 17 minutes;
(5) mixed material 2 is put into double screw extruder and carries out extruding pelletization, 188 degrees Celsius of extrusion temperature, screw rod turns
95 revs/min of speed, pellet is cooled to room temperature to get the noctilucence mouse case material.
Embodiment 5
A kind of Luminous casing mouse material includes the raw material of following parts by weight meter:
35 parts of makrolon, 25 parts of fluorine silicone rubber, 12 parts of polycaprolactone, 4.5 parts of tributyl citrate, 8 parts of tossa,
8 parts of diatomite, 6 parts of glass fibre, 8 parts of profound spar powder, 6 parts of luminescent powder, 4.5 parts of nanometer silicon carbide, beta-phenyl methyl acrylate 3
Part, 3 parts of tea seed cake powder, 4.5 parts of silicone oil, 2.0 parts of silane coupling agent, 1.5 parts of antiseptic and 2.1 parts of antioxidant.
Luminescent powder is alkali earth metal aluminate.
Silane coupling agent is γ-glycidyl ether oxygen propyl trimethoxy silicane.
Antiseptic is zinc oxide, ammonium dihydrogen phosphate and lithium carbonate according to mass ratio 1:2:2 mixing compositions.
Antioxidant is N, and N- diphenyl-para-phenylene diamines and bis- (2,4- diaminodiphenyl ethers) imines of N, N- are according to mass ratio
1:1 mixing composition.
A kind of preparation method of above-mentioned noctilucence mouse case material is also disclosed in the present embodiment, specifically, including it is following
Step:
(1) each raw material is weighed according to the raw material weight number of noctilucence mouse case material;
(2) tossa is put into sodium hydroxide solution, after impregnating 13 hours, after being rinsed well repeatedly with clear water, is set
Dry ester moisture is less than 1% in 86 degrees Celsius of vacuum drying oven, is placed in pulverizer and crushes, and crosses 400 mesh sieve,
Obtain tossa powder;
(3) diatomite, glass fibre, profound spar powder, luminescent powder, nanometer silicon carbide are respectively put into vacuum drying oven,
It is dried in the environment of 110 degrees Celsius after being less than 1% to moisture, it is uniform to be put into stirrer for mixing, obtains mixed material 1;
(4) tossa powder and mixed material 1 are added in high-speed mixer, temperature control to after 68 degrees Celsius, 4 minutes,
Silane coupling agent is added, makrolon, fluorine silicone rubber, polycaprolactone, tributyl citrate, β-is added after 8 minutes in mixed at high speed
Phenylacrylic acid methyl esters, tea seed cake powder, silicone oil, antiseptic and antioxidant, mixed at high speed obtain mixed material 2 after 18 minutes;
(5) mixed material 2 is put into double screw extruder and carries out extruding pelletization, 185 degrees Celsius of extrusion temperature, screw rod turns
90 revs/min of speed, pellet is cooled to room temperature to get the noctilucence mouse case material.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although with reference to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution recorded in example is modified or equivalent replacement of some of the technical features.All essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.
Claims (8)
1. a kind of noctilucence mouse case material, which is characterized in that including following raw material by weight:Makrolon 30-40
Part, 20-30 parts of fluorine silicone rubber, 8-15 parts of polycaprolactone, 3-6 parts of tributyl citrate, 5-10 parts of tossa, diatomite 5-10
Part, 4-8 parts of glass fibre, 5-10 parts of profound spar powder, 4-8 parts of luminescent powder, 3-6 parts of nanometer silicon carbide, beta-phenyl methyl acrylate
2-4 parts, 2-4 parts of tea seed cake powder, 3-6 parts of silicone oil, 1.2-2.4 parts of silane coupling agent, 1.2-1.8 parts of antiseptic and antioxidant 1.5-
2.5 part.
2. noctilucence mouse case material according to claim 1, which is characterized in that include the raw material of following parts by weight meter:
33-37 parts of makrolon, 24-26 parts of fluorine silicone rubber, 10-13 parts of polycaprolactone, 4-5 parts of tributyl citrate, tossa 7-9
Part, 7-9 parts of diatomite, 5-7 parts of glass fibre, 7-9 parts of profound spar powder, 5-7 parts of luminescent powder, 4-5 parts of nanometer silicon carbide, beta-phenyl
2.5-3.5 parts of methyl acrylate, 2.5-3.5 parts of tea seed cake powder, 4-5 parts of silicone oil, 1.8-2.1 parts of silane coupling agent, antiseptic 1.4-
1.6 parts and 1.8-2.2 parts of antioxidant.
3. noctilucence mouse case material according to claim 1, which is characterized in that include the raw material of following parts by weight meter:
35 parts of makrolon, 25 parts of fluorine silicone rubber, 12 parts of polycaprolactone, 4.5 parts of tributyl citrate, 8 parts of tossa, diatomite 8
Part, 6 parts of glass fibre, 8 parts of profound spar powder, 6 parts of luminescent powder, 4.5 parts of nanometer silicon carbide, 3 parts of beta-phenyl methyl acrylate, tea seed cake
2.1 parts of 3 parts of powder, 4.5 parts of silicone oil, 2.0 parts of silane coupling agent, 1.5 parts of antiseptic and antioxidant.
4. noctilucence mouse case material according to claim 1, which is characterized in that the luminescent powder is alkaline-earth metal aluminic acid
Salt or manosil AS strontium.
5. noctilucence mouse case material according to claim 1, which is characterized in that the silane coupling agent is γ-ammonia third
Ethyl triethoxy silicane alkane, γ-glycidyl ether oxygen propyl trimethoxy silicane, N- (β-aminoethyl)-γ-aminopropyl trimethoxies
One or more of silane and N- (β-aminoethyl)-gamma-aminopropyl-triethoxy-silane combine.
6. noctilucence mouse case material according to claim 1, which is characterized in that the antiseptic is zinc oxide, phosphoric acid
Ammonium dihydrogen and lithium carbonate are according to mass ratio 1:2:2 mixing compositions.
7. noctilucence mouse case material according to claim 1, which is characterized in that the antioxidant is N, N- diphenyl
P-phenylenediamine, N, bis- (2,4- diaminodiphenyl ethers) imines of N- and one kind in bis- (the 2,4- diiminos diphenyl ether) imines of N- or
Several combinations.
8. a kind of preparation method of such as claim 1-7 any one of them noctilucence mouse case materials, which is characterized in that including
Following steps:
(1) each raw material is weighed according to the raw material weight number of noctilucence mouse case material;
(2) tossa is put into sodium hydroxide solution, after impregnating 10-15 hours, after being rinsed well repeatedly with clear water, is placed in
Dry ester moisture is less than 1% in 80-90 degrees Celsius of vacuum drying oven, is placed in pulverizer and crushes, crosses 200-500
Mesh sieves, and obtains tossa powder;
(3) diatomite, glass fibre, profound spar powder, luminescent powder, nanometer silicon carbide are respectively put into vacuum drying oven, in 100-
It is dried in the environment of 120 degrees Celsius after being less than 1% to moisture, it is uniform to be put into stirrer for mixing, obtains mixed material 1;
(4) tossa powder and mixed material 1 are added in high-speed mixer, temperature control to after 60-70 degrees Celsius, 3-5 minutes,
Silane coupling agent is added, makrolon, fluorine silicone rubber, polycaprolactone, three fourth of citric acid is added after 5-10 minutes in mixed at high speed
Ester, beta-phenyl methyl acrylate, tea seed cake powder, silicone oil, antiseptic and antioxidant, mixed at high speed obtain mixture after 10-20 minutes
Material 2;
(5) mixed material 2 is put into double screw extruder and carries out extruding pelletization, 180-190 degrees Celsius of extrusion temperature, screw rod turns
Fast 80-100 revs/min, pellet is cooled to room temperature to get the noctilucence mouse case material.