CN108545740A - A kind of preparation method of efficient water purification active carbon - Google Patents
A kind of preparation method of efficient water purification active carbon Download PDFInfo
- Publication number
- CN108545740A CN108545740A CN201810718241.8A CN201810718241A CN108545740A CN 108545740 A CN108545740 A CN 108545740A CN 201810718241 A CN201810718241 A CN 201810718241A CN 108545740 A CN108545740 A CN 108545740A
- Authority
- CN
- China
- Prior art keywords
- carbonized material
- water purification
- active carbon
- activator
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods of efficient water purification active carbon, are made of petroleum coke, feed coal, binder and activator, and the weight content of feed components is as follows:Petroleum coke 50 70%, feed coal 10 40%, binder 5 20%, activator 0.5 10%;Specific preparation process is as follows:(1)It weighs petroleum coke respectively in proportion and feed coal carries out break process and is uniformly mixed;(2)Binder compound stalk forming is proportionally added into briquetting material;(3)Retort charing process;(4)Carbonized material is crushed, with activator mixing;(5)Activation process;(6)It washs, be dried to obtain efficient water purification active carbon.Preparation method technological process provided by the invention is simple, and operating cost is low, and the activated carbon product prepared has many advantages, such as that high mechanical strength, absorption property are good, has preferable effects of purification quality.
Description
Technical field
The present invention relates to technical field of active carbon, and in particular to a kind of preparation method of efficient water purification active carbon.
Background technology
Activated carbon is due to the gap structure with huge specific surface area and prosperity, to dissolved organic matter in water
Such as phenolic compound has stronger adsorption capacity, is suitable for the purification of drinking water.The activated carbon production used currently on the market
There are two main classes for product, i.e., is made of column-shaped active carbon, or directly broken using raw coal, this two classes product is equal for purification of water quality
There are insoluble drawbacks, it is difficult to reach purpose of purifying the water quality.
In view of the above problems, proposing a kind of coal activated carbon and its manufacturing method in Chinese patent CN1194235.It should
Anthracite is broken into certain particle size particle, is added in activation furnace and passes through height by activated carbon in production without powder processed, molding procedure
Heated steam, which is activated, is made product.The raw coal of this method production is directly broken, and there are bulk densities for activated carbon gently, mechanical strength
Low disadvantage, it is difficult to play purpose of purifying the water quality.
And a kind of efficient water purification active carbon is proposed in Chinese patent CN201710466241.9, it is by following step
It is rapid to be made:It after stalk is dried, pulverizes and sieves to 10-60 mesh, is uniformly mixed;It tentatively carbonizes, makes in microwave cracking reacting furnace
Material must be pre-processed;Microwave power 1000-1500W, preliminary carbonization time are 3-15min;By pretreatment material in 15-35wt% hydrochloric acid
3-20h is impregnated in solution, then immersion-the 5h in 15-30wt% sodium hydroxide solutions again, washed repeatedly with deionized water until
Semi-finished product are made after dry in neutrality;Semi-finished product are placed in isothermal holding 0.5-2h in 380-420 DEG C of Muffle furnace, are down to room temperature
To obtain the final product.The invention reduces production cost to a certain extent by using stalk, but during straw charring surface energy to be formed
Mesoporous with preferable adsorption capacity and macropore cause its adsorption capacity to decline, it is difficult to play purpose of purifying the water quality.
Based on this, it is necessary to a kind of preparation method of efficient water purification active carbon is provided, to solve existing activated carbon water purification
Effect is undesirable, purifies halfway problem.
Invention content
The purpose of the present invention is to provide the preparation method methods of efficient water purification active carbon, are lived with solving existing efficient water purification
Property charcoal purifying water effect is undesirable, the halfway problem of purification.
In order to solve the above-mentioned technical problem, the present invention adopts the following technical scheme that:
A kind of preparation method of efficient water purification active carbon, is made of, and raw material is each petroleum coke, feed coal, binder and activator
The weight content of component is as follows:
Petroleum coke 50-70%;
Feed coal 10-40%;
Binder 5-20%;
Activator 0.5-10%;
Specific preparation process is as follows:
(1)It weighs petroleum coke respectively in proportion and feed coal carries out break process, screening obtains the petroleum coke that grain size is 3-5mm
Grain and raw material coal particle, and petroleum coke particles and raw material coal particle are uniformly mixed;
(2)It is proportionally added into binder to be stirred mixing, mediate, then briquetting material is obtained through cuber compound stalk forming;
(3)Briquetting material is put into retort, heating charing, obtains carbonized material under inert gas protection;
(4)Carbonized material is crushed, crosses 100-200 mesh sieve, and activator mixing is added;
(5)The carbonized material for being mixed with activator is put into activation furnace, and activation process is carried out under 2 atmosphere of high-purity N, is activated
Material;
(6)By step(5)In activated material cooling after through washing, being dried to obtain efficient water purification active carbon;
Wherein, the step(5)Activation process includes the following steps:
(1)Pre-activate:The carbonized material for being mixed with activator is put into activation furnace, in high-purity N2In atmosphere, with the liter of 10 DEG C/min
Warm rate is warming up to 350 DEG C, and constant temperature 1.5h obtains pre-activate carbonized material;
(2)Middle low-temperature activation:By step(1)Pre-activate carbonized material continue to heat up, be warming up to 600 DEG C with 15 DEG C/min, constant temperature
1.0h obtains middle low-temperature activation carbonized material;
(3)High-temperature activation:By step(2)Middle low-temperature activation carbonized material continues to heat up, and is warming up to 800 DEG C with 20 DEG C/min, constant temperature
0.5h is to get activated material
Preferably, ash content≤0.50% of the petroleum coke raw material, moisture≤5.0%, phosphorus content >=95%.
Preferably, it is 3 that the feed coal, which is weight ratio,:1 bituminous coal and the mixture of lignite.
Preferably, the binder is one or more of in selected from coal tar pitch and petroleum asphalt, cracking slurry oil.
Preferably, the activator is NaOH or KOH.
Preferably, the pressure of the compound stalk forming is 25-35MPa.
Preferably, the step(3)Middle inert gas is nitrogen or argon gas.
Preferably, the step(3)Carbonizing specific steps includes:
(1)Briquetting material is placed in retort, and carries out charing process under nitrogen or argon, first controlling heating rate is
8 DEG C/min, 300 DEG C are warming up to, 2h is kept to carry out pre- charing process early period, obtains pretreatment carbonized material;
(2)By step(1)Obtained pretreatment carbonized material, under nitrogen or argon, control heating rate are 15 DEG C/min,
550 DEG C of heating keeps 1.5h to carry out medium temperature charing process;
(3)By step(2)The carbonized material of medium temperature charing process, under nitrogen or argon, control heating rate be 25 DEG C/
Min is warming up to 750 DEG C, and 1h is kept to carry out high temperature carbonization processing;
(4)By step(3)The activated carbon for obtaining high temperature carbonization processing naturally cools to 250 DEG C, in the case of air circulation,
5h is kept to carry out airoxidation to get carbonized material.
Compared with prior art, the present invention has following advantageous effect:
(1)Preparation method technological process provided by the invention is simple, and operating cost is low, and the activated carbon product prepared has
The advantages that high mechanical strength, absorption property are good has preferable effects of purification quality.
(2)Charing process of the present invention includes:Early period pre- charing process, medium temperature charing process and high temperature carbonization processing, pass through
To the treatment by stages of carbonized material, overcomes microcrystalline carbon and mix crosslinking with the excessive of random carbon, reduce the graphitization of carbonized material
Degree increases the content of " active component " in inorganic mineral, convenient for the progress of subsequent activation reaction.
(3)Activation process of the present invention is carried out by segmented, is lived by pre-activate processing, middle low-temperature activation, high temperature
Change, be gradually expanded by intensive micropore enhances purification of water quality effect for mesoporous and macropore to improve the absorption property of activated carbon
Fruit.
Specific implementation mode
Present invention will be further explained below with reference to specific examples.These embodiments are merely to illustrate the present invention and do not have to
In limiting the scope of the invention.
Embodiment 1:
The preparation method of the efficient water purification active carbon of the present embodiment, is made of petroleum coke, feed coal, binder and activator, and
The weight content of feed components is as follows:
Petroleum coke 55%;
Feed coal 35%;
Binder 15%;
Activator 5%;
Specific preparation process is as follows:
(1)It weighs petroleum coke respectively in proportion and feed coal carries out break process, screening obtains the petroleum coke that grain size is 3-5mm
Grain and raw material coal particle, and petroleum coke particles and raw material coal particle are uniformly mixed;
(2)It is proportionally added into binder to be stirred mixing, mediate, then briquetting material is obtained through cuber compound stalk forming;
(3)Briquetting material is put into retort, heating charing, obtains carbonized material under inert gas protection;
(4)Carbonized material is crushed, crosses 100-200 mesh sieve, and activator mixing is added;
(5)The carbonized material for being mixed with activator is put into activation furnace, and activation process is carried out under 2 atmosphere of high-purity N, is activated
Material;
(6)By step(5)In activated material cooling after through washing, being dried to obtain efficient water purification active carbon.
Ash content≤0.50% of the petroleum coke raw material, moisture≤5.0%, phosphorus content >=95%.
The feed coal is that weight ratio is 3:1 bituminous coal and the mixture of lignite.
The binder is coal tar pitch.
The activator is NaOH.
The pressure of the compound stalk forming is 25MPa.
The step(3)Middle inert gas is nitrogen.
The step(3)Carbonizing specific steps includes:
(1)Briquetting material is placed in retort, and carries out charing process under nitrogen or argon, first controlling heating rate is
8 DEG C/min, 300 DEG C are warming up to, 2h is kept to carry out pre- charing process early period, obtains pretreatment carbonized material;
(2)By step(1)Obtained pretreatment carbonized material, under nitrogen or argon, control heating rate are 15 DEG C/min,
550 DEG C of heating keeps 1.5h to carry out medium temperature charing process;
(3)By step(2)The carbonized material of medium temperature charing process, under nitrogen or argon, control heating rate be 25 DEG C/
Min is warming up to 750 DEG C, and 1h is kept to carry out high temperature carbonization processing;
(4)By step(3)The activated carbon for obtaining high temperature carbonization processing naturally cools to 250 DEG C, in the case of air circulation,
5h is kept to carry out airoxidation to get carbonized material.
The step(5)Activation process includes the following steps:
(1)Pre-activate:The carbonized material for being mixed with activator is put into activation furnace, in high-purity N2In atmosphere, with the liter of 10 DEG C/min
Warm rate is warming up to 350 DEG C, and constant temperature 1.5h obtains pre-activate carbonized material;
(2)Middle low-temperature activation:By step(1)Pre-activate carbonized material continue to heat up, be warming up to 600 DEG C with 15 DEG C/min, constant temperature
1.0h obtains middle low-temperature activation carbonized material;
(3)High-temperature activation:By step(2)Middle low-temperature activation carbonized material continues to heat up, and is warming up to 800 DEG C with 20 DEG C/min, constant temperature
0.5h is to get activated material.
Embodiment 2:
The preparation method of the efficient water purification active carbon of the present embodiment, is made of petroleum coke, feed coal, binder and activator, and
The weight content of feed components is as follows:
Petroleum coke 60%;
Feed coal 25%;
Binder 10%;
Activator 5%;
Specific preparation process is as follows:
(1)It weighs petroleum coke respectively in proportion and feed coal carries out break process, screening obtains the petroleum coke that grain size is 3-5mm
Grain and raw material coal particle, and petroleum coke particles and raw material coal particle are uniformly mixed;
(2)It is proportionally added into binder to be stirred mixing, mediate, then briquetting material is obtained through cuber compound stalk forming;
(3)Briquetting material is put into retort, heating charing, obtains carbonized material under inert gas protection;
(4)Carbonized material is crushed, crosses 100-200 mesh sieve, and activator mixing is added;
(5)The carbonized material for being mixed with activator is put into activation furnace, and activation process is carried out under 2 atmosphere of high-purity N, is activated
Material;
(6)By step(5)In activated material cooling after through washing, being dried to obtain efficient water purification active carbon.
Ash content≤0.50% of the petroleum coke raw material, moisture≤5.0%, phosphorus content >=95%.
The feed coal is that weight ratio is 3:1 bituminous coal and the mixture of lignite.
The binder is asphalt.
The activator is KOH.
The pressure of the compound stalk forming is 35MPa.
The step(3)Middle inert gas is argon gas.
The step(3)Carbonizing specific steps includes:
(1)Briquetting material is placed in retort, and carries out charing process under nitrogen or argon, first controlling heating rate is
8 DEG C/min, 300 DEG C are warming up to, 2h is kept to carry out pre- charing process early period, obtains pretreatment carbonized material;
(2)By step(1)Obtained pretreatment carbonized material, under nitrogen or argon, control heating rate are 15 DEG C/min,
550 DEG C of heating keeps 1.5h to carry out medium temperature charing process;
(3)By step(2)The carbonized material of medium temperature charing process, under nitrogen or argon, control heating rate be 25 DEG C/
Min is warming up to 750 DEG C, and 1h is kept to carry out high temperature carbonization processing;
(4)By step(3)The activated carbon for obtaining high temperature carbonization processing naturally cools to 250 DEG C, in the case of air circulation,
5h is kept to carry out airoxidation to get carbonized material.
The step(5)Activation process includes the following steps:
(1)Pre-activate:The carbonized material for being mixed with activator is put into activation furnace, in high-purity N2In atmosphere, with the liter of 10 DEG C/min
Warm rate is warming up to 350 DEG C, and constant temperature 1.5h obtains pre-activate carbonized material;
(2)Middle low-temperature activation:By step(1)Pre-activate carbonized material continue to heat up, be warming up to 600 DEG C with 15 DEG C/min, constant temperature
1.0h obtains middle low-temperature activation carbonized material;
(3)High-temperature activation:By step(2)Middle low-temperature activation carbonized material continues to heat up, and is warming up to 800 DEG C with 20 DEG C/min, constant temperature
0.5h is to get activated material.
Embodiment 3:
The preparation method of the efficient water purification active carbon of the present embodiment, is made of petroleum coke, feed coal, binder and activator, and
The weight content of feed components is as follows:
Petroleum coke 60%;
Feed coal 28%;
Binder 8%;
Activator 4%;
Specific preparation process is as follows:
(1)It weighs petroleum coke respectively in proportion and feed coal carries out break process, screening obtains the petroleum coke that grain size is 3-5mm
Grain and raw material coal particle, and petroleum coke particles and raw material coal particle are uniformly mixed;
(2)It is proportionally added into binder to be stirred mixing, mediate, then briquetting material is obtained through cuber compound stalk forming;
(3)Briquetting material is put into retort, heating charing, obtains carbonized material under inert gas protection;
(4)Carbonized material is crushed, crosses 100-200 mesh sieve, and activator mixing is added;
(5)The carbonized material for being mixed with activator is put into activation furnace, and activation process is carried out under 2 atmosphere of high-purity N, is activated
Material;
(6)By step(5)In activated material cooling after through washing, being dried to obtain efficient water purification active carbon.
Ash content≤0.50% of the petroleum coke raw material, moisture≤5.0%, phosphorus content >=95%.
The feed coal is that weight ratio is 3:1 bituminous coal and the mixture of lignite.
The binder is asphalt.
The activator is KOH.
The pressure of the compound stalk forming is 30MPa.
The step(3)Middle inert gas is nitrogen or argon gas.
The step(3)Carbonizing specific steps includes:
(1)Briquetting material is placed in retort, and carries out charing process under nitrogen or argon, first controlling heating rate is
8 DEG C/min, 300 DEG C are warming up to, 2h is kept to carry out pre- charing process early period, obtains pretreatment carbonized material;
(2)By step(1)Obtained pretreatment carbonized material, under nitrogen or argon, control heating rate are 15 DEG C/min,
550 DEG C of heating keeps 1.5h to carry out medium temperature charing process;
(3)By step(2)The carbonized material of medium temperature charing process, under nitrogen or argon, control heating rate be 25 DEG C/
Min is warming up to 750 DEG C, and 1h is kept to carry out high temperature carbonization processing;
(4)By step(3)The activated carbon for obtaining high temperature carbonization processing naturally cools to 250 DEG C, in the case of air circulation,
5h is kept to carry out airoxidation to get carbonized material.
The step(5)Activation process includes the following steps:
(1)Pre-activate:The carbonized material for being mixed with activator is put into activation furnace, in high-purity N2In atmosphere, with the liter of 10 DEG C/min
Warm rate is warming up to 350 DEG C, and constant temperature 1.5h obtains pre-activate carbonized material;
(2)Middle low-temperature activation:By step(1)Pre-activate carbonized material continue to heat up, be warming up to 600 DEG C with 15 DEG C/min, constant temperature
1.0h obtains middle low-temperature activation carbonized material;
(3)High-temperature activation:By step(2)Middle low-temperature activation carbonized material continues to heat up, and is warming up to 800 DEG C with 20 DEG C/min, constant temperature
0.5h is to get activated material.
Embodiment 4:
The preparation method of the efficient water purification active carbon of the present embodiment, is made of petroleum coke, feed coal, binder and activator, and
The weight content of feed components is as follows:
Petroleum coke 65%;
Feed coal 20%;
Binder 10%;
Activator 5%;
Specific preparation process is as follows:
(1)It weighs petroleum coke respectively in proportion and feed coal carries out break process, screening obtains the petroleum coke that grain size is 3-5mm
Grain and raw material coal particle, and petroleum coke particles and raw material coal particle are uniformly mixed;
(2)It is proportionally added into binder to be stirred mixing, mediate, then briquetting material is obtained through cuber compound stalk forming;
(3)Briquetting material is put into retort, heating charing, obtains carbonized material under inert gas protection;
(4)Carbonized material is crushed, crosses 100-200 mesh sieve, and activator mixing is added;
(5)The carbonized material for being mixed with activator is put into activation furnace, and activation process is carried out under 2 atmosphere of high-purity N, is activated
Material;
(6)By step(5)In activated material cooling after through washing, being dried to obtain efficient water purification active carbon.
Ash content≤0.50% of the petroleum coke raw material, moisture≤5.0%, phosphorus content >=95%.
The feed coal is that weight ratio is 3:1 bituminous coal and the mixture of lignite.
The binder is cracking slurry oil.
The activator is NaOH.
The pressure of the compound stalk forming is 28MPa.
The step(3)Middle inert gas is argon gas.
The step(3)Carbonizing specific steps includes:
(1)Briquetting material is placed in retort, and carries out charing process under nitrogen or argon, first controlling heating rate is
8 DEG C/min, 300 DEG C are warming up to, 2h is kept to carry out pre- charing process early period, obtains pretreatment carbonized material;
(2)By step(1)Obtained pretreatment carbonized material, under nitrogen or argon, control heating rate are 15 DEG C/min,
550 DEG C of heating keeps 1.5h to carry out medium temperature charing process;
(3)By step(2)The carbonized material of medium temperature charing process, under nitrogen or argon, control heating rate be 25 DEG C/
Min is warming up to 750 DEG C, and 1h is kept to carry out high temperature carbonization processing;
(4)By step(3)The activated carbon for obtaining high temperature carbonization processing naturally cools to 250 DEG C, in the case of air circulation,
5h is kept to carry out airoxidation to get carbonized material.
The step(5)Activation process includes the following steps:
(1)Pre-activate:The carbonized material for being mixed with activator is put into activation furnace, in high-purity N2In atmosphere, with the liter of 10 DEG C/min
Warm rate is warming up to 350 DEG C, and constant temperature 1.5h obtains pre-activate carbonized material;
(2)Middle low-temperature activation:By step(1)Pre-activate carbonized material continue to heat up, be warming up to 600 DEG C with 15 DEG C/min, constant temperature
1.0h obtains middle low-temperature activation carbonized material;
(3)High-temperature activation:By step(2)Middle low-temperature activation carbonized material continues to heat up, and is warming up to 800 DEG C with 20 DEG C/min, constant temperature
0.5h is to get activated material.
Embodiment 5:
The preparation method of the efficient water purification active carbon of the present embodiment, is made of petroleum coke, feed coal, binder and activator, and
The weight content of feed components is as follows:
Petroleum coke 50%;
Feed coal 30%;
Binder 15%;
Activator 5%;
Specific preparation process is as follows:
(1)It weighs petroleum coke respectively in proportion and feed coal carries out break process, screening obtains the petroleum coke that grain size is 3-5mm
Grain and raw material coal particle, and petroleum coke particles and raw material coal particle are uniformly mixed;
(2)It is proportionally added into binder to be stirred mixing, mediate, then briquetting material is obtained through cuber compound stalk forming;
(3)Briquetting material is put into retort, heating charing, obtains carbonized material under inert gas protection;
(4)Carbonized material is crushed, crosses 100-200 mesh sieve, and activator mixing is added;
(5)The carbonized material for being mixed with activator is put into activation furnace, and activation process is carried out under 2 atmosphere of high-purity N, is activated
Material;
(6)By step(5)In activated material cooling after through washing, being dried to obtain efficient water purification active carbon.
Ash content≤0.50% of the petroleum coke raw material, moisture≤5.0%, phosphorus content >=95%.
The feed coal is that weight ratio is 3:1 bituminous coal and the mixture of lignite.
The binder is cracking slurry oil.
The activator is NaOH.
The pressure of the compound stalk forming is 33MPa.
The step(3)Middle inert gas is nitrogen.
The step(3)Carbonizing specific steps includes:
(1)Briquetting material is placed in retort, and carries out charing process under nitrogen or argon, first controlling heating rate is
8 DEG C/min, 300 DEG C are warming up to, 2h is kept to carry out pre- charing process early period, obtains pretreatment carbonized material;
(2)By step(1)Obtained pretreatment carbonized material, under nitrogen or argon, control heating rate are 15 DEG C/min,
550 DEG C of heating keeps 1.5h to carry out medium temperature charing process;
(3)By step(2)The carbonized material of medium temperature charing process, under nitrogen or argon, control heating rate be 25 DEG C/
Min is warming up to 750 DEG C, and 1h is kept to carry out high temperature carbonization processing;
(4)By step(3)The activated carbon for obtaining high temperature carbonization processing naturally cools to 250 DEG C, in the case of air circulation,
5h is kept to carry out airoxidation to get carbonized material.
The step(5)Activation process includes the following steps:
(1)Pre-activate:The carbonized material for being mixed with activator is put into activation furnace, in high-purity N2In atmosphere, with the liter of 10 DEG C/min
Warm rate is warming up to 350 DEG C, and constant temperature 1.5h obtains pre-activate carbonized material;
(2)Middle low-temperature activation:By step(1)Pre-activate carbonized material continue to heat up, be warming up to 600 DEG C with 15 DEG C/min, constant temperature
1.0h obtains middle low-temperature activation carbonized material;
(3)High-temperature activation:By step(2)Middle low-temperature activation carbonized material continues to heat up, and is warming up to 800 DEG C with 20 DEG C/min, constant temperature
0.5h is to get activated material.
Comparative example 1:
The water purification active carbon prepared using the method for Chinese invention patent application CN1194235.
Comparative example 2:
The water purification active carbon prepared using the method for Chinese invention patent application CN201710466241.9.
Experimental example 1:
By the average pore size of embodiment 1-5 and comparative example 1, comparative example 2 the water purification active carbon material being prepared, total pore volume and
Specific area measuring, concrete outcome are shown in Table 1.
Table 1
From table 1 it follows that the average pore size of water purification active carbon material produced by the present invention, microporosity, total pore volume and comparing table
Area is above the water purification activity that existing preparation method is produced.
Experimental example 2:
(1)Experimental instrument and equipment
High speed disintegrator, drier sieve Kun high pressure forming devices, glass filters filter, 100 mesh, ENOVI companies
ET99732 iodine numbers test tester, HANNA companies MI-99636 methylene blues Meter, Beijing sources Feng Jiexing scientific & technical corporation
MY-4455 ash analysis instrument etc..
(2)Several Judging index measure
Iodine number:It is measured by GB/T7702.7-2008 iodine sorption values;
Methylene blue value:By the measurement of GB/T7702.6-2008 methylenum careuleum adsorptive values;
Ash content:The measurement of GB/T7702.15-2008 ash contents;
Wear-resistant strength:The measurement of GB/T7702.3-2008 intensity.
Water purification active carbon progress performance is made in water purification active carbon made from embodiment 1-5 and comparative example 1, comparative example 2 to refer to
Mark detection, concrete outcome are shown in Table 1.
Table 1
Compare from table 1 and finds out, it is an advantage of the invention that:
A, relative to comparative example 1, comparative example 2, iodine number and the methylene blue value for weighing activated carbon adsorption performance index are much high
In comparative example 1, comparative example 2, illustrate that activated carbon adsorptive capacity of the present invention is strong, water purification capabilities are strong, purifying water effect is good;
B, it is directed to wear-resistant strength, activated carbon wear-resistant strength of the invention is less than higher than comparative example 1, comparative example 2, ash content to comparative example
1, comparative example 2 illustrate that activated carbon high mechanical strength or lower fracture strength of the present invention are high.
In conclusion preparation method technological process provided by the invention is simple, operating cost is low, and the activity prepared
Charcoal product has many advantages, such as that high mechanical strength, absorption property are good, has preferable effects of purification quality.
Charing process of the present invention includes:Early period pre- charing process, medium temperature charing process and high temperature carbonization processing, by charcoal
The treatment by stages of material overcomes microcrystalline carbon and mixes crosslinking with the excessive of random carbon, reduces the degree of graphitization of carbonized material, increase
Add in inorganic mineral the content of " active component ", convenient for the progress of subsequent activation reaction.
Activation process of the present invention is carried out by segmented, by pre-activate processing, middle low-temperature activation, high-temperature activation,
Be gradually expanded by intensive micropore enhances effects of purification quality for mesoporous and macropore to improve the absorption property of activated carbon.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although with reference to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution recorded in example is modified or equivalent replacement of some of the technical features.All essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.
Claims (8)
1. a kind of preparation method of efficient water purification active carbon, it is characterised in that:By petroleum coke, feed coal, binder and activator
Composition, and the weight content of feed components is as follows:
Petroleum coke 50-70%;
Feed coal 10-40%;
Binder 5-20%;
Activator 0.5-10%;
Specific preparation process is as follows:
(1)It weighs petroleum coke respectively in proportion and feed coal carries out break process, screening obtains the petroleum coke that grain size is 3-5mm
Grain and raw material coal particle, and petroleum coke particles and raw material coal particle are uniformly mixed;
(2)It is proportionally added into binder to be stirred mixing, mediate, then briquetting material is obtained through cuber compound stalk forming;
(3)Briquetting material is put into retort, heating charing, obtains carbonized material under inert gas protection;
(4)Carbonized material is crushed, crosses 100-200 mesh sieve, and activator mixing is added;
(5)The carbonized material for being mixed with activator is put into activation furnace, and activation process is carried out under 2 atmosphere of high-purity N, is activated
Material;
(6)By step(5)In activated material cooling after through washing, being dried to obtain efficient water purification active carbon;
Wherein, the step(5)Activation process includes the following steps:
(1)Pre-activate:The carbonized material for being mixed with activator is put into activation furnace, in high-purity N2In atmosphere, with the heating of 10 DEG C/min
Rate is warming up to 350 DEG C, and constant temperature 1.5h obtains pre-activate carbonized material;
(2)Middle low-temperature activation:By step(1)Pre-activate carbonized material continue to heat up, be warming up to 600 DEG C with 15 DEG C/min, constant temperature
1.0h obtains middle low-temperature activation carbonized material;
(3)High-temperature activation:By step(2)Middle low-temperature activation carbonized material continues to heat up, and is warming up to 800 DEG C with 20 DEG C/min, constant temperature
0.5h is to get activated material.
2. the preparation method of efficient water purification active carbon according to claim 1, it is characterised in that:The petroleum coke raw material
Ash content≤0.50%, moisture≤5.0%, phosphorus content >=95%.
3. the preparation method of efficient water purification active carbon according to claim 1, it is characterised in that:The feed coal is weight
Than being 3:1 bituminous coal and the mixture of lignite.
4. the preparation method of efficient water purification active carbon according to claim 1, it is characterised in that:The binder drips for coal
It is one or more of in blueness, asphalt, cracking slurry oil.
5. according to the preparation method of efficient water purification active carbon described in claim 1, it is characterised in that:The activator be NaOH or
KOH。
6. the preparation method of efficient water purification active carbon according to claim 1, it is characterised in that:The pressure of the compound stalk forming
Power is 25-35MPa.
7. the preparation method of efficient water purification active carbon according to claim 1, it is characterised in that:The step(3)In it is lazy
Property gas be nitrogen or argon gas.
8. the preparation method of efficient water purification active carbon according to claim 1, it is characterised in that:The step(3)Charing
Specific steps include:
(1)Briquetting material is placed in retort, and carries out charing process under nitrogen or argon, first controlling heating rate is
8 DEG C/min, 300 DEG C are warming up to, 2h is kept to carry out pre- charing process early period, obtains pretreatment carbonized material;
(2)By step(1)Obtained pretreatment carbonized material, under nitrogen or argon, control heating rate are 15 DEG C/min,
550 DEG C of heating keeps 1.5h to carry out medium temperature charing process;
(3)By step(2)The carbonized material of medium temperature charing process, under nitrogen or argon, control heating rate be 25 DEG C/
Min is warming up to 750 DEG C, and 1h is kept to carry out high temperature carbonization processing;
(4)By step(3)The activated carbon for obtaining high temperature carbonization processing naturally cools to 250 DEG C, in the case of air circulation,
5h is kept to carry out airoxidation to get carbonized material.