CN108517061A - A kind of nanometer of reinforcement bellows material and preparation method thereof - Google Patents
A kind of nanometer of reinforcement bellows material and preparation method thereof Download PDFInfo
- Publication number
- CN108517061A CN108517061A CN201810232447.XA CN201810232447A CN108517061A CN 108517061 A CN108517061 A CN 108517061A CN 201810232447 A CN201810232447 A CN 201810232447A CN 108517061 A CN108517061 A CN 108517061A
- Authority
- CN
- China
- Prior art keywords
- added
- mentioned
- taken
- nanometer
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of nanometer of reinforcement bellows materials, it is made of the raw material of following weight parts:High density polyethylene (HDPE) 110 140, methyl methacrylate 20 30, sodium peroxydisulfate 0.6 0.7, nano silicon dioxide 10 16, dithio-salicylic acid 13, Diacetone Acrylamide 0.8 1, tertiary butyl are to biphenol 0.8 2, dodecyl trimethyl ammonium chloride 12, polyvinyl alcohol 34, it is compatible that the present invention realizes effectively dispersion of the nano silicon dioxide in polyester liquid, improves the mechanical stability and intensity of finished-product material.
Description
Technical field
The invention belongs to tubing fields, and in particular to a kind of nanometer of reinforcement bellows material and preparation method thereof.
Background technology
Polytene corrugated tube is a kind of novel tube with Special-shaped section ring-type ripple struction, may replace common modeling
Expects pipe and other materials pipe are used as wiring architecture casing, irrigation and water conservancy infiltration drainpipe, cable guide, casing etc.;Application number
201510230205.3 disclosing a kind of manufacturing process of single wall bellows, include the following steps:S1, by following parts by weight
Hot melt adhesive 50-70, vistanex 30-50, tackifying resin 3-5, compound stabilizer 1.2-2, fire retardant 1-2, reinforcing agent 5-
30, compatilizer 0.02-0.05, toughener 5-8 are added in the closed mixer to run at high speed;S2, by the mixing in step S1
After object is kneaded and is granulated at 100-140 DEG C with mixer, puts into single screw extrusion machine, squeeze out, cut at 100-150 DEG C
Grain, air-cooled molding;S3, the material grain and hot melt adhesive that are obtained in step S2 are melted respectively after co-extrusion at double wall casing, in this method
The compatibility of each filler and interlaminar resin is poor, is easily reduced the stability_intensity of finished product bellows.
Invention content
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of nanometer of reinforcement bellows material and
Preparation method.
To achieve the above object, the present invention uses following technical scheme:
A kind of nanometer of reinforcement bellows material, it is made of the raw material of following weight parts:
High density polyethylene (HDPE) 110-140, methyl methacrylate 20-30, sodium peroxydisulfate 0.6-0.7, nano silicon dioxide 10-
16, dithio-salicylic acid 1-3, Diacetone Acrylamide 0.8-1, tertiary butyl are to biphenol 0.8-2, trimethyl chlorination
Ammonium 1-2, polyvinyl alcohol 3-4.
The preparation method of a kind of nanometer of reinforcement bellows material, includes the following steps:
(1)It takes tertiary butyl to biphenol, is added in the absolute ethyl alcohol of 10-13 times of its weight, stirs evenly, obtain alcoholic solution;
(2)Sodium peroxydisulfate is taken, is added in the deionized water of 20-25 times of its weight, stirs evenly;
(3)Nano silicon dioxide, Diacetone Acrylamide mixing are taken, is added in the deionized water of 20-30 times of mixture weight,
It is 55-60 DEG C to increase temperature, and insulated and stirred 1-2 hours obtains nano dispersion fluid;
(4)Methyl methacrylate is taken, is added in above-mentioned alcoholic solution, stirs evenly, be sent in reaction kettle, be passed through nitrogen,
It is 60-70 DEG C to adjust temperature of reaction kettle, and above-mentioned sodium persulfate aqueous solution, insulation reaction 4-5 hours is added, and discharging cooling is added
Above-mentioned nano dispersion fluid, it is 76-80 DEG C to increase temperature, insulated and stirred 1-2 hours, and discharging cooling obtains polymer emulsion;
(5)Polyvinyl alcohol is taken, is added in above-mentioned polymer emulsion, 10-20 minutes ultrasonic, filtering washes precipitation, vacuum
It is 1-2 hours dry at 50-55 DEG C, it obtains polymer-modified;
(6)It takes above-mentioned polymer-modified, is mixed with remaining each raw material, stir evenly, be sent in extruder, melting extrusion is cold
But to get.
Advantages of the present invention:
Nano silicon dioxide is used the aqueous dispersions decentralized processing of Diacetone Acrylamide by the present invention first, then with methyl-prop
E pioic acid methyl ester is monomer, is polymerize under sodium peroxydisulfate effect, by the dispersion liquid of obtained polymer solution and nano silicon dioxide
It is blended, it is compatible to realize effectively dispersion of the nano silicon dioxide in polyester liquid, improves the mechanical stability of finished-product material
And intensity.
Specific implementation mode
Embodiment 1
A kind of nanometer of reinforcement bellows material, it is made of the raw material of following weight parts:
High density polyethylene (HDPE) 110, methyl methacrylate 20, sodium peroxydisulfate 0.6, nano silicon dioxide 10, dithio-salicylic acid
1, Diacetone Acrylamide 0.8, tertiary butyl are to biphenol 0.8, dodecyl trimethyl ammonium chloride 1, polyvinyl alcohol 3.
The preparation method of a kind of nanometer of reinforcement bellows material, includes the following steps:
(1)It takes tertiary butyl to biphenol, is added in the absolute ethyl alcohol of 10 times of its weight, stirs evenly, obtain alcoholic solution;
(2)Sodium peroxydisulfate is taken, is added in the deionized water of 20 times of its weight, stirs evenly;
(3)Nano silicon dioxide, Diacetone Acrylamide mixing are taken, is added in the deionized water of 20 times of mixture weight, rises
High-temperature is 55 DEG C, and insulated and stirred 1 hour obtains nano dispersion fluid;
(4)Methyl methacrylate is taken, is added in above-mentioned alcoholic solution, stirs evenly, be sent in reaction kettle, be passed through nitrogen,
It is 60 DEG C to adjust temperature of reaction kettle, and above-mentioned sodium persulfate aqueous solution, insulation reaction 4 hours is added, and above-mentioned receive is added in discharging cooling
Rice dispersion liquid, it is 76 DEG C to increase temperature, insulated and stirred 1 hour, and discharging cooling obtains polymer emulsion;
(5)Polyvinyl alcohol is taken, is added in above-mentioned polymer emulsion, ultrasound 10 minutes, filtering washes precipitation, 50 DEG C of vacuum
Lower drying 1 hour, obtains polymer-modified;
(6)It takes above-mentioned polymer-modified, is mixed with remaining each raw material, stir evenly, be sent in extruder, melting extrusion is cold
But to get.
Embodiment 2
A kind of nanometer of reinforcement bellows material, it is made of the raw material of following weight parts:
High density polyethylene (HDPE) 140, methyl methacrylate 30, sodium peroxydisulfate 0.7, nano silicon dioxide 16, dithio-salicylic acid
1-3, Diacetone Acrylamide 1, tertiary butyl are to biphenol 2, dodecyl trimethyl ammonium chloride 2, polyvinyl alcohol 4.
The preparation method of a kind of nanometer of reinforcement bellows material, includes the following steps:
(1)It takes tertiary butyl to biphenol, is added in the absolute ethyl alcohol of 13 times of its weight, stirs evenly, obtain alcoholic solution;
(2)Sodium peroxydisulfate is taken, is added in the deionized water of 25 times of its weight, stirs evenly;
(3)Nano silicon dioxide, Diacetone Acrylamide mixing are taken, is added in the deionized water of 30 times of mixture weight, rises
High-temperature is 60 DEG C, and insulated and stirred 2 hours obtains nano dispersion fluid;
(4)Methyl methacrylate is taken, is added in above-mentioned alcoholic solution, stirs evenly, be sent in reaction kettle, be passed through nitrogen,
It is 70 DEG C to adjust temperature of reaction kettle, and above-mentioned sodium persulfate aqueous solution, insulation reaction 5 hours is added, and above-mentioned receive is added in discharging cooling
Rice dispersion liquid, it is 80 DEG C to increase temperature, insulated and stirred 2 hours, and discharging cooling obtains polymer emulsion;
(5)Polyvinyl alcohol is taken, is added in above-mentioned polymer emulsion, ultrasound 20 minutes, filtering washes precipitation, 55 DEG C of vacuum
Lower drying 2 hours, obtains polymer-modified;
(6)It takes above-mentioned polymer-modified, is mixed with remaining each raw material, stir evenly, be sent in extruder, melting extrusion is cold
But to get.
Claims (2)
1. a kind of nanometer of reinforcement bellows material, which is characterized in that it is made of the raw material of following weight parts:
High density polyethylene (HDPE) 110-140, methyl methacrylate 20-30, sodium peroxydisulfate 0.6-0.7, nano silicon dioxide 10-
16, dithio-salicylic acid 1-3, Diacetone Acrylamide 0.8-1, tertiary butyl are to biphenol 0.8-2, trimethyl chlorination
Ammonium 1-2, polyvinyl alcohol 3-4.
2. a kind of preparation method of nanometer reinforcement bellows material as described in claim 1, which is characterized in that including following step
Suddenly:
(1)It takes tertiary butyl to biphenol, is added in the absolute ethyl alcohol of 10-13 times of its weight, stirs evenly, obtain alcoholic solution;
(2)Sodium peroxydisulfate is taken, is added in the deionized water of 20-25 times of its weight, stirs evenly;
(3)Nano silicon dioxide, Diacetone Acrylamide mixing are taken, is added in the deionized water of 20-30 times of mixture weight,
It is 55-60 DEG C to increase temperature, and insulated and stirred 1-2 hours obtains nano dispersion fluid;
(4)Methyl methacrylate is taken, is added in above-mentioned alcoholic solution, stirs evenly, be sent in reaction kettle, be passed through nitrogen,
It is 60-70 DEG C to adjust temperature of reaction kettle, and above-mentioned sodium persulfate aqueous solution, insulation reaction 4-5 hours is added, and discharging cooling is added
Above-mentioned nano dispersion fluid, it is 76-80 DEG C to increase temperature, insulated and stirred 1-2 hours, and discharging cooling obtains polymer emulsion;
(5)Polyvinyl alcohol is taken, is added in above-mentioned polymer emulsion, 10-20 minutes ultrasonic, filtering washes precipitation, vacuum
It is 1-2 hours dry at 50-55 DEG C, it obtains polymer-modified;
(6)It takes above-mentioned polymer-modified, is mixed with remaining each raw material, stir evenly, be sent in extruder, melting extrusion is cold
But to get.