CN108501494A - A kind of production method of lint Polyester Taffeta Compound Fabric - Google Patents
A kind of production method of lint Polyester Taffeta Compound Fabric Download PDFInfo
- Publication number
- CN108501494A CN108501494A CN201810273176.2A CN201810273176A CN108501494A CN 108501494 A CN108501494 A CN 108501494A CN 201810273176 A CN201810273176 A CN 201810273176A CN 108501494 A CN108501494 A CN 108501494A
- Authority
- CN
- China
- Prior art keywords
- cloth
- polyester taffeta
- feeding
- composite material
- lint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of production method of lint Polyester Taffeta Compound Fabric, by Polyester Taffeta cloth and tweed with single layer matte by glue spraying, hot pressing, drying, cool down and etc. carry out it is compound, finally and constitute composite material-feeding, composite material-feeding is relative to pervious Polyester Taffeta cloth, increase the density of whole cloth, increase its wind-proof performance, and then reduces the live load of air charging system；By lint cloth, Polyester Taffeta cloth is compound and constitutes composite material-feeding, and composite material-feeding is wherein lint cloth on one side, and wherein lint cloth appearance is light refreshing clean, has good drapability, the inflation cloth doll appearance of reason composite material-feeding construction true to nature；And soft texture, frivolous transparent, the smooth high resilience of feel, while good physical performance, fibre strength is high, and wear-resisting, prolonged endurable chemical property is good, alkaline-resisting, chemical-resistant resistance, anti-insect, antifungi, can face outdoor complex environment.
Description
Technical field
The present invention relates to cloth field of compounding, espespecially a kind of production method of lint Polyester Taffeta Compound Fabric.
Background technology
At present on large-scale activity meeting-place, sponsor is to attract the crowd, often meeting-place lay large-scale theme cloth occasionally compared with
The appearance cloth that the crowd looks around can be attracted even.Such cloth is even nothing more than quiet, two kinds of forms of dynamic are divided into, and wherein dynamic cloth occasionally can most recruit
Pull the crowd aggregation, but mostly people dress or be dressed up as specific appearance cloth occasionally at.
Be mostly occasionally large scale as static cloth, to reach advertisement and decorative effect, cloth on a rare occasion as include a tailor
At the cloth ontology and an air charging system of specific doll appearance, which is set to the bottom of cloth ontology, provides prolonged drum
Wind function；The inflation cloth doll mainly utilizes air charging system that air is full of cloth body interior space, and it is in state of standing upright to enable cloth ontology,
And the cloth that cloth idol ontology uses generally uses Polyester Taffeta cloth, the required long term activation of inner inflatable device, due to Polyester Taffeta cloth
The cloth density of material is insufficient, and wind-proof performance is insufficient, there are problems that inner air leakage, it is therefore desirable to enhance air charging system
Power could realize effect, waste electricity indirectly；And single Polyester Taffeta cloth inflation cloth doll effect is not true to nature enough, feel
It is bad, give a kind of very cheap feeling of people so that be easy to that life is invited to detest, lose interest.
Invention content
To solve the above problems, the present invention provides a kind of production method of lint Polyester Taffeta Compound Fabric, by by Polyester Taffeta
Cloth and tweed are combined into composite material-feeding, increase the density of whole cloth, to increase its wind-proof performance, and tweed
Expect the appearance as composite material-feeding, improves the fidelity of its cloth idol appearance, and the feel of lint is good.
To achieve the above object, the technical solution adopted by the present invention is to provide a kind of producer of lint Polyester Taffeta Compound Fabric
Method includes the following steps：
S1. the surface of the tweed by compound Polyester Taffeta cloth is needed and with single layer matte carries out impurity treatment；
S2. by by step S1 processing Polyester Taffeta cloth and tweed be placed on the putting on cloth holder of compounding machine, by defeated
Roller is sent to be introduced into the upper glue groove of glue-spraying device；
S3. by glue-spraying device to the surface of Polyester Taffeta cloth or/and the non-matte glue spraying of tweed；
S4. the Polyester Taffeta cloth and tweed for passing through step S3 processing are introduced directly into hot-pressing roller by conveying roller, carry out heat
Pressing so that the non-matte of one of Polyester Taffeta cloth surface and tweed mutually bonds and constitutes composite material-feeding；
S5. by the composite material-feeding by step S4 processing, drier roll is transported to the glue in composite material-feeding by conveying roller
Water high temperature is evaporated；
S6. by the composite material-feeding by step S5 processing, wind-cooling heat dissipating taste removal is carried out, is then wound by winder.
Further, the tweed is imitative PV suedes or arctic suede or sheepfold suede or Sunday Angora Yarns.
Further, the density of the Polyester Taffeta cloth is 170T-210T.
Further, in the step S4, the operating temperature of hot-pressing roller is 180 DEG C~200 DEG C, and pressure is 180~220Mpa,
Conveying speed is 600 yards/hour.
Further, in the step S5, the operating temperature of the drier roll is 80 DEG C~200 DEG C, pressure is 180~
220Mpa。
The beneficial effects of the present invention are：1. Polyester Taffeta cloth and the tweed with single layer matte are passed through glue spraying, heat
Press, dry, cooling down and etc. carry out compound, final and constitute composite material-feeding, composite material-feeding increases relative to pervious Polyester Taffeta cloth
The big density of whole cloth, increases its wind-proof performance, and then reduce the live load of air charging system；2. by lint cloth, washing
Ta Fubu is compound and constitutes composite material-feeding, and composite material-feeding is wherein lint cloth on one side, and wherein lint cloth appearance is light refreshing clean,
With good drapability, the inflation cloth doll appearance of reason composite material-feeding construction is true to nature；And soft texture, frivolous transparent, hand
Feel smooth high resilience, while good physical performance, fibre strength is high, and wear-resisting, prolonged endurable chemical property is good, alkaline-resisting, chemically-resistant
Drug, anti-insect, antifungi can face outdoor complex environment.
Description of the drawings
Fig. 1 is existing technology composite aircraft structure schematic diagram.
Drawing reference numeral explanation：1. putting cloth holder；11. conveying roller；2. Polyester Taffeta cloth；3. tweed；4. glue-spraying device；5. hot pressing
Roller；6. drier roll；7. composite material-feeding；8. winder.
Specific implementation mode
The present invention is described in detail with reference to specific embodiment and Figure of description.
Refering to Figure 1, the present invention is about a kind of production method of lint Polyester Taffeta Compound Fabric, by by Polyester Taffeta cloth
2 and the tweed 3 with single layer matte carry out compound, and constitute composite material-feeding 7, increase the density of whole cloth, to
Increase its wind-proof performance, and appearance of the tweed 3 as composite material-feeding 7, improves the fidelity of its cloth idol appearance, and lint
Feel it is good.
Refering to Figure 1, below by specific implementation mode, the invention will be further described.
Specific embodiment 1, process of the invention：
S1. the surface of the arctic suede by compound Polyester Taffeta cloth 2 is needed and with single layer matte carries out impurity treatment；Its
Used in 2 density of Polyester Taffeta cloth be 170T；
S2. by by step S1 processing 170T Polyester Taffetas cloth and arctic suede be placed on the putting on cloth holder 1 of compounding machine, lead to
Conveying roller 11 is crossed to be introduced into the upper glue groove of glue-spraying device 4；
S3. by glue-spraying device 4 to the non-matte glue spraying of the surface of Polyester Taffeta cloth 2 and arctic suede respectively；
S4. the Polyester Taffeta cloth 2 and arctic suede for passing through step S3 processing, wherein by the surface and north of glue spraying Polyester Taffeta cloth 2
The non-matte of pole suede faces each other, and is introduced directly into hot-pressing roller 5 by conveying roller 11, carries out hot pressing so that Polyester Taffeta cloth 2
One of the non-matte of surface and arctic suede mutually bond and constitute composite material-feeding 7；The operating temperature of wherein hot-pressing roller 5 is
180 DEG C, pressure 220Mpa, 5 conveying speed of hot-pressing roller is 600 yards/hour.
S5. by the composite material-feeding 7 by step S4 processing, drier roll 6 is transported to in composite material-feeding 7 by conveying roller 11
Glue high temperature be evaporated；Wherein the operating temperature of the drier roll 6 is 80 DEG C, pressure 180Mpa.
S6. by the composite material-feeding 7 by step S5 processing, wind-cooling heat dissipating taste removal is carried out, is then wound by winder 8；
Specific embodiment 2, process of the invention：
S1. the surface of the imitative PV suedes by compound Polyester Taffeta cloth 2 is needed and with single layer matte carries out impurity treatment；Its
Used in 2 density of Polyester Taffeta cloth be 210T
S2. by by step S1 processing 210T Polyester Taffetas cloth 2 and imitative PV suedes be placed on the putting on cloth holder 1 of compounding machine,
It is introduced into the upper glue groove of glue-spraying device 4 by conveying roller 11；
S3. by glue-spraying device 4 to one of 210T Polyester Taffetas cloth 2 surface glue spraying, the non-matte of imitative PV suedes is not required to
Want glue spraying；
S4. pass through the 210T Polyester Taffetas cloth 2 of step S3 processing and imitative PV suedes, wherein by the 210T Polyester Taffetas cloth 2 of glue spraying
Surface and the non-matte of imitative PV suedes face each other, and are introduced directly into hot-pressing roller 5 by conveying roller 11, carry out hot pressing so that
The non-matte on the surface and imitative PV suedes by glue spraying of 210T Polyester Taffetas cloth 2 mutually bonds and constitutes composite material-feeding 7；Wherein hot-pressing roller
5 operating temperature is 200 DEG C, pressure 180Mpa, and 5 conveying speed of hot-pressing roller is 600 yards/hour.
S5. by the composite material-feeding 7 by step S4 processing, drier roll 6 is transported to in composite material-feeding 7 by conveying roller 11
Glue high temperature be evaporated；Wherein the operating temperature of the drier roll 6 is 80 DEG C, pressure 220Mpa.
S6. by the composite material-feeding 7 by step S5 processing, wind-cooling heat dissipating taste removal is carried out, is then wound by winder 8；
Specific embodiment 3, process of the invention：
S1. the surface of the Sunday Angora Yarns by compound Polyester Taffeta cloth 2 is needed and with single layer matte carries out impurity treatment；Its
The density of middle Polyester Taffeta cloth 2 is 210T；
S2. by by step S1 processing 210T Polyester Taffetas cloth 2 and Sunday Angora Yarns be placed on the putting on cloth holder 1 of compounding machine,
It is introduced into the upper glue groove of glue-spraying device 4 by conveying roller 11；
S3. by glue-spraying device 4 to the non-matte glue spraying of Sunday Angora Yarns, 210T Polyester Taffetas cloth 2 does not need glue spraying；
S4. pass through the 210T Polyester Taffetas cloth 2 and Sunday Angora Yarns of step S3 processing, the wherein surface of 210T Polyester Taffetas cloth 2 and quilt
The non-matte of the Sunday Angora Yarns of glue spraying faces each other, and is introduced directly into hot-pressing roller 5 by conveying roller 11, carries out hot pressing so that
The non-matte by the surface of glue spraying and Sunday Angora Yarns of 210T Polyester Taffetas cloth 2 mutually bonds and constitutes composite material-feeding 7；Wherein hot-pressing roller
5 operating temperature is 180 DEG C, pressure 180Mpa, and 5 conveying speed of hot-pressing roller is 600 yards/hour.
S5. by the composite material-feeding 7 by step S4 processing, drier roll 6 is transported to in composite material-feeding 7 by conveying roller 11
Glue high temperature be evaporated；Wherein the operating temperature of the drier roll 6 is 80 DEG C, pressure 220Mpa.
S6. by the composite material-feeding 7 by step S5 processing, wind-cooling heat dissipating taste removal is carried out, is then wound by winder 8；
Polyester Taffeta cloth 2 and tweed 3 with single layer matte are passed through the steps such as glue spraying, hot pressing, drying, cooling by the present invention
Suddenly carry out compound, final and constitute composite material-feeding 7, composite material-feeding 7 increases whole cloth relative to pervious Polyester Taffeta cloth 2
Density, increase its wind-proof performance, and then reduce the live load of air charging system；By tweed 3, Polyester Taffeta cloth 2 is compound and structure
At composite material-feeding 7, the wherein one side of composite material-feeding 7 is tweed 3, and wherein 3 appearance of tweed is light refreshing clean, has good pendency
Property, the inflation cloth doll appearance that reason composite material-feeding 7 constructs is true to nature；And it is soft texture, frivolous transparent, feel is smooth rich in bullet
Property, while good physical performance, fibre strength are high, wear-resisting, prolonged endurable chemical property is good, alkaline-resisting, chemical-resistant resistance, anti-insect,
Antifungi can face outdoor complex environment.
Embodiment of above be only the preferred embodiment of the present invention is described, not to the scope of the present invention into
Row limits, under the premise of not departing from design spirit of the present invention, technical side of this field ordinary engineering and technical personnel to the present invention
The various modifications and improvement that case is made should all be fallen into the protection domain of claims of the present invention determination.
Claims (5)
1. a kind of production method of lint Polyester Taffeta Compound Fabric, it is characterised in that include the following steps：
S1. the surface of the tweed by compound Polyester Taffeta cloth is needed and with single layer matte carries out impurity treatment；
S2. by by step S1 processing Polyester Taffeta cloth and tweed be placed on the putting on cloth holder of compounding machine, pass through conveying roller
It is introduced into the upper glue groove of glue-spraying device；
S3. by glue-spraying device to the surface of Polyester Taffeta cloth or/and the non-matte glue spraying of tweed；
S4. the Polyester Taffeta cloth and tweed for passing through step S3 processing are introduced directly into hot-pressing roller by conveying roller, carry out hot pressing
It closes so that the non-matte of one of Polyester Taffeta cloth surface and tweed mutually bonds and constitutes composite material-feeding；
S5. by the composite material-feeding by step S4 processing, it is high to the glue in composite material-feeding that drier roll is transported to by conveying roller
Temperature is evaporated；
S6. by the composite material-feeding by step S5 processing, wind-cooling heat dissipating taste removal is carried out, is then wound by winder.
2. a kind of production method of lint Polyester Taffeta Compound Fabric according to claim 1, it is characterised in that：The tweed
For imitative PV suedes or arctic suede or sheepfold suede or Sunday Angora Yarns.
3. a kind of production method of lint Polyester Taffeta Compound Fabric according to claim 1, it is characterised in that：The Polyester Taffeta
The density of cloth is 170T-210T.
4. a kind of production method of lint Polyester Taffeta Compound Fabric according to claim 1, it is characterised in that：The step S4
In, the operating temperature of hot-pressing roller is 180 DEG C~200 DEG C, and pressure is 180~220Mpa, and conveying speed is 600 yards/hour.
5. a kind of production method of lint Polyester Taffeta Compound Fabric according to claim 1, it is characterised in that：The step S5
In, the operating temperature of the drier roll is 80 DEG C~200 DEG C, and pressure is 180~220Mpa.