CN108486412A - Titanium alloy - Google Patents
Titanium alloy Download PDFInfo
- Publication number
- CN108486412A CN108486412A CN201810592092.5A CN201810592092A CN108486412A CN 108486412 A CN108486412 A CN 108486412A CN 201810592092 A CN201810592092 A CN 201810592092A CN 108486412 A CN108486412 A CN 108486412A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- titanium alloy
- present
- lace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of titanium alloys, including following raw material:Si:39 parts by weight;V:0.6 0.8 parts by weight;Nd:26 parts by weight;Na:15 parts by weight;Mo:0.5 1.2 parts by weight;B:1 5.2 parts by weight;Al:10 22 parts by weight;C:22 28 parts by weight;Y:29 parts by weight;LaCe:1.2 2.9 parts by weight;Ti:1088 1160 parts by weight.Beneficial effects of the present invention are:It is with higher intensity.
Description
Technical field
The present invention relates to a kind of titanium alloys.
Background technology
There is also certain deficiencies for the intensity of existing titanium alloy.
Invention content
The purpose of the present invention is to provide a kind of titanium alloys, with higher intensity.
To achieve the above object, the technical scheme is that
A kind of titanium alloy, including following raw material:
Si:3-9 parts by weight;
V:0.6-0.8 parts by weight;
Nd:2-6 parts by weight;
Na:1-5 parts by weight;
Mo:0.5-1.2 parts by weight;
B:1-5.2 parts by weight;
Al:10-22 parts by weight;
C:22-28 parts by weight;
Y:2-9 parts by weight;
LaCe:1.2-2.9 parts by weight;
Ti:1088-1160 parts by weight.
The operation principle of the present invention is that:The addition of LaCe so that impurity is removed in alloy, forms strengthening phase, and then have
Higher intensity.
Beneficial effects of the present invention are:It is with higher intensity.
Specific implementation mode
With reference to embodiment, the specific embodiment of the present invention is further described.Following embodiment is only used for more
Add and clearly demonstrate technical scheme of the present invention, and not intended to limit the protection scope of the present invention.
The technical solution that the present invention embodies is:
Embodiment 1
A kind of titanium alloy, including following raw material:
Si:3 parts by weight;
V:0.6 parts by weight;
Nd:2 parts by weight;
Na:1 parts by weight;
Mo:0.5 parts by weight;
B:1 parts by weight;
Al:10 parts by weight;
C:22 parts by weight;
Y:2 parts by weight;
LaCe:1.2 parts by weight;
Ti:1088 parts by weight.
Embodiment 2
A kind of titanium alloy, including following raw material:
Si:9 parts by weight;
V:0.8 parts by weight;
Nd:6 parts by weight;
Na:5 parts by weight;
Mo:1.2 parts by weight;
B:5.2 parts by weight;
Al:22 parts by weight;
C:28 parts by weight;
Y:9 parts by weight;
LaCe:2.9 parts by weight;
Ti:1160 parts by weight.
Embodiment 3
A kind of titanium alloy, including following raw material:
Si:6 parts by weight;
V:0.7 parts by weight;
Nd:4 parts by weight;
Na:4 parts by weight;
Mo:1.1 parts by weight;
B:2.6 parts by weight;
Al:16 parts by weight;
C:25 parts by weight;
Y:6 parts by weight;
LaCe:7 parts by weight;
Ti:1140 parts by weight.
The above is only a preferred embodiment of the present invention, it is noted that those skilled in the art are come
It says, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (1)
1. a kind of titanium alloy, which is characterized in that including following raw material:
Si:3-9 parts by weight;
V:0.6-0.8 parts by weight;
Nd:2-6 parts by weight;
Na:1-5 parts by weight;
Mo:0.5-1.2 parts by weight;
B:1-5.2 parts by weight;
Al:10-22 parts by weight;
C:22-28 parts by weight;
Y:2-9 parts by weight;
LaCe:1.2-2.9 parts by weight;
Ti:1088-1160 parts by weight.