CN108442035B - A kind of preparation method and non-woven cloth of unidirectional miniature non-woven cloth - Google Patents
A kind of preparation method and non-woven cloth of unidirectional miniature non-woven cloth Download PDFInfo
- Publication number
- CN108442035B CN108442035B CN201810400648.6A CN201810400648A CN108442035B CN 108442035 B CN108442035 B CN 108442035B CN 201810400648 A CN201810400648 A CN 201810400648A CN 108442035 B CN108442035 B CN 108442035B
- Authority
- CN
- China
- Prior art keywords
- composite fibre
- woven cloth
- unidirectional
- preparation
- facial mask
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of preparation method of unidirectional miniature non-woven cloth, including composite fibre, blowing combing, stacking lapping, spun lacing and degreasing, bleaching, drying, wherein including wool fiber in vertical orientation composite fibre.By the wool fiber for introducing orientation into non-woven fabrics, the characteristics of using its moisture absorption and felting, its surface is carried out after soaking non-woven fabrics to comfort touching massage, with the absorption or evaporation of moisture, miniature effect can be presented in wool fiber orientation in non-woven fabrics, above-mentioned miniature processing is consistent with the use habit of docile formula facial mask, so that applying lifting active force to skin of face in facial mask use process.The invention also discloses a kind of unidirectional miniature non-woven cloth, utilize the method for unidirectional miniature non-woven cloth manufacture facial mask.
Description
Technical field
The invention belongs to field of nonwoven fabric technology, and in particular to a kind of preparation method of unidirectional miniature non-woven cloth non-is knitted
Make the preparation method of cloth and unidirectional miniature non-woven cloth facial mask.
Background technique
Spunlace non-woven cloth is to intertwine with each other fiber one on high pressure fine water flow jet to one or more layers web
It rises, to enable fibre web to reinforce and have certain strength, obtained fabric is spunlace non-woven cloth.Its fibrous raw material source is wide
It is general, it is fine to can be terylene, polyamide fibre, polypropylene fibre, viscose rayon, chitin fiber, superfine fibre, tencel, silk, bamboo fibre, wood pulp
Dimension, alginate fibre etc..Compared with needle punched non-woven fabrics, the grammes per square metre of spunlace non-woven cloth is smaller, is suitable as beauty mask consumptive material and doctor
Use dressing.
Common pasting type facial mask can be divided into non-woven fabrics facial mask, silk mask and gel mask according to the material of carrier.Nothing
The characteristics of woven fabric facial mask is that carrying Essence is relatively more, applies and feels soft and moist comfortable, good airproof performance, its shortcoming is that skin affinity is not
It is good, the only carrier of Essence；Silk mask is since quality is frivolous, for keeping the gap of Essence few between fiber, because
The Essence of this carrying is few, is readily retained in facial mask bag.Sometimes Essence can flow in neck during deposited.It is high-end
The facial mask of brand mostly uses long-staple cotton fiber as non-woven fabrics base material, and it is with certain thickness.In order to skin of face
The effect of lifting drawing-off is played, improved technical solution uses gel or pectin fiber as membrane material, but smart in above-mentioned substrate
The magnificent liquid volume of holding is few, and face mask substrate material higher cost.
Therefore, it is necessary to carry out structure improvement to common non-woven fabric facial mask in the prior art.
Summary of the invention
It is an object of the present invention to overcoming defect existing in the prior art, a kind of unidirectional miniature non-woven cloth is provided
Preparation method, above-mentioned non-woven fabrics is after steeping liq, and with the volatilization of moisture, perpendicular orientation can be in miniature state.
To achieve the above object, the technical solution of the present invention is as follows: a kind of preparation method of unidirectional miniature non-woven cloth, special
Sign is, comprising the following steps:
Horizontal orientation composite fibre and vertical orientation composite fibre is respectively configured in S1, indulges fine comprising wool in orientation composite fibre
Dimension；
S2 carries out blowing, combing to horizontal orientation composite fibre and vertical orientation composite fibre respectively；
According to orthogonal direction lapping, horizontal orientation composite fibre is laid with for S3, horizontal orientation composite fibre and vertical orientation composite fibre
In the lower section of vertical orientation composite fibre or horizontal orientation composite fibre and the vertical orientation alternately laminated lapping of composite fibre；
S4 carries out spun lacing processing to web obtained by S3；
S5, degreasing, bleaching, drying obtain unidirectional miniature non-woven cloth finished product.
In order to guarantee that the skin-friendly of non-woven fabrics, preferred technical solution are that horizontal orientation composite fibre is cotton fiber, orientation is indulged
Main group of composite fibre becomes cotton fiber and wool fiber.
Preferred technical solution is that the content of wool fiber is 25-50% in vertical orientation composite fibre.Wool fiber content
It is excessive, then it will lead to non-woven fabrics and unidirectionally shrink obviously, felting readily occurs in nonwoven production process.
Preferred technical solution is that the weight ratio of horizontal orientation composite fibre and vertical orientation composite fibre is 1:(1.3-1.5).
Horizontal orientation composite fibre is excessive, then forms drawing-off positioning action for vertical directional fiber, constrains the contraction of vertical directional fiber.
Preferred technical solution is that the grammes per square metre of unidirectional miniature non-woven cloth is 30-55g/m2。
Preferred technical solution is that wool fiber is the wool fiber by mercerization finish, and mercerization finish process includes oxygen
Chemical industry sequence:
The composition of oxidation operation oxidation treatment liquid includes bleeding agent, 30% hydrogen peroxide and hydrogen peroxide stabilizer, wherein 30% pair
The concentration of oxygen water is 20-26ml/L, 40-45 DEG C of oxidation processes 35-45min, oxidation processes bath raio 1:30.
Preferred technical solution be further include enzymatic treatment process after oxidation operation, the group of enzymatic treatment liquid in enzymatic treatment process
At comprising dispersing agent, middle spinning protease, the middle weight percent for spinning protease is 1-1.5%, and the pH value of enzymatic treatment liquid is 8,45-
50 DEG C of enzymatic treatment 45-55min；The bath raio 1:30 of enzymatic treatment.
Preferred technical solution is that spun lacing processing is single side spun lacing, and the fine water (flow) direction of the high pressure of single side spun lacing is by fibre
Dimension sieve bottom punctures upwards.Compared with two-sided spun lacing, horizontal orientation cotton fiber is only punctured in web by single side water side, without inciting somebody to action
Wool fiber is punctured to the bottom surface of non-woven fabrics, when being used as facial mask, reduces wool scale sense of discomfort in direct contact with the skin.
The second object of the present invention is to provide a kind of unidirectional miniature non-woven cloth, which is characterized in that uses above-mentioned list
It is made to the preparation method of miniature non-woven cloth.
The second object of the present invention is to provide a kind of preparation method of unidirectional miniature non-woven cloth facial mask, including following step
It is rapid:
S1, facial mask unit is cut out in above-mentioned unidirectional miniature non-woven cloth upper mold；
S2, facial mask unit impregnate facial mask liquid；
It is characterized in that, the forehead of facial mask unit applies the direction and unidirectionally miniature non-woven cloth that area to chin applies area
The orientation lapping direction of vertical orientation composite fibre is consistent.
The advantages and beneficial effects of the present invention are:
By introducing the wool fiber of orientation into non-woven fabrics, the characteristics of using its moisture absorption and felting, soaked by non-woven fabrics
Its surface is carried out after wet to comfort touching massage, with the absorption or evaporation of moisture, wool fiber orientation can be presented micro- in non-woven fabrics
Contracting effect, above-mentioned miniature processing is consistent with the use habit of docile formula facial mask, so that applying in facial mask use process to skin of face
Add lifting active force.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following embodiment is only used for more
Add and clearly demonstrate technical solution of the present invention, and not intended to limit the protection scope of the present invention.
Embodiment 1
Embodiment 1
The preparation method of unidirectional miniature non-woven cloth, comprising the following steps:
Horizontal orientation composite fibre and vertical orientation composite fibre is respectively configured in S1, indulges fine comprising wool in orientation composite fibre
Dimension；
S2 carries out blowing, combing to horizontal orientation composite fibre and vertical orientation composite fibre respectively；
According to orthogonal direction lapping, horizontal orientation composite fibre is laid with for S3, horizontal orientation composite fibre and vertical orientation composite fibre
In the lower section of vertical orientation composite fibre；
S4 carries out spun lacing processing to web obtained by S3；
S5, degreasing, bleaching, drying obtain unidirectional miniature non-woven cloth finished product.
The horizontal orientation composite fibre of embodiment 1 is polyester fiber, and vertical orientation composite fibre is mixed by polyester fiber and wool fiber
It closes, wherein wool fiber content is 60%.Wool is the wool fiber without mercerization finish.Horizontal orientation composite fibre with
The weight ratio of vertical orientation composite fibre is 1:1.The grammes per square metre of unidirectional miniature non-woven cloth is 45g/m2。
Spun lacing process uses two-sided spun lacing.
Embodiment 2
Embodiment 2 the difference from embodiment 1 is that: horizontal orientation composite fibre be long-staple cotton fiber, indulge orientation composite fibre
Main group become long-staple cotton and wool fiber, also containing 2% bombax cotton.Horizontal orientation composite fibre and vertical orientation mixing are fine
Tie up alternately laminated lapping.
The content of wool fiber is 25% in vertical orientation composite fibre.
The weight ratio of horizontal orientation composite fibre and vertical orientation composite fibre is 1:1.3.
Spun lacing processing is single side spun lacing, and the fine water (flow) direction of the high pressure of single side spun lacing is to be punctured upwards by fiber sieve bottom.
Embodiment 3
Embodiment 3 the difference from example 2 is that: the content of wool fiber is 50% in vertical orientation composite fibre.Horizontal orientation
The weight ratio of composite fibre and vertical orientation composite fibre is 1:1.5.
Embodiment 4
Embodiment 4 and the difference of embodiment 3 are: wool fiber is the wool fiber by mercerization finish, mercerization finish
Process includes oxidation operation:
The composition of oxidation operation oxidation treatment liquid includes bleeding agent, 30% hydrogen peroxide and hydrogen peroxide stabilizer, wherein 30% pair
The concentration of oxygen water is 20-26ml/L, 40-45 DEG C of oxidation processes 35-45min, oxidation processes bath raio 1:30.
It further include enzymatic treatment process after oxidation operation, the composition of enzymatic treatment liquid includes dispersing agent, middle spinning in enzymatic treatment process
Protease, the middle weight percent for spinning protease are 1-1.5%, and the pH value of enzymatic treatment liquid is 8,45-50 DEG C of enzymatic treatment 45-
55min；The bath raio 1:30 of enzymatic treatment.
Embodiment 5
The difference of embodiment 5 and embodiment 4 is the process conditions of mercerization finish, essentially consists in oxidation operation 30% pair
The concentration of oxygen water is 35ml/L.
Comparative example
Comparative example 1 does not have point of horizontal directional fiber and vertical directional fiber, and fiber architecture is non-directional, grammes per square metre in non-woven fabrics
Consistent with embodiment 1, used fiber is polyester fiber.
Horizontal orientation composite fibre and vertical orientation composite fibre are long-staple cotton in comparative example 2.
Non-woven fabrics performance comparison:
Non-woven fabrics obtained by embodiment and comparative example is prepared into application facial mask by the following method:
S1, facial mask unit is cut out in above-mentioned unidirectional miniature non-woven cloth upper mold；
S2, facial mask unit impregnate facial mask liquid；
The direction that the forehead of facial mask unit applies area to chin application area is mixed with the vertical orientation of unidirectional miniature non-woven cloth
The orientation lapping direction of fiber is consistent.
Facial mask liquid is substituted using plain chocolate of the same race, facial mask is placed in glass surface, and simulate to the facial mask of glass surface real
Interphase film use process comfort touching massage, and measurement is stood 20min at 25 DEG C, surveyed by the length L1 of forehead to chin application
Amount is calculated the parallel 5 groups of tests of miniature ratio L%=(L1-L2)/L1*100%(and is averaged by the length L2 of forehead to chin application
Value), the miniature ratio of embodiment and comparative example see the table below:
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Comparative example 1 | Comparative example 2 | |
| Miniature ratio (%) | 3.35 | 2.93 | 3.18 | 2.41 | 0.49 | 0 | 0.07 |
As seen from the above table, terylene nonwoven cloth cover that is miniature, and being laid at random in comparative example 1 is presented in facial mask unit in the longitudinal direction
Film length is unchanged, and the contraction of long-staple cotton is minimum.Mercerization finish is the scale layer removing of Jiang's wool surfaces, and mercerization finish is also
Help alleviate the sense of discomfort that facial mask leather hard lower face skin is contacted with scale layer.The degree of removing determines the list of non-woven fabrics
To miniature amount, the scale of 5 wool surface of embodiment is removed completely during mercerization finish, therefore miniature ratio is smaller.
The grammes per square metre of unidirectional miniature non-woven cloth suitable for facial mask is 30-55g/m2。
It is only the preferred embodiment of the present invention described in upper, it is noted that for those skilled in the art
For, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (8)
1. a kind of preparation method of unidirectional miniature non-woven cloth, which comprises the following steps:
Horizontal orientation composite fibre and vertical orientation composite fibre is respectively configured in S1, and indulging in orientation composite fibre includes wool fiber；
S2 carries out blowing, combing to horizontal orientation composite fibre and vertical orientation composite fibre respectively；
According to orthogonal direction lapping, horizontal orientation composite fibre is laid on vertical for S3, horizontal orientation composite fibre and vertical orientation composite fibre
The lower section of orientation composite fibre or horizontal orientation composite fibre and the vertical orientation alternately laminated lapping of composite fibre；
S4 carries out spun lacing processing to web obtained by S3；
S5, degreasing, bleaching, drying obtain unidirectional miniature non-woven cloth finished product;Wool fiber is the wool by mercerization finish
Fiber, mercerization finish process includes oxidation operation:
The composition of oxidation operation oxidation treatment liquid includes bleeding agent, 30% hydrogen peroxide and hydrogen peroxide stabilizer, wherein 30% hydrogen peroxide
Concentration be 20-26ml/L, 40-45 DEG C of oxidation processes 35-45min, oxidation processes bath raio 1:30;Further include after oxidation operation
Enzymatic treatment process, the composition of enzymatic treatment liquid includes dispersing agent, middle spinning protease, the middle weight hundred for spinning protease in enzymatic treatment process
Divide than being 1-1.5%, the pH value of enzymatic treatment liquid is 8,45-50 DEG C of enzymatic treatment 45-55min；The bath raio 1:30 of enzymatic treatment.
2. the preparation method of unidirectional miniature non-woven cloth according to claim 1, which is characterized in that horizontal orientation composite fibre
For cotton fiber, indulging main group of orientation composite fibre becomes cotton fiber and wool fiber.
3. the preparation method of unidirectional miniature non-woven cloth according to claim 2, which is characterized in that vertical orientation composite fibre
The content of middle wool fiber is 25-50%.
4. the preparation method of unidirectional miniature non-woven cloth according to claim 2 or 3, which is characterized in that horizontal orientation mixing
The weight ratio of fiber and vertical orientation composite fibre is 1:(1.3-1.5).
5. the preparation method of unidirectional miniature non-woven cloth according to claim 3, which is characterized in that unidirectional miniature non-woven
The grammes per square metre of cloth is 30-55g/m2.
6. the preparation method of unidirectional miniature non-woven cloth according to claim 1, which is characterized in that spun lacing processing is single side
Spun lacing, the fine water (flow) direction of the high pressure of single side spun lacing are to be punctured upwards by fiber sieve bottom.
7. a kind of unidirectional miniature non-woven cloth, which is characterized in that using unidirectional micro- described in any one of claim 1 to 6
The preparation method of contracting non-woven cloth is made.
8. a kind of preparation method of unidirectional miniature non-woven cloth facial mask, comprising the following steps:
S1, facial mask unit is cut out in unidirectional miniature non-woven cloth upper mold as claimed in claim 7；
S2, facial mask unit impregnate facial mask liquid；
It is characterized in that, facial mask unit forehead apply area to chin application area direction with unidirectionally miniature non-woven cloth it is vertical fixed
It is consistent to the orientation lapping direction of composite fibre.