CN108440937A - A kind of preparation method of New Antistatic Materials - Google Patents
A kind of preparation method of New Antistatic Materials Download PDFInfo
- Publication number
- CN108440937A CN108440937A CN201810252792.XA CN201810252792A CN108440937A CN 108440937 A CN108440937 A CN 108440937A CN 201810252792 A CN201810252792 A CN 201810252792A CN 108440937 A CN108440937 A CN 108440937A
- Authority
- CN
- China
- Prior art keywords
- parts
- product
- glass fibre
- spare
- antistatic materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of New Antistatic Materials, anti-static material proposed by the present invention substitutes some Imported material with domestic raw material, product cost is greatly lowered, and be modified by activeness and quietness, properties of product increase on existing anti-static material.Its formula is:20 parts~30 parts of polyphenylene oxide, 620 parts~30 parts of nylon, 0~5 part of toughener, 0~5 part of compatilizer, 10 parts~30 parts of glass fibre, 10 parts~20 parts of carbon nanotube master batch, 0~0.5 part of antioxidant, 0~0.5 part of lubricant.It weighs up that each component is spare according to formula constituent, by other raw materials in addition to glass fibre, puts into blender together, after being dried under the conditions of 140 DEG C, stirring 2~3H, it is spare to be discharged to turnover box;Production equipment temperature is set at 260~290 DEG C, the raw material being stirred is through double screw extruder melt blending, extrusion, check rod, pelletizing up to product.
Description
Technical field
The present invention relates to anti-static material technical field, more particularly to a kind of preparation method of New Antistatic Materials.
Background technology
Existing anti-static material cost is excessively high, and supply falls short of demand for raw material, leads to market unsettled of supplying;Production technology
Cumbersome, low production efficiency, environmental pollution is big.
Invention content
The technical problem to be solved in the present invention is to provide a kind of preparation methods of New Antistatic Materials, overcome above existing
The defect of technology has many advantages, such as that production cost is low, efficient, energy conservation and environmental protection.
In order to solve the above-mentioned technical problem, the technical scheme is that:
A kind of preparation method of New Antistatic Materials:
Anti-static material proposed by the present invention substitutes some Imported material with domestic raw material, product cost is greatly lowered,
And be modified by activeness and quietness, properties of product increase on existing anti-static material.Its formula is:Polyphenylene oxide 20 parts~30
Part, 620 parts~30 parts of nylon, 0~5 part of toughener, 0~5 part of compatilizer, 10 parts~30 parts of glass fibre, carbon nanotube master batch
10 parts~20 parts, 0~0.5 part of antioxidant, 0~0.5 part of lubricant.
It weighs up that each component is spare according to formula constituent, by other raw materials in addition to glass fibre, puts into blender together,
It is dried under the conditions of 140 DEG C, after 2~3H of stirring, it is spare to be discharged to turnover box;Be arranged production equipment temperature at 260~290 DEG C,
The raw material being stirred is through double screw extruder melt blending, extrusion, check rod, pelletizing up to product.
The beneficial effects of the invention are as follows:
This formula and the made anti-static material of technological process, production cost is low, product strength height (tensile strength >
80MPa, bending strength > 130MPa), good toughness (notch impact strength > 2Kj/m2), low (the < 2*10-5/ of coefficient of thermal expansion
DEG C), heat distortion temperature height (200 DEG C of 1.82MPa, HDT >), processing performance is good.Production efficiency can be improved in this method, reduces environment
Pollution.
It can guarantee the stabilization of raw material supply;
The use ratio of high cost polyphenylene oxide is greatly lowered, and has high price advantage;
The physical property of product compares current material raising, and cost performance is high;
In production process, volatile organic matter (VOC) is greatly lowered, high environment friendly;
Secondary recovery is convenient, and antistatic property conservation rate is high when recycling is processed;
Improve production efficiency.
Description of the drawings
Fig. 1 is that a kind of New Antistatic Materials of the present invention fill Cost comparisons' figure of anti-static material with conventional carbon black.
Fig. 2 is that a kind of New Antistatic Materials of the present invention fill the intensity contrast figure of anti-static material with conventional carbon black.
Fig. 3 is that a kind of New Antistatic Materials of the present invention fill the high temperature resistant comparison of anti-static material with conventional carbon black
Figure.
Specific implementation mode
The specific implementation mode of the present invention is described further below in conjunction with the accompanying drawings.It should be noted that for
The explanation of these embodiments is used to help understand the present invention, but does not constitute limitation of the invention.In addition, disclosed below
The each embodiment of the present invention in involved technical characteristic can be combined with each other as long as they do not conflict with each other.
A kind of preparation method of New Antistatic Materials:
Anti-static material proposed by the present invention substitutes some Imported material with domestic raw material, product cost is greatly lowered,
And be modified by activeness and quietness, properties of product increase on existing anti-static material.Its formula is:Polyphenylene oxide 20 parts~30
Part, 620 parts~30 parts of nylon, 0~5 part of toughener, 0~5 part of compatilizer, 10 parts~30 parts of glass fibre, carbon nanotube master batch
10 parts~20 parts, 0~0.5 part of antioxidant, 0~0.5 part of lubricant.
It weighs up that each component is spare according to formula constituent, by other raw materials in addition to glass fibre, puts into blender together,
It is dried under the conditions of 140 DEG C, after 2~3H of stirring, it is spare to be discharged to turnover box;Be arranged production equipment temperature at 260~290 DEG C,
The raw material being stirred is through double screw extruder melt blending, extrusion, check rod, pelletizing up to product.
As shown in Figure 1-Figure 3, the performance comparison figure of New Antistatic Materials and conventional carbon black filling anti-static material;
Compatilizer, the selection of toughener and dosage are conducive to improve the physical property of product;
The dosage of nylon 6, glass fibre utilizes raising cost performance;
Carbon nanotube replaces conductive black energy conservation and environmental protection.
Embodiments of the present invention are explained in detail above in association with attached drawing, but the present invention is not limited to described implementations
Mode.For a person skilled in the art, in the case where not departing from the principle of the invention and spirit, to these embodiments
A variety of change, modification, replacement and modification are carried out, are still fallen in protection scope of the present invention.
Claims (1)
1. a kind of preparation method of New Antistatic Materials, includes the following steps:
The formula proportion of the New Antistatic Materials is:
It weighs up that each component is spare according to formula constituent, by other raw materials in addition to glass fibre, puts into blender together,
It is dried under the conditions of 140 DEG C, after 2~3H of stirring, it is spare to be discharged to turnover box;
Production equipment temperature is set at 260~290 DEG C, the raw material that has been stirred through double screw extruder melt blending, squeeze out, lead
Item, pelletizing are up to product.