CN108410237A - A kind of the Galfan alloys anticorrosive additive and anti-decaying paint of addition graphene - Google Patents
A kind of the Galfan alloys anticorrosive additive and anti-decaying paint of addition graphene Download PDFInfo
- Publication number
- CN108410237A CN108410237A CN201810261131.3A CN201810261131A CN108410237A CN 108410237 A CN108410237 A CN 108410237A CN 201810261131 A CN201810261131 A CN 201810261131A CN 108410237 A CN108410237 A CN 108410237A
- Authority
- CN
- China
- Prior art keywords
- paint
- graphene
- additive
- galfan
- zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of the Galfan alloy anticorrosive additive and anti-decaying paint of addition graphene, each component is as follows according to weight percent in the additive:Aluminium 46, zinc 94 95, graphene 0.5 1, other impurities≤0.5;Wherein, the other impurities are the metal and/or nonmetallic inclusion element that cannot thoroughly remove during preparing the additive.The anti-decaying paint includes the Galfan alloy anticorrosive additive of priming paint and above-mentioned addition graphene, and the priming paint is one kind in epoxy primer, the inorganic priming paint of alcohol-soluble and aqueous inorganic priming paint;This case improves film apparent property by controlling the grain size of powdery paints, to reach uniform coating thickness, the purpose of appearance good leveling property, coating is not easily to fall off.In the anti-decaying paint of this case, the synergistic effect between graphene and Zn Al elements is made full use of, anti-corrosion primer corrosion resistance is effectively improved.
Description
Technical field
The present invention relates to a kind of metal surface heavy antisepsis additive and anti-decaying paint, more particularly to a kind of addition graphene
Galfan alloy additions and anti-decaying paint.
Background technology
Zinc rich paint has cathodic protection effect due to being rich in zinc powder, to steel substrate, therefore is preferred anti-corrosive primer.Zinc-rich
Priming paint is in terms of anticorrosion of steel structure, at present mainly by three important kinds:Epoxy zinc rich primer, alcohol-soluble zinc-rich coating and
Waterborne inorganic einc-rich primer.
Zinc rich primer is current corrosion of steel structure and most-often used one of the anti-corrosion primer in protection field, which has excellent
Long-effective corrosion performance and good mechanical performance, can be mating with a variety of upper coatings.Zinc-rich bottom on domestic and international market at present
Paint is all made of spherical zinc powder as filler, and the dosage of spherical zinc powder accounts for 60% or more of zinc-rich paint formula.How zinc-rich is reduced
The dosage and wear rate of zinc powder in priming paint, are the important research contents of anti-corrosion industry.
In zinc rich primer film, zinc primarily serves cathodic protection effect, must contain a large amount of zinc fine particles in dry film,
They must contact with each other and keep good contact that could form galvanic circle with base material.But high zinc powder in zinc rich primer
Content also brings along a series of problem.Main problem is:1 zinc content is high, and the compactness of paint film declines, and can influence coating
Water resistance, adhesive force and impact resistance etc..2, production, storage and transportation of the high zinc content to zinc rich primer in zinc rich primer
And construction etc. brings inconvenience.For metallic zinc when producing and preparing coating, stably dispersing is more difficult, during storage
It easy tos produce and serious sinks to the bottom phenomenon.3, the steel substrate containing zinc rich primer can be due to the height in priming paint in welding and cutting
Zinc content will produce a large amount of zinc fume, endanger the health of staff.
The inert graphene of sheet is New Two Dimensional nano material, has excellent electric conductivity, physical mechanical property and right
The shielding properties of hydrone, air.Using the superpower electric conductivity of graphene microchip and superhigh intensity and the cathode of zinc powder is combined to protect
Shield is applied to anticorrosive paint, and after construction solidification, the graphene in paint film mutually overlaps the " graphene+zinc-formed with zinc powder
Aluminium powder " conductive film, the conductive film generate synergistic effect, both may be used using the zinc powder in the good electric conductivity activation coating of graphene
Zinc powder dosage in paint film is greatly reduced, the content of zinc powder only has 30% or so in traditional zinc rich primer, and paint film can be improved
Cathodic protection acts on, and shows superior antiseptic property and matching performance.
Therefore, it is that traditional anticorrosive paint upgrades using graphene microchip new material as the anticorrosive paint of critical material
Product, be a significant technology innovation of anticorrosive paint, have boundless application space
Galfan alloy be the 1970s Centre De Recherches Metallurgiques of Belgium developed under the support of international lead zinc tissue
Coating alloy, be mainly Zn-Al- with its ingredient with hot dip(Rare-earth elements La+Ce)(mass fraction).Galfan alloys
With replacement coating the features such as its low melting point, good corrosion resistance and suitable for wire galvanization.
Galfan coated articles would generally be bent, knot in practical applications, and the craze of coating thus caused can serious shadow
The corrosion resistance for ringing coating, to influence the service life of product, Galfan coated articles are only applicable in and the hot dip of steel wire wire rod,
To the finished product of steel construction, hot dip can not be taken.
Invention content
In order to solve the above-mentioned technical problem, the first object of the present invention is to provide a kind of Galfan alloys of graphene-containing
Anticorrosive additive;The second object of the present invention is to provide the anti-decaying paint added with the anticorrosive additive.
In order to realize that the first purpose of foregoing invention, the present invention use following first technical solution:
A kind of Galfan alloy anticorrosive additive of addition graphene, the group of following weight percent is contained in the additive
Part:
Aluminium 4-6%,
Zinc 94-95%,
Graphene 0.5-1%,
Other impurities≤0.5%;
Wherein, the other impurities are the metal that cannot thoroughly remove and/or nonmetallic during preparing the additive
Impurity element, the metal and nonmetallic inclusion element include sulphur, iron, chromium, copper, cadmium and crystalline flake graphite.
In above-mentioned first technical solution, it is in powder shaped to have choosing, the additive, and grain size is in 500-6000 mesh models
In enclosing.
In order to realize that the second purpose of foregoing invention, the present invention use following second technical solution:A kind of anti-decaying paint, this is anti-
Rotten enamel-cover includes the addition graphene in the preferred embodiment of priming paint and above-mentioned first technical solution or the first technical solution
Galfan alloy anticorrosive additives, the priming paint are one in epoxy primer, the inorganic priming paint of alcohol-soluble and aqueous inorganic priming paint
Kind.
In above-mentioned second technical solution, it is preferred that the Galfan alloy anticorrosive additives of the addition graphene
Additive amount is calculated as with the total weight percent of the anti-decaying paint:13.5-22.5%.
The present invention obtains following advantageous effect compared with prior art:Improved by controlling the grain size of powdery paints
Film apparent property, to reach uniform coating thickness, the purpose of appearance good leveling property, coating is not easily to fall off.This case is prevented
In corruption paint, the synergistic effect between graphene and Zn-Al elements is made full use of, anti-corrosion primer corrosion resistance is effectively improved.
Specific implementation mode
Invention is not limited to these embodiments, under the enlightenment of disclosure of the present invention made by it is any variation also all fall
In the range of the claims in the present invention are protected.
Embodiment 1
The parts by weight of a kind of Galfan alloy anticorrosive additives of graphene-containing, component and each component are:
500 mesh aluminium powders 4.5,
500 mesh zinc powders 95,
Graphene-ethanol solution 50 that mass percent concentration is 1%;
It after stirring ultrasound, filters, drying is ground into 500 mesh powder shapes.
Embodiment 2
The parts by weight of a kind of Galfan alloy anticorrosive additives of graphene-containing, component and each component are:
1000 mesh aluminium powders 5,
1000 mesh zinc powders 94,
Graphene-ethanol solution 100 that mass percent concentration is 1%;
It after stirring ultrasound, filters, drying is ground into 1000 mesh powder shapes.
Embodiment 3
The parts by weight of a kind of Galfan alloy anticorrosive additives of graphene-containing, component and each component are:
3000 mesh aluminium powders 5,
3000 mesh zinc powders 94,
Mass percent concentration is graphene-ethanol solution 100;
It after stirring ultrasound, filters, drying is ground into 3000 mesh powder shapes.
Embodiment 4
The parts by weight of a kind of Galfan alloy anticorrosive additives of graphene-containing, component and each component are:
6000 mesh aluminium powders 5,
6000 mesh zinc powders 94,
Mass percent concentration is 1% graphene-ethanol solution 100;
It after stirring ultrasound, filters, drying is ground into 6000 mesh powder shapes.
Embodiment 5
The Galfan alloy anticorrosive additives of graphene-containing that is prepared by above-described embodiment 1, being ground into 500 mesh powder shapes
It is 15% according to weight percent, is added in epoxy resin, the epoxy resin graphene that additive amount is 15% is prepared and is modified
Galfan alloy anti-decaying paints.
Embodiment 6
The Galfan alloys anticorrosive additive of graphene-containing prepared by above-described embodiment 4 adds according to weight percent 22.5
Enter into epoxy resin, the epoxy resin graphene that additive amount is 22.5% is prepared and is modified Galfan alloy anti-decaying paints.
According to the brushing technique of zinc-riched epoxy anti-decaying paint, respectively on galvanized sheet iron brushing zinc content be 45% routine
The anti-decaying paint that zinc-riched epoxy paint and embodiment 5,6 obtain, brushing thickness are 100 microns.After brushing, solidification respectively obtains
Sample 1,2,3.
Above-mentioned sample 1,2,3 is respectively put into salt fog machine, in 5% sodium chloride solution salt spray test 1000 hours, from outer
It observes in portion:The sample 1 of conventional zinc-riched epoxy paint is brushed, squeegee section has the white point being corroded;The ring that brushing additive amount is 15%
Oxygen resin graphene is modified the sample 2 of Galfan alloy anti-decaying paints, squeegee section any surface finish, the white point not being corroded;It applies
The epoxy resin graphene that brush additive amount is 22.5% is modified the sample 3 of Galfan alloy anti-decaying paints, and squeegee section surface is also protected
Hold bright and clean, not to be corroded white point.Therefore, the Galfan alloy anticorrosive additive for adding graphene can make full use of graphite
Synergistic effect between alkene and Zn-Al elements effectively improves anti-corrosion primer corrosion resistance.
The above embodiments merely illustrate the technical concept and features of the present invention, is to allow person skilled in the art can
Understand present disclosure and implement according to this, it is not intended to limit the scope of the present invention.It is all according to spirit of that invention institute
The equivalent change or modification of work, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of Galfan alloy anticorrosive additive of addition graphene, which is characterized in that containing as follows in the additive
The component of weight percent:
Aluminium 4-6%,
Zinc 94-95%,
Graphene 0.5-1%,
Other impurities≤0.5%;
Wherein, the other impurities are the metal that cannot be thoroughly removed during preparing the additive and/or nonmetallic
Impurity element, the metal and nonmetallic inclusion element include sulphur, iron, chromium, copper, cadmium and crystalline flake graphite.
2. according to a kind of Galfan alloy anticorrosive additives of addition graphene described in claim 1, which is characterized in that
The additive is in powder shaped, and grain size is within the scope of 500-6000 mesh.
3. a kind of anti-decaying paint, it is characterised in that:The anti-decaying paint includes the addition graphite in priming paint and the claims 1 or 2
The Galfan alloy anticorrosive additives of alkene, the priming paint are epoxy primer, the inorganic priming paint of alcohol-soluble and aqueous inorganic priming paint
In one kind.
4. according to the anti-decaying paint described in claim 1, it is characterised in that:The Galfan alloys of the addition graphene are anti-
The additive amount of rotten additive is calculated as with the total weight percent of the anti-decaying paint:13.5-22.5%.