CN108410038A - One kind being suitable for wood plastic injection molding material formula - Google Patents
One kind being suitable for wood plastic injection molding material formula Download PDFInfo
- Publication number
- CN108410038A CN108410038A CN201810240191.7A CN201810240191A CN108410038A CN 108410038 A CN108410038 A CN 108410038A CN 201810240191 A CN201810240191 A CN 201810240191A CN 108410038 A CN108410038 A CN 108410038A
- Authority
- CN
- China
- Prior art keywords
- injection molding
- plastic injection
- wood plastic
- molding material
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides one kind and being suitable for wood plastic injection molding material formula, is made of following raw material：Acrylonitrile-butadiene rubber powder, zinc borate, zinc oxide, high density polyethylene (HDPE), talcum powder, paraffin, calcium stearate, aniline, compared with prior art, the present invention have following advantageous effect：Using recyclable regenerative, environmental protection, and the injected plastics material to novel wooden injected plastics material of the human body without any injury instead of tradition based on plastics, raw material is cheap and easy to get, can increase the intensity on moulding surface, prevent surface from having cut.
Description
Technical field
The present invention is that one kind being suitable for wood plastic injection molding material formula, belongs to injection molding technology field.
Background technology
Many injecting products currently on the market are mainly with injected plastics materials such as styrene, makrolon and polystyrene
Formed, these materials on the one hand contain many harmful chemical components, health can be damaged, another aspect cost compared with
Height cannot recycle, and be difficult to degrade after discarding, and can cause serious environmental pollution.
Invention content
In view of the deficienciess of the prior art, it is an object of the present invention to provide one kind being suitable for wood plastic injection molding material formula, with
Solve the problems mentioned above in the background art.
To achieve the goals above, the present invention is to realize by the following technical solutions：One kind being suitable for wooden injection molding
Material prescription is made of following raw material：It is acrylonitrile-butadiene rubber powder, zinc borate, zinc oxide, high density polyethylene (HDPE), talcum powder, paraffin, hard
Resin acid calcium, aniline.
Further, it after zinc ingot metal made from electrolysis being heated to 600~700 DEG C of meltings, is placed in high-temperature crucible, makes
1250~1300 DEG C of high temperature under fusion and gasification, import hot-air and aoxidized, the zinc oxide of generation through cooling, cyclonic separation,
Fine particle is trapped with cloth bag, obtains the zinc oxide in raw material.
Further, the paraffin is a kind of semi-refined paraffin wax extracted from the distillate of oil or shale oil.
Further, stearic acid is dissolved in the hot water of 20 times of quality, the soda bath of content saturation is added, in environment temperature
Saponification is carried out in the case of 75 DEG C of degree, generates dilute sodium stearate solution, then the calcium chloride that content is 1074kg/m3 is molten
Liquid is added in sodium stearate solution, metathesis reaction is carried out in the case of 65 DEG C of environment temperature, product calcium stearate is with heavy
Precipitation goes out, and is then dried to get the calcium stearate in raw material through filtering, washing, in the case of 90 DEG C of environment temperature.
Further, nitrobenzene, solution of ferrous chloride and the iron filings that grind are added in batch reactor, at 100 DEG C
It is reacted under counterflow condition, being neutralized with lime for subsequent interval is sent to separator, and water phase, organic phase and oxidation iron cement are divided into
Slurry, organic phase are siphoned off, and obtain the aniline in raw material by stripping, distillation process.
Beneficial effects of the present invention：One kind of the present invention being suitable for wood plastic injection molding material formula, using recyclable regenerative, ring
It protects, and the injected plastics material to novel wooden injected plastics material of the human body without any injury instead of tradition based on plastics, raw material
It is cheap and easy to get, the intensity on moulding surface can be increased, prevent surface from having cut.
Specific implementation mode
To make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, with reference to
Specific implementation mode, the present invention is further explained.
The present invention provides a kind of technical solution：One kind being suitable for wood plastic injection molding material formula, is made of following raw material：Butyronitrile
Rubber powder, zinc borate, zinc oxide, high density polyethylene (HDPE), talcum powder, paraffin, calcium stearate, aniline.
After zinc ingot metal made from electrolysis is heated to 600~700 DEG C of meltings, it is placed in high-temperature crucible, it is allowed to 1250~
Fusion and gasification under 1300 DEG C of high temperature imports hot-air and is aoxidized, and the zinc oxide of generation is through cooling, cyclonic separation, by fine particle
It is trapped with cloth bag, obtains the zinc oxide in raw material.
Paraffin is a kind of semi-refined paraffin wax extracted from the distillate of oil or shale oil.
Stearic acid is dissolved in the hot water of 20 times of quality, the soda bath of content saturation is added, in 75 DEG C of environment temperature
In the case of carry out saponification, generate dilute sodium stearate solution, then the calcium chloride solution that content is 1074kg/m3 is added to
In sodium stearate solution, metathesis reaction is carried out in the case of 65 DEG C of environment temperature, product calcium stearate is with Precipitation, so
By filtering, washing, in the case of 90 DEG C of environment temperature it is dry, up to the calcium stearate in raw material.
Nitrobenzene, solution of ferrous chloride and the iron filings that grind are added in batch reactor, under 100 DEG C of counterflow conditions
It is reacted, being neutralized with lime for subsequent interval is sent to separator, and water phase, organic phase and iron oxide mud, organic phase quilt are divided into
It siphons off, and the aniline in raw material is obtained by stripping, distillation process.
As an embodiment of the present invention：One kind of the present invention being suitable for wood plastic injection molding material formula, using recyclable
Regeneration, environmental protection, and the injected plastics material to novel wooden injected plastics material of the human body without any injury instead of tradition based on plastics,
Its raw material is cheap and easy to get, can increase the intensity on moulding surface, prevent surface from having cut.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from the present invention spirit or
In the case of essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that come within the meaning and range of equivalency of the claims in the present invention
It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (5)
1. one kind being suitable for wood plastic injection molding material formula, it is characterised in that：It is made of following raw material：Acrylonitrile-butadiene rubber powder, zinc borate,
Zinc oxide, high density polyethylene (HDPE), talcum powder, paraffin, calcium stearate, aniline.
2. according to claim 1 a kind of suitable for wood plastic injection molding material formula, it is characterised in that：Made from electrolysis
After zinc ingot metal is heated to 600~700 DEG C of meltings, it is placed in high-temperature crucible, is allowed to fusion and gasification under 1250~1300 DEG C of high temperature, leads
Enter hot-air to be aoxidized, fine particle is trapped with cloth bag, obtained in raw material through cooling, cyclonic separation by the zinc oxide of generation
Zinc oxide.
3. according to claim 1 a kind of suitable for wood plastic injection molding material formula, it is characterised in that：The paraffin is one kind
From the semi-refined paraffin wax extracted in the distillate of oil or shale oil.
4. according to claim 1 a kind of suitable for wood plastic injection molding material formula, it is characterised in that：Stearic acid is dissolved in 20
In the hot water of times quality, the soda bath of content saturation is added, carries out saponification in the case of 75 DEG C of environment temperature, generates
Dilute sodium stearate solution, then the calcium chloride solution that content is 1074kg/m3 is added in sodium stearate solution, in environment temperature
Metathesis reaction is carried out in the case of 65 DEG C of degree, product calcium stearate is with Precipitation, then through filtering, washing, in environment temperature
It is dry in the case of 90 DEG C of degree, up to the calcium stearate in raw material.
5. according to claim 1 a kind of suitable for wood plastic injection molding material formula, it is characterised in that：By nitrobenzene, chlorination
Ferrous iron solution and the iron filings ground are added in batch reactor, are reacted under 100 DEG C of counterflow conditions, the use of subsequent interval
Lime neutralizes, and send to separator, is divided into water phase, organic phase and iron oxide mud, and organic phase is siphoned off, and by stripping,
Distillation process obtains the aniline in raw material.