CN108409284A - A kind of novel magnesium oxychloride plank - Google Patents
A kind of novel magnesium oxychloride plank Download PDFInfo
- Publication number
- CN108409284A CN108409284A CN201810390034.4A CN201810390034A CN108409284A CN 108409284 A CN108409284 A CN 108409284A CN 201810390034 A CN201810390034 A CN 201810390034A CN 108409284 A CN108409284 A CN 108409284A
- Authority
- CN
- China
- Prior art keywords
- parts
- plank
- magnesium oxychloride
- novel magnesium
- magnesia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of novel magnesium oxychloride plank, includes following component by weight percentage：12 25 parts of magnesium chloride, 6 12 parts of talcum powder, 30 45 parts of magnesia, 69 parts of iron oxide red, 4 11 parts of reinforcing fiber, 5 10 parts of latex powder, 12 18 parts of epsom salt, 8 15 parts of light calcined magnesia.The novel magnesium oxychloride plank stuff production technology of the present invention is simple, advantageously reduces the production cost of novel magnesium oxychloride plank, achieves preferable economic benefit, while also helping the popularization and application of novel magnesium oxychloride plank.
Description
Technical field
The present invention relates to a kind of plank more particularly to a kind of novel magnesium oxychloride planks.
Background technology
Chlorination magnesium sheet material is a kind of building board, with relatively broad application field, can be used as the outer of building
Plaque also can be used as the plank of interior decoration in building.However, existing magnesium chloride board cost is higher, and preparation process
Complexity is unfavorable for reducing the cost of construction.Therefore, in view of the above-mentioned problems, it is necessary to propose further solution.
Invention content
The purpose of the present invention is to provide a kind of novel magnesium oxychloride planks, to overcome the deficiencies in the prior art.
For achieving the above object, the present invention provides a kind of novel magnesium oxychloride plank, includes such as by weight percentage
Lower component：12-25 parts of magnesium chloride, 6-12 parts of talcum powder, 30-45 parts of magnesia, 6-9 parts of iron oxide red, 4-11 parts of reinforcing fiber,
5-10 parts of latex powder, 12-18 parts of epsom salt, 8-15 parts of light calcined magnesia；
Based on each component as above, the novel magnesium oxychloride plank is prepared as follows：
S1,12-25 parts of magnesium chloride, 6-12 parts of talcum powder, 30-45 parts of magnesia, 6-9 parts of iron oxide red, enhancing fibre are weighed
4-11 parts of dimension, after each raw material weighed are sufficiently stirred, obtains the mixture of each raw material, mixture is carried out secondary stir
It mixes, until it forms the first slurry of paste；
S2,5-10 parts of latex powder, 12-18 parts of epsom salt, 8-15 parts of light calcined magnesia, each former material that will be weighed are weighed
After material is sufficiently stirred, the mixture of each raw material is obtained, mixture is subjected to secondary agitation, until it forms the second slurry of paste
Material；
S3, the ABS templates that two sides is sprayed with releasing agent are provided, the slurry of the first paste of acquisition is coated on the ABS
The slurry of second paste is coated on the another side of the ABS templates by the one side of template；
S4, after dry tack free, in the upper covering non-woven fabrics of ABS templates, and roll forming；
Plank after S5, roll forming carries out in 35-45 DEG C of temperature, the environment of humidity 80-90% after static 1-2 days
Demoulding.
The improvement of novel magnesium oxychloride plank as the present invention, the novel magnesium oxychloride plank include such as by weight percentage
Lower component：12 parts of magnesium chloride, 6 parts of talcum powder, 30 parts of magnesia, 6 parts of iron oxide red, 4 parts of reinforcing fiber, 5 parts of latex powder, seven water
13 parts of magnesium sulfate, 9 parts of light calcined magnesia, remaining is diatomite.
The improvement of novel magnesium oxychloride plank as the present invention, the novel magnesium oxychloride plank include such as by weight percentage
Lower component：12 parts of magnesium chloride, 8 parts of talcum powder, 32 parts of magnesia, 6 parts of iron oxide red, 5 parts of reinforcing fiber, 6 parts of latex powder, seven water
14 parts of magnesium sulfate, 10 parts of light calcined magnesia, remaining is the mixture of aluminium oxide and silica.
The improvement of novel magnesium oxychloride plank as the present invention, the novel magnesium oxychloride plank include such as by weight percentage
Lower component：12 parts of magnesium chloride, 6 parts of talcum powder, 32 parts of magnesia, 6 parts of iron oxide red, 6 parts of reinforcing fiber, 6 parts of latex powder, seven water
13 parts of magnesium sulfate, 10 parts of light calcined magnesia, remaining is the mixture of activated carbon and flyash.
The improvement of novel magnesium oxychloride plank as the present invention, the releasing agent are saponification oils releasing agent.
The improvement of novel magnesium oxychloride plank as the present invention, the plank after roll forming, in 38 DEG C of temperature, humidity 85%
Environment in demoulded after static 1.5 days.
The improvement of novel magnesium oxychloride plank as the present invention, the plank after roll forming, in 40 DEG C of temperature, humidity 82%
Environment in demoulded after static 1.2 days.
The improvement of novel magnesium oxychloride plank as the present invention, the plank after roll forming, in 41 DEG C of temperature, humidity 83%
Environment in demoulded after static 1.1 days.
Compared with prior art, the beneficial effects of the invention are as follows：The novel magnesium oxychloride plank stuff production technology of the present invention is simple,
The production cost for advantageously reducing novel magnesium oxychloride plank achieves preferable economic benefit, while also helping novel chlorine oxygen
The popularization and application of magnesium sheet material.
Specific implementation mode
With reference to specific embodiment, the present invention is described in detail, but it should explanation, these embodiment party
Formula is not limitation of the present invention, and those of ordinary skill in the art are according to function, method or knot made by these embodiments
Equivalent transformation on structure or replacement, all belong to the scope of protection of the present invention within.
The present invention provides a kind of novel magnesium oxychloride plank, includes following component by weight percentage：Magnesium chloride 12-25
Part, 6-12 parts of talcum powder, 30-45 parts of magnesia, 6-9 parts of iron oxide red, 4-11 parts of reinforcing fiber, 5-10 parts of latex powder, seven water
12-18 parts of magnesium sulfate, 8-15 parts of light calcined magnesia；
Based on each component as above, the novel magnesium oxychloride plank is prepared as follows：
S1,12-25 parts of magnesium chloride, 6-12 parts of talcum powder, 30-45 parts of magnesia, 6-9 parts of iron oxide red, enhancing fibre are weighed
4-11 parts of dimension, after each raw material weighed are sufficiently stirred, obtains the mixture of each raw material, mixture is carried out secondary stir
It mixes, until it forms the first slurry of paste；
S2,5-10 parts of latex powder, 12-18 parts of epsom salt, 8-15 parts of light calcined magnesia, each former material that will be weighed are weighed
After material is sufficiently stirred, the mixture of each raw material is obtained, mixture is subjected to secondary agitation, until it forms the second slurry of paste
Material；
S3, the ABS templates that two sides is sprayed with releasing agent are provided, the slurry of the first paste of acquisition is coated on the ABS
The slurry of second paste is coated on the another side of the ABS templates by the one side of template；
S4, after dry tack free, in the upper covering non-woven fabrics of ABS templates, and roll forming；
Plank after S5, roll forming carries out in 35-45 DEG C of temperature, the environment of humidity 80-90% after static 1-2 days
Demoulding.
In one embodiment, novel magnesium oxychloride plank of the invention includes following component by weight percentage：Chlorination
12 parts of magnesium, 6 parts of talcum powder, 30 parts of magnesia, 6 parts of iron oxide red, 4 parts of reinforcing fiber, 5 parts of latex powder, 13 parts of epsom salt,
9 parts of light calcined magnesia, remaining is diatomite.
At this point, being based on each component as above, the novel magnesium oxychloride plank is prepared as follows：
S1,12 parts of magnesium chloride, 6 parts of talcum powder, 30 parts of magnesia, 6 parts of iron oxide red, 4 parts of reinforcing fiber are weighed, will weighed
Each raw material be sufficiently stirred after, obtain the mixture of each raw material, mixture be subjected to secondary agitation, until its formed paste
The first slurry；
S2,5 parts of latex powder, 13 parts of epsom salt, 9 parts of light calcined magnesia are weighed, each raw material weighed is fully stirred
After mixing, the mixture of each raw material is obtained, mixture is subjected to secondary agitation, until it forms the second slurry of paste；
S3, the ABS templates that two sides is sprayed with releasing agent are provided, the slurry of the first paste of acquisition is coated on the ABS
The slurry of second paste is coated on the another side of the ABS templates by the one side of template；
S4, after dry tack free, in the upper covering non-woven fabrics of ABS templates, and roll forming；
Plank after S5, roll forming is demoulded in 38 DEG C of temperature, the environment of humidity 85% after static 1.5 days.
In another embodiment, novel magnesium oxychloride plank of the invention includes following component by weight percentage：Chlorine
Change 12 parts of magnesium, 8 parts of talcum powder, 32 parts of magnesia, 6 parts of iron oxide red, 5 parts of reinforcing fiber, 6 parts of latex powder, epsom salt 14
Part, 10 parts of light calcined magnesia, remaining is the mixture of aluminium oxide and silica.
At this point, being based on each component as above, the novel magnesium oxychloride plank is prepared as follows：
S1,12 parts of magnesium chloride, 8 parts of talcum powder, 32 parts of magnesia, 6 parts of iron oxide red, 5 parts of reinforcing fiber are weighed, will weighed
Each raw material be sufficiently stirred after, obtain the mixture of each raw material, mixture be subjected to secondary agitation, until its formed paste
The first slurry；
S2,6 parts of latex powder, 15 parts of epsom salt, 10 parts of light calcined magnesia are weighed, each raw material weighed is fully stirred
After mixing, the mixture of each raw material is obtained, mixture is subjected to secondary agitation, until it forms the second slurry of paste；
S3, the ABS templates that two sides is sprayed with releasing agent are provided, the slurry of the first paste of acquisition is coated on the ABS
The slurry of second paste is coated on the another side of the ABS templates by the one side of template；
S4, after dry tack free, in the upper covering non-woven fabrics of ABS templates, and roll forming；
Plank after S5, roll forming is demoulded in 40 DEG C of temperature, the environment of humidity 82% after static 1.2 days.
In yet another embodiment, novel magnesium oxychloride plank of the invention includes following component by weight percentage：Chlorine
Change 12 parts of magnesium, 6 parts of talcum powder, 32 parts of magnesia, 6 parts of iron oxide red, 6 parts of reinforcing fiber, 6 parts of latex powder, epsom salt 13
Part, 10 parts of light calcined magnesia, remaining is the mixture of activated carbon and flyash.
At this point, being based on each component as above, the novel magnesium oxychloride plank is prepared as follows：
S1,12 parts of magnesium chloride, 6 parts of talcum powder, 32 parts of magnesia, 6 parts of iron oxide red, 6 parts of reinforcing fiber are weighed, will weighed
Each raw material be sufficiently stirred after, obtain the mixture of each raw material, mixture be subjected to secondary agitation, until its formed paste
The first slurry；
S2,6 parts of latex powder, 13 parts of epsom salt, 10 parts of light calcined magnesia are weighed, each raw material weighed is fully stirred
After mixing, the mixture of each raw material is obtained, mixture is subjected to secondary agitation, until it forms the second slurry of paste；
S3, the ABS templates that two sides is sprayed with releasing agent are provided, the slurry of the first paste of acquisition is coated on the ABS
The slurry of second paste is coated on the another side of the ABS templates by the one side of template；
S4, after dry tack free, in the upper covering non-woven fabrics of ABS templates, and roll forming；
Plank after S5, roll forming is demoulded in 41 DEG C of temperature, the environment of humidity 83% after static 1.1 days.
In conclusion the novel magnesium oxychloride plank stuff production technology of the present invention is simple, novel magnesium oxychloride plank is advantageously reduced
Production cost, achieve preferable economic benefit, while also helping the popularization and application of novel magnesium oxychloride plank.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (8)
1. a kind of novel magnesium oxychloride plank, which is characterized in that the novel magnesium oxychloride plank includes such as the following group by weight percentage
Point：12-25 parts of magnesium chloride, 6-12 parts of talcum powder, 30-45 parts of magnesia, 6-9 parts of iron oxide red, 4-11 parts of reinforcing fiber, latex
5-10 parts of powder, 12-18 parts of epsom salt, 8-15 parts of light calcined magnesia；
Based on each component as above, the novel magnesium oxychloride plank is prepared as follows：
S1,12-25 parts of magnesium chloride, 6-12 parts of talcum powder, 30-45 parts of magnesia, 6-9 parts of iron oxide red, reinforcing fiber 4- are weighed
11 parts, after each raw material weighed are sufficiently stirred, the mixture of each raw material is obtained, mixture is subjected to secondary agitation, directly
The first slurry of paste is formed to it；
S2,5-10 parts of latex powder, 12-18 parts of epsom salt, 8-15 parts of light calcined magnesia are weighed, each raw material weighed is filled
After dividing stirring, the mixture of each raw material is obtained, mixture is subjected to secondary agitation, until it forms the second slurry of paste；
S3, the ABS templates that two sides is sprayed with releasing agent are provided, the slurry of the first paste of acquisition is coated on the ABS templates
One side, by the slurry of the second paste be coated on the ABS templates another side；
S4, after dry tack free, in the upper covering non-woven fabrics of ABS templates, and roll forming；
Plank after S5, roll forming is demoulded in 35-45 DEG C of temperature, the environment of humidity 80-90% after static 1-2 days.
2. novel magnesium oxychloride plank according to claim 1, which is characterized in that the novel magnesium oxychloride plank by weight hundred
Divide than including following component：12 parts of magnesium chloride, 6 parts of talcum powder, 30 parts of magnesia, 6 parts of iron oxide red, 4 parts of reinforcing fiber, latex
5 parts of powder, 13 parts of epsom salt, 9 parts of light calcined magnesia, remaining is diatomite.
3. novel magnesium oxychloride plank according to claim 1, which is characterized in that the novel magnesium oxychloride plank by weight hundred
Divide than including following component：12 parts of magnesium chloride, 8 parts of talcum powder, 32 parts of magnesia, 6 parts of iron oxide red, 5 parts of reinforcing fiber, latex
6 parts of powder, 14 parts of epsom salt, 10 parts of light calcined magnesia, remaining is the mixture of aluminium oxide and silica.
4. novel magnesium oxychloride plank according to claim 1, which is characterized in that the novel magnesium oxychloride plank by weight hundred
Divide than including following component：12 parts of magnesium chloride, 6 parts of talcum powder, 32 parts of magnesia, 6 parts of iron oxide red, 6 parts of reinforcing fiber, latex
6 parts of powder, 13 parts of epsom salt, 10 parts of light calcined magnesia, remaining is the mixture of activated carbon and flyash.
5. novel magnesium oxychloride plank according to claim 1, which is characterized in that the releasing agent demoulds for saponification oils
Agent.
6. novel magnesium oxychloride plank according to claim 1, which is characterized in that the plank after roll forming, in temperature 38
DEG C, it is demoulded after static 1.5 days in the environment of humidity 85%.
7. novel magnesium oxychloride plank according to claim 1, which is characterized in that the plank after roll forming, in temperature 40
DEG C, it is demoulded after static 1.2 days in the environment of humidity 82%.
8. novel magnesium oxychloride plank according to claim 1, which is characterized in that the plank after roll forming, in temperature 41
DEG C, it is demoulded after static 1.1 days in the environment of humidity 83%.