A kind of high whiteness cigarette pack cast-coated paperboard of unstressed configuration and preparation method thereof
Technical field
The invention belongs to cigarette pack paperboard fields, and in particular to the cigarette of the unstressed configuration Gao Bai of coating method production
Pack paperboard and preparation method thereof field.
Background technology
The paperboard for being used for cigarette packaging currently on the market is usually the unstressed configuration raw white coated white cardboard of 215-250g/ ㎡,
For whiteness no more than 80% (generally in 75%-78%), eye sight whiteness is lower, and milky, Wu Faman is presented in printing product background color
The requirement of the high whiteness of foot (whiteness is more than 83%) exquisite printing, also useful above-mentioned paperboard is processed into as base stock currently on the market
For the method and product of cast-coated paperboard, but since this highlight coating is transparent material, product whiteness can not continue to improve.
Also the high white glass paperboard of useful unstressed configuration produces (whiteness is in 83%-85%) for cigarette packet on existing market, but should
Product has the following problems, due to being to carry out unstressed configuration dyeing in paper pulp and coating in paper-making process to brighten if in paper
Dyeing, which is brightened, in slurry is brightened form and aspect by PH difference slurry colorings and different slurry kind there are greatest differences.It cannot be simultaneously to paper pulp
Middle difference slurry is brightened or the paper of multilayer difference pulp production carries out unstressed configuration and brightens, but the production of cigarette packet paperboard is adopted
With three kinds or more different pulp varieties, at least four-layer structure produces.Therefore existing product can only be carried out uniformly with a kind of slurry
It brightens, causes product to be deformed in printing process very big, printing difficulty is high, yield rate bottom 5- compared with normal cigarette card product
8%, deflection and the low 30-40% compared with quantitative similar cigarette card, upper cigarette packing machine packet cigarette molding effect is poor, low production efficiency,
It is influenced by the pH value of slurry and coating, the factors such as content of beary metal when due to being brightened in paper pulp, the aberration of batch is larger, makes
Product can not fully meet the requirement of cigarette packet paperboard.
In addition in the prior art, brighten in paper pulp or coating in unstressed configuration brighten there are coloring agent tinctorial yield is low, waste water
In have a large amount of dye solutions, cause pulping wastewater treatment of high cost and PH of the tinctorial yield in by slurry, content of beary metal
Influence causes to brighten unstable, larger difference occur, and this method improves under the premise of without fluorescent whitening agent
Whiteness is only 3-5%.
Prior art, which also has, produces the high art post paperboard (85% or more) containing fluorescent whitening agent by coating waste water mode
As cast-coated paperboard, to adapt to exquisite printing.But since the product uses fluorescent whitening agent to improve whiteness, it is not used to perfume (or spice)
Cigarette packaging (cigarette packet paperboard requires to be forbidden to use fluorescent whitening agent).
The prior art also has the face layer whiteness that cigarette card is improved using one layer of titanium dioxide of coating, although and using rubbing method
Whiteness is improved under the premise of without fluorescent whitening agent, but due to keeping the folding strength of paperboard big after being coated on original cigarette cardboard
Width reduces, and occurs a large amount of quick-fried black phenomenons after causing product to print when packet cigarette, and cannot be used for cigarette packet.
Invention content
It is excellent it is an object of the invention to solve at least the above and/or defect, and provide at least to will be described later
Point.
In order to realize these purposes and other advantages according to the present invention, a kind of high whiteness cigarette packets of unstressed configuration are provided
Glaze paperboard, including:
Base's paperboard;
Printing layer, is located at base's paperboard top surface, and being coated with printing layer in the printing layer brightens coating;
Bottom surface layer, is located at base's paperboard bottom surface, and the bottom surface layer is coated with bottom and brightens coating thereon;
High photosphere is located on the printing layer, transparent high-gloss paint is coated on the high photosphere.
Preferably, wherein the printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:0-10%, alkali blue:0-10%, transparent red:0-5%, transparent blue:0-15%, basic yellow:0-
30%, transparent yellow:0-30%, wetting agent:0.2-1.3% infilters agent:0.1-5%, levelling agent:0.3-5%, color fixing agent:
0.7-8%, water:0-100%, ethyl alcohol:0-100%, ethyl acetate:0-50%, two butanol:2-15%, silicone oil:0.1-
1.2%;
The bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:0-10%, acid blue:0-20%, Indian yellow:0-30%, solvent red:0-2%, solvent blue:0-
15%, solvent yellow:0-30%, wetting agent:1-1.3%, bleeding agent:0.5-5%, white ink:0-30%, titanium dioxide:2-
10%, color fixing agent:0.5-10%, ethyl acetate:0-30%, two butanol:1-20%, silicone oil:0.05-0.8%, acrylic acid tree
Fat:0-35%;
The raw material of the transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:0-85%, ethylene-vinyl acetate copolymer emulsion:0-50%, methylcellulose:0-30%, third
Olefin(e) acid lotion:0-100%, water-based gloss oil:Aqueous silicone oil is shifted in 0-100%, coating:0.5-20%, styrene-butadiene emulsion:0-50%.
Preferably, wherein the raw material during the printing layer brightens coating, bottom brightens coating and transparent high-gloss paint
It forms and further includes:Antifoaming agent:0.5-2%, rheological agent:1-3%, dispersant 1-5%, antioxidant 2-10%, tackifier:
1-5%, water-soluble ageing resistance agent 1-2%.
Preferably, wherein the printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:8%, alkali blue:8%, transparent red:5%, transparent blue:10%, basic yellow:15%, transparent yellow:
15%, wetting agent:1%, infilter agent:3%, levelling agent:4%, color fixing agent:3%, water:5%, ethyl alcohol:5%, ethyl acetate:
5%, two butanol:5.8%, silicone oil:1.2%, antifoaming agent:1.2%, rheological agent:1.8%, dispersant 1%, antioxidant
0.5%, tackifier:1.2%, water-soluble ageing resistance agent 0.3%;
The bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:7%, acid blue:7%, Indian yellow:7%, solvent red:2%, solvent blue:10%, solvent yellow:15%,
Wetting agent:1.2%, bleeding agent:3.8%, white ink:5%, titanium dioxide:8%, color fixing agent:5%, ethyl acetate:2%, two
Butanol:6%, silicone oil:0.8%, acrylic resin:9.2%, antifoaming agent:1.1%, rheological agent:1.7%, dispersant 3% resists
Oxidant 1.2%, tackifier:1.8%, water-soluble ageing resistance agent 1.2%;
The raw material of the transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:12.6%, ethylene-vinyl acetate copolymer emulsion:10%, methylcellulose:12.5%, propylene
Yogurt liquid:25.4%, water-based gloss oil:15.9%, aqueous silicone oil is shifted in coating:1.5%, styrene-butadiene emulsion:12.4%, antifoaming agent:
2%, rheological agent:3%, dispersant 2%, antioxidant 1%, tackifier:2%, water-soluble ageing resistance agent 0.7%.
Preferably, wherein the wetting agent is:Any one in tween -12, Tween-20 or Tween-40;
The levelling agent is:Any one in paregal O -20, peregal O-25 or paregal O S15;
The color fixing agent is cation-type water-thinned polyurethane color fixing agent;
The bleeding agent is:Polyoxyethylene ether is selected from alkyl polyoxyethylene ether, aliphatic acid polyethenoxy ether or poly alkyl alcohol
Any one in ethylene oxide ether;
The group of the dispersant becomes:1-2 parts by weight α-methacrylic acid, 2-5 parts by weight propylene amide, 3-15 weight
Part sodium acrylate, 20 parts by weight water and 10 parts of w ethanols;
The group of the antioxidant becomes:1-2 parts by weight diphenylamines, 1-2 parts by weight p-phenylenediamine, 1-2 parts by weight dihydros
The ethanol water of quinoline, 10 parts by weight 85%;
The group of the tackifier becomes:4 parts of vinylsiloxanes and 3 parts of epoxy radical siloxanes;
The group of the water-soluble ageing resistance agent becomes:30-40 part by weight of liquid paraffin, 10-15 parts by weight of phosphoric acid tri butyl ester,
20-25 parts by weight lauryl sodium sulfate, 10-20 parts by weight hydroxyethyl cellulose, 10-20 parts of 5-8 parts by weight sodium metasilicate, 50
The water of parts by weight.
The present invention also provides a kind of preparation methods of the high whiteness cigarette pack cast-coated paperboard of unstressed configuration, include the following steps:
Step 1: base's paperboard is put into the machine of broadcasting, the tension for broadcasting machine is then right between 2.1-4.8N
The printing layer of base's paperboard carries out sided corona treatment, then heats base's paperboard bottom surface layer, the heating roller with heating roller
Temperature control at 130-140 DEG C, base's paperboard bottom surface layer is heated to 110-120 DEG C, the voltage of the sided corona treatment
For 20-35kV, electric current 15-20A;
It is packed into coating feeding roller Step 2: the bottom is first brightened coating, then will handle and complete in step 1 again
Base's paperboard be placed on and carry out bottom under coating feeding roller and brighten the feeding operation of coating, wait for being sent to after the completion of feeding dry
It is dry in dry channel, after to be dried, then base's paperboard is placed in progress printing layer under coating feeding roller and brightens the upper of coating
Expect operation, wherein the cable on the coating feeding roller is 170 lines, and depth is 25 μm, pressure 0.35Mpa;The drying is logical
The drying temperature in road is 155 DEG C, and hot wind wind pressure is 0.02-0.1Mpa;The cable of the coating feeding roller surface is 200 lines, deep
25 μm of degree, pressure 0.25Mpa;
Step 3: applying one layer thoroughly using coating transfer method or rubbing method to the base's paperboard for handling completion in step 2
High photosphere is formed on bright high-gloss paint to the printing layer of base's paperboard, to prepare cast-coated paperboard.
Preferably, wherein the rubbing method in the step 3 includes the following steps:
Step A, base's paperboard that processing is completed is put into the machine of broadcasting, the printing for broadcasting machine by base's paperboard
Face is sent under the airblade coating roller that the steel wire that thickness is 0.3-0.5mm includes cutter painting cloth rewinder roll or air pressure is 0.2-0.35Mpa and is applied
Cloth operation, coating weight 15-20g/m2, the tension force of base's paperboard is between 2.3-4.2N;
Step B, it is put into dry channel to the base's paperboard for completing step A to be dried, drying temperature is adjusted to
150 DEG C, to be dried after the completion again into using mirror roller to carry out light to paperboard, 100-110 DEG C of the temperature of the mirror roller rises
Light pressure 0.4-0.6Mpa, then complete to wind.
Preferably, wherein the coating transfer method in the step 3 includes the following steps:
The base's paperboard handled is put into the machine of broadcasting by step I, is sent into composite roll by the machine of broadcasting, described
Machine is broadcasted by the tension force of base's paperboard between 2.8-6.3N;
Step II will be put into the machine of broadcasting for shifting the PET transfer membranes of transparent high-gloss paint, and the machine of broadcasting turns PET
The tension force of film is moved between 1.3-2.0N, then the PET transfer membranes are sent into upper glue roller by the machine of broadcasting, it is described on
Rubber roller is glued using 150 mesh anilox rolls, high optical cement is coated on PET transfer membranes, coating weight 6-8g/m2, then will coating
PET transfer membranes after the completion are re-fed into composite roll and the printing surface of base paperboard is compound, composite pressure 0.2-0.4Mpa, will
Paperboard after compound, which is re-fed into drying machine, to be dried, and drying temperature is 100-110 DEG C;
Step III, step II is dried after paperboard on PET transfer film strippings, peel angle is 25-30 °, final to make
At cast-coated paperboard.
Preferably, wherein the preparation method that the bottom brightens coating is:
Step a, acid red is injected in solvent red, Indian yellow is injected in solvent yellow, acid blue is injected into solvent blue
In, then three kinds of mixed liquors are put into ultrasonic vibration machine and rock uniform, three kinds of uniform mixtures then will be rocked and all injects
In high-speed inks oscillator, the frequency of the ultrasonic vibration machine is:25000-40000 hertz;
Step b, the high-speed inks oscillator in starting step a, and white ink is constantly added into blender,
Ethyl acetate, two butanol, silicone oil, acrylic resin, the vibration frequency of the high-speed inks oscillator about 500-1000 times/
Minute;
Step c, the mixture by the completion shaken in step b is transferred in blender, and titanium white is added into blender
Powder, wetting agent, bleeding agent, color fixing agent, antifoaming agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent, directly
Become bottom that is uniform, stablizing to all substances in the blender and brighten coating, the mixing speed of the blender exists
300-500 revs/min of kind.
The present invention includes at least following advantageous effect:Materials and methods provided by the invention can (whiteness be not by base material paperboard
More than high white glass paperboard 80%) is produced under conditions of without using fluorescent whitening agent, the present invention uses the printing of special formula
Layer brightens coating, bottom brightens coating, transparent high-gloss paint and antifoaming agent, rheological agent, dispersant, antioxidant viscosify
Agent, water-soluble ageing resistance agent make its printing layer whiteness be increased to 84-87% by 78-80%, and bottom whiteness is increased to by 75-85%
82-93%, and increase permeability and the brightness of transparent high-gloss paint, so that the whiteness of entire paperboard is improved.
Part is illustrated to embody by further advantage, target and the feature of the present invention by following, and part will also be by this
The research and practice of invention and be understood by the person skilled in the art.
Description of the drawings:
Fig. 1 is subbing and printing layer in the high whiteness cigarette pack cast-coated paperboard preparation method of unstressed configuration of the present invention
The feeding process flow chart of coating;
Fig. 2 be the present invention the high whiteness cigarette pack cast-coated paperboard preparation method of unstressed configuration in high photosphere rubbing method work
Skill flow chart;
Fig. 3 shifts for the coating of high photosphere in the high whiteness cigarette pack cast-coated paperboard preparation method of unstressed configuration of the present invention
Method process flow chart.
Specific implementation mode:
Present invention will be described in further detail below with reference to the accompanying drawings, to enable those skilled in the art with reference to specification
Word can be implemented according to this.
It should be appreciated that such as " having ", "comprising" and " comprising " term used herein do not allot one or more
The presence or addition of a other elements or combinations thereof.
Embodiment 1:
A kind of high whiteness cigarette pack cast-coated paperboard of unstressed configuration, including:
Base's paperboard;
Printing layer, is located at base's paperboard top surface, and being coated with printing layer in the printing layer brightens coating;
Bottom surface layer, is located at base's paperboard bottom surface, and the bottom surface layer is coated with bottom and brightens coating thereon;
High photosphere is located on the printing layer, transparent high-gloss paint is coated on the high photosphere;
Printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:9%, alkali blue:9%, transparent red:6%, transparent blue:11%, basic yellow:15%, transparent yellow:
15%, wetting agent:1%, infilter agent:3%, levelling agent:6%, color fixing agent:3%, water:5%, ethyl alcohol:5%, ethyl acetate:
5%, two butanol:5.8%, silicone oil:1.2%;
Bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:7%, acid blue:7%, Indian yellow:7%, solvent red:2%, solvent blue:10%, solvent yellow:20%,
Wetting agent:1.2%, bleeding agent:3.8%, white ink:5%, titanium dioxide:8%, color fixing agent:6%, ethyl acetate:3%, two
Butanol:7%, silicone oil:1.8%, acrylic resin:11.2%;
The raw material of transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:12.3%, ethylene-vinyl acetate copolymer emulsion:15%, methylcellulose:12.5%, propylene
Yogurt liquid:25.4%, water-based gloss oil:15.9%, aqueous silicone oil is shifted in coating:6.5%, styrene-butadiene emulsion:12.4%;
Wherein, the wetting agent is:Tween-20;
The levelling agent is:Paregal O S15;
The color fixing agent is cation-type water-thinned polyurethane color fixing agent;
The bleeding agent is:Aliphatic acid polyethenoxy ether;
The preparation method that the printing layer brightens coating is:
Step a, acid red is injected in solvent red, Indian yellow is injected in solvent yellow, acid blue is injected into solvent blue
In, then three kinds of mixed liquors are put into ultrasonic vibration machine and rock uniform, three kinds of uniform mixtures then will be rocked and all injects
In high-speed inks oscillator, the frequency of the ultrasonic vibration machine is:40000 hertz;
Step b, the high-speed inks oscillator in starting step a, and white ink is constantly added into blender,
Ethyl acetate, two butanol, silicone oil, acrylic resin, the vibration frequency of the high-speed inks oscillator is about at 500 beats/min;
Step c, the mixture by the completion shaken in step b is transferred in blender, and titanium white is added into blender
Powder, wetting agent, bleeding agent, color fixing agent brighten painting until all substances in the blender become bottom that is uniform, stablizing
Material, the mixing speed of the blender is in 450 revs/min of kinds;
The preparation method of the high whiteness cigarette pack cast-coated paperboard of unstressed configuration, including:Step 1: base's paperboard is put
Entering to broadcast in machine, then the tension for broadcasting machine carries out sided corona treatment in 2.6N to the printing layer of base's paperboard, then
Base's paperboard bottom surface layer is heated with heating roller, the temperature of the heating roller is controlled at 135 DEG C, by base's paperboard bottom
Face layer is heated to 119 DEG C, and the voltage of the sided corona treatment is 30kV, electric current 17A;
It is packed into coating feeding roller Step 2: the bottom is first brightened coating, then will handle and complete in step 1 again
Base's paperboard be placed on and carry out bottom under coating feeding roller and brighten the feeding operation of coating, wait for being sent to after the completion of feeding dry
It is dry in dry channel, after to be dried, then base's paperboard is placed in progress printing layer under coating feeding roller and brightens the upper of coating
Expect operation, wherein the cable on the coating feeding roller is 170 lines, and depth is 25 μm, pressure 0.35Mpa;The drying is logical
The drying temperature in road is 155 DEG C, and hot wind wind pressure is 0.04Mpa;The cable of the coating feeding roller surface is 200 lines, depth 25
μm, pressure 0.25Mpa;
Step 3: applying layer of transparent high-gloss paint extremely using rubbing method to the base's paperboard for handling completion in step 2
High photosphere is formed in the printing layer of base's paperboard;
Wherein, rubbing method includes the following steps:
Step A, base's paperboard that processing is completed is put into the machine of broadcasting, the printing for broadcasting machine by base's paperboard
Face is sent under the airblade coating roller that the steel wire that thickness is 0.32mm includes cutter painting cloth rewinder roll or air pressure is 0.25Mpa and is coated operation,
Coating weight is 15g/m2, the tension force of base's paperboard is in 2.3N;
Step B, it is put into dry channel to the base's paperboard for completing step A to be dried, drying temperature is adjusted to
150 DEG C, to be dried after the completion again into using mirror roller to carry out light to paperboard, 102 DEG C of the temperature of the mirror roller plays optical pressure
Power 0.4Mpa, then complete winding and prepare cast-coated paperboard;
By paperboard prepared by this embodiment, it is in the result by the test of whiteness instrument:Printing layer whiteness 84%, bottom are white
Degree 82%.
Embodiment 2:
A kind of high whiteness cigarette pack cast-coated paperboard of unstressed configuration, including:
Base's paperboard;
Printing layer, is located at base's paperboard top surface, and being coated with printing layer in the printing layer brightens coating;
Bottom surface layer, is located at base's paperboard bottom surface, and the bottom surface layer is coated with bottom and brightens coating thereon;
High photosphere is located on the printing layer, transparent high-gloss paint is coated on the high photosphere;
Printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:9%, alkali blue:9%, transparent red:4%, transparent blue:9%, basic yellow:17%, transparent yellow:17%,
Wetting agent:1%, infilter agent:1%, levelling agent:3%, color fixing agent:4%, water:3%, ethyl alcohol:10%, ethyl acetate:5%, two
Butanol:5.8%, silicone oil:2.2%;
Bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:10%, acid blue:10%, Indian yellow:8%, solvent red:4%, solvent blue:9%00, solvent yellow:
14%, wetting agent:4.2%, bleeding agent:5.8%, white ink:4%, titanium dioxide:9%, color fixing agent:4%, ethyl acetate:
2.5%, two butanol:6.5%, silicone oil:0.8%, acrylic resin:8.2%;
The raw material of transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:18.6%, ethylene-vinyl acetate copolymer emulsion:13%, methylcellulose:14.5%, propylene
Yogurt liquid:26.4%, water-based gloss oil:13.6%, aqueous silicone oil is shifted in coating:1.5%, styrene-butadiene emulsion:12.4%;
Wherein, the wetting agent is:Tween-20;
The levelling agent is:Peregal O-25;
The color fixing agent is cation-type water-thinned polyurethane color fixing agent;
The bleeding agent is:Fatty alcohol polyoxyethylene ether;
The preparation method that the printing layer brightens coating is:
Step a, acid red is injected in solvent red, Indian yellow is injected in solvent yellow, acid blue is injected into solvent blue
In, then three kinds of mixed liquors are put into ultrasonic vibration machine and rock uniform, three kinds of uniform mixtures then will be rocked and all injects
In high-speed inks oscillator, the frequency of the ultrasonic vibration machine is:35000 hertz;
Step b, the high-speed inks oscillator in starting step a, and white ink is constantly added into blender,
Ethyl acetate, two butanol, silicone oil, acrylic resin, the vibration frequency of the high-speed inks oscillator is about at 650 beats/min;
Step c, the mixture by the completion shaken in step b is transferred in blender, and titanium white is added into blender
Powder, wetting agent, bleeding agent, color fixing agent brighten painting until all substances in the blender become bottom that is uniform, stablizing
Material, the mixing speed of the blender is in 450 revs/min of kinds;
The preparation method of the high whiteness cigarette pack cast-coated paperboard of unstressed configuration, which is characterized in that include the following steps:
Step 1: base's paperboard is put into the machine of broadcasting, the tension for broadcasting machine is in 2.6N, then to the base
The printing layer of paperboard carries out sided corona treatment, then heats base's paperboard bottom surface layer, the temperature control of the heating roller with heating roller
System is heated to 120 DEG C at 135 DEG C, by base's paperboard bottom surface layer, and the voltage of the sided corona treatment is 30kV, and electric current is
16A;
It is packed into coating feeding roller Step 2: the bottom is first brightened coating, then will handle and complete in step 1 again
Base's paperboard be placed on and carry out bottom under coating feeding roller and brighten the feeding operation of coating, wait for being sent to after the completion of feeding dry
It is dry in dry channel, after to be dried, then base's paperboard is placed in progress printing layer under coating feeding roller and brightens the upper of coating
Expect operation, wherein the cable on the coating feeding roller is 170 lines, and depth is 25 μm, pressure 0.35Mpa;The drying is logical
The drying temperature in road is 155 DEG C, and hot wind wind pressure is 0.08Mpa;The cable of the coating feeding roller surface is 200 lines, depth 25
μm, pressure 0.27Mpa;
It is applied Step 3: applying layer of transparent bloom using coating transfer method to the base's paperboard for handling completion in step 2
High photosphere is formed in material to the printing layer of base's paperboard;
Wherein, the coating transfer method includes the following steps:
The base's paperboard handled is put into the machine of broadcasting by step I, is sent into composite roll by the machine of broadcasting, described
Machine is broadcasted by the tension force of base's paperboard in 5N;
Step II will be put into the machine of broadcasting for shifting the PET transfer membranes of transparent high-gloss paint, and the machine of broadcasting turns PET
The tension force of film is moved in 2.5N, then the PET transfer membranes are sent into upper glue roller by the machine of broadcasting, and the upper glue roller uses
150 mesh anilox rolls glue, and high optical cement are coated on PET transfer membranes, coating weight 7g/m2, then will be after the completion of coating
PET transfer membranes are re-fed into composite roll and the printing surface of base paperboard is compound, composite pressure 0.26Mpa, will be compound after paperboard
It is re-fed into drying machine and is dried, drying temperature is 110 DEG C;
Step III, step II is dried after paperboard on PET transfer film stripping, peel angle be 30 °, be finally made
Cast-coated paperboard;
By paperboard prepared by this embodiment, it is in the result by the test of whiteness instrument:Printing layer whiteness 85%, bottom are white
Degree 83%.
Embodiment 3:
A kind of high whiteness cigarette pack cast-coated paperboard of unstressed configuration, including:
Base's paperboard;
Printing layer, is located at base's paperboard top surface, and being coated with printing layer in the printing layer brightens coating;
Bottom surface layer, is located at base's paperboard bottom surface, and the bottom surface layer is coated with bottom and brightens coating thereon;
High photosphere is located on the printing layer, transparent high-gloss paint is coated on the high photosphere;
Printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:10%, alkali blue:10%, transparent red:6%, transparent blue:10%, basic yellow:15%, transparent yellow:
15%, wetting agent:2%, infilter agent:1%, levelling agent:2%, color fixing agent:4%, water:3%, ethyl alcohol:11%, ethyl acetate:
6%, two butanol:2.8%, silicone oil:1.2%;
Bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:8.2%, acid blue:9%, Indian yellow:6%, solvent red:2.8%, solvent blue:7%, solvent yellow:
16%, wetting agent:4.2%, bleeding agent:7.7%, white ink:6.1%, titanium dioxide:9%, color fixing agent:4%, acetic acid second
Ester:3.5%, two butanol:7.5%, silicone oil:0.8%, acrylic resin:8.2%;
The raw material of transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:13%, ethylene-vinyl acetate copolymer emulsion:16.6%, methylcellulose:11.5%, propylene
Yogurt liquid:27.5%, water-based gloss oil:18.8%, aqueous silicone oil is shifted in coating:1.5%, styrene-butadiene emulsion:11.1%;
Wherein, the wetting agent is:Tween-40;
The levelling agent is:Peregal O-25;
The color fixing agent is cation-type water-thinned polyurethane color fixing agent;
The bleeding agent is:Fatty alcohol polyoxyethylene ether;
The preparation method that the printing layer brightens coating is:
Step a, acid red is injected in solvent red, Indian yellow is injected in solvent yellow, acid blue is injected into solvent blue
In, then three kinds of mixed liquors are put into ultrasonic vibration machine and rock uniform, three kinds of uniform mixtures then will be rocked and all injects
In high-speed inks oscillator, the frequency of the ultrasonic vibration machine is:40000 hertz;
Step b, the high-speed inks oscillator in starting step a, and white ink is constantly added into blender,
Ethyl acetate, two butanol, silicone oil, acrylic resin, the vibration frequency of the high-speed inks oscillator is about at 750 beats/min;
Step c, the mixture by the completion shaken in step b is transferred in blender, and titanium white is added into blender
Powder, wetting agent, bleeding agent, color fixing agent brighten painting until all substances in the blender become bottom that is uniform, stablizing
Material, the mixing speed of the blender is in 550 revs/min of kinds;
The preparation method of the high whiteness cigarette pack cast-coated paperboard of unstressed configuration, which is characterized in that include the following steps:
Step 1: base's paperboard is put into the machine of broadcasting, then the tension for broadcasting machine blocks the base in 3N
The printing layer of paper carries out sided corona treatment, then heats base's paperboard bottom surface layer, the temperature control of the heating roller with heating roller
At 135 DEG C, base's paperboard bottom surface layer is heated to 120 DEG C, the voltage of the sided corona treatment is 30kV, electric current 16A;
It is packed into coating feeding roller Step 2: the bottom is first brightened coating, then will handle and complete in step 1 again
Base's paperboard be placed on and carry out bottom under coating feeding roller and brighten the feeding operation of coating, wait for being sent to after the completion of feeding dry
It is dry in dry channel, after to be dried, then base's paperboard is placed in progress printing layer under coating feeding roller and brightens the upper of coating
Expect operation, wherein the cable on the coating feeding roller is 170 lines, and depth is 25 μm, pressure 0.35Mpa;The drying is logical
The drying temperature in road is 155 DEG C, and hot wind wind pressure is 0.08Mpa;The cable of the coating feeding roller surface is 200 lines, depth 25
μm, pressure 0.27Mpa;
It is applied Step 3: applying layer of transparent bloom using coating transfer method to the base's paperboard for handling completion in step 2
High photosphere is formed in material to the printing layer of base's paperboard;
Wherein, the coating transfer method includes the following steps:
The base's paperboard handled is put into the machine of broadcasting by step I, is sent into composite roll by the machine of broadcasting, described
Machine is broadcasted by the tension force of base's paperboard in 5N;
Step II will be put into the machine of broadcasting for shifting the PET transfer membranes of transparent high-gloss paint, and the machine of broadcasting turns PET
The tension force of film is moved in 2.5N, then the PET transfer membranes are sent into upper glue roller by the machine of broadcasting, and the upper glue roller uses
150 mesh anilox rolls glue, and high optical cement are coated on PET transfer membranes, coating weight 7g/m2, then will be after the completion of coating
PET transfer membranes are re-fed into composite roll and the printing surface of base paperboard is compound, composite pressure 0.26Mpa, will be compound after paperboard
It is re-fed into drying machine and is dried, drying temperature is 110 DEG C;
Step III, step II is dried after paperboard on PET transfer film stripping, peel angle be 30 °, be finally made
Cast-coated paperboard;
By paperboard prepared by this embodiment, it is in the result by the test of whiteness instrument:Printing layer whiteness 83%, bottom are white
Degree 85%.
Embodiment 4:
A kind of high whiteness cigarette pack cast-coated paperboard of unstressed configuration, including:
Base's paperboard;
Printing layer, is located at base's paperboard top surface, and being coated with printing layer in the printing layer brightens coating;
Bottom surface layer, is located at base's paperboard bottom surface, and the bottom surface layer is coated with bottom and brightens coating thereon;
High photosphere is located on the printing layer, transparent high-gloss paint is coated on the high photosphere;
The printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:8%, alkali blue:8%, transparent red:5%, transparent blue:10%, basic yellow:15%, transparent yellow:
15%, wetting agent:1%, infilter agent:3%, levelling agent:4%, color fixing agent:3%, water:5%, ethyl alcohol:5%, ethyl acetate:
5%, two butanol:5.8%, silicone oil:1.2%, antifoaming agent:1.2%, rheological agent:1.8%, dispersant 1%, antioxidant
0.5%, tackifier:1.2%, water-soluble ageing resistance agent 0.3%;
The bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:7%, acid blue:7%, Indian yellow:7%, solvent red:2%, solvent blue:10%, solvent yellow:15%,
Wetting agent:1.2%, bleeding agent:3.8%, white ink:5%, titanium dioxide:8%, color fixing agent:5%, ethyl acetate:2%, two
Butanol:6%, silicone oil:0.8%, acrylic resin:9.2%, antifoaming agent:1.1%, rheological agent:2.7%, dispersant 3% resists
Oxidant 1.2%, tackifier:1.8%, water-soluble ageing resistance agent 1.2%;
The raw material of the transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:15.6%, ethylene-vinyl acetate copolymer emulsion:13%, methylcellulose:12.5%, propylene
Yogurt liquid:25.4%, water-based gloss oil:8.9%, aqueous silicone oil is shifted in coating:1.5%, styrene-butadiene emulsion:12.4%, antifoaming agent:
2%, rheological agent:2.5%, dispersant 2.5%, antioxidant 1%, tackifier:1.9%, water-soluble ageing resistance agent 0.8%;
The wetting agent is:Tween -12;
The levelling agent is:Paregal O -20;
The color fixing agent is cation-type water-thinned polyurethane color fixing agent;
The bleeding agent is:Polyoxyethylene ether is selected from alkyl polyoxyethylene ether;
The group of the dispersant becomes:1 parts by weight α-methacrylic acid, 2 parts by weight propylene amides, 3 parts by weight of acrylic acid
Sodium, 20 parts by weight water and 10 parts of w ethanols;
The group of the antioxidant becomes:1 parts by weight diphenylamines, 1 parts by weight p-phenylenediamine, 2 parts by weight dihydroquinoline, 8
The ethanol water of parts by weight 85%;
The group of the tackifier becomes:4 parts of vinylsiloxanes and 3 parts of epoxy radical siloxanes;
The group of the water-soluble ageing resistance agent becomes:30 part by weight of liquid paraffin, 10 parts by weight of phosphoric acid tri butyl esters, 25 weight
The water of part lauryl sodium sulfate, 15 parts by weight hydroxyethyl celluloses, 10 parts of 5 parts by weight sodium metasilicate, 50 parts by weight;
The preparation method that the printing layer brightens coating is:
Step a, acid red is injected in solvent red, Indian yellow is injected in solvent yellow, acid blue is injected into solvent blue
In, then three kinds of mixed liquors are put into ultrasonic vibration machine and rock uniform, three kinds of uniform mixtures then will be rocked and all injects
In high-speed inks oscillator, the frequency of the ultrasonic vibration machine is:40000 hertz;
Step b, the high-speed inks oscillator in starting step a, and white ink is constantly added into blender,
Ethyl acetate, two butanol, silicone oil, acrylic resin, the vibration frequency of the high-speed inks oscillator is about at 500 beats/min;
Step c, the mixture by the completion shaken in step b is transferred in blender, and titanium white is added into blender
Powder, wetting agent, bleeding agent, color fixing agent, antifoaming agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent, directly
Become bottom that is uniform, stablizing to all substances in the blender and brighten coating, the mixing speed of the blender exists
450 revs/min of kinds;
The preparation method of the high whiteness cigarette pack cast-coated paperboard of unstressed configuration, which is characterized in that include the following steps:
Step 1: base's paperboard is put into the machine of broadcasting, the tension for broadcasting machine is in 2.6N, then to the base
The printing layer of paperboard carries out sided corona treatment, then heats base's paperboard bottom surface layer, the temperature control of the heating roller with heating roller
System is heated to 119 DEG C at 135 DEG C, by base's paperboard bottom surface layer, and the voltage of the sided corona treatment is 30kV, and electric current is
17A;
It is packed into coating feeding roller Step 2: the bottom is first brightened coating, then will handle and complete in step 1 again
Base's paperboard be placed on and carry out bottom under coating feeding roller and brighten the feeding operation of coating, wait for being sent to after the completion of feeding dry
It is dry in dry channel, after to be dried, then base's paperboard is placed in progress printing layer under coating feeding roller and brightens the upper of coating
Expect operation, wherein the cable on the coating feeding roller is 170 lines, and depth is 25 μm, pressure 0.35Mpa;The drying is logical
The drying temperature in road is 155 DEG C, and hot wind wind pressure is 0.04Mpa;The cable of the coating feeding roller surface is 200 lines, depth 25
μm, pressure 0.25Mpa;
It is applied Step 3: applying layer of transparent bloom using coating transfer method to the base's paperboard for handling completion in step 2
High photosphere is formed in material to the printing layer of base's paperboard;
Wherein, rubbing method includes the following steps:
Step A, base's paperboard that processing is completed is put into the machine of broadcasting, the printing for broadcasting machine by base's paperboard
Face is sent under the airblade coating roller that the steel wire that thickness is 0.32mm includes cutter painting cloth rewinder roll or air pressure is 0.25Mpa and is coated operation,
Coating weight is 15g/m2, the tension force of base's paperboard is in 2.3N;
Step B, it is put into dry channel to the base's paperboard for completing step A to be dried, drying temperature is adjusted to
150 DEG C, to be dried after the completion again into using mirror roller to carry out light to paperboard, 102 DEG C of the temperature of the mirror roller plays optical pressure
Power 0.4Mpa, then complete winding and prepare cast-coated paperboard;
By paperboard prepared by this embodiment, defoaming is added since printing layer brightens coating, subbing, high photosphere
Agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent are printing layer in the result by the test of whiteness instrument
Whiteness 87%, bottom whiteness 90%, greatly improve the whiteness of paperboard, simultaneously because it uses PET transfer methods
The white luminance of paperboard can also be improved to a certain extent.
Embodiment 5:
A kind of high whiteness cigarette pack cast-coated paperboard of unstressed configuration, including:
Base's paperboard;
Printing layer, is located at base's paperboard top surface, and being coated with printing layer in the printing layer brightens coating;
Bottom surface layer, is located at base's paperboard bottom surface, and the bottom surface layer is coated with bottom and brightens coating thereon;
High photosphere is located on the printing layer, transparent high-gloss paint is coated on the high photosphere;
The printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:8.5%, alkali blue:8.5%, transparent red:4.5%, transparent blue:9.5%, basic yellow:16%, it is transparent
It is yellow:16%, wetting agent:1%, infilter agent:3%, levelling agent:4%, color fixing agent:3%, water:4.8%, ethyl alcohol:5.2%, acetic acid
Ethyl ester:5.5%, two butanol:5.3%, silicone oil:1.2%, antifoaming agent:1.2%, rheological agent:1.8%, dispersant 1%, antioxygen
Agent 0.5%, tackifier:1.2%, water-soluble ageing resistance agent 0.3%;
The bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:7.8%, acid blue:7.8%, Indian yellow:7.8%, solvent red:2.6%, solvent blue:9.2%, it is molten
Agent is yellow:14.2%, wetting agent:0.4%, bleeding agent:3%, white ink:5%, titanium dioxide:8%, color fixing agent:5%, acetic acid
Ethyl ester:2%, two butanol:5.4%, silicone oil:0.8%, acrylic resin:9.2%, antifoaming agent:1.1%, rheological agent:2.7%,
Dispersant 3%, antioxidant 1.2%, tackifier:1.8%, water-soluble ageing resistance agent 1.2%;
The raw material of the transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:15.6%, ethylene-vinyl acetate copolymer emulsion:13%, methylcellulose:12.5%, propylene
Yogurt liquid:25.4%, water-based gloss oil:8.9%, aqueous silicone oil is shifted in coating:1.5%, styrene-butadiene emulsion:12.4%, antifoaming agent:
2%, rheological agent:2.5%, dispersant 2.5%, antioxidant 1%, tackifier:1.9%, water-soluble ageing resistance agent 0.8%;
The wetting agent is:Tween-20;
The levelling agent is:Paregal O S15;
The color fixing agent is cation-type water-thinned polyurethane color fixing agent;
The bleeding agent is:Aliphatic acid polyethenoxy ether;
The group of the dispersant becomes:2 parts by weight α-methacrylic acids, 1.5 parts by weight propylene amides, 3 parts by weight propylene
Sour sodium, 10 parts by weight water and 10 parts of w ethanols;
The group of the antioxidant becomes:1.5 parts by weight diphenylamines, 1.5 parts by weight p-phenylenediamine, 2.5 parts by weight dihydros
The ethanol water of quinoline, 9 parts by weight 85%;
The group of the tackifier becomes:4 parts of vinylsiloxanes and 3 parts of epoxy radical siloxanes;
The group of the water-soluble ageing resistance agent becomes:35 part by weight of liquid paraffin, 10 parts by weight of phosphoric acid tri butyl esters, 25 weight
The water of part lauryl sodium sulfate, 15 parts by weight hydroxyethyl celluloses, 10 parts by weight sodium metasilicate, 50 parts by weight;
The preparation method that the printing layer brightens coating is:
Step a, acid red is injected in solvent red, Indian yellow is injected in solvent yellow, acid blue is injected into solvent blue
In, then three kinds of mixed liquors are put into ultrasonic vibration machine and rock uniform, three kinds of uniform mixtures then will be rocked and all injects
In high-speed inks oscillator, the frequency of the ultrasonic vibration machine is:35000 hertz;
Step b, the high-speed inks oscillator in starting step a, and white ink is constantly added into blender,
Ethyl acetate, two butanol, silicone oil, acrylic resin, the vibration frequency of the high-speed inks oscillator is about at 600 beats/min;
Step c, the mixture by the completion shaken in step b is transferred in blender, and titanium white is added into blender
Powder, wetting agent, bleeding agent, color fixing agent, antifoaming agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent, directly
Become bottom that is uniform, stablizing to all substances in the blender and brighten coating, the mixing speed of the blender exists
400 revs/min of kinds;
The preparation method of the high whiteness cigarette pack cast-coated paperboard of unstressed configuration, which is characterized in that include the following steps:
Step 1: base's paperboard is put into the machine of broadcasting, the tension for broadcasting machine is in 2.6N, then to the base
The printing layer of paperboard carries out sided corona treatment, then heats base's paperboard bottom surface layer, the temperature control of the heating roller with heating roller
System is heated to 120 DEG C at 135 DEG C, by base's paperboard bottom surface layer, and the voltage of the sided corona treatment is 30kV, and electric current is
16A;
It is packed into coating feeding roller Step 2: the bottom is first brightened coating, then will handle and complete in step 1 again
Base's paperboard be placed on and carry out bottom under coating feeding roller and brighten the feeding operation of coating, wait for being sent to after the completion of feeding dry
It is dry in dry channel, after to be dried, then base's paperboard is placed in progress printing layer under coating feeding roller and brightens the upper of coating
Expect operation, wherein the cable on the coating feeding roller is 170 lines, and depth is 25 μm, pressure 0.35Mpa;The drying is logical
The drying temperature in road is 155 DEG C, and hot wind wind pressure is 0.08Mpa;The cable of the coating feeding roller surface is 200 lines, depth 25
μm, pressure 0.27Mpa;
It is applied Step 3: applying layer of transparent bloom using coating transfer method to the base's paperboard for handling completion in step 2
High photosphere is formed in material to the printing layer of base's paperboard;
Wherein, rubbing method includes the following steps:
Step A, base's paperboard that processing is completed is put into the machine of broadcasting, the printing for broadcasting machine by base's paperboard
Face is sent under the airblade coating roller that the steel wire that thickness is 0.32mm includes cutter painting cloth rewinder roll or air pressure is 0.25Mpa and is coated operation,
Coating weight is 15g/m2, the tension force of base's paperboard is in 2.3N;
Step B, it is put into dry channel to the base's paperboard for completing step A to be dried, drying temperature is adjusted to
150 DEG C, to be dried after the completion again into using mirror roller to carry out light to paperboard, 102 DEG C of the temperature of the mirror roller plays optical pressure
Power 0.4Mpa, then complete winding and prepare cast-coated paperboard;
By paperboard prepared by this embodiment, defoaming is added since printing layer brightens coating, subbing, high photosphere
Agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent are printing layer in the result by the test of whiteness instrument
Whiteness 86%, bottom whiteness 89%, greatly improve the whiteness of paperboard, simultaneously because it uses PET transfer methods
The white luminance of paperboard can also be improved to a certain extent.
Embodiment 6:
A kind of high whiteness cigarette pack cast-coated paperboard of unstressed configuration, including:
Base's paperboard;
Printing layer, is located at base's paperboard top surface, and being coated with printing layer in the printing layer brightens coating;
Bottom surface layer, is located at base's paperboard bottom surface, and the bottom surface layer is coated with bottom and brightens coating thereon;
High photosphere is located on the printing layer, transparent high-gloss paint is coated on the high photosphere;
The printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:5.5%, alkali blue:5.5%, transparent red:7.5%, transparent blue:9.5%, basic yellow:16%, it is transparent
It is yellow:16%, wetting agent:4%, infilter agent:3%, levelling agent:4%, color fixing agent:3%, water:4.8%, ethyl alcohol:5.2%, acetic acid
Ethyl ester:5.5%, two butanol:5.3%, silicone oil:1.2%, antifoaming agent:1.2%, rheological agent:1.8%, dispersant 1%, antioxygen
Agent 0.5%, tackifier:1.2%, water-soluble ageing resistance agent 0.3%;
The bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:8.8%, acid blue:6.8%, Indian yellow:8.8%, solvent red:1.6%, solvent blue:9.2%, it is molten
Agent is yellow:14.2%, wetting agent:0.4%, bleeding agent:3%, white ink:5%, titanium dioxide:8%, color fixing agent:5%, acetic acid
Ethyl ester:2%, two butanol:5.4%, silicone oil:0.8%, acrylic resin:9.2%, antifoaming agent:1.1%, rheological agent:2.7%,
Dispersant 3%, antioxidant 1.2%, tackifier:1.8%, water-soluble ageing resistance agent 1.2%;
The raw material of the transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:15.6%, ethylene-vinyl acetate copolymer emulsion:13%, methylcellulose:12.5%, propylene
Yogurt liquid:25.4%, water-based gloss oil:8.9%, aqueous silicone oil is shifted in coating:1.5%, styrene-butadiene emulsion:12.4%, antifoaming agent:
2%, rheological agent:2.5%, dispersant 2.5%, antioxidant 1%, tackifier:1.9%, water-soluble ageing resistance agent 0.8%;
The wetting agent is:Tween-20;
The levelling agent is:Peregal O-25;
The color fixing agent is cation-type water-thinned polyurethane color fixing agent;
The bleeding agent is:Aliphatic acid polyethenoxy ether;
The group of the dispersant becomes:1.5 parts by weight α-methacrylic acids, 1.5 parts by weight propylene amides, 3 parts by weight third
Olefin(e) acid sodium, 15 parts by weight water and 10 parts of w ethanols;
The group of the antioxidant becomes:1.5 parts by weight diphenylamines, 1.5 parts by weight p-phenylenediamine, 2.5 parts by weight dihydros
The ethanol water of quinoline, 9 parts by weight 85%;
The group of the tackifier becomes:4 parts of vinylsiloxanes and 3 parts of epoxy radical siloxanes;
The group of the water-soluble ageing resistance agent becomes:40 part by weight of liquid paraffin, 10 parts by weight of phosphoric acid tri butyl esters, 25 weight
The water of part lauryl sodium sulfate, 15 parts by weight hydroxyethyl celluloses, 10 parts by weight sodium metasilicate, 50 parts by weight;
The preparation method that the printing layer brightens coating is:
Step a, acid red is injected in solvent red, Indian yellow is injected in solvent yellow, acid blue is injected into solvent blue
In, then three kinds of mixed liquors are put into ultrasonic vibration machine and rock uniform, three kinds of uniform mixtures then will be rocked and all injects
In high-speed inks oscillator, the frequency of the ultrasonic vibration machine is:35000 hertz;
Step b, the high-speed inks oscillator in starting step a, and white ink is constantly added into blender,
Ethyl acetate, two butanol, silicone oil, acrylic resin, the vibration frequency of the high-speed inks oscillator is about at 650 beats/min;
Step c, the mixture by the completion shaken in step b is transferred in blender, and titanium white is added into blender
Powder, wetting agent, bleeding agent, color fixing agent, antifoaming agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent, directly
Become bottom that is uniform, stablizing to all substances in the blender and brighten coating, the mixing speed of the blender exists
450 revs/min of kinds;
The preparation method of the high whiteness cigarette pack cast-coated paperboard of unstressed configuration, which is characterized in that include the following steps:
Step 1: base's paperboard is put into the machine of broadcasting, the tension for broadcasting machine is in 2.6N, then to the base
The printing layer of paperboard carries out sided corona treatment, then heats base's paperboard bottom surface layer, the temperature control of the heating roller with heating roller
System is heated to 120 DEG C at 135 DEG C, by base's paperboard bottom surface layer, and the voltage of the sided corona treatment is 30kV, and electric current is
16A;
It is packed into coating feeding roller Step 2: the bottom is first brightened coating, then will handle and complete in step 1 again
Base's paperboard be placed on and carry out bottom under coating feeding roller and brighten the feeding operation of coating, wait for being sent to after the completion of feeding dry
It is dry in dry channel, after to be dried, then base's paperboard is placed in progress printing layer under coating feeding roller and brightens the upper of coating
Expect operation, wherein the cable on the coating feeding roller is 170 lines, and depth is 25 μm, pressure 0.35Mpa;The drying is logical
The drying temperature in road is 155 DEG C, and hot wind wind pressure is 0.08Mpa;The cable of the coating feeding roller surface is 200 lines, depth 25
μm, pressure 0.27Mpa;
It is applied Step 3: applying layer of transparent bloom using coating transfer method to the base's paperboard for handling completion in step 2
High photosphere is formed in material to the printing layer of base's paperboard;
Wherein, the coating transfer method includes the following steps:
The base's paperboard handled is put into the machine of broadcasting by step I, is sent into composite roll by the machine of broadcasting, described
Machine is broadcasted by the tension force of base's paperboard in 5N;
Step II will be put into the machine of broadcasting for shifting the PET transfer membranes of transparent high-gloss paint, and the machine of broadcasting turns PET
The tension force of film is moved in 2.5N, then the PET transfer membranes are sent into upper glue roller by the machine of broadcasting, and the upper glue roller uses
150 mesh anilox rolls glue, and high optical cement are coated on PET transfer membranes, coating weight 7g/m2, then will be after the completion of coating
PET transfer membranes are re-fed into composite roll and the printing surface of base paperboard is compound, composite pressure 0.26Mpa, will be compound after paperboard
It is re-fed into drying machine and is dried, drying temperature is 110 DEG C;
Step III, step II is dried after paperboard on PET transfer film stripping, peel angle be 30 °, be finally made
Cast-coated paperboard;
By paperboard prepared by this embodiment, defoaming is added since printing layer brightens coating, subbing, high photosphere
Agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent are printing layer in the result by the test of whiteness instrument
Whiteness 88%, bottom whiteness 90%, greatly improve the whiteness of paperboard, simultaneously because it uses PET transfer methods
The white luminance of paperboard can also be improved to a certain extent.
Embodiment 7:
A kind of high whiteness cigarette pack cast-coated paperboard of unstressed configuration, including:
Base's paperboard;
Printing layer, is located at base's paperboard top surface, and being coated with printing layer in the printing layer brightens coating;
Bottom surface layer, is located at base's paperboard bottom surface, and the bottom surface layer is coated with bottom and brightens coating thereon;
High photosphere is located on the printing layer, transparent high-gloss paint is coated on the high photosphere;
The printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:6.5%, alkali blue:5.5%, transparent red:8.5%, transparent blue:10.5%, basic yellow:15%, thoroughly
Bright Huang:16%, wetting agent:4%, infilter agent:3%, levelling agent:4%, color fixing agent:3%, water:4.8%, ethyl alcohol:5.2%, second
Acetoacetic ester:5.5%, two butanol:5.3%, silicone oil:1.2%, antifoaming agent:1.2%, rheological agent:1.8%, dispersant 1% resists
Oxidant 0.5%, tackifier:1.2%, water-soluble ageing resistance agent 0.3%;
The bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:8.8%, acid blue:8.8%, Indian yellow:6.8%, solvent red:1.6%, solvent blue:9.2%, it is molten
Agent is yellow:14.2%, wetting agent:0.4%, bleeding agent:3%, white ink:5%, titanium dioxide:8%, color fixing agent:4%, acetic acid
Ethyl ester:3%, two butanol:7.4%, silicone oil:0.8%, acrylic resin:9.2%, antifoaming agent:1.1%, rheological agent:2.7%,
Dispersant 3%, antioxidant 1.2%, tackifier:1.8%, water-soluble ageing resistance agent 1.2%;
The raw material of the transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:15.6%, ethylene-vinyl acetate copolymer emulsion:13%, methylcellulose:12.5%, propylene
Yogurt liquid:25.4%, water-based gloss oil:8.9%, aqueous silicone oil is shifted in coating:1.5%, styrene-butadiene emulsion:12.4%, antifoaming agent:
2%, rheological agent:2.5%, dispersant 2.5%, antioxidant 1%, tackifier:1.9%, water-soluble ageing resistance agent 0.8%;
The wetting agent is:Tween-20;
The levelling agent is:Peregal O-25;
The color fixing agent is cation-type water-thinned polyurethane color fixing agent;
The bleeding agent is:Fatty alcohol polyoxyethylene ether;
The group of the dispersant becomes:2 parts by weight α-methacrylic acids, 1.5 parts by weight propylene amides, 3 parts by weight propylene
Sour sodium, 15 parts by weight water and 10 parts of w ethanols;
The group of the antioxidant becomes:2 parts by weight diphenylamines, 1.5 parts by weight p-phenylenediamine, 2.5 parts by weight dihydro quinolines
The ethanol water of quinoline, 9 parts by weight 85%;
The group of the tackifier becomes:4 parts of vinylsiloxanes and 3 parts of epoxy radical siloxanes;
The group of the water-soluble ageing resistance agent becomes:40 part by weight of liquid paraffin, 10 parts by weight of phosphoric acid tri butyl esters, 25 weight
The water of part lauryl sodium sulfate, 16 parts by weight hydroxyethyl celluloses, 18 parts by weight sodium metasilicate, 50 parts by weight;
The preparation method that the printing layer brightens coating is:
Step a, acid red is injected in solvent red, Indian yellow is injected in solvent yellow, acid blue is injected into solvent blue
In, then three kinds of mixed liquors are put into ultrasonic vibration machine and rock uniform, three kinds of uniform mixtures then will be rocked and all injects
In high-speed inks oscillator, the frequency of the ultrasonic vibration machine is:35000 hertz;
Step b, the high-speed inks oscillator in starting step a, and white ink is constantly added into blender,
Ethyl acetate, two butanol, silicone oil, acrylic resin, the vibration frequency of the high-speed inks oscillator is about at 650 beats/min;
Step c, the mixture by the completion shaken in step b is transferred in blender, and titanium white is added into blender
Powder, wetting agent, bleeding agent, color fixing agent brighten painting until all substances in the blender become bottom that is uniform, stablizing
Material, the mixing speed of the blender is in 450 revs/min of kinds;
The preparation method of the high whiteness cigarette pack cast-coated paperboard of unstressed configuration, which is characterized in that include the following steps:
Step 1: base's paperboard is put into the machine of broadcasting, the tension for broadcasting machine is in 2.6N, then to the base
The printing layer of paperboard carries out sided corona treatment, then heats base's paperboard bottom surface layer, the temperature control of the heating roller with heating roller
System is heated to 120 DEG C at 135 DEG C, by base's paperboard bottom surface layer, and the voltage of the sided corona treatment is 30kV, and electric current is
16A;
It is packed into coating feeding roller Step 2: the bottom is first brightened coating, then will handle and complete in step 1 again
Base's paperboard be placed on and carry out bottom under coating feeding roller and brighten the feeding operation of coating, wait for being sent to after the completion of feeding dry
It is dry in dry channel, after to be dried, then base's paperboard is placed in progress printing layer under coating feeding roller and brightens the upper of coating
Expect operation, wherein the cable on the coating feeding roller is 170 lines, and depth is 25 μm, pressure 0.35Mpa;The drying is logical
The drying temperature in road is 155 DEG C, and hot wind wind pressure is 0.08Mpa;The cable of the coating feeding roller surface is 200 lines, depth 25
μm, pressure 0.27Mpa;
It is applied Step 3: applying layer of transparent bloom using coating transfer method to the base's paperboard for handling completion in step 2
High photosphere is formed in material to the printing layer of base's paperboard;
Wherein, the coating transfer method includes the following steps:
The base's paperboard handled is put into the machine of broadcasting by step I, is sent into composite roll by the machine of broadcasting, described
Machine is broadcasted by the tension force of base's paperboard in 5N;
Step II will be put into the machine of broadcasting for shifting the PET transfer membranes of transparent high-gloss paint, and the machine of broadcasting turns PET
The tension force of film is moved in 2.5N, then the PET transfer membranes are sent into upper glue roller by the machine of broadcasting, and the upper glue roller uses
150 mesh anilox rolls glue, and high optical cement are coated on PET transfer membranes, coating weight 7g/m2, then will be after the completion of coating
PET transfer membranes are re-fed into composite roll and the printing surface of base paperboard is compound, composite pressure 0.26Mpa, will be compound after paperboard
It is re-fed into drying machine and is dried, drying temperature is 110 DEG C;
Step III, step II is dried after paperboard on PET transfer film stripping, peel angle be 30 °, be finally made
Cast-coated paperboard;
By paperboard prepared by this embodiment, defoaming is added since printing layer brightens coating, subbing, high photosphere
Agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent are printing layer in the result by the test of whiteness instrument
Whiteness 89%, bottom whiteness 88%, greatly improve the whiteness of paperboard, simultaneously because it uses PET transfer methods
The white luminance of paperboard can also be improved to a certain extent.
Embodiment 8:
A kind of high whiteness cigarette pack cast-coated paperboard of unstressed configuration, including:
Base's paperboard;
Printing layer, is located at base's paperboard top surface, and being coated with printing layer in the printing layer brightens coating;
Bottom surface layer, is located at base's paperboard bottom surface, and the bottom surface layer is coated with bottom and brightens coating thereon;
High photosphere is located on the printing layer, transparent high-gloss paint is coated on the high photosphere;
The printing layer brightens the raw material composition of coating and its is by mass percentage:
Alkalinity is red:6.6%, alkali blue:5.4%, transparent red:8.6%, transparent blue:10.4%, basic yellow:15%, thoroughly
Bright Huang:16%, wetting agent:4%, infilter agent:3%, levelling agent:4%, color fixing agent:3%, water:4.8%, ethyl alcohol:4.2%, second
Acetoacetic ester:6.5%, two butanol:5.3%, silicone oil:1.2%, antifoaming agent:1.2%, rheological agent:0.8%, dispersant 2% resists
Oxidant 0.5%, tackifier:1.2%, water-soluble ageing resistance agent 0.3%;
The bottom brightens the raw material composition of coating and its is by mass percentage:
Acid red:9.8%, acid blue:7.8%, Indian yellow:6.8%, solvent red:1.6%, solvent blue:9.2%, it is molten
Agent is yellow:14.2%, wetting agent:0.4%, bleeding agent:3%, white ink:5%, titanium dioxide:8%, color fixing agent:4%, acetic acid
Ethyl ester:3%, two butanol:8.4%, silicone oil:1.8%, acrylic resin:8.2%, antifoaming agent:1.1%, rheological agent:1.7%,
Dispersant 3%, antioxidant 1.2%, tackifier:1.8%, water-soluble ageing resistance agent 1.2%;
The raw material of the transparent high-gloss paint forms and its is by mass percentage:
Polyvinyl alcohol:13.6%, ethylene-vinyl acetate copolymer emulsion:13%, methylcellulose:13.5%, propylene
Yogurt liquid:27.4%, water-based gloss oil:8.9%, aqueous silicone oil is shifted in coating:1.5%, styrene-butadiene emulsion:11.4%, antifoaming agent:
2%, rheological agent:2.5%, dispersant 2.5%, antioxidant 1%, tackifier:1.9%, water-soluble ageing resistance agent 0.8%;
The wetting agent is:Tween-40;
The levelling agent is:Peregal O-25;
The color fixing agent is cation-type water-thinned polyurethane color fixing agent;
The bleeding agent is:Fatty alcohol polyoxyethylene ether;
The group of the dispersant becomes:1.3 parts by weight α-methacrylic acids, 1.5 parts by weight propylene amides, 3 parts by weight third
Olefin(e) acid sodium, 14 parts by weight water and 10 parts of w ethanols;
The group of the antioxidant becomes:2 parts by weight diphenylamines, 1.5 parts by weight p-phenylenediamine, 2.5 parts by weight dihydro quinolines
The ethanol water of quinoline, 9 parts by weight 85%;
The group of the tackifier becomes:4 parts of vinylsiloxanes and 3 parts of epoxy radical siloxanes;
The group of the water-soluble ageing resistance agent becomes:40 part by weight of liquid paraffin, 10 parts by weight of phosphoric acid tri butyl esters, 25 weight
The water of part lauryl sodium sulfate, 14 parts by weight hydroxyethyl celluloses, 16 parts by weight sodium metasilicate, 400 parts by weight;
The preparation method that the printing layer brightens coating is:
Step a, acid red is injected in solvent red, Indian yellow is injected in solvent yellow, acid blue is injected into solvent blue
In, then three kinds of mixed liquors are put into ultrasonic vibration machine and rock uniform, three kinds of uniform mixtures then will be rocked and all injects
In high-speed inks oscillator, the frequency of the ultrasonic vibration machine is:40000 hertz;
Step b, the high-speed inks oscillator in starting step a, and white ink is constantly added into blender,
Ethyl acetate, two butanol, silicone oil, acrylic resin, the vibration frequency of the high-speed inks oscillator is about at 750 beats/min;
Step c, the mixture by the completion shaken in step b is transferred in blender, and titanium white is added into blender
Powder, wetting agent, bleeding agent, color fixing agent, antifoaming agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent, directly
Become bottom that is uniform, stablizing to all substances in the blender and brighten coating, the mixing speed of the blender exists
550 revs/min of kinds;
The preparation method of the high whiteness cigarette pack cast-coated paperboard of unstressed configuration, which is characterized in that include the following steps:
Step 1: base's paperboard is put into the machine of broadcasting, then the tension for broadcasting machine blocks the base in 3N
The printing layer of paper carries out sided corona treatment, then heats base's paperboard bottom surface layer, the temperature control of the heating roller with heating roller
At 135 DEG C, base's paperboard bottom surface layer is heated to 120 DEG C, the voltage of the sided corona treatment is 30kV, electric current 16A;
It is packed into coating feeding roller Step 2: the bottom is first brightened coating, then will handle and complete in step 1 again
Base's paperboard be placed on and carry out bottom under coating feeding roller and brighten the feeding operation of coating, wait for being sent to after the completion of feeding dry
It is dry in dry channel, after to be dried, then base's paperboard is placed in progress printing layer under coating feeding roller and brightens the upper of coating
Expect operation, wherein the cable on the coating feeding roller is 170 lines, and depth is 25 μm, pressure 0.35Mpa;The drying is logical
The drying temperature in road is 155 DEG C, and hot wind wind pressure is 0.08Mpa;The cable of the coating feeding roller surface is 200 lines, depth 25
μm, pressure 0.27Mpa;
It is applied Step 3: applying layer of transparent bloom using coating transfer method to the base's paperboard for handling completion in step 2
High photosphere is formed in material to the printing layer of base's paperboard;
Wherein, the coating transfer method includes the following steps:
The base's paperboard handled is put into the machine of broadcasting by step I, is sent into composite roll by the machine of broadcasting, described
Machine is broadcasted by the tension force of base's paperboard in 5N;
Step II will be put into the machine of broadcasting for shifting the PET transfer membranes of transparent high-gloss paint, and the machine of broadcasting turns PET
The tension force of film is moved in 2.5N, then the PET transfer membranes are sent into upper glue roller by the machine of broadcasting, and the upper glue roller uses
150 mesh anilox rolls glue, and high optical cement are coated on PET transfer membranes, coating weight 7g/m2, then will be after the completion of coating
PET transfer membranes are re-fed into composite roll and the printing surface of base paperboard is compound, composite pressure 0.26Mpa, will be compound after paperboard
It is re-fed into drying machine and is dried, drying temperature is 110 DEG C;
Step III, step II is dried after paperboard on PET transfer film stripping, peel angle be 30 °, be finally made
Cast-coated paperboard;
By paperboard prepared by this embodiment, defoaming is added since printing layer brightens coating, subbing, high photosphere
Agent, rheological agent, dispersant, antioxidant, tackifier, water-soluble ageing resistance agent are printing layer in the result by the test of whiteness instrument
Whiteness 89%, bottom whiteness 90%, greatly improve the whiteness of paperboard, simultaneously because it uses PET transfer methods
The white luminance of paperboard can also be improved to a certain extent.
Number of devices and treatment scale described herein are the explanations for simplifying the present invention.To the present invention without glimmering
The application of the high whiteness cigarette pack cast-coated paperboard of light and preparation method thereof, modifications and variations are to one skilled in the art
It is obvious.
Although the embodiments of the present invention have been disclosed as above, but its institute not only in the description and the implementation
Row use, it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can hold
It changes places and realizes other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, the present invention is simultaneously
It is not limited to specific details and legend shown and described herein.