CN108394161A - A kind of cigarette aluminium-foil paper of two-sided fitting - Google Patents
A kind of cigarette aluminium-foil paper of two-sided fitting Download PDFInfo
- Publication number
- CN108394161A CN108394161A CN201810179294.7A CN201810179294A CN108394161A CN 108394161 A CN108394161 A CN 108394161A CN 201810179294 A CN201810179294 A CN 201810179294A CN 108394161 A CN108394161 A CN 108394161A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- foil paper
- cigarette
- fitting
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cigarette aluminium-foil paper of two-sided fitting, including aluminium foil paper layer and adhesive-layer, the one side of the aluminium foil paper layer is uniformly provided with butterfly slot；The production technology of the cigarette of two-sided fitting aluminium-foil paper is：S1, the one side of two-sided smooth aluminium-foil paper is uniformly suppressed by the groove face containing butterfly slot using roll squeezer, aluminium foil paper layer is made；One layer of mucigel is uniformly coated on S2, aluminium foil paper layer groove face, single side aluminium-foil paper is made, single side aluminium-foil paper is individually positioned on the rack of both sides, the single side aluminium-foil paper of left and right sides is sent between fitting roller set simultaneously using heat preservation conveyer, through fitting, the mucigel bonding of two single side aluminium-foil papers forms adhesive-layer；S3, the aluminium-foil paper of fitting is continued to be fed into shaping roller group compression moulding, finished product is obtained through air cooling, cutting edge；The cigarette of two-sided fitting obtained is good with aluminium-foil paper dampproof effect, can preserve for a long time in a variety of contexts.
Description
Technical field
The invention belongs to aluminium-foil paper technical fields, and in particular to a kind of cigarette aluminium-foil paper of two-sided fitting.
Background technology
With society and expanding economy, the packaging of commodity also constantly updates the replacement, based on paper and plastic film
Packaging material is gradually replaced by exquisite beautiful aluminium-foil paper, and the usage amount of aluminium-foil paper is increasingly incremental, this gives the life of aluminium-foil paper
Production brings new business opportunity.
Cigarette is important one of the packaging material of cigarette with aluminium-foil paper, now widely used single side composite aluminium foil paper, due to
Its quality is thin, and leakproofness is inadequate, is easy that the filter core at cigarette and cigarette butt is made to make moist so that the holding time shorten, cause waste and
Loss, and filter core make moist after cause suction-operated to be deteriorated, harmful substance sucking lung in cause actual bodily harm；In addition, existing aluminium
Foil paper bonding is not secured enough, makes moist all it is easier that aluminium-foil paper interlayer is peeling-off, influences product quality.
Invention content
The purpose of the present invention is to provide a kind of cigarette aluminium-foil papers of two-sided fitting so that aluminium-foil paper is more secured, significantly
Improve its humidity resistance.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of cigarette aluminium-foil paper of two-sided fitting, including aluminium foil paper layer and adhesive-layer, the one side of the aluminium foil paper layer are equal
It is even to be provided with butterfly slot；
The production technology of the cigarette of two-sided fitting aluminium-foil paper is：
S1, the one side of two-sided smooth aluminium-foil paper is uniformly suppressed by the groove face containing butterfly slot using roll squeezer, be made
Aluminium foil paper layer；
One layer of mucigel is uniformly coated on S2, aluminium foil paper layer groove face, single side aluminium-foil paper is made, single side aluminium-foil paper is put respectively
Set on the rack of both sides, using heat preservation conveyer simultaneously by the single side aluminium-foil paper of left and right sides be sent to fitting roller set it
Between, through fitting, the mucigel bonding of two single side aluminium-foil papers forms adhesive-layer；
S3, the aluminium-foil paper of fitting is continued to be fed into shaping roller group compression moulding, is obtained into through air cooling, cutting edge
Product.
Further, the rotation direction of roller is opposite rotation in the fitting roller set and shaping roller group.
Further, the viscose includes following components by weight percent raw material：Water 5-10%, ethyl maleate-silicon rubber copolymerization
Lotion 50-80%, polyvinyl alcohol 7-15%, sodium cellulose glycolate 5-10%, 0.2% calcium chloride solution 0.5-1%, transparent
Matter acid sodium 0.5-2%, tobacco essence 0.5-1%, dehydroactic acid sodium 2-5%, glycerine 3-8%.
Further, the viscose includes following components by weight percent raw material：Water 6%, ethyl maleate-silicon rubber copolymer emulsion
68%, polyvinyl alcohol 10%, the calcium chloride solution 0.7% of sodium cellulose glycolate 5%, 0.2%, Sodium Hyaluronate 0.6%, cigarette
Hay-scented essence 0.7%, dehydroactic acid sodium 4%, glycerine 5%.
Further, the preparation method of the ethyl maleate-silicon rubber copolymer emulsion is：Silicone rubber solution is added to
In reaction tube, monomer ethyl maleate, initiator benzoyl peroxide and crosslinking agent 2 isopropyl imidazole are sequentially added, stirring is equal
It is even to be swollen 2h at room temperature, reducing agent butylated hydroxy anisole is then added under nitrogen protection, is heated to 80-90 DEG C of stirring and carries out
Copolyreaction 5h is added 0.01M biphosphate sodium water solutions stirring 2h and reaction solution is made to be condensed into latex solution, i.e., after completion of the reaction
Obtain ethyl maleate-silicon rubber copolymer emulsion.
Further, the silicone rubber solution, ethyl maleate, initiator, crosslinking agent, reducing agent, 0.01M biphosphates
The mass ratio of sodium water solution is 100:20:1-5:1-5:3:0.2-0.5.
Further, the preparation method of the viscose is：Retort is put into water bath sonicator instrument, is 20KHz- in frequency
30KHz, bath temperature are to sequentially add water, ethyl maleate-silicon rubber copolymer emulsion, polyvinyl alcohol and hydroxyl first at 45-50 DEG C
Base sodium cellulosate, after ultrasonic 30min, every sequentially adding glycerine, Sodium Hyaluronate, dehydroactic acid sodium, 0.2% after ten minutes
Calcium chloride solution and tobacco essence, tobacco essence be added after, take out retort be put into blender, at 35-40 DEG C
30-60min is stirred, 2h is stood and obtains viscose.
Beneficial effects of the present invention：
A kind of cigarette aluminium-foil paper of two-sided fitting provided by the invention, the one side of aluminium foil paper layer are uniformly provided with butterfly slot,
Uniformly coat one layer of mucigel on aluminium foil paper layer groove face and be made single side aluminium-foil paper, two single side aluminium-foil papers through fitting, compression moulding,
The cigarette aluminium-foil paper of two-sided fitting has been made in cooling cutting edge, and viscose is immersed in butterfly slot, increases bonding plane, and in butterfly slot
Between narrow slit so that viscose is not easily to fall off so that the bonding between aluminium-foil paper is more secured, is bonded the two-sided attaching process of roller set
Improve production efficiency；The cigarette of two-sided fitting obtained is good with aluminium-foil paper dampproof effect, in a variety of contexts can be for a long time
It preserves.
Description of the drawings
In order to illustrate the technical solution of the embodiments of the present invention more clearly, will be described below to embodiment required
Attached drawing is briefly described, it should be apparent that, drawings in the following description are only some embodiments of the invention, for ability
For the those of ordinary skill of domain, without creative efforts, it can also be obtained according to these attached drawings other attached
Figure.
Fig. 1 is a kind of cigarette aluminium-foil paper structural schematic diagram of two-sided fitting of the present invention；
Fig. 2 is a kind of cigarette aluminium-foil paper production technology schematic diagram of two-sided fitting of the present invention；
In attached drawing, parts list represented by the reference numerals are as follows：
1- aluminium foil paper layers, 2- adhesive-layers, 3- butterfly slots, 4- are bonded roller set, 5- shaping roller groups.
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained all other without creative efforts
Embodiment shall fall within the protection scope of the present invention.
Embodiment 1
(1) preparation of ethyl maleate-silicon rubber copolymer emulsion
100g silicone rubber solutions are added in reaction tube, 20g monomers ethyl maleate, 1g initiator peroxides are sequentially added
Change benzoyl and 1g crosslinking agent 2 isopropyl imidazoles, stirs evenly and be swollen 2h at 25 DEG C, 3g is then added under nitrogen protection
Reducing agent butylated hydroxy anisole is heated to 80-90 DEG C of stirring and carries out copolyreaction 5h, 0.2g 0.01M are added after completion of the reaction
Biphosphate sodium water solution stirring 2h makes reaction solution be condensed into latex solution to get to ethyl maleate-silicon rubber copolymer emulsion；
(2) preparation of viscose：
Retort is put into water bath sonicator instrument, in the case where frequency is 20KHz-30KHz, bath temperature is 45-50 DEG C, successively
6g water, 68g ethyl maleates-silicon rubber copolymer emulsion, 10g polyvinyl alcohol and 5g sodium cellulose glycolates, ultrasonic 30min is added
Afterwards, every the chlorination for sequentially adding 5g glycerine, 0.6g Sodium Hyaluronates, 4g dehydroactic acid sodiums, 0.7g 0.2% after ten minutes
Calcium solution and 0.7g tobacco essences after tobacco essence is added, takes out retort and are put into blender, stirred at 35-40 DEG C
30-60min is mixed, 2h is stood and obtains viscose；
(3) preparation of the cigarette aluminium-foil paper of two-sided fitting：
As shown in Figs. 1-2, the cigarette aluminium-foil paper of the two-sided fitting includes aluminium foil paper layer 1 and adhesive-layer 2, the aluminium-foil paper
The one side of layer 1 is uniformly provided with butterfly slot 3；
S1, the one side of two-sided smooth aluminium-foil paper is uniformly suppressed by the groove face containing butterfly slot 3 using roll squeezer, be made
Aluminium foil paper layer 1；
One layer of mucigel is uniformly coated on S2,1 groove face of aluminium foil paper layer, single side aluminium-foil paper is made, single side aluminium-foil paper is distinguished
It is placed on the rack of both sides, temperature is used simultaneously to be sent to the single side aluminium-foil paper of left and right sides for 50 DEG C of heat preservation conveyer
It is bonded between roller set 4, through fitting, the mucigel bonding of two single side aluminium-foil papers forms adhesive-layer 2；
S3, the aluminium-foil paper of fitting is continued to be fed into 5 compression moulding of shaping roller group, is obtained into through air cooling, cutting edge
Product；
The rotation direction of roller is opposite rotation in the fitting roller set 4 and shaping roller group 5.
Embodiment 2
(1) preparation of ethyl maleate-silicon rubber copolymer emulsion
100g silicone rubber solutions are added in reaction tube, 20g monomers ethyl maleate, 5g initiator peroxides are sequentially added
Change benzoyl and 5g crosslinking agent 2 isopropyl imidazoles, stirs evenly and be swollen 2h at 25 DEG C, 3g is then added under nitrogen protection
Reducing agent butylated hydroxy anisole is heated to 90 DEG C of stirrings and carries out copolyreaction 5h, 0.5g 0.01M phosphorus is added after completion of the reaction
Acid dihydride sodium water solution stirring 2h makes reaction solution be condensed into latex solution to get to ethyl maleate-silicon rubber copolymer emulsion；
(2) preparation of viscose：
Retort is put into water bath sonicator instrument, in the case where frequency is 30KHz, bath temperature is 50 DEG C, sequentially add 8g water,
50g ethyl maleates-silicon rubber copolymer emulsion, 15g polyvinyl alcohol and 10g sodium cellulose glycolates, after ultrasonic 30min, every
8g glycerine, 2g Sodium Hyaluronates, 5g dehydroactic acid sodiums, the calcium chloride solution of 1g 0.2% and 1g cigarettes are sequentially added after ten minutes
Hay-scented essence after tobacco essence is added, is taken out retort and is put into blender, 60min is stirred at 40 DEG C, stand 2h to obtain the final product
To viscose；
(3) preparation of the cigarette aluminium-foil paper of two-sided fitting is the same as embodiment 1.
Embodiment 3
(1) preparation of ethyl maleate-silicon rubber copolymer emulsion
100g silicone rubber solutions are added in reaction tube, 20g monomers ethyl maleate, 2g initiator peroxides are sequentially added
Change benzoyl and 3.5g crosslinking agent 2 isopropyl imidazoles, stirs evenly and be swollen 2h at 25 DEG C, be then added under nitrogen protection
3g reducing agent butylated hydroxy anisoles are heated to 80 DEG C of stirrings and carry out copolyreaction 5h, 0.3g 0.01M are added after completion of the reaction
Biphosphate sodium water solution stirring 2h makes reaction solution be condensed into latex solution to get to ethyl maleate-silicon rubber copolymer emulsion；
(2) preparation of viscose：
Retort is put into water bath sonicator instrument, in the case where frequency is 20KHz, bath temperature is 48 DEG C, sequentially add 5g water,
76g ethyl maleates-silicon rubber copolymer emulsion, 7.5g polyvinyl alcohol and 5g sodium cellulose glycolates, after ultrasonic 30min, every
Sequentially add after ten minutes 3g glycerine, 0.5g Sodium Hyaluronates, 2g dehydroactic acid sodiums, 0.5g 0.2% calcium chloride solution and
0.5g tobacco essences after tobacco essence is added, takes out retort and are put into blender, 30min is stirred at 35 DEG C, stand
2h obtains viscose；
(3) preparation of the cigarette aluminium-foil paper of two-sided fitting is the same as embodiment 1.
The above content is just an example and description of the concept of the present invention, affiliated those skilled in the art
It makes various modifications or additions to the described embodiments or substitutes by a similar method, without departing from invention
Design or beyond the scope defined by this claim, be within the scope of protection of the invention.
Claims (7)
1. a kind of cigarette aluminium-foil paper of two-sided fitting, including aluminium foil paper layer (1) and adhesive-layer (2), it is characterised in that：The aluminium
The one side of foil paper layer (1) is uniformly provided with butterfly slot (3)；
The production technology of the cigarette of two-sided fitting aluminium-foil paper is：
S1, the one side of two-sided smooth aluminium-foil paper is uniformly suppressed by the groove face containing butterfly slot (3) using roll squeezer, aluminium is made
Foil paper layer (1)；
One layer of mucigel is uniformly coated on S2, aluminium foil paper layer (1) groove face, single side aluminium-foil paper is made, single side aluminium-foil paper is put respectively
It sets on the rack of both sides, the single side aluminium-foil paper of left and right sides is sent to by fitting roller set (4) using heat preservation conveyer simultaneously
Between, through fitting, the mucigel bonding of two single side aluminium-foil papers forms adhesive-layer (2)；
S3, the aluminium-foil paper of fitting is continued to be fed into shaping roller group (5) compression moulding, finished product is obtained through air cooling, cutting edge.
2. a kind of cigarette aluminium-foil paper of two-sided fitting according to claim 1, it is characterised in that：The fitting roller set
(4) and in shaping roller group (5) rotation direction of roller is opposite rotation.
3. a kind of cigarette aluminium-foil paper of two-sided fitting according to claim 1, it is characterised in that：The viscose include with
Lower components by weight percent raw material：Water 5-10%, ethyl maleate-silicon rubber copolymer emulsion 50-80%, polyvinyl alcohol 7-15%, hydroxyl first
Base sodium cellulosate 5-10%, 0.2% calcium chloride solution 0.5-1%, Sodium Hyaluronate 0.5-2%, tobacco essence 0.5-1%,
Dehydroactic acid sodium 2-5%, glycerine 3-8%.
4. a kind of cigarette aluminium-foil paper of two-sided fitting according to claim 3, it is characterised in that：The viscose include with
Lower components by weight percent raw material：Water 6%, ethyl maleate-silicon rubber copolymer emulsion 68%, polyvinyl alcohol 10%, hydroxymethyl cellulose
The calcium chloride solution 0.7% of sodium 5%, 0.2%, Sodium Hyaluronate 0.6%, tobacco essence 0.7%, dehydroactic acid sodium 4%, the third three
Alcohol 5%.
5. a kind of cigarette aluminium-foil paper of two-sided fitting according to claim 3, it is characterised in that：The maleic acid second
The preparation method of ester-silicon rubber copolymer emulsion is：Silicone rubber solution is added in reaction tube, monomer maleic acid second is sequentially added
Ester, initiator benzoyl peroxide and crosslinking agent 2 isopropyl imidazole, stir evenly and are swollen 2h at room temperature, then in nitrogen protection
Lower addition reducing agent butylated hydroxy anisole is heated to 80-90 DEG C of stirring and carries out copolyreaction 5h, is added after completion of the reaction
0.01M biphosphate sodium water solutions stirring 2h makes reaction solution be condensed into latex solution and be copolymerized to get to ethyl maleate-silicon rubber
Lotion.
6. a kind of cigarette aluminium-foil paper of two-sided fitting according to claim 5, it is characterised in that：The silicon rubber is molten
Liquid, ethyl maleate, initiator, crosslinking agent, reducing agent, 0.01M biphosphate sodium water solutions mass ratio be 100:20:1-5:
1-5:3:0.2-0.5。
7. a kind of cigarette aluminium-foil paper of two-sided fitting according to claim 3, it is characterised in that：The preparation of the viscose
Method is：Retort is put into water bath sonicator instrument, in the case where frequency is 20KHz-30KHz, bath temperature is 45-50 DEG C, successively
Water, ethyl maleate-silicon rubber copolymer emulsion, polyvinyl alcohol and sodium cellulose glycolate is added, after ultrasonic 30mi n, every 10
Sequentially added after minute glycerine, Sodium Hyaluronate, dehydroactic acid sodium, 0.2% calcium chloride solution and tobacco essence, tobacco is fragrant
It after finishing enters, takes out retort and is put into blender, 30-60mi n are stirred at 35-40 DEG C, stand 2h and sticked
Glue.