CN108384304A - A kind of spectrum light absorption paint and its preparation method and application - Google Patents
A kind of spectrum light absorption paint and its preparation method and application Download PDFInfo
- Publication number
- CN108384304A CN108384304A CN201810179943.3A CN201810179943A CN108384304A CN 108384304 A CN108384304 A CN 108384304A CN 201810179943 A CN201810179943 A CN 201810179943A CN 108384304 A CN108384304 A CN 108384304A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal
- light absorption
- spectrum light
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of spectrum light absorption paints and its preparation method and application, belong to paint field.Spectrum light absorption paint it include metal mill base, synthetic resin, auxiliary agent.Preparation method includes：Resin coated silver strip is ground into fine powder, argentine pigment is made；The photochromic film of different colours is attached to the surface of metal silver strip respectively, after removing hymeniderm, is pulverized, yellow metal pigment, red metallic pigments, blue metallic pigments and green metal pigment are respectively obtained；The metallic pigments of different colours obtained are mixed according to the proportioning in above-mentioned spectrum light absorption paint again, obtain metal mill base；And metal mill base is mixed with synthetic resin, auxiliary agent.This spectrum light absorption paint can effectively absorb the light of different wave length, can be used for preparing projecting glass screen, imaging effect is clear.
Description
Technical field
The present invention relates to paint fields, in particular to a kind of spectrum light absorption paint and its preparation method and application.
Background technology
Line holographic projections technology, also referred to as virtual image technology are that simultaneously reconstructed object is true using interference and diffraction principle record
3-D view technology.Line holographic projections technology can not only generate three-dimensional aerial mirage, can also make mirage and performing artist
Interaction is generated, performance is completed together, generates shocking performing effect.
In recent years, with the rapid development of line holographic projections technology, also emerged on the market some for projection holography
Projecting glass.The imaging effect of this line holographic projections glass is preferable, but if if watching for a long time, it is easy to it is tired vision occur
The use feeling degree of labor, client is bad.
Invention content
The first object of the present invention is to provide a kind of spectrum light absorption paint and its preparation method and application, and this spectrum is inhaled
Optical coating can be used for preparing projecting glass screen, and imaging effect is clear.
In order to realize that the above-mentioned purpose of the present invention, spy use following technical scheme：
A kind of spectrum light absorption paint, in parts by weight meter include：
45~90 parts of metal mill base, 30~50 parts of synthetic resin, 3~6 parts of auxiliary agent；
Metal mill base is that metal mill base is counted in parts by weight includes by being mixed to prepare the metallic pigments of different colours：
35~65 parts of argentine pigment, 0~13 part of yellow metal pigment, red 0~5 part of metallic pigments, blue metal
2~10 parts of pigment, 2~9 parts of green metal pigment.
Further, in preferred embodiments of the present invention, count in parts by weight, argentine pigment be 35~45 parts,
Yellow metal pigment is 7~13 parts, red metallic pigments are 1~5 part, blue metallic pigments are 2~8 parts, green metal pigment
It is 2~6 parts.
Further, in preferred embodiments of the present invention, count in parts by weight, argentine pigment be 55~65 parts,
Yellow metal pigment is 0~2 part, red metallic pigments are 0~2 part, blue metallic pigments are 2~10 parts, green metal pigment
It is 4~9 parts.
Further, in preferred embodiments of the present invention, argentine pigment is by grinding resin coated silver strip
Fine powder is worn into be made.
Further, in preferred embodiments of the present invention, yellow metal pigment, red metallic pigments, blue metal face
Material, green metal pigment are made by the way that the silver strip after being coloured with different colours is ground into fine powder.
Further, in preferred embodiments of the present invention, the silver strip after coloring includes metallic silver layer and is evenly applied to
The thickness ratio of dyed layer in metallic silver layer, metallic silver layer and dyed layer is 10~30：1.
Further, in preferred embodiments of the present invention, dyed layer is by the way that the photochromic film of different colours to be attached at
What the surface of metallic silver layer was formed.
Further, in preferred embodiments of the present invention, auxiliary agent include adhesive, antifoaming agent, levelling agent, scratch resistance agent,
At least one of curing agent and its group.
A kind of preparation method of spectrum light absorption paint, which is characterized in that it includes：
Resin coated silver strip is ground into fine powder, argentine pigment is made；
The photochromic film of yellow, red photochromic film, the photochromic film of blue and the photochromic film of green are attached to the table of metal silver strip respectively
Face after removing hymeniderm, is pulverized, and yellow metal pigment, red metallic pigments, blue metallic pigments and green gold are respectively obtained
Belong to pigment；
The metallic pigments of different colours obtained are mixed according to the proportioning in above-mentioned spectrum light absorption paint again, obtain metal
Mill base；And
Metal mill base is mixed with synthetic resin, auxiliary agent.
A kind of application of above-mentioned spectrum light absorption paint in preparing projecting glass screen.
Compared with prior art, beneficial effects of the present invention for example including：
This spectrum light absorption paint provided by the invention and preparation method thereof, using argentine pigment as Essential colour, passes through
Compounding between the metallic pigments of different colours, obtain can to the metal mill base that the light of different wave length is effectively absorbed, and
By synthetic resin and auxiliary agent, spectrum light absorption paint is formed.This light absorption paint can be used for preparing projecting glass screen, such as family
The projection screen of front yard movie theatre or the projection screen of teaching white board, imaging effect are clear.
Specific implementation mode
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the invention.It is not specified in embodiment specific
Condition person carries out according to conventional conditions or manufacturer's recommended conditions.Reagents or instruments used without specified manufacturer is
The conventional products that can be obtained by commercially available purchase.
Present embodiment provides a kind of spectrum light absorption paint, and meter includes in parts by weight：
45~90 parts of metal mill base, 30~50 parts of synthetic resin, 3~6 parts of auxiliary agent.
More preferred, meter includes in parts by weight：47~88 parts of metal mill base, 34~47 parts of synthetic resin, auxiliary agent 3
~5 parts.
More preferably, meter includes in parts by weight：47~77 parts of metal mill base, 37~43 parts of synthetic resin, auxiliary agent 4
~5 parts.
More preferably, meter includes in parts by weight：61~88 parts of metal mill base, 38~41 parts of synthetic resin, auxiliary agent 4
~5 parts.
Wherein, synthetic resin includes thermoplastic resin and thermosetting resin, thermoplastic resin include polyethylene, polypropylene,
Poly 1-butene, polyvinyl chloride and at least one of polystyrene and its group；Thermosetting resin includes phenolic resin, ureaformaldehyde tree
Fat, melamine formaldehyde resin, epoxy resin, unsaturated polyester resin and at least one of polyurethane and its group.
Auxiliary agent includes at least one of adhesive, antifoaming agent, levelling agent, scratch resistance agent, curing agent and its group.Wherein,
Adhesive includes waterglass, synthetic rubber etc.；Antifoaming agent includes dimethicone, tributyl phosphate etc.；Levelling agent includes poly- third
Olefin(e) acid, carboxymethyl cellulose etc.；Scratch resistance agent includes polyester-modified polysiloxanes, fluorinated polymer etc.；Curing agent includes vinyl
Triamine, m-phenylene diamine (MPD), diaminodiphenyl-methane etc..
Metal mill base is by being mixed to prepare the metallic pigments of different colours, and metal mill base counts packet in parts by weight
It includes：
35~65 parts of argentine pigment, 0~13 part of yellow metal pigment, red 0~5 part of metallic pigments, blue metal
2~10 parts of pigment, 2~9 parts of green metal pigment.
Further, for the projection screen of home theater, metal mill base is counted in parts by weight includes：Silver color gold
Belong to pigment be 35~45 parts, yellow metal pigment is 7~13 parts, red metallic pigments are 1~5 part, blue metallic pigments be 2~
8 parts, green metal pigment be 2~6 parts.
Preferably, metal mill base is counted in parts by weight includes：Argentine pigment is 38~42 parts, yellow metal pigment is
7~13 parts, red metallic pigments be 2~4 parts, blue metallic pigments are 3~6 parts, green metal pigment is 4~6 parts.
Further, for the projection screen (blank) of teaching or business, metal mill base counts packet in parts by weight
It includes：Argentine pigment is 55~65 parts, yellow metal pigment is 0~2 part, red metallic pigments are 0~2 part, blue metal
Pigment is 2~10 parts, green metal pigment is 4~9 parts.
Preferably, metal mill base is counted in parts by weight includes：Argentine pigment is 57~61 parts, yellow metal pigment is
0~1 part, red metallic pigments be 0~1 part, blue metallic pigments are 4~9 parts, green metal pigment is 5~9 parts.
Further, yellow metal pigment, red metallic pigments, blue metallic pigments, green metal pigment pass through
Silver strip after being coloured with different colours is ground into fine powder to be made.
Further, the silver strip after coloring includes metallic silver layer and the dyed layer that is evenly applied in metallic silver layer, metal
The thickness of silver layer and dyed layer ratio is 10~30：1, or be 15~25：1, or be 17~23：1.
Further, dyed layer is formed by the way that the photochromic film of different colours to be attached to the surface of metallic silver layer.
Present embodiment also provides a kind of preparation method of spectrum light absorption paint comprising：
Step S1:Resin coated silver strip is ground into fine powder, argentine pigment is made.
Step S2:The photochromic film of yellow, red photochromic film, the photochromic film of blue and the photochromic film of green are attached at metallic silver respectively
The surface of piece after removing hymeniderm, is pulverized, respectively obtain yellow metal pigment, red metallic pigments, blue metallic pigments and
Green metal pigment；
Step S3:The metallic pigments of different colours obtained are subjected to allotment mixing according to said ratio again, obtain metal
Mill base；
Step S4：The metal mill base of gained is mixed with synthetic resin and auxiliary agent again.
The feature and performance of the present invention are described in further detail with reference to embodiments：
Embodiment 1
The present embodiment provides a kind of spectrum light absorption paint, meter in parts by weight includes：
90 parts of metal mill base, 30 parts of synthetic resin, 6 parts of auxiliary agent.
Wherein, metal mill base is counted in parts by weight includes：
It is 65 parts of argentine pigment, 13 parts of yellow metal pigment, red 4 parts of metallic pigments, blue 3 parts of metallic pigments, green
5 parts of non-ferrous metal pigment.
The preparation method of this spectrum light absorption paint is：
A. resin coated silver strip is ground into fine powder, argentine pigment is made.
B. the photochromic film of yellow, red photochromic film, the photochromic film of blue and the photochromic film of green are attached at metal silver strip respectively
Surface, the ratio between metal silver strip and the thickness of photochromic film are 30：1, it after removing hymeniderm, pulverizes, respectively obtains yellow metal face
Material, red metallic pigments, blue metallic pigments and green metal pigment；
C. the metallic pigments of different colours obtained are subjected to allotment mixing according to said ratio again, obtain metal mill base；
D. the metal mill base of gained is mixed with synthetic resin and auxiliary agent again.
Embodiment 2
The present embodiment provides a kind of spectrum light absorption paint, meter in parts by weight includes：
45 parts of metal mill base, 50 parts of synthetic resin, 3 parts of auxiliary agent.
Wherein, metal mill base is counted in parts by weight includes：
35 parts of argentine pigment, 3 parts of yellow metal pigment, red 2 parts of metallic pigments, blue 3 parts of metallic pigments, green
2 parts of metallic pigments.
The preparation method of this spectrum light absorption paint is：
A. resin coated silver strip is ground into fine powder, argentine pigment is made.
B. the photochromic film of yellow, red photochromic film, the photochromic film of blue and the photochromic film of green are attached at metal silver strip respectively
Surface, the ratio between metal silver strip and the thickness of photochromic film are 10：1, it after removing hymeniderm, pulverizes, respectively obtains yellow metal face
Material, red metallic pigments, blue metallic pigments and green metal pigment；
C. the metallic pigments of different colours obtained are subjected to allotment mixing according to said ratio again, obtain metal mill base；
D. the metal mill base of gained is mixed with synthetic resin and auxiliary agent again.
Embodiment 3
The present embodiment provides a kind of spectrum light absorption paint, meter in parts by weight includes：
59 parts of metal mill base, 40 parts of synthetic resin, 5 parts of auxiliary agent.
Wherein, metal mill base is counted in parts by weight includes：
40 parts of argentine pigment, 8 parts of yellow metal pigment, red 2 parts of metallic pigments, blue 6 parts of metallic pigments, green
3 parts of metallic pigments.
The preparation method of this spectrum light absorption paint is：
A. resin coated silver strip is ground into fine powder, argentine pigment is made.
B. the photochromic film of yellow, red photochromic film, the photochromic film of blue and the photochromic film of green are attached at metal silver strip respectively
Surface, the ratio between metal silver strip and the thickness of photochromic film are 25：1, it after removing hymeniderm, pulverizes, respectively obtains yellow metal face
Material, red metallic pigments, blue metallic pigments and green metal pigment；
C. the metallic pigments of different colours obtained are subjected to allotment mixing according to said ratio again, obtain metal mill base；
D. the metal mill base of gained is mixed with synthetic resin and auxiliary agent again.
Embodiment 4
The present embodiment provides a kind of spectrum light absorption paint, meter in parts by weight includes：
61 parts of metal mill base, 35 parts of synthetic resin, 5 parts of auxiliary agent.
Wherein, metal mill base is counted in parts by weight includes：
It is 35 parts of argentine pigment, 12 parts of yellow metal pigment, red 4 parts of metallic pigments, blue 4 parts of metallic pigments, green
6 parts of non-ferrous metal pigment.
Preparation method is consistent with embodiment 1.
Embodiment 5
The present embodiment provides a kind of spectrum light absorption paint, meter in parts by weight includes：
72 parts of metal mill base, 36 parts of synthetic resin, 4 parts of auxiliary agent.
Wherein, metal mill base is counted in parts by weight includes：
60 parts of argentine pigment, blue 4 parts of metallic pigments, 8 parts of green metal pigment.
Preparation method is consistent with embodiment 1.
Embodiment 6
The present embodiment provides a kind of spectrum light absorption paint, meter in parts by weight includes：
75 parts of metal mill base, 33 parts of synthetic resin, 4 parts of auxiliary agent.
Wherein, metal mill base is counted in parts by weight includes：
62 parts of argentine pigment, blue 8 parts of metallic pigments, 5 parts of green metal pigment.
Preparation method is consistent with embodiment 1.
Embodiment 7~13
The present embodiment provides a kind of projecting glass screen, preparation method includes：
A. after using etching method that the first surface of transparent glass substrate is carried out rough surface processing so that first surface
After roughness is 0.05 μm, tempering processing is carried out, then spray the nano self-cleaning coating with photocatalysis, be for thickness
2 μm of nano-titanium oxide coating layer；
B. the spectrum provided in the second surface of transparent glass (i.e. the opposite face of first surface) spraying Examples 1 to 6 is inhaled
Optical coating forms spectrum light-absorbing coating；
C. last to paste rupture pressure disc on the surface of spectrum light-absorbing coating again, form explosion-proof layer.
This projecting glass screen and preparation method thereof is layer structure, and the direction irradiated from light source is by closely to far successively
For nano self-cleaning coating, transparent glass substrate and spectrum light-absorbing coating, wherein nano self-cleaning coating has photocatalysis work(
Can, there is automatical cleaning ability under ultraviolet irradiation, which can be divided
Solution；Transparent glass substrate can effectively reduce the intensity of reflected light with Rough Horizontal Plane, reduce glare, be conducive to protection and see
The eyes for the person of seeing weaken its visual fatigue sense；Spectrum light-absorbing coating can effectively absorb the light of different wave length, be
Imaging picture it is clear.Therefore the projecting glass screen, can effectively solve the problem that the imaging effect of existing line holographic projections glass it is poor,
It is easy the defect of visual fatigue.
Although illustrate and describing the present invention with specific embodiment, it will be appreciated that without departing substantially from the present invention's
Many other change and modification can be made in the case of spirit and scope.It is, therefore, intended that in the following claims
Including belonging to all such changes and modifications in the scope of the invention.
Claims (10)
1. a kind of spectrum light absorption paint, which is characterized in that it is counted in parts by weight includes：
45~90 parts of metal mill base, 30~50 parts of synthetic resin, 3~6 parts of auxiliary agent；
The metal mill base is by being mixed to prepare the metallic pigments of different colours, and the metal mill base counts packet in parts by weight
It includes：
35~65 parts of argentine pigment, 0~13 part of yellow metal pigment, red 0~5 part of metallic pigments, blue metallic pigments 2
~10 parts, 2~9 parts of green metal pigment.
2. spectrum light absorption paint according to claim 1, which is characterized in that count in parts by weight, the argentine face
Material is 35~45 parts, the yellow metal pigment is 7~13 parts, the red metallic pigments are 1~5 part, the blue metal
Pigment is 2~8 parts, the green metal pigment is 2~6 parts.
3. spectrum light absorption paint according to claim 1, which is characterized in that count in parts by weight, the argentine face
Material is 55~65 parts, the yellow metal pigment is 0~2 part, the red metallic pigments are 0~2 part, the blue metal face
Material is 2~10 parts, the green metal pigment is 4~9 parts.
4. according to claims 1 to 3 any one of them spectrum light absorption paint, which is characterized in that the argentine pigment is
It is made by the way that resin coated silver strip is ground into fine powder.
5. according to claims 1 to 3 any one of them spectrum light absorption paint, which is characterized in that the yellow metal pigment, institute
State red metallic pigments, the blue metallic pigments, the green metal pigment be by that will be coloured with different colours after
Silver strip is ground into fine powder and is made.
6. spectrum light absorption paint according to claim 5, which is characterized in that the silver strip after coloring includes metallic silver layer
With the dyed layer being evenly applied in the metallic silver layer, the thickness ratio of the metallic silver layer and the dyed layer is 10~30：
1。
7. spectrum light absorption paint according to claim 6, which is characterized in that the dyed layer is by by different colours
Photochromic film is attached at the surface formation of metallic silver layer.
8. spectrum light absorption paint according to claim 1, which is characterized in that the auxiliary agent includes adhesive, antifoaming agent, stream
At least one of flat agent, scratch resistance agent, curing agent and its group.
9. a kind of preparation method of spectrum light absorption paint, which is characterized in that it includes：
Resin coated silver strip is ground into fine powder, argentine pigment is made；
The photochromic film of yellow, red photochromic film, the photochromic film of blue and the photochromic film of green are attached to the surface of metal silver strip respectively, torn
It after hymeniderm, pulverizes, respectively obtains yellow metal pigment, red metallic pigments, blue metallic pigments and green metal face
Material；
Again by the metallic pigments of different colours obtained according in claims 1 to 3 any one of them spectrum light absorption paint
Proportioning mixing, obtains metal mill base；And
The metal mill base is mixed with synthetic resin, auxiliary agent.
10. a kind of such as application of the claim 1~8 any one of them spectrum light absorption paint in preparing projecting glass screen.