CN108384065A - A kind of degradable packaging film made using food wastes - Google Patents
A kind of degradable packaging film made using food wastes Download PDFInfo
- Publication number
- CN108384065A CN108384065A CN201810191378.2A CN201810191378A CN108384065A CN 108384065 A CN108384065 A CN 108384065A CN 201810191378 A CN201810191378 A CN 201810191378A CN 108384065 A CN108384065 A CN 108384065A
- Authority
- CN
- China
- Prior art keywords
- parts
- added
- packaging film
- food wastes
- brazil wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of degradable packaging films made using food wastes, it is related to packing technical field of membrane, the present invention is aided with various auxiliary agents using eggshell and starch as primary raw material, and packaging film obtained is made to have stronger physical mechanical property, selective penetrated property and antibacterial, antioxidation;And selected raw material is easily degraded, and so as to avoid white pollution, preserves the ecological environment.
Description
Technical field:
The present invention relates to food packaging technical field of membrane, and in particular to a kind of degradable packet made using food wastes
Fill film.
Background technology:
Plastic film packaging is current fresh fruit and the upper most widely used packaging material of vegetables production.It has transparent
Property, it may be clearly seen that the situation of packaging product;It has moisture retention, it is possible to reduce the moisture loss of product increases new
Freshness;It has gas permeability, can play the role of spontaneous controlled atmosphere, extends fresh keeping time, it has leakproofness, can protect production
Product are not contaminated.
Currently, it is base that food package film used in the country, which is generally the polymer such as polyethylene, polypropylene, polyvinyl chloride,
Body, by the way that film made of the mixing such as some plasticizer, inorganic filler, antiseptic is added.On the one hand, these packaging films there is
Long disadvantage, be easy to cause white pollution, influences environment the time required to difficult to degrade or degradation;On the other hand, these packaging films
Gas permeability is bad, if the oxygen concentration in packaging film is too low or gas concentration lwevel is excessively high, fruit just will produce anaerobic respiration,
Cause the volatile materials such as ethyl alcohol, acetaldehyde accumulate, generate peculiar smell and it is different smell, reduce the flavor quality of fruit.
Invention content:
Technical problem to be solved by the present invention lies in provide the utilization food that a kind of preparation method is simple, of good preservation effect
The degradable packaging film of waste-material-preparing.
The technical problems to be solved by the invention are realized using technical solution below:
A kind of degradable packaging film made using food wastes, is made of the raw material of following mass fraction:
60-80 parts of eggshell, 40-50 parts of starch, 15-20 parts of analysis for soybean powder, 12-18 parts of Brazil wax, nano-calcium carbonate 15-
18 parts, 12-15 parts of aerosil, 10-12 parts of polyvinyl alcohol, 8-10 parts of sodium alginate, 8-10 parts of gelatin, sodium bicarbonate 6-
9 parts, it is 5-8 parts of konjaku glucomannan, 5-8 parts of low methoxy pectin, 3-5 parts of citric acid, 3-6 parts of agar, 3-5 parts of Geniposide, poly-
2-3 parts of fatty acid glyceride, 800-1000 parts of water.
The degradable packaging film made using food wastes, the raw material of preferably following mass fraction are made:
70 parts of eggshell, 45 parts of starch, 18 parts of analysis for soybean powder, 15 parts of Brazil wax, 16 parts of nano-calcium carbonate, gas phase titanium dioxide
13 parts of silicon, 11 parts of polyvinyl alcohol, 9 parts of sodium alginate, 9 parts of gelatin, 8 parts of sodium bicarbonate, 7 parts of konjaku glucomannan, low-methoxy
6 parts of pectin, 4 parts of citric acid, 5 parts of agar, 4 parts of Geniposide, 3 parts of polyglyceryl fatty acid ester, 900 parts of water.
The grain size of the nano-calcium carbonate is 30-50nm.
The preparation method of the degradable packaging film made using food wastes, is included the following steps:
(1) eggshell, sodium bicarbonate and Brazil wax are added in ultrasonic extraction tank, add the body of 5 times of weight
The ethyl alcohol of a concentration of 85%-95% of product, through ultrasonic extraction three times, gained filtrate decompression is distilled to recover ethyl alcohol to a concentration of 55%-
60%, precipitation is filtered out to get albumen powder and Brazil wax extracting solution after standing 12h;
(2) albumen powder, starch, analysis for soybean powder are mixed in the water for being added portionwise and being measured to 5 times under stirring, formed after mixing
Slurry, then the alkaline solution for being 3-5% with mass fraction adjust pH value to 6-7, then heat to 60-80 DEG C of stirring 20-30min
Form uniform paste mixing solution;
(3) sodium alginate and citric acid is added under stirring into remaining water, paste mixing solution is fully added after dissolving completely, receives
Rice calcium carbonate, aerosil and polyvinyl alcohol, mixture keep the temperature 20-25min after being warming up to 60-70 DEG C, add konjaku
Glucomannan, low methoxy pectin are continuously heating to 90-100 DEG C, and gelatin, agar, Geniposide and polyglycereol fat is then added
Acid esters reacts 45-60min, and mixed solution slow cooling cools down after reaction, is cooled to room temperature and Brazil wax extraction is added
Liquid is sufficiently mixed uniformly, finally filters into film liquid;
(4) first will be at film liquid in 3500-4000rpm/min homogenous disperse 10-15min, then base material will be coated at film liquid
On, then the dry 12-15h at 40-45 DEG C, film is taken off after dry, saves it in the closed container that ambient humidity is 55-60%
In.
The beneficial effects of the invention are as follows:The present invention is aided with various auxiliary agents using eggshell and starch as primary raw material, makes obtained
Packaging film has stronger physical mechanical property, selective penetrated property and antibacterial, antioxidation;And selected raw material is easily dropped
Solution, so as to avoid white pollution, preserves the ecological environment.
Specific implementation mode:
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1
A kind of degradable packaging film made using food wastes, is made of the raw material of following mass fraction:
60 parts of eggshell, 40 parts of starch, 15 parts of analysis for soybean powder, 12 parts of Brazil wax, 15 parts of nano-calcium carbonate, gas phase titanium dioxide
12 parts of silicon, 10 parts of polyvinyl alcohol, 8 parts of sodium alginate, 8 parts of gelatin, 6 parts of sodium bicarbonate, 5 parts of konjaku glucomannan, low-methoxy
5 parts of pectin, 3 parts of citric acid, 3 parts of agar, 3 parts of Geniposide, 2 parts of polyglyceryl fatty acid ester, 800 parts of water.
The grain size of the nano-calcium carbonate is 30nm.
The preparation method of the degradable packaging film made using food wastes, is included the following steps:
(1) eggshell, sodium bicarbonate and Brazil wax are added in ultrasonic extraction tank, add the body of 5 times of weight
The ethyl alcohol of product a concentration of 85%, through ultrasonic extraction three times, gained filtrate decompression is distilled to recover ethyl alcohol to a concentration of 55%, stands
Precipitation is filtered out after 12h to get albumen powder and Brazil wax extracting solution;
(2) albumen powder, starch, analysis for soybean powder are mixed in the water for being added portionwise and being measured to 5 times under stirring, formed after mixing
Slurry, then the alkaline solution for being 3% with mass fraction adjust pH value to 6, then heat to 60 DEG C of stirring 20min and form homogeneous powder
Paste solution;
(3) sodium alginate and citric acid is added under stirring into remaining water, paste mixing solution is fully added after dissolving completely, receives
Rice calcium carbonate, aerosil and polyvinyl alcohol, mixture keep the temperature 20min after being warming up to 60 DEG C, add konjak portuguese gansu polyose
Sugar, low methoxy pectin, are continuously heating to 90 DEG C, and gelatin, agar, Geniposide and polyglyceryl fatty acid ester, reaction is then added
45min, after reaction mixed solution slow cooling cooling, is cooled to room temperature and Brazil wax extracting solution is added, be sufficiently mixed
Uniformly, finally filter into film liquid;
(4) first will be at film liquid in 3500rpm/min homogenous disperse 10min, then will be coated on base material at film liquid, then exist
Dry 12h, film is taken off after dry at 40 DEG C, is saved it in the closed container that ambient humidity is 55%.
Embodiment 2
A kind of degradable packaging film made using food wastes, is made of the raw material of following mass fraction:
80 parts of eggshell, 50 parts of starch, 20 parts of analysis for soybean powder, 18 parts of Brazil wax, 18 parts of nano-calcium carbonate, gas phase titanium dioxide
15 parts of silicon, 12 parts of polyvinyl alcohol, 10 parts of sodium alginate, 10 parts of gelatin, 9 parts of sodium bicarbonate, 8 parts of konjaku glucomannan, low methoxy
8 parts of base pectin, 5 parts of citric acid, 6 parts of agar, 5 parts of Geniposide, 3 parts of polyglyceryl fatty acid ester, 1000 parts of water.
The grain size of the nano-calcium carbonate is 50nm.
The preparation method of the degradable packaging film made using food wastes, is included the following steps:
(1) eggshell, sodium bicarbonate and Brazil wax are added in ultrasonic extraction tank, add the body of 5 times of weight
The ethyl alcohol of product a concentration of 95%, through ultrasonic extraction three times, gained filtrate decompression is distilled to recover ethyl alcohol to a concentration of 60%, stands
Precipitation is filtered out after 12h to get albumen powder and Brazil wax extracting solution;
(2) albumen powder, starch, analysis for soybean powder are mixed in the water for being added portionwise and being measured to 5 times under stirring, formed after mixing
Slurry, then the alkaline solution for being 5% with mass fraction adjust pH value to 7, then heat to 80 DEG C of stirring 30min and form homogeneous powder
Paste solution;
(3) sodium alginate and citric acid is added under stirring into remaining water, paste mixing solution is fully added after dissolving completely, receives
Rice calcium carbonate, aerosil and polyvinyl alcohol, mixture keep the temperature 25min after being warming up to 70 DEG C, add konjak portuguese gansu polyose
Sugar, low methoxy pectin, are continuously heating to 100 DEG C, and gelatin, agar, Geniposide and polyglyceryl fatty acid ester, reaction is then added
60min, after reaction mixed solution slow cooling cooling, is cooled to room temperature and Brazil wax extracting solution is added, be sufficiently mixed
Uniformly, finally filter into film liquid;
(4) first will be at film liquid in 4000rpm/min homogenous disperse 15min, then will be coated on base material at film liquid, then exist
Dry 15h, film is taken off after dry at 45 DEG C, is saved it in the closed container that ambient humidity is 60%.
Embodiment 3
A kind of degradable packaging film made using food wastes, is made of the raw material of following mass fraction:
70 parts of eggshell, 45 parts of starch, 18 parts of analysis for soybean powder, 15 parts of Brazil wax, 16 parts of nano-calcium carbonate, gas phase titanium dioxide
13 parts of silicon, 11 parts of polyvinyl alcohol, 9 parts of sodium alginate, 9 parts of gelatin, 8 parts of sodium bicarbonate, 7 parts of konjaku glucomannan, low-methoxy
6 parts of pectin, 4 parts of citric acid, 5 parts of agar, 4 parts of Geniposide, 3 parts of polyglyceryl fatty acid ester, 900 parts of water.
The grain size of the nano-calcium carbonate is 40nm.
The preparation method of the degradable packaging film made using food wastes, is included the following steps:
(1) eggshell, sodium bicarbonate and Brazil wax are added in ultrasonic extraction tank, add the body of 5 times of weight
The ethyl alcohol of product a concentration of 95%, through ultrasonic extraction three times, gained filtrate decompression is distilled to recover ethyl alcohol to a concentration of 60%, stands
Precipitation is filtered out after 12h to get albumen powder and Brazil wax extracting solution;
(2) albumen powder, starch, analysis for soybean powder are mixed in the water for being added portionwise and being measured to 5 times under stirring, formed after mixing
Slurry, then the alkaline solution for being 4% with mass fraction adjust pH value to 7, then heat to 70 DEG C of stirring 25min and form homogeneous powder
Paste solution;
(3) sodium alginate and citric acid is added under stirring into remaining water, paste mixing solution is fully added after dissolving completely, receives
Rice calcium carbonate, aerosil and polyvinyl alcohol, mixture keep the temperature 25min after being warming up to 65 DEG C, add konjak portuguese gansu polyose
Sugar, low methoxy pectin, are continuously heating to 95 DEG C, and gelatin, agar, Geniposide and polyglyceryl fatty acid ester, reaction is then added
55min, after reaction mixed solution slow cooling cooling, is cooled to room temperature and Brazil wax extracting solution is added, be sufficiently mixed
Uniformly, finally filter into film liquid;
(4) first will be at film liquid in 3800rpm/min homogenous disperse 15min, then will be coated on base material at film liquid, then exist
Dry 14h, film is taken off after dry at 45 DEG C, is saved it in the closed container that ambient humidity is 60%.
The performance measurement result of 1 food package film of the present invention of table
Test event | Embodiment 1 | Embodiment 2 | Embodiment 3 | Ordinary food packaging film |
Tensile strength (MPa) | 30 | 35 | 32 | 11 |
Elongation at break (%) | 184 | 198 | 187 | 125 |
Light transmittance (%) | 91 | 93 | 92 | 89 |
Rate of perviousness (g/m2·24h) | 7.2 | 7.8 | 7.6 | 16 |
O2Transmitance (cm3/m2·24h) | 18 | 22 | 20 | 45 |
CO2Transmitance (cm3/m2·24h) | 12 | 14 | 11 | 26 |
Nerve | It is excellent | It is excellent | It is excellent | Generally |
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (4)
1. a kind of degradable packaging film made using food wastes, is made of the raw material of following mass fraction:Eggshell 60-80
Part, 40-50 parts of starch, 15-20 parts of analysis for soybean powder, 12-18 parts of Brazil wax, 15-18 parts of nano-calcium carbonate, aerosil
12-15 parts, 10-12 parts of polyvinyl alcohol, 8-10 parts of sodium alginate, 8-10 parts of gelatin, 6-9 parts of sodium bicarbonate, konjaku glucomannan
5-8 parts, 5-8 parts of low methoxy pectin, 3-5 parts of citric acid, 3-6 parts of agar, 3-5 parts of Geniposide, polyglyceryl fatty acid ester 2-3
Part, 800-1000 parts of water.
2. the degradable packaging film according to claim 1 made using food wastes, it is characterised in that:It is preferred that as follows
The raw material of mass fraction is made, 70 parts of eggshell, 45 parts of starch, 18 parts of analysis for soybean powder, 15 parts of Brazil wax, nano-calcium carbonate 16
Part, 13 parts of aerosil, 11 parts of polyvinyl alcohol, 9 parts of sodium alginate, 9 parts of gelatin, 8 parts of sodium bicarbonate, konjaku glucomannan
7 parts, 6 parts of low methoxy pectin, 4 parts of citric acid, 5 parts of agar, 4 parts of Geniposide, 3 parts of polyglyceryl fatty acid ester, 900 parts of water.
3. the degradable packaging film according to claim 1 made using food wastes, it is characterised in that:The nanometer
The grain size of calcium carbonate is 30-50nm.
4. the degradable packaging film according to claim 1 made using food wastes, it is characterised in that:Its making side
Method includes the following steps:
(1) eggshell, sodium bicarbonate and Brazil wax are added in ultrasonic extraction tank, the volume for adding 5 times of weight is dense
Degree is the ethyl alcohol of 85%-95%, through ultrasonic extraction three times, gained filtrate decompression distillation recovery ethyl alcohol to a concentration of 55%-60%,
Precipitation is filtered out to get albumen powder and Brazil wax extracting solution after standing 12h;
(2) albumen powder, starch, analysis for soybean powder are mixed in the water for being added portionwise and being measured to 5 times under stirring, form powder after mixing
Slurry, then the alkaline solution for being 3-5% with mass fraction adjust pH value to 6-7, then heat to 60-80 DEG C of stirring 20-30min shape
At uniform paste mixing solution;
(3) sodium alginate and citric acid is added under stirring into remaining water, paste mixing solution, nano-sized carbon fully is added after dissolving completely
Sour calcium, aerosil and polyvinyl alcohol, mixture keep the temperature 20-25min after being warming up to 60-70 DEG C, add Amorphophallus rivieri glucomannan
Glycan, low methoxy pectin are continuously heating to 90-100 DEG C, and gelatin, agar, Geniposide and polyglycerol fatty acid is then added
Ester reacts 45-60min, and mixed solution slow cooling cools down after reaction, is cooled to room temperature and Brazil wax extraction is added
Liquid is sufficiently mixed uniformly, finally filters into film liquid;
(4) first will be at film liquid in 3500-4000rpm/min homogenous disperse 10-15min, then will be coated on base material at film liquid, so
The dry 12-15h at 40-45 DEG C afterwards, film is taken off after dry, is saved it in the closed container that ambient humidity is 55-60%.