CN108340648A - Surfing paddle board made from the preparation method and this method of surfing paddle board - Google Patents
Surfing paddle board made from the preparation method and this method of surfing paddle board Download PDFInfo
- Publication number
- CN108340648A CN108340648A CN201810135847.9A CN201810135847A CN108340648A CN 108340648 A CN108340648 A CN 108340648A CN 201810135847 A CN201810135847 A CN 201810135847A CN 108340648 A CN108340648 A CN 108340648A
- Authority
- CN
- China
- Prior art keywords
- inner core
- panel
- paddle board
- bottom plate
- surfing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of preparation methods of surfing paddle board, and two layers of epoxy resin and glass-fiber-fabric are at least brushed in the both side surface up and down of inner core;Bottom plate and panel are respectively placed in below inner core and above, binded with inner core;The panel to stick together, inner core and bottom plate are wrapped up with plastic film;Again by way of vacuumizing, inner core is made to be combined into one with panel, bottom plate;After continuing 3~6 minutes, the plastic film of removal vacuum package.The preparation method of surfing paddle board provided by the invention, eliminates craft in the prior art or the step of mould heat pressure pastes, simplification improves manufacturing process, enhances the stability between each layer of paddle board, improves production efficiency, and product rejection rate is extremely low.
Description
Technical field
The present invention relates to technical field of sports apparatus, particularly, are related to a kind of preparation method and this method of surfing paddle board
Surfing paddle board obtained.
Background technology
Paddle board is for sportsman's surfing, the sports equipment struck, raced.Paddle board is to utilize fortune with paddle and/or wave for power
Itself showmanship and balanced capacity are mobilized, water wave is fought with or obtains a movement of the sense of equilibrium waterborne and speed sense.Paddle
Plate movement is that sportsman first kneels sleeping or stands on paddle board, is paddled to certain speed, or when wave pushes paddle board sliding
When to certain speed, sportsman makes paddle board keep balance, opens naturally before and after two legs, and two knees are micro- to bend, and is accelerated with paddle, or with wave by
Wave quickly slides.There are mainly two types of existing surfing paddle board production methods:
The first glass epoxy, center core are light foam, first use mold foaming that inner core is made, then in inner core table
Face pastes multilayer carbon fiber cloth etc. with epoxy resin, then covers one layer thicker of epoxy resin re-polishing, to increase its intensity and prevent
Water.It is that craft or mould heat pressure paste that the surface of the production method, which pastes, and efficiency is low, and yield is not high, easily scraps, surfacing
It selects relatively simple;In addition, existing glass epoxy production method can not be done in glass epoxy surface (including top and bottom)
Some complicated shapes (shape such as sharp-featured, depth disparity is big) and color jump, bright-coloured color lump.It is such
Surfing panel products hydrophily is strong, but easy clashing and breaking, and maintenance Expenses Cost is higher, is suitble to high-end user group.
Second of gas panel, using DWF wire drawings cloth and PVC waterproof fabrics, the PVC folders of upper layer and lower layer single layer or bilayer
Screen cloth or reinforcement are held by rope one by one, in order that having better stability and planarization, side by double-deck or
The PVC of single layer is sealed, and EVA sliding-proof pads are then used on surface, is stood with facilitating.Production method be it is hand-made, comparatively efficiency compared with
It is low.Such surfing panel products have portability, still, since using needing inflation to deflate, it is great to expend user every time
Muscle power and time, and need to give shade maintenance, otherwise spoilage can be relatively high.
Surfing paddle board is to use glass epoxy earliest, and glass epoxy is exactly " hardboard " that we are commonly called as, using carbon fiber+glass
Method, glass epoxy hydrophily is strong, but is easy to collide with, and due at high price, repair and cost of upkeep are very high.Later in order to
It being convenient for carrying, there is gas panel, gas panel is inflatable, is convenient for carrying, convenient for travelling leisure, scratch-resistant crashworthiness, and opposite fiberglass
It is cheap for plate.
But since for new hand and experiencer, the stability of equilibrium of hardboard is more preferable, it is more suitable for beginner's use,
For most of clubs, use will inflate gas panel every time, and be in inflated condition for a long time, or the ring being exposed to the sun
Under border, it is extremely easy to happen explosion, therefore for individual is particularly with club, using gas panel, not only cumbersome trouble,
And loss is very high, and use glass epoxy, then it is with high costs.
Invention content
The present invention provides a kind of preparation methods of surfing paddle board, eliminate craft in the prior art or mould heat pressure pastes
The step of, simplification improves manufacturing process, enhances the stability between each layer of paddle board, improves production efficiency, and product report
Useless rate is extremely low.
The present invention also provides a kind of surfing paddle boards, and sound construction, survivable abrasion, service life is long, comprehensive performance
It is good, be suitable for beginner, and it is of low cost, facilitate maintenance.
To achieve the above object, the present invention proposes a kind of preparation method of surfing paddle board, includes the following steps:
(1) expanded material is used to prepare surfing paddle board inner core by foaming;
(2) molding is cut using the panel material and baseboard material that are different from inner core material respectively and panel and bottom plate is made;
(3) two layers of epoxy resin+glass-fiber-fabric is at least brushed in the both side surface up and down of inner core;
(4) bottom plate and panel are respectively placed in below inner core and above, are binded with inner core;
(5) panel, inner core and bottom plate that step (4) sticks together are wrapped up with plastic film;
(6) by way of vacuumizing, inner core is made to be combined into one with panel, bottom plate;
(7) after step (6) continues 3~6 minutes, the plastic film of removal vacuum package;
The panel is selected from ethylene-vinyl acetate copolymer, electronic crosslinked polyethylene or acrylonitrile-butadiene-styrene (ABS)
One kind in copolymer;
The bottom plate is selected from makrolon, high density polyethylene (HDPE), polyamide or acrylonitrile-butadiene-styrene copolymer
In one kind.
Preferably, the inner core uses expandable polystyrene foaming.
Preferably, the bottom plate is made using acrylonitrile-butadiene-styrene copolymer.
Preferably, the step (3) inner core two layers of the epoxy resin of brushing of both side surface up and down, and in every layer of asphalt mixtures modified by epoxy resin
Glass-fiber-fabric is laid in lipid layer.
The invention also provides a kind of surfing paddle boards, including inner core and the panel and the bottom that fit in the inner core upper and lower surface
Plate is made by above-mentioned preparation method.
Advantageous effect:
The preparation method of surfing paddle board provided by the invention, by the upper and lower surface of inner core brushwork epoxy resin repeatedly
And glass-fiber-fabric, in conjunction with vacuum pumping method so that panel and bottom plate are close therewith, strength viscous on the upper and lower surface of inner core respectively
Be combined to form a firm entirety, optimize in technique more science, rationally, eliminate craft in the prior art or mold
The step of hot pressing pastes, process implementing are more convenient, efficient.
Surfing paddle board provided by the invention, comprehensive performance is good and heat-resisting, and high temperature resistant is corrosion-resistant, crashworthiness;Balance existing skill
Contradiction existing for the glass epoxy and gas panel of art also has while realizing solid paddle board, durable, service free and safeguard
There is better stability of equilibrium, is suitable for beginner, and of low cost.
Description of the drawings
Fig. 1 is the structural schematic diagram of 1 surfing paddle board of the embodiment of the present invention;
In figure:1- inner cores;2- panels;3- bottom plates;4- epoxy resin+glass layer of cloth.
Specific implementation mode
In order to make the foregoing objectives, features and advantages of the present invention clearer and more comprehensible, below in conjunction with the accompanying drawings and specific real
Applying mode, the present invention is described in further detail.
Embodiment 1
The present embodiment provides a kind of surfing paddle board, referring to Fig. 1, including inner core 1 and 1 upper and lower surface of the inner core is fitted in
Panel 2 and bottom plate 3 are painted with epoxy resin+glass layer of cloth 4 between inner core 1 and panel 2, inner core 1 and bottom plate 3, prepare
Method includes the following steps:
(1) expanded material is used to prepare surfing paddle board inner core by foaming;
(2) molding is cut using the panel material and baseboard material that are different from inner core material respectively and panel and bottom plate is made;
(3) in two layers of epoxy resin+glass-fiber-fabric of the brushing of both side surface up and down of inner core;
(4) bottom plate and panel are respectively placed in below inner core and above, are binded with inner core;
(5) panel, inner core and bottom plate that step (4) sticks together are wrapped up with plastic film;
(6) by way of vacuumizing, inner core is made to be combined into one with panel, bottom plate;
(7) after step (6) continues 6 minutes, the plastic film of removal vacuum package;
Wherein, the inner core uses expandable polystyrene foaming;The panel and bottom plate are all made of acrylic nitrile-butadiene
Diene-styrene copolymer (ABS).
The present embodiment surfing paddle board, the bonding force of inner core and bottom plate, bottom plate is strong, and stability is good, and comprehensive performance is good, resistance to
Heat, high temperature resistant is corrosion-resistant, crashworthiness, service free and maintenance, of low cost, and surface can also do a variety of figures, shape design, shape
Formula change is various.
Optionally, panel and baseboard material can freely be selected according to environmental requirement, and surface can also make some corner angle
Clearly, the big complicated shape of depth disparity solves the abrasion of glass epoxy destructible, the cumbersome link of inflation deflation of gas panel.
Embodiment 2
The present embodiment provides a kind of surfing paddle board, difference from Example 1 is, wherein step (7) is in step (6)
After continuing 3 minutes, the plastic film of removal vacuum package.
Wherein, the inner core uses expandable polystyrene foaming;The panel is copolymerized using ethene-vinyl acetate
Object (EVA);The bottom plate uses electronic crosslinked polyethylene expanded material (IXPE).
Other with it is consistent described in embodiment 1.
Embodiment 3
The present embodiment provides a kind of surfing paddle board, difference from Example 1 is, wherein step (7) is in step (6)
Continue after five minutes, the plastic film of removal vacuum package.
Wherein, the inner core uses expandable polystyrene foaming;The panel is sent out using electronic crosslinked polyethylene
Foam material (IXPE);The bottom plate uses high density polyethylene (HDPE).
The embodiment of the present invention is described in detail above, specific case used herein to the principle of the present invention and
Embodiment is expounded, and the explanation of above example is only intended to facilitate the understanding of the method and its core concept of the invention;
Meanwhile for those of ordinary skill in the art, according to the thought of the present invention, can in specific embodiments and applications
There is change place, in conclusion the content of the present specification should not be construed as limiting the invention.
Claims (5)
1. a kind of preparation method of surfing paddle board, which is characterized in that include the following steps:
(1) expanded material is used to prepare surfing paddle board inner core by foaming;
(2) molding is cut using the panel material and baseboard material that are different from inner core material respectively and panel and bottom plate is made;
(3) two layers of epoxy resin+glass-fiber-fabric is at least brushed in the both side surface up and down of inner core;
(4) bottom plate and panel are respectively placed in below inner core and above, are binded with inner core;
(5) panel, inner core and bottom plate that step (4) sticks together are wrapped up with plastic film;
(6) by way of vacuumizing, inner core is made to be combined into one with panel, bottom plate;
(7) after step (6) continues 3~6 minutes, the plastic film of removal vacuum package;
The panel is selected from ethylene-vinyl acetate copolymer, electronic crosslinked polyethylene or acrylonitrile-butadiene-styrene (ABS) copolymerization
One kind in object;
The bottom plate is in makrolon, high density polyethylene (HDPE), polyamide or acrylonitrile-butadiene-styrene copolymer
It is a kind of.
2. the preparation method of surfing paddle board according to claim 1, which is characterized in that the inner core uses expandability polyphenyl
Ethylene foaming.
3. the preparation method of surfing paddle board according to claim 1, which is characterized in that the bottom plate uses acrylic nitrile-butadiene
Diene-styrene copolymer is made.
4. the preparation method of surfing paddle board according to claim 1, which is characterized in that the step (3) is in the upper of inner core
Two layers of epoxy resin of lower both side surface brushing, and it is laid with glass-fiber-fabric on every layer of epoxy resin layer.
5. a kind of surfing paddle board, including inner core and the panel and bottom plate that fit in the inner core upper and lower surface, which is characterized in that root
It is made according to any preparation method of Claims 1-4.