CN108340129A - A kind of preparation method of the stainless steel and carbon steel composite tube on the deposited side of easy welding - Google Patents
A kind of preparation method of the stainless steel and carbon steel composite tube on the deposited side of easy welding Download PDFInfo
- Publication number
- CN108340129A CN108340129A CN201810203210.9A CN201810203210A CN108340129A CN 108340129 A CN108340129 A CN 108340129A CN 201810203210 A CN201810203210 A CN 201810203210A CN 108340129 A CN108340129 A CN 108340129A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- welding
- clad plate
- pipe
- tube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of method that stainless steel tube is rolled into multiple tube with carbon steel pipe, belongs to metal composite pipe manufacturing process technology field.It is characterized in:(1)Make blank using the stainless steel clad plate manufactured in entitled " the easily manufacturing method of the deposited side stainless steel clad plate of welding ";(2)The surrounding of composite plate blanks is applied into side milling and goes out welding groove, the impurity such as grinder buffing removal iron scale are used in combination;(3)Bend to the tubulose of opening to stainless steel clad plate with the JCO methods of forming on bend pipe shaping apparatus;(4)Side is applied using argon arc welding or agitating friction welding method along the stainless steel of stainless steel clad plate after bending to be welded;(5)Soldered stainless steel composite pipe is subjected to oblique milling thermal expansion on diagonal rolling expanding pipe;(6)Carry out subsequent heat treatment and tube surfaces polishing.Advantage is:The double layer of metal multiple tube of this method production is easy welding, improves production efficiency, enhances weld seam bond strength.
Description
Technical field
The invention belongs to stainless steels and carbon steel composite tube technology of preparing neighborhood, and in particular to it is a kind of it is easy welding apply side it is stainless
The preparation method of steel and carbon steel composite tube.
Background technology
Stainless steel and carbon steel composite tube are a kind of widely used composite bimetal pipes, and giving full play to, base tube carbon steel layer is excellent
The feature for covering that pipe stainless steel layer is corrosion-resistant, wear-resisting and specious is remained while good mechanical mechanics property, is saved
Material.Space is had a wide range of applications in oil, petrochemical industry and the stronger environment of marine corrosive.
Stainless steel and carbon steel composite tube in actual use, the connectivity problem of bimetal tube is always current skill
Art problem.Especially pipeline of the diameter between 100mm-200mm causes existing since the ingredient properties of two kinds of metals are different
Welding technique it is difficult to ensure that welding quality.Application No. is 201210408747.1 patent applications to disclose a kind of stainless steel
Combined Welding takes over and its manufacturing method, is first to weld middle layer using protection weldering, then use stainless steel electrode in its patent document
Stainless steel cladding welding is welded out in a manner of argon arc welding welding, is then used carbon steel to exchange submerged arc welding and is gone out carbon steel weldering
Seam.This technology is when welding two pieces unlike material, very airplane crash.And production efficiency is low, and cost increases.
Existing composite tube welding technology, different-metal material welding base, transition zone, coating use different welding methods, make
Increase at the welding difficulty increase of stainless steel composite pipe, inefficiency, cost.
Invention content
It is an object of the present invention to provide the preparation methods that the stainless steel composite pipe on side is applied in a kind of easy welding, can be efficiently against both
There is disadvantage present in technology.
The invention is realized in this way, it is characterised in that implementation is as follows:
(1)Using application No. is a kind of 201610078667.2, entitled " manufactures of the easy deposited side stainless steel clad plate of welding
The stainless steel of method " manufacture makees blank with carbon steel composite board;
(2)The surrounding of above-mentioned stainless steel and carbon steel composite board is applied into side milling and goes out the welding groove that angle α is 45 ° -60 °, sand is used in combination
The impurity such as wheel polishing removal iron scale, make surfacing, as shown in Figure 1;
(3)It is detected a flaw with carbon steel composite board to above-mentioned stainless steel using ultrasonic wave, the JCO methods of forming is used on bend pipe shaping apparatus
The tubulose of opening is bent to stainless steel clad plate, and composite plate both ends stainless steel of the same race is made to apply the groove opening on side after bending
Distance d is 10-15mm, as shown in Figure 2;
(4)Using welding methods such as argon arc welding or agitating friction welderings along the stainless steel of stainless steel after bending and carbon steel composite tube base
It is welded on deposited side;
(5)Machinery expanding:Soldered stainless steel composite pipe is heated to 1050 DEG C -1150 DEG C, it is enterprising in diagonal rolling expanding pipe
Row oblique milling thermal expansion, expanding relative quantity are 50% -70%;
(6)Carry out subsequent heat treatment and tube surfaces polishing.
Advantage of the present invention and good effect:
With advantages of the present invention compared with conventional method:The present invention solves current double layer of metal multiple tube difficulty welding, efficiency
Low problem.The double layer composite board that steel plate both ends are high strength stainless steel materials of the same race is produced first, is then bent to stainless
Steel pipe, and be welded to connect, this method is more advantageous to the welding between multiple tube.To simplified two layers of multiple tube
Welding procedure improves production efficiency.
Description of the drawings
Fig. 1 is that easily side stainless steel and carbon steel composite board are applied in welding
Fig. 2 is the schematic diagram that composite plate bends to composite pipe blank
1-carbon steel in figure, 2-stainless steels, 3-stainless steels apply side, 4-weld seams.
Specific implementation:
Now by taking 316 stainless steels are to cover pipe, 15CrMoR steel for the multiple tube of base tube as an example, production stage is as follows:
1. as shown in Figure 1, according to compound application No. is double-layer stainless steel/carbon steel is manufactured in 201610078667.2 patent of invention
Plate is pipe, and base is the 14CrMoR steel of 14mm thickness, and coating is 316 stainless steels of 3mm thickness, and corrugated applies the corrugated interfaces on side
Trough a height of 2.4mm, wavelength 9.6mm, it is 4.5mm to apply side thickness;
2. milling side:The surrounding of composite plate is applied into side milling and goes out the welding groove that angle α is 60 °, grinder buffing is used in combination to remove iron oxide
The impurity such as skin, make surfacing;
3. detecting a flaw to stainless steel clad plate using ultrasonic wave, use the JCO methods of forming by stainless steel double on bend pipe shaping apparatus
Plywood bends to the tubulose of opening, includes J moldings, bending C moldings and the O forming of pre-bending, makes composite plate both ends of the same race after bending
The groove extended distance d that stainless steel applies side is 13mm;
4. applying side along the stainless steel of stainless steel clad plate after bending using welding methods such as argon arc welding or agitating friction welderings to carry out
Welding, 4 width of weld seam are 13mm;
5. soldered stainless steel composite pipe is heated to 1050 DEG C, oblique milling thermal expansion is carried out on diagonal rolling expanding pipe, relatively
Expanding amount is 60%;
6. carrying out other heat treatments.
Claims (1)
1. a kind of stainless steel that side is applied in easy welding is rolled into the preparation method of multiple tube with carbon steel, it is characterized in that:(1)Request for utilization
Number for 201610078667.2, the stainless steel clad plate of entitled " easily the manufacturing method of side stainless steel clad plate is applied in welding " manufacture
Make blank;(2)The surrounding of above-mentioned composite plate is applied into side milling and goes out welding groove, the angle α of welding groove is 60 °, and grinding wheel is used in combination to beat
It grinds off except impurity such as iron scales, makes surfacing;
(3)Stainless steel clad plate is bent to on bend pipe shaping apparatus with the JCO methods of forming tubulose of opening;
(4)Side is applied using argon arc welding or agitating friction welding method along the stainless steel of stainless steel clad plate after bending to be welded
It connects;
(5)Soldered stainless steel composite pipe is heated to 1050 DEG C -1150 DEG C, oblique milling heat is carried out on diagonal rolling expanding pipe
Expanding, expanding relative quantity is 50% -70%;
(6)Carry out subsequent heat treatment and tube surfaces polishing.