CN108329791A - A kind of insulating paint for motor and preparation method thereof - Google Patents
A kind of insulating paint for motor and preparation method thereof Download PDFInfo
- Publication number
- CN108329791A CN108329791A CN201711380081.2A CN201711380081A CN108329791A CN 108329791 A CN108329791 A CN 108329791A CN 201711380081 A CN201711380081 A CN 201711380081A CN 108329791 A CN108329791 A CN 108329791A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulating paint
- paint
- preparation
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of insulating paint for motor and preparation method thereof, the manufacture material of the insulated paint includes following mass fraction：25 30 parts of phenolic resin, 18 20 parts of polyurethane, 18 23 parts of vinylacetate, 15 20 parts of phenyl vinyl polysiloxane, 15 18 parts of mica powder, 8 13 parts of glass fibre, 56 parts of dilauroyl peroxide, 10 14 parts of bentonite, 58 parts of boron compound, 46 parts of antimony oxide.The present invention is using the insulated paint of the present invention for computer cable using phenolic resin, Organic Sodium Salt modified soluble acrylic emulsion, polyurethane, vinylacetate, phenyl vinyl polysiloxane as raw material, it cooperates between raw material, the insulated paint performance prepared is stablized, good insulation preformance, film-formation result is good, the additives such as fire retardant, curing agent are added in insulated paint, significantly improve the overall performance of insulated paint, use scope is wider, and the preparation method of this insulating paint for motor is simple, easy to operate, is suitble to industrial production.
Description
Technical field
The present invention relates to technical field of motors, specially a kind of insulating paint for motor and preparation method thereof.
Background technology
Motor refers to a kind of calutron realized electric energy conversion according to the law of electromagnetic induction or transmitted, its main function
It is to be converted into electric energy using mechanical energy, generates driving torque, it is most common at present as electrical appliance or the power source of various machineries
It is to be generated electricity using pushing generators rotors such as thermal energy, water energy, with reaching its maturity for wind generating technology, wind-powered electricity generation also tromps
Into our life, working power type divides：Direct current generator and alternating current generator can be divided into, dc motor is to rely on direct current work
Make voltage-operated motor, is widely used in radio cassette player, video recorder, video disc player, electric shaver, hair dryer, electronic watch, object for appreciation
Tool etc..
Many circuits are distributed in the inside of motor, and these line insulation performances are that many motor original papers or equipment are necessary
The performance of satisfaction, while protecting motor running, coating also must satisfy above-mentioned performance, although many coating are with good at present
Good insulation performance, but the problem of due to coating stability and film-formation result, and can not be used on these motor lines roads, it is
This, it is proposed that a kind of insulating paint for motor and preparation method thereof.
Invention content
The purpose of the present invention is to provide a kind of insulating paint for motor and preparation method thereof, to solve to propose in background technology
The problem of.
To achieve the above object, the present invention provides the following technical solutions：A kind of insulating paint for motor and preparation method thereof, institute
The manufacture material for stating insulated paint includes following mass fraction：25-30 parts of phenolic resin, 18-20 parts of polyurethane, vinylacetate
18-23 parts, 15-20 parts of phenyl vinyl polysiloxane, 15-18 parts of mica powder, 8-13 parts of glass fibre, dilauroyl peroxide 5-6
Part, 10-14 parts of bentonite, 5-8 parts of boron compound, 4-6 parts of antimony oxide, 15-20 parts of linoleic acid, 3-6 parts of Ricinate,
3-6 parts of fire retardant, 3-4 parts of antifoaming agent, 2-3 parts of curing agent, 3-4 parts of diluent, 25-30 parts of acrylic emulsion.
Preferably, the manufacture material of the insulated paint includes following mass fraction：28 parts of phenolic resin, 19 parts of polyurethane,
20 parts of vinylacetate, 17 parts of phenyl vinyl polysiloxane, 17 parts of mica powder, 10 parts of glass fibre, dilauroyl peroxide 5.5
Part, 4 parts of fire retardant, disappears at 12 parts of bentonite, 7 parts of boron compound, 5 parts of antimony oxide, 18 parts of linoleic acid, 5 parts of Ricinate
3.5 parts of infusion, 2.5 parts of curing agent, 3.5 parts of diluent, 28 parts of acrylic emulsion.
Preferably, the fire retardant is one kind in halogenated flame retardant and magnesium hydroxide.
Preferably, the antifoaming agent is one kind in silicone emulsion and polyethers antifoaming agent.
Preferably, the curing agent is one kind in vinyl triamine and ethylenediamine.
Preferably, the diluent is one kind in ethyl alcohol and ethyl acetate.
Preferably, the preparation method of the insulated paint includes the following steps：
（1）Phenolic resin, polyurethane, vinylacetate, phenyl vinyl polysiloxane, the cloud of certain number are weighed by above-mentioned formula
It is female powder, glass fibre, dilauroyl peroxide, bentonite, boron compound, antimony oxide, linoleic acid, Ricinate, fire-retardant
Agent, antifoaming agent, curing agent, diluent, acrylic emulsion are spare；
（2）Vinylacetate is put into reaction kettle, phenyl vinyl polysiloxane, mica powder, glass fibre, stirring is then added
Antimony oxide, linoleic acid, Ricinate, fire retardant, antifoaming agent, solidification is added after evenly dispersed in mixing 2-3 hours
Agent, diluent, after mixing, mixture A is made in ground filtering；
（3）Phenolic resin, Organic Sodium Salt modified soluble acrylic emulsion, polyurethane are put into reaction kettle, at 80-95 DEG C
At a temperature of, it stirs 30-40 minutes, dilauroyl peroxide 1-2h is then added, bentonite and boron compound are added, with 2300-
The rotating speed of 2500r/min disperses 3-4 hours, and mixture B is made；
（4）By step（2）The mixture A and step of gained（3）The mixture B of gained is uniformly mixed, and is ultrasonically treated 25-30 points
Clock is to get the insulating paint for motor.
The present invention is using the insulated paint of the present invention for computer cable using phenolic resin, Organic Sodium Salt modified water
Soluble acrylic lotion, polyurethane, vinylacetate, phenyl vinyl polysiloxane are cooperated between raw material as raw material, are made
Stablize for the insulated paint performance gone out, good insulation preformance, film-formation result is good, and the additions such as fire retardant, curing agent are added in insulated paint
Agent significantly improves the overall performance of insulated paint, and use scope is wider, and the preparation method of this insulating paint for motor it is simple,
It is easy to operate, it is suitble to industrial production.
Specific implementation mode
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is only
It is a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ordinary skill people
The every other embodiment that member is obtained without making creative work, shall fall within the protection scope of the present invention.
Embodiment one：
A kind of insulating paint for motor and preparation method thereof, the manufacture material of the insulated paint includes following mass fraction：Phenolic aldehyde tree
25 parts of fat, 18 parts of polyurethane, 18 parts of vinylacetate, 15 parts of phenyl vinyl polysiloxane, 15 parts of mica powder, 8 parts of glass fibre,
5 parts of dilauroyl peroxide, 10 parts of bentonite, 5 parts of boron compound, 4 parts of antimony oxide, 15 parts of linoleic acid, Ricinate 3
Part, 3 parts of fire retardant, 3 parts of antifoaming agent, 2 parts of curing agent, 3 parts of diluent, 25 parts of acrylic emulsion.
The fire retardant is halogenated flame retardant.
The antifoaming agent is silicone emulsion.
The curing agent is vinyl triamine.
The diluent is ethyl alcohol.
The preparation method of the insulated paint includes the following steps：
（1）Phenolic resin, polyurethane, vinylacetate, phenyl vinyl polysiloxane, the cloud of certain number are weighed by above-mentioned formula
It is female powder, glass fibre, dilauroyl peroxide, bentonite, boron compound, antimony oxide, linoleic acid, Ricinate, fire-retardant
Agent, antifoaming agent, curing agent, diluent, acrylic emulsion are spare；
（2）Vinylacetate is put into reaction kettle, phenyl vinyl polysiloxane, mica powder, glass fibre, stirring is then added
Mixing 2 hours, after evenly dispersed, be added antimony oxide, linoleic acid, Ricinate, fire retardant, antifoaming agent, curing agent,
Diluent, after mixing, mixture A is made in ground filtering；
（3）Phenolic resin, Organic Sodium Salt modified soluble acrylic emulsion, polyurethane are put into reaction kettle, in 80 DEG C of temperature
It under degree, stirs 30 minutes, dilauroyl peroxide 1h is then added, adds bentonite and boron compound, with turning for 2300r/min
Speed dispersion 3 hours, is made mixture B；
（4）By step（2）The mixture A and step of gained（3）The mixture B of gained is uniformly mixed, supersound process 25 minutes, i.e.,
Obtain the insulating paint for motor.
Embodiment two：
A kind of insulating paint for motor and preparation method thereof, the manufacture material of the insulated paint includes following mass fraction：Phenolic aldehyde tree
28 parts of fat, 19 parts of polyurethane, 20 parts of vinylacetate, 18 parts of phenyl vinyl polysiloxane, 17 parts of mica powder, glass fibre 11
Part, 5.5 parts of dilauroyl peroxide, 12 parts of bentonite, 7 parts of boron compound, 5 parts of antimony oxide, 18 parts of linoleic acid, moistening dispersion
5 parts of agent, 5 parts of fire retardant, 3.5 parts of antifoaming agent, 2.5 parts of curing agent, 3.5 parts of diluent, 28 parts of acrylic emulsion.
The fire retardant is in magnesium hydroxide.
The antifoaming agent is polyethers antifoaming agent.
The curing agent is in ethylenediamine.
The diluent is ethyl acetate.
The preparation method of the insulated paint includes the following steps：
（1）Phenolic resin, polyurethane, vinylacetate, phenyl vinyl polysiloxane, the cloud of certain number are weighed by above-mentioned formula
It is female powder, glass fibre, dilauroyl peroxide, bentonite, boron compound, antimony oxide, linoleic acid, Ricinate, fire-retardant
Agent, antifoaming agent, curing agent, diluent, acrylic emulsion are spare；
（2）Vinylacetate is put into reaction kettle, phenyl vinyl polysiloxane, mica powder, glass fibre, stirring is then added
Antimony oxide, linoleic acid, Ricinate, fire retardant, antifoaming agent, solidification is added after evenly dispersed in mixing 2.5 hours
Agent, diluent, after mixing, mixture A is made in ground filtering；
（3）Phenolic resin, Organic Sodium Salt modified soluble acrylic emulsion, polyurethane are put into reaction kettle, in 88 DEG C of temperature
Under degree, stirs 35 minutes, dilauroyl peroxide 1.5h is then added, bentonite and boron compound are added, with 2400r/min's
Rotating speed disperses 3.5 hours, and mixture B is made；
（4）By step（2）The mixture A and step of gained（3）The mixture B of gained is uniformly mixed, supersound process 28 minutes, i.e.,
Obtain the insulating paint for motor.
Embodiment three：
A kind of insulating paint for motor and preparation method thereof, the manufacture material of the insulated paint includes following mass fraction：Phenolic aldehyde tree
30 parts of fat, 20 parts of polyurethane, 23 parts of vinylacetate, 20 parts of phenyl vinyl polysiloxane, 18 parts of mica powder, glass fibre 13
Part, 6 parts of dilauroyl peroxide, 10 parts of bentonite, 5 parts of boron compound, 4 parts of antimony oxide, 15 parts of linoleic acid, Ricinate
3 parts, 3 parts of fire retardant, 4 parts of antifoaming agent, 3 parts of curing agent, 3 parts of diluent, 25 parts of acrylic emulsion.
The fire retardant is halogenated flame retardant.
The antifoaming agent is in polyethers antifoaming agent.
The curing agent is ethylenediamine.
The diluent is in ethyl alcohol and ethyl acetate.
The preparation method of the insulated paint includes the following steps：
（1）Phenolic resin, polyurethane, vinylacetate, phenyl vinyl polysiloxane, the cloud of certain number are weighed by above-mentioned formula
It is female powder, glass fibre, dilauroyl peroxide, bentonite, boron compound, antimony oxide, linoleic acid, Ricinate, fire-retardant
Agent, antifoaming agent, curing agent, diluent, acrylic emulsion are spare；
（2）Vinylacetate is put into reaction kettle, phenyl vinyl polysiloxane, mica powder, glass fibre, stirring is then added
Mixing 3 hours, after evenly dispersed, be added antimony oxide, linoleic acid, Ricinate, fire retardant, antifoaming agent, curing agent,
Diluent, after mixing, mixture A is made in ground filtering；
（3）Phenolic resin, Organic Sodium Salt modified soluble acrylic emulsion, polyurethane are put into reaction kettle, in 95 DEG C of temperature
It under degree, stirs 40 minutes, dilauroyl peroxide 2h is then added, adds bentonite and boron compound, with turning for 2500r/min
Speed dispersion 4 hours, is made mixture B；
（4）By step（2）The mixture A and step of gained（3）The mixture B of gained is uniformly mixed, supersound process 30 minutes, i.e.,
Obtain the insulating paint for motor.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of insulating paint for motor and preparation method thereof, it is characterised in that：The manufacture material of the insulated paint includes following matter
Measure score：25-30 parts of phenolic resin, 18-20 parts of polyurethane, 18-23 parts of vinylacetate, phenyl vinyl polysiloxane 15-20
Part, 15-18 parts of mica powder, 8-13 parts of glass fibre, 5-6 parts of dilauroyl peroxide, 10-14 parts of bentonite, boron compound 5-8
Part, 4-6 parts of antimony oxide, 15-20 parts of linoleic acid, 3-6 parts of Ricinate, 3-6 parts of fire retardant, 3-4 parts of antifoaming agent, solidification
2-3 parts of agent, 3-4 parts of diluent, 25-30 parts of acrylic emulsion.
2. a kind of insulating paint for motor according to claim 1 and preparation method thereof, it is characterised in that：The insulated paint
Manufacture material includes following mass fraction：28 parts of phenolic resin, 19 parts of polyurethane, 20 parts of vinylacetate, phenyl vinyl silicon
17 parts of resin, 17 parts of mica powder, 10 parts of glass fibre, 5.5 parts of dilauroyl peroxide, 12 parts of bentonite, 7 parts of boron compound, three
Aoxidize 5 parts of two antimony, 18 parts of linoleic acid, 5 parts of Ricinate, 4 parts of fire retardant, 3.5 parts of antifoaming agent, 2.5 parts of curing agent, diluent
3.5 parts, 28 parts of acrylic emulsion.
3. a kind of insulating paint for motor according to claim 1, it is characterised in that：The fire retardant be halogenated flame retardant and
One kind in magnesium hydroxide.
4. a kind of insulating paint for motor according to claim 1, it is characterised in that：The antifoaming agent is silicone emulsion and gathers
One kind in ethers antifoaming agent.
5. a kind of insulating paint for motor according to claim 1, it is characterised in that：The curing agent be vinyl triamine and
One kind in ethylenediamine.
6. a kind of insulating paint for motor according to claim 1, it is characterised in that：The diluent is ethyl alcohol and acetic acid second
One kind in ester.
7. a kind of insulating paint for motor according to claim 1-6 and preparation method thereof, it is characterised in that：The insulated paint
Preparation method include the following steps：
（1）Phenolic resin, polyurethane, vinylacetate, phenyl vinyl polysiloxane, the cloud of certain number are weighed by above-mentioned formula
It is female powder, glass fibre, dilauroyl peroxide, bentonite, boron compound, antimony oxide, linoleic acid, Ricinate, fire-retardant
Agent, antifoaming agent, curing agent, diluent, acrylic emulsion are spare；
（2）Vinylacetate is put into reaction kettle, phenyl vinyl polysiloxane, mica powder, glass fibre, stirring is then added
Antimony oxide, linoleic acid, Ricinate, fire retardant, antifoaming agent, solidification is added after evenly dispersed in mixing 2-3 hours
Agent, diluent, after mixing, mixture A is made in ground filtering；
（3）Phenolic resin, Organic Sodium Salt modified soluble acrylic emulsion, polyurethane are put into reaction kettle, at 80-95 DEG C
At a temperature of, it stirs 30-40 minutes, dilauroyl peroxide 1-2h is then added, bentonite and boron compound are added, with 2300-
The rotating speed of 2500r/min disperses 3-4 hours, and mixture B is made；
（4）By step（2）The mixture A and step of gained（3）The mixture B of gained is uniformly mixed, and is ultrasonically treated 25-30 points
Clock is to get the insulating paint for motor.