CN108327034A - A kind of fire-proof and damp-proof timber and its manufacturing method - Google Patents
A kind of fire-proof and damp-proof timber and its manufacturing method Download PDFInfo
- Publication number
- CN108327034A CN108327034A CN201810101337.XA CN201810101337A CN108327034A CN 108327034 A CN108327034 A CN 108327034A CN 201810101337 A CN201810101337 A CN 201810101337A CN 108327034 A CN108327034 A CN 108327034A
- Authority
- CN
- China
- Prior art keywords
- proof
- damp
- timber
- solid wood
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire-proof and damp-proof timber, the fire-proof and damp-proof timber includes fireprotection layer, damp-proof layer, solid wood door plate and two blocks of pattern for surface plates.The present invention can carry out volume production using the basic production method of solid wood timber to it, and the asbestos fireprotection layer wherein filled can improve the fire protecting performance of timber to a certain extent, and the damp-proof layer added can be prevented because of bacteria breed caused by wet weather etc., and the material price that fireprotection layer and damp-proof layer use is cheap cost-effective.
Description
Technical field
The present invention relates to household technical field, specially a kind of fire-proof and damp-proof timber and its manufacturing method.
Background technology
The performance that market is visited is more and more, but can prevent fires while can also be moisture-proof, and there is presently no the productions of this respect
Product.The fire prevention of timber and it is moisture-proof be to protection during it is considerable, make moist and be easy to grow bacterium, it is strong to influence resident family
Health, such as occur fire when, fire resistant doorsets be also together important protection defence line, for this purpose, it is proposed that a kind of fire-proof and damp-proof timber and its
Manufacturing method.
Invention content
The purpose of the present invention is to provide a kind of fire-proof and damp-proof timber and its manufacturing methods, to solve to propose in background technology
The problem of.
To achieve the above object, the present invention provides the following technical solutions：A kind of fire-proof and damp-proof timber, the fire-proof and damp-proof wood
Door includes fireprotection layer, damp-proof layer, solid wood door plate and two blocks of pattern for surface plates.
Preferably, a kind of manufacturing method of fire-proof and damp-proof timber includes the following steps：
（1）Solid wood door plate is chosen：The solid wood board having good quality is chosen, according to the length, width and height of certain specification cut spare；
（2）Solid wood door plate pre-processes：The solid wood door plate for cutting completion is subjected to hot pressing, cold pressing and fine grinding processing, the hot pressing
Temperature setting is 170-180 DEG C, and processing time 30-35min, the temperature of colding pressing is set as 20-25 DEG C, and processing time is
25-30min；
（3）Damp-proof layer makes：The damp-proof layer is composed of polyethylene, polyester fiber, bamboo fibre, wherein by polyethylene, is gathered
Ester fiber, bamboo fibre are uniformly applied to step（2）Solid wood door plate front surface after pretreated, the smearing thickness are 0.3-
0.5mm；
（4）Fireprotection layer makes：The manufacture material of the fireprotection layer is asbestos material, and asbestos material is uniformly applied to step（2）
Solid wood door plate rear surface after pretreated, the smearing thickness are 0.3-0.5mm；
（5）Pattern for surface plate bonds：Two layers of diamond plate is glued respectively to the both side surface of solid wood door plate；
（6）Fine grinding is handled：To step（5）It bonds the timber after completing and carries out fine grinding processing, the burr on timber surface is carried out
Fine grinding removal；
（7）Spray painting：To step（6）The timber that fine grinding processing is completed carries out spray painting processing, chooses the paint spray of an orthochromatic plate tone
It covers to the surface of two pieces of diamond plates, the surface that paint is sprayed at diamond plate by way of planar magnetic control sputtering forms skin of paint,
The thickness of the skin of paint sprays as 0.05-0.1mm；
（8）Drying：By step（7）The timber that spray painting is completed carries out drying and processing, and the drying temperature is 35-45 DEG C, when drying
Between be 45-65min, drying complete after can be obtained a kind of fire-proof and damp-proof timber.
The present invention can carry out volume production using the basic production method of solid wood timber to it, and the asbestos fire prevention wherein filled
Layer can improve the fire protecting performance of timber to a certain extent, and the damp-proof layer added can prevent because caused by wet weather etc.
Bacteria breed, and the material price that fireprotection layer and damp-proof layer use is cheap cost-effective.
Specific implementation mode
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is only
It is a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ordinary skill people
The every other embodiment that member is obtained without making creative work, shall fall within the protection scope of the present invention.
A kind of fire-proof and damp-proof timber, the fire-proof and damp-proof timber include fireprotection layer, damp-proof layer, solid wood door plate and two pieces of surface layers
Diamond plate
Embodiment one：
A kind of manufacturing method of fire-proof and damp-proof timber includes the following steps：
（1）Solid wood door plate is chosen：The solid wood board having good quality is chosen, according to the length, width and height of certain specification cut spare；
（2）Solid wood door plate pre-processes：The solid wood door plate for cutting completion is subjected to hot pressing, cold pressing and fine grinding processing, the hot pressing
Temperature setting is 170 DEG C, processing time 30min, and the temperature of colding pressing is set as 20 DEG C, processing time 25min；
（3）Damp-proof layer makes：The damp-proof layer is composed of polyethylene, polyester fiber, bamboo fibre, wherein by polyethylene, is gathered
Ester fiber, bamboo fibre are uniformly applied to step（2）Solid wood door plate front surface after pretreated, the smearing thickness are 0.3mm；
（4）Fireprotection layer makes：The manufacture material of the fireprotection layer is asbestos material, and asbestos material is uniformly applied to step（2）
Solid wood door plate rear surface after pretreated, the smearing thickness are 0.3mm；
（5）Pattern for surface plate bonds：Two layers of diamond plate is glued respectively to the both side surface of solid wood door plate；
（6）Fine grinding is handled：To step（5）It bonds the timber after completing and carries out fine grinding processing, the burr on timber surface is carried out
Fine grinding removal；
（7）Spray painting：To step（6）The timber that fine grinding processing is completed carries out spray painting processing, chooses the paint spray of an orthochromatic plate tone
It covers to the surface of two pieces of diamond plates, the surface that paint is sprayed at diamond plate by way of planar magnetic control sputtering forms skin of paint,
The thickness of the skin of paint sprays as 0.05mm；
（8）Drying：By step（7）The timber that spray painting is completed carries out drying and processing, and the drying temperature is 35 DEG C, and drying time is
45min, drying can be obtained a kind of fire-proof and damp-proof timber after completing.
Embodiment two：
A kind of manufacturing method of fire-proof and damp-proof timber includes the following steps：
（1）Solid wood door plate is chosen：The solid wood board having good quality is chosen, according to the length, width and height of certain specification cut spare；
（2）Solid wood door plate pre-processes：The solid wood door plate for cutting completion is subjected to hot pressing, cold pressing and fine grinding processing, the hot pressing
Temperature setting is 180 DEG C, processing time 35min, and the temperature of colding pressing is set as 25 DEG C, processing time 30min；
（3）Damp-proof layer makes：The damp-proof layer is composed of polyethylene, polyester fiber, bamboo fibre, wherein by polyethylene, is gathered
Ester fiber, bamboo fibre are uniformly applied to step（2）Solid wood door plate front surface after pretreated, the smearing thickness are 0.5mm；
（4）Fireprotection layer makes：The manufacture material of the fireprotection layer is asbestos material, and asbestos material is uniformly applied to step（2）
Solid wood door plate rear surface after pretreated, the smearing thickness are 0.5mm；
（5）Pattern for surface plate bonds：Two layers of diamond plate is glued respectively to the both side surface of solid wood door plate；
（6）Fine grinding is handled：To step（5）It bonds the timber after completing and carries out fine grinding processing, the burr on timber surface is carried out
Fine grinding removal；
（7）Spray painting：To step（6）The timber that fine grinding processing is completed carries out spray painting processing, chooses the paint spray of an orthochromatic plate tone
It covers to the surface of two pieces of diamond plates, the surface that paint is sprayed at diamond plate by way of planar magnetic control sputtering forms skin of paint,
The thickness of the skin of paint sprays as 0.1mm；
（8）Drying：By step（7）The timber that spray painting is completed carries out drying and processing, and the drying temperature is 45 DEG C, and drying time is
65min, drying can be obtained a kind of fire-proof and damp-proof timber after completing.
Embodiment three：
A kind of manufacturing method of fire-proof and damp-proof timber includes the following steps：
（1）Solid wood door plate is chosen：The solid wood board having good quality is chosen, according to the length, width and height of certain specification cut spare；
（2）Solid wood door plate pre-processes：The solid wood door plate for cutting completion is subjected to hot pressing, cold pressing and fine grinding processing, the hot pressing
Temperature setting is 175 DEG C, processing time 33min, and the temperature of colding pressing is set as 23 DEG C, processing time 27min；
（3）Damp-proof layer makes：The damp-proof layer is composed of polyethylene, polyester fiber, bamboo fibre, wherein by polyethylene, is gathered
Ester fiber, bamboo fibre are uniformly applied to step（2）Solid wood door plate front surface after pretreated, the smearing thickness are 0.4mm；
（4）Fireprotection layer makes：The manufacture material of the fireprotection layer is asbestos material, and asbestos material is uniformly applied to step（2）
Solid wood door plate rear surface after pretreated, the smearing thickness are 0.4mm；
（5）Pattern for surface plate bonds：Two layers of diamond plate is glued respectively to the both side surface of solid wood door plate；
（6）Fine grinding is handled：To step（5）It bonds the timber after completing and carries out fine grinding processing, the burr on timber surface is carried out
Fine grinding removal；
（7）Spray painting：To step（6）The timber that fine grinding processing is completed carries out spray painting processing, chooses the paint spray of an orthochromatic plate tone
It covers to the surface of two pieces of diamond plates, the surface that paint is sprayed at diamond plate by way of planar magnetic control sputtering forms skin of paint,
The thickness of the skin of paint sprays as 0.08mm；
（8）Drying：By step（7）The timber that spray painting is completed carries out drying and processing, and the drying temperature is 40 DEG C, and drying time is
55min, drying can be obtained a kind of fire-proof and damp-proof timber after completing.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (2)
1. a kind of fire-proof and damp-proof timber, it is characterised in that：The fire-proof and damp-proof timber includes fireprotection layer, damp-proof layer, solid wood door plate
With two blocks of pattern for surface plates.
2. a kind of fire-proof and damp-proof timber according to claim 1, it is characterised in that：A kind of system of the fire-proof and damp-proof timber
The method of making includes the following steps：
（1）Solid wood door plate is chosen：The solid wood board having good quality is chosen, according to the length, width and height of certain specification cut spare；
（2）Solid wood door plate pre-processes：The solid wood door plate for cutting completion is subjected to hot pressing, cold pressing and fine grinding processing, the hot pressing
Temperature setting is 170-180 DEG C, and processing time 30-35min, the temperature of colding pressing is set as 20-25 DEG C, and processing time is
25-30min；
（3）Damp-proof layer makes：The damp-proof layer is composed of polyethylene, polyester fiber, bamboo fibre, wherein by polyethylene, is gathered
Ester fiber, bamboo fibre are uniformly applied to step（2）Solid wood door plate front surface after pretreated, the smearing thickness are 0.3-
0.5mm；
（4）Fireprotection layer makes：The manufacture material of the fireprotection layer is asbestos material, and asbestos material is uniformly applied to step（2）
Solid wood door plate rear surface after pretreated, the smearing thickness are 0.3-0.5mm；
（5）Pattern for surface plate bonds：Two layers of diamond plate is glued respectively to the both side surface of solid wood door plate；
（6）Fine grinding is handled：To step（5）It bonds the timber after completing and carries out fine grinding processing, the burr on timber surface is carried out
Fine grinding removal；
（7）Spray painting：To step（6）The timber that fine grinding processing is completed carries out spray painting processing, chooses the paint spray of an orthochromatic plate tone
It covers to the surface of two pieces of diamond plates, the surface that paint is sprayed at diamond plate by way of planar magnetic control sputtering forms skin of paint,
The thickness of the skin of paint sprays as 0.05-0.1mm；
（8）Drying：By step（7）The timber that spray painting is completed carries out drying and processing, and the drying temperature is 35-45 DEG C, when drying
Between be 45-65min, drying complete after can be obtained a kind of fire-proof and damp-proof timber.