CN108315821A - A kind of layered double hydroxide LDH-I2-CO32-Whisker and its preparation method and application - Google Patents

A kind of layered double hydroxide LDH-I2-CO32-Whisker and its preparation method and application Download PDF

Info

Publication number
CN108315821A
CN108315821A CN201810288870.1A CN201810288870A CN108315821A CN 108315821 A CN108315821 A CN 108315821A CN 201810288870 A CN201810288870 A CN 201810288870A CN 108315821 A CN108315821 A CN 108315821A
Authority
CN
China
Prior art keywords
whisker
preparation
layered double
ldh
concentration
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810288870.1A
Other languages
Chinese (zh)
Inventor
吴健松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lingnan Normal University
Original Assignee
Lingnan Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lingnan Normal University filed Critical Lingnan Normal University
Priority to CN201810288870.1A priority Critical patent/CN108315821A/en
Publication of CN108315821A publication Critical patent/CN108315821A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of layered double hydroxide LDH I2‑CO3 2‑Whisker and its preparation method and application.Layered double-metal hydroxide LDH I2‑CO3 2‑The chemical formula of whisker is Mg6Al2(OH)14I2CO3·5H2O, the whisker pass through metal cation Mg2+、Al3+With anion I‑、CO3 2‑And OH‑React precipitate and wash, dry after obtain.Layered double hydroxide LDH I provided by the invention2‑CO3 2‑Whisker is a kind of houghite compound of crystal whisker-shaped, both had the function of crystal whisker toughened reinforcement, there is the function of the classes talcs compounds such as adjustable denaturation, larger specific surface area and the interlayer ion interchangeability in aperture again, there is very extensive application prospect in toughened and reinforced material, the fields such as catalysis, fire-retardant, sorbing material.Preparation method provided by the invention, it is simple for process easy to operate, it is of low cost, it is suitble to large-scale promotion application.

Description

A kind of layered double hydroxide LDH-I2-CO32-Whisker and preparation method thereof and Using
Technical field
The present invention relates to technical field of inorganic material, and in particular, to a kind of layered double hydroxide LDH-I2- CO3 2-Whisker and its preparation method and application.
Background technology
Layered double hydroxide (Layered Double Hydroxide, LDH) is hydrotalcite The general designation of (Hydrotalcite, HT) and houghite compound (Hydrotalcite-Like Compounds, HTLc) is A kind of important inorganic functional material has the function of catalysis, absorption, fire-retardant etc., is a kind of multifunctional inorganic material of environment-friendly type.
Most typical LDH is Mg6Al2(OH)16CO3·4H2O, also referred to as magnalium hydrotalcite, if in this magnalium hydrotalcite Mg2+、Al3+Or CO3 2-Ion is replaced by other ions, you can obtains houghite (HTLc).The general formula of HTLc is：(wherein M2+For bivalent metal ion, such as Mg2+、 Ni2+、 Co2+、Zn2+、Cu2+Deng；M3+For trivalent metal ion, such as Al3+、Cr3+、Fe3+、Sc3+Deng；A is interlayer anion, such as CO3 2-、 NO3-、Cl-、SO4 2-、PO4 3-、C6H4(COO)2 2-Deng；M is Coating combination water number mesh).ByIt is formed Plate layer be known as sheet-metal layers, byThe layer of composition is known as anion layer.This layer structure is as shown in Figure 5.
Since HTLc has the adjustable denaturation in aperture, and there are larger specific surface area and interlayer ion interchangeability, therefore its There is very extensive application prospect in the fields such as catalysis, fire-retardant, absorption, medicine, gene storage.
For LDH, HTLc class compound, the researcher that domestic and international many is engaged in this respect at present does a lot of work, and Gratifying achievement is all achieved in respective field.Research both domestic and external is concentrated mainly on setting for sheet-metal layers bivalent cation It changes, such as magnesium ion is replaced into copper ion or cobalt ions etc., anion metathesis is some such as amino by the design also having The organic biomolecules such as acid.At home, Beijing University of Chemical Technology achieves prodigious achievement to the research of LDH.They are designing Prodigious achievement in research is achieved in the intercalations LDH field of compound material such as cupric, cobalt, nickel, organic acid, polyacid.At abroad, also having Many scholars synthesize numerous important organic compounds and inorganization on preparing LDH technologies or using LDH as catalyst It closes on object or as many gratifying achievements are also achieved in the researchs such as fire retardant, adsorbent, provides a large amount of useful Experimental data.But to currently, LDH and HTLc class compounds are mainly laminated structure, LDH the and HTLc class compounds of crystal whisker-shaped are several Do not report.And the inorganic material of crystal whisker-shaped has toughened and reinforced function, develops LDH the or HTLc classes compound of crystal whisker-shaped then It can assign LDH and HTLc classes inorganic material preferably toughened and reinforced function, to further expand its application.
It is using certain whisker (such as magnesium hydroxide crystal whisker) as predecessor, again that LDH, which is prepared into whisker mostly, at present Or technology of preparing route is tediously long, of high cost etc., is not suitable for large-scale application.Therefore, develop a kind of crystal whisker-shaped LDH and/or HTLc classes compound and its corresponding preparation process have great research significance and application value.
Invention content
The purpose of the invention is to overcome the above-mentioned deficiency of the prior art, a kind of layered double hydroxide is provided LDH-I2-CO3 2-Whisker.Layered double-metal hydroxide whisker removes the adjustable denaturation with aperture, larger specific surface area Outside the function of the houghites class compound such as interlayer ion interchangeability, while also having the function of crystal whisker toughened reinforcement.
Another object of the present invention is to provide layered double-metal hydroxide LDH-I2-CO3 2-The preparation side of whisker Method.
Another object of the present invention is to provide layered double-metal hydroxide LDH-I2-CO3 2-Whisker is preparing increasing Application in tough supporting material, catalysis material, fire proofing or sorbing material.
The above-mentioned purpose of the present invention is achieved by following scheme：
A kind of layered double hydroxide LDH-I2-CO3 2-The chemical formula of whisker, the whisker is Mg6Al2(OH)14I2CO3·5H2O, the whisker pass through metal cation Mg2+、Al3+With anion I-、CO3 2-And OH-It reacts to precipitate and wash Wash, dry after obtain.
The present invention provides a kind of layered double hydroxide LDH-I of specific composition2-CO3 2-Whisker has whisker Toughened and reinforced function caused by structure；Simultaneously the substance again have HTLc class compounds possessed by aperture can modulation Property, the function of larger specific surface area and interlayer ion interchangeability, in toughened and reinforced material, catalysis, fire-retardant, sorbing material etc. There is very extensive application prospect in field.
The present invention also protects layered double-metal hydroxide LDH-I simultaneously2-CO3 2-The preparation method of whisker.It is described Preparation method includes the following steps：
S1. MgI is prepared2·8H2O and Al (NO3)3·9H2The mixed solution A of O, it is molten with the NaOH of 0.05~0.15mol/L Liquid adjusts pH to 7.45~7.55；Mg in the mixed solution A2+A concentration of 2.10~2.70mol/L, Al3+It is a concentration of 0.70~0.90mol/L；
S2. compound concentration is the NaCO of 0.95~1.05mol/L3NaCO is used in combination in solution3It is molten that solution adjusts mixing obtained by S1 After liquid is 8.05~8.25 to pH, it is placed at 4~45 DEG C and reacts 140~149h generation precipitations, filter and wash precipitation, after drying Up to layered double-metal hydroxide LDH-I2-CO3 2-Whisker.
Inventor is to layered double hydroxide LDH-I2-CO3 2-It is found unintentionally in the exploration of preparation process, it is former Expect that type and its proportioning, pH regulation and control, reaction temperature and time have very big shadow to the pattern of final layered double hydroxide It rings.Such as metal cation Mg2+And Al3+, anion I-、CO3 2-And OH-Concentration it is excessive or too small, pH is excessively high or pH fluctuation ranges Excessive, reaction temperature excessively high (water evaporation rate is too fast) is unable to get whisker morphology or obtains the yield of whisker morphology very It is low.The present invention finally prepares the layered double hydroxide LDH-I of crystal whisker-shaped by the preferred of this series of conditions2- CO3 2-, preparation method is simple.
In addition, Qinghai Salt Lake (such as Hoh Yanhu bittern, Chaka Salt lake bittern or Cha Er Han Salt Lake) has the hardship of enormous amount Halogen, these bitterns are to prepare LDH-I2-CO3 2-The extremely excellent natural resources of whisker.But these resources cannot get always science, effectively It utilizes, but leaves unused always, this not only wastes salt lake resources, also so that the serious salination of salt lake Soil Surrounding and plant are withered Extremely, it is damaged to the ecological environment in salt lake, while also bringing difficulty to saltern resource exploitation in future.Using bittern in salt lake as Mg2+And Al3+Source, the natural resources can be made full use of, it is cost-effective, have important economic value.
Preferably, pH to 7.5 is adjusted in S1.
Preferably, Mg in mixed solution A described in S12+A concentration of 2.40mol/L, Al3+A concentration of 0.80mol/L.
Preferably, a concentration of 0.1mol/L of NaOH solution described in S1.
Preferably, NaCO in S23A concentration of 1.0mol/L.
Preferably, NaCO is added in S23Solution adjusts pH to 8.2.
In order to preferably regulate and control pH, prevents pH too low or fluctuation is excessive, it is preferable that protected in S2 by adding NaOH solution A NaOH solution is added every 8h so that pH value of reaction system increases by 0.05 in the pH for holding mixed solution.
In order to enable moisture evaporation is more uniformly distributed, further including wind step in S2 makes moisture evaporation, it is preferable that the wind Wind speed be 4~5m/s.
Preferably, the reaction time described in S2 is the 144h that exposes to the weather.
Qinghai Salt Lake area has abundant solar energy resources and wind energy resources, and long-term temperature is at 5~45 DEG C, and wind speed is 4 Precipitation obtained by S2 can be placed at the spaciousness of Qinghai Salt Lake area, water is realized using natural solar energy and wind energy resources by~5m/s Divide slow evaporation, not only saves energy and realize green chemical industry.
Layered double-metal hydroxide LDH-I2-CO3 2-The application of whisker is also within the scope of the present invention, institute Show that it is layered double-metal hydroxide LDH-I to apply2-CO3 2-Whisker is preparing toughened and reinforced material, catalysis material, fire-retardant Application in material or sorbing material.
Compared with prior art, the invention has the advantages that：
Layered double hydroxide LDH-I provided by the invention2-CO3 2-Whisker is a kind of houghite of crystal whisker-shaped Object is closed, had not only had the function of crystal whisker toughened reinforcement, but also have adjustable denaturation, larger specific surface area and the interlayer ion in aperture that can hand over The function of the classes talcs compound such as transsexual has very in toughened and reinforced material, the fields such as catalysis, fire-retardant, sorbing material It is widely applied foreground.Preparation method provided by the invention, simple for process easy to operate, of low cost, suitable large-scale promotion is answered With.
Description of the drawings
Fig. 1 is that embodiment 1 prepares layered double hydroxide LDH-I2-CO3 2-The route map of whisker.
Fig. 2 is layered double hydroxide LDH-I prepared by embodiment 12-CO3 2-The SEM spectrum of whisker.
Fig. 3 is layered double hydroxide LDH-I prepared by embodiment 12-CO3 2-The XRD spectrum of whisker.
Fig. 4 is layered double hydroxide LDH-I prepared by comparative example 12-CO3 2-SEM spectrum.
Fig. 5 is the layer structure schematic diagram of HTLc.
Specific implementation mode
The present invention is made with reference to specific embodiment and further being elaborated, the embodiment is served only for explaining this Invention, is not intended to limit the scope of the present invention.Test method used in following embodiments is normal unless otherwise specified Rule method；Used material, reagent etc., unless otherwise specified, for the reagent and material commercially obtained.
Embodiment 1
Present embodiments provide a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, chemical formula Mg6Al2 (OH)14I2CO3·5H2O, preparation process are following (as shown in Figure 1)：
(I) prepares 4.80molL-1MgI2·8H2O and 1.6molL-1Al(NO3)3·9H2O solution, take this two kinds it is molten Liquid is mixed in stirring volumetric in a beaker, and the pH value of mixed system is adjusted to the NaOH solution of 0.1mol/L PH=7.50, at this point, due to Al3+The hydrolysis of ion and so that solution is become muddy, but generate this phenomenon and do not interfere with subsequently LDH-I2-CO3 2-The growth of whisker.
(II) prepares the Na of 1.00mol/L2CO3Solution is added in the mixed liquor obtained by two steps, always while stirring Then system is placed in the ground of sunny (temperature is 5~45 DEG C, and wind speed is 4~5m/s) by the pH to pH=8.2 for adding to system It just allows after exposing to the weather 144h, filters and wash precipitation, dry to get sample.In the time of this 144h, added every 8 hours The NaOH solution for entering a 0.010mol/L, the amount being added every time are：The pH value for first measuring current arrangements, is then added alkali, makes It obtains pH value and increases by 0.05 unit, for example, after the 50h that exposes to the weather, it is 8.45 to measure system pH values at this time, then alkali is added Shi Yizhi, which is added to when system pH is 8.5, to be terminated.
The layered double hydroxide LDH-I that the present embodiment is prepared2-CO3 2-The draw ratio of whisker is 15~25: 1, good dispersion, whisker good crystalline have preferable toughened and reinforced function.
Embodiment 2
Present embodiments provide a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, chemical formula Mg6Al2 (OH)14I2CO3·5H2O, the preparation process with embodiment 1, the difference is that, MgI in step (I)2·8H2O and Al (NO3)3·9H2After O mixing, MgI in mixed liquor2·8H2A concentration of 2.30molL of O-1With Al (NO3)3·9H2The concentration of O For 0.75molL-1。
The layered double hydroxide LDH-I that the present embodiment is prepared2-CO3 2-The draw ratio of whisker is 15~25: 1, good dispersion, whisker good crystalline have preferable toughened and reinforced function.
Embodiment 3
Present embodiments provide a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, chemical formula Mg6Al2 (OH)14I2CO3·5H2O, the preparation process is with embodiment 1, MgI in step (I)2·8H2O and Al (NO3)3·9H2O is mixed Afterwards, MgI in mixed liquor2·8H2A concentration of 2.51molL of O-1With Al (NO3)3·9H2A concentration of 0.82molL of O-1, add After entering NaOH solution, the pH value of mixed liquor is 7.48.
The layered double hydroxide LDH-I that the present embodiment is prepared2-CO3 2-The draw ratio of whisker is 15~25: 1, good dispersion, whisker good crystalline have preferable toughened and reinforced function.
Embodiment 4
Present embodiments provide a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, chemical formula Mg6Al2 (OH)14I2CO3·5H2O, the preparation process is with embodiment 1, MgI in step (I)2·8H2O and Al (NO3)3·9H2O is mixed Afterwards, after NaOH solution being added, the pH value of mixed liquor is 7.49；NaCO is added in step (II)3After solution, the pH value of mixed liquor is 8.19；Reaction time is 146.
The layered double hydroxide LDH-I that the present embodiment is prepared2-CO3 2-The draw ratio of whisker is 15~25: 1, good dispersion, whisker good crystalline have preferable toughened and reinforced function.
Comparative example 1
This comparative example provides a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, the preparation process is the same as real Example 1 is applied, the difference is that, MgI in step (I)2·8H2O and Al (NO3)3·9H2After O mixing, MgI in mixed liquor2· 8H2A concentration of 0.80molL of O-1。
As a result, after according to the implementation Process in embodiment 1, since magnesium ion concentration and iodide ion concentration are too low, obtain not To the substance with Whiskers shape.
Comparative example 2
This comparative example provides a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, the preparation process is the same as real Example 1 is applied, the difference is that, MgI in step (I)2·8H2O and Al (NO3)3·9H2After O mixing, Al in mixed liquor (NO3)3·9H2A concentration of 0.3molL of O-1。
As a result, after according to the implementation Process in embodiment 1, since aluminium ion concentration concentration is too low, there cannot be crystalline substance The substance of palpiform shape.
Comparative example 3
This comparative example provides a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, the preparation process is the same as real Example 1 is applied, the difference is that, MgI in step (I)2·8H2O and Al (NO3)3·9H2After O mixing, it will be mixed with NaOH solution It is 9.5 that the pH value of liquid, which is adjusted to,.
As a result, after according to the implementation Process in embodiment 1, it, cannot be with the substance of Whiskers shape after 7d.
Comparative example 4
This comparative example provides a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, the preparation process is the same as real Example 1 is applied, the difference is that, NaCO is added in step (ii)3After solution, the pH value of mixed liquor is 10.
As a result, after according to the implementation Process in embodiment 1, it, cannot be with the substance of Whiskers shape after 7d.
Comparative example 5
This comparative example provides a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, the preparation process is the same as real Example 1 is applied, the difference is that, the reaction temperature of last mixed liquor is 92 DEG C in step (ii).
As a result, after according to the implementation Process in embodiment 1, it, cannot be with the substance of Whiskers shape after 7d.
Performance evaluation
1, scanning electron microscope (SEM) is analyzed
Fig. 2 is the shape appearance figure for the sample that embodiment 1 is prepared.From figure 2 it can be seen that embodiment 1 was prepared It is almost all whisker, yield is high, and the draw ratio of whisker is 15~25: 1, good dispersion, whisker good crystalline.And comparative example 1~5 The sample being prepared not instead of crystal whisker-shaped, other non-crystal whisker-shapeds, as shown in figure 4, Fig. 4 is 1 products therefrom of comparative example.
2, X-ray diffraction (XRD) is analyzed
Fig. 3 is layered double hydroxide LDH-I prepared by embodiment 12-CO3 2-The XRD diagram of whisker.From XRD diffraction Figure is as can be seen that layered double hydroxide LDH-I2-CO3 2-Whisker has the layer structure of LDH, the LDH of layer structure In (003) crystal face diffracted intensity maximum, followed by (006) crystal face, minimum is (009), this is because lamellar compound is to XRD " delustring " effect caused by.(003), (006), the corresponding diffraction maximum of (009) crystal face have been marked in attached drawing.Prove embodiment 1 The sample of preparation is exactly the substance for having LDH structures.
3, elemental analysis
Sample topography prepared by Examples 1 to 4 is similar, by taking sample prepared by embodiment 1 as an example, divides into row element sample Analysis, the results are shown in Table 1.Table 1 statistics indicate that, embodiment 1 provide sample substantially conform to nMg∶nAl∶nI∶nc=6: 2: 2: 1, In conjunction with oxygen (content of oxygen is obtained by minusing), protium content, it can deduce that its chemical formula is Mg6Al2(OH)14I2CO3· 5H2O。
1 LDH-I of table2-CO3 2-Elemental analysis result
ω (Mg) % ω (Al) % ω (I) % ω (C) % ω (H) % Mg/Al/I/C
Embodiment 1 17.19 6.28 30.18 1.43 2.86 0.716∶0.233∶0.238∶0.119
Elemental analysis is carried out to the sample that other embodiment is prepared, each sample substantially conforms to nMg∶nAl∶nI∶nc=6: 2: 2: 1, in conjunction with oxygen (content of oxygen is obtained by minusing), protium content, it can deduce that its chemical formula is Mg6Al2(OH)14I2CO3·5H2O。
Finally, it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention rather than is protected to the present invention The limitation of shield range can also be made on the basis of above description and thinking for those of ordinary skill in the art Other various forms of variations or variation, there is no necessity and possibility to exhaust all the enbodiments.It is all the present invention All any modification, equivalent and improvement etc., should be included in the protection of the claims in the present invention made by within spirit and principle Within the scope of.

Claims (10)

1. a kind of layered double hydroxide LDH-I2-CO3 2-Whisker, which is characterized in that the chemical formula of the whisker is Mg6Al2(OH)14I2CO3·5H2O。
2. the layered double-metal hydroxide LDH-I of claim 12-CO3 2-The preparation method of whisker, which is characterized in that including Following steps：
S1. MgI is prepared2·8H2O and Al (NO3)3·9H2The mixed solution A of O, with the NaOH solution tune of 0.05~0.15mol/L Save pH to 7.45~7.55；Mg in the mixed solution A2+A concentration of 2.10~2.70mol/L, Al3+A concentration of 0.70~ 0.90mol/L；
S2. compound concentration is the NaCO of 0.95~1.05mol/L3NaCO is used in combination in solution3Solution adjust S1 obtained by mixed solution to After pH is 8.05~8.25, is placed at 4~45 DEG C and reacts 140~149h generation precipitations, filter and wash precipitation, after drying to obtain the final product Layered double-metal hydroxide LDH-I2-CO3 2-Whisker.
3. preparation method according to claim 2, which is characterized in that adjust pH to 7.5 in S1.
4. preparation method according to claim 2, which is characterized in that Mg in mixed solution A described in S12+It is a concentration of 2.40mol/L Al3+A concentration of 0.80mol/L.
5. preparation method according to claim 2, which is characterized in that a concentration of 0.1mol/L of NaOH solution described in S1.
6. preparation method according to claim 2, which is characterized in that NaCO in S23A concentration of 1.0mol/L.
7. preparation method according to claim 2, which is characterized in that NaCO is added in S23Solution adjusts pH to 8.2.
8. preparation method according to claim 7, which is characterized in that keep mixed solution by adding NaOH solution in S2 PH, every 8h be added a NaOH solution so that pH value of reaction system increase by 0.05.
9. preparation method according to claim 2, which is characterized in that the reaction time described in S2 is the 144h that exposes to the weather, institute The wind speed for stating wind is 4~5m/s.
10. the layered double-metal hydroxide LDH-I of claim 12-CO3 2-Whisker is preparing toughened and reinforced material, catalysis material Application in material, fire proofing or sorbing material.
CN201810288870.1A 2018-03-30 2018-03-30 A kind of layered double hydroxide LDH-I2-CO32-Whisker and its preparation method and application Withdrawn CN108315821A (en)