CN108312080A - A kind of medal polish disk and its manufacturing method - Google Patents
A kind of medal polish disk and its manufacturing method Download PDFInfo
- Publication number
- CN108312080A CN108312080A CN201810293659.9A CN201810293659A CN108312080A CN 108312080 A CN108312080 A CN 108312080A CN 201810293659 A CN201810293659 A CN 201810293659A CN 108312080 A CN108312080 A CN 108312080A
- Authority
- CN
- China
- Prior art keywords
- pellet
- diamond
- fluted disc
- shapes
- ontology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of medal polish disk and its manufacturing methods, the medal polish disk includes metal fluted disc (1), the metal fluted disc (1) is provided centrally with shaft hole (4), shaft hole (4) periphery is provided with a circle mounting hole (2), it is provided with diamond pellet (3) in the mounting hole (2), the diamond pellet (3) includes the pellet ontology (3.1) of T shapes, the pellet ontology (3.1) of the T shapes is plugged in mounting hole (2), the leading flank of the pellet ontology (3.1) of the T shapes is provided with diamond abrasive layer (3.2) by soldering.A kind of medal polish disk of the present invention and its manufacturing method, are simple to manufacture, easy to operate, diamond abrasive grain is not easy to fall, and can greatly improve the service life of polishing disk, polishing effect is effectively ensured.
Description
Technical field
The present invention relates to a kind of medal polish disk and its manufacturing methods.
Background technology
Natural stone and artificial stone material for decoration use surface have higher gloss and clarity, can more show the color and dress of stone material
Effect is adornd, therefore people are often using the height of stone surface glossiness as the mark of evaluation processing of stone quality and surface effect
It is accurate.Grinding and polishing when the surface grinding polishing of masonry slab, stone floor renovation, is all by the different professional equipment of performance
The material with grinding function is coordinated to realize.Thus has the function of the grinding and polishing material of preferably grinding, polishing and efficiency
The project that material pays high attention to as processing of stone and stone material nursing industry.
In stone grinding field, stone surface is ground and is polished, it is intended to make preferably being put down for stone surface
Whole or brightness effect.Polishing is ground to stone material, can simply be divided into three corase grinding, fine grinding and polishing processes.It is grinding
Expect that on design system and operating procedure be a process from coarse to fine, from coarse to smooth.Certainly, stone surface grinding and polishing
Effect and the performance of milling apparatus have larger relationship.The promotion of milling apparatus performance was to stone grinding polishing effect in recent years
Being promoted influences very big, and the raising of abrasive polishing materials (piece) performance seems lag or stagnation.
Stone grinding polished silicon wafer is manufactured there are mainly three types of matrix and form both at home and abroad at present, one is mine soil matrix body,
One is alloy bases, and one is resin matrixes.These three different matrixes are all to merge a certain amount of people in addition
It makes and completes grinding function on the basis of the abrasive materials such as diamond, silicon carbide and aluminium oxide.
Mine soil abrasive sheet is a kind of traditional way that stone grinding polished silicon wafer is prepared using magnesia, due to production technology
Cumbersome, manufacture efficiency is low, and hardness is difficult to adjust, and seldom uses at present;
Usually there are two types of forms for alloy base abrasive sheet, and one is formed by being electroplated on alloy base
Diamond abrasive layer, usage time is shorter, is very easy to drop;Another kind is set by bonding agent on alloy base
Diamond pellet is set, due to inside and outside linear velocity difference, diamond pellet outer wear is fast, and Innerside wear is slower, it is therefore desirable to pass through
Perseverance is reprocessed, and considerably increases workload, and be easy diamond, to cause large area to scratch workpiece;
Resin matrix abrasive sheet, matrix is relatively low relative to hardness of stone, and polyurethane resin is the mainstream type of existing market,
Resin has included cerium oxide or alumina abrasive, and this abrasive sheet is easy to form micropore on surface, to scratch polished surface, and
Grinding rate is slower.
Invention content
The technical problem to be solved by the present invention is to provide a kind of medal polish disk and its manufacture for the above-mentioned prior art
Method is simple to manufacture, easy to operate, and diamond abrasive grain is not easy to fall, and can greatly improve the service life of polishing disk, effectively
Ensure polishing effect.
Technical solution is used by the present invention solves the above problems:A kind of medal polish disk, it includes metal fluted disc, institute
It states metal-toothed disk center and is provided with shaft hole, the shaft hole periphery is provided with a circle mounting hole, is provided in the mounting hole
Diamond pellet, the diamond pellet include the pellet ontology of T shapes, and the pellet ontology of the T shapes is plugged in mounting hole, institute
The leading flank for stating the pellet ontology of T shapes is provided with diamond abrasive layer by soldering.
The diamond pellet is bonding by anaerobic adhesive and metal fluted disc.
Metal fluted disc periphery is provided with a circle tooth, and the outer surface of the tooth is provided with frosted layer.
A kind of manufacturing method of medal polish disk, the described method comprises the following steps:
Step 1: the pellet ontology of batch making T shapes, gluing operation is carried out in the pellet body upper surface of T shapes;
Step 2: being laid with one layer of silk screen above the pellet ontology of T shapes, 400~600 μm of net is uniformly provided on silk screen
Hole;
Step 3: the brush diamond powder on the silk screen of step 2, makes diamond powder pass through silk screen and is uniformly layed in ball
On the glue of piece body upper surface;
Step 4: upper brazing solder is gone forward side by side, stove is sintered, and forms diamond pellet;
Step 5: carrying out brushing flat operation to the upper surface of diamond pellet;
Step 6: taking a metal fluted disc, it is provided with frosted layer on the tooth of metal fluted disc periphery, one is offered on metal fluted disc
Mounting hole is enclosed, brushes flat the diamond pellet of operation by passing through in anaerobic adhesive installation steps five in each mounting hole, and 200
So that diamond pellet is adhesively fixed with metal fluted disc at DEG C, forms medal polish disk;
Step 7: carrying out dressing operation to the medal polish disk obtained in step 6 obtains final product.
Compared with the prior art, the advantages of the present invention are as follows:
A kind of medal polish disk of the present invention and its manufacturing method, are simple to manufacture, easy to operate, and when use can first pass through gold
The frosted tooth for belonging to polishing disk periphery carries out rough polishing, then carries out finishing polish in the diamond pellet by front side, on the one hand big
The big service life for improving medal polish disk, has on the other hand been effectively ensured polishing effect;Diamond pellet individually makes, easily
Soldering processes are used in the diamond abrasive layer in control pellet processing quality, pellet, is not likely to produce and falls;Ball when in addition polishing
There are gap between piece and pellet, the clast generated in polishing process can be fallen from centre, be not easy to be adhered to pellet surface pair
Quality of finish has an impact, and also improves polishing efficiency.
Description of the drawings
Fig. 1 is a kind of structural schematic diagram of medal polish disk of the present invention.
Fig. 2 is the A-A sectional views of Fig. 1.
Wherein:
Metal fluted disc 1
Mounting hole 2
Diamond pellet 3
Pellet ontology 3.1
Diamond abrasive layer 3.2
Shaft hole 4
Tooth 5
Frosted layer 6.
Specific implementation mode
Below in conjunction with attached drawing embodiment, present invention is further described in detail.
As shown in Figure 1 and Figure 2, a kind of medal polish disk in the present embodiment, it includes metal fluted disc 1, the metal fluted disc
1 is provided centrally with shaft hole 4, and 4 periphery of the shaft hole is provided with a circle mounting hole 2, diamond is provided in the mounting hole 2
Pellet 3, the diamond pellet 3 include the pellet ontology 3.1 of T shapes, and the pellet ontology 3.1 of the T shapes is plugged in mounting hole 2
Interior, the leading flank of the pellet ontology 3.1 of the T shapes is provided with diamond abrasive layer 3.2 by soldering;
The diamond pellet 3 is bonding by anaerobic adhesive and metal fluted disc 1;
1 periphery of metal fluted disc is provided with a circle tooth 5, and the outer surface of the tooth 5 is provided with frosted layer 6.
A kind of manufacturing method of medal polish disk, it is comprised the following steps that:
Step 1: the pellet ontology of batch making T shapes, gluing operation is carried out in the pellet body upper surface of T shapes;
Step 2: being laid with one layer of silk screen above the pellet ontology of T shapes, 400~600 μm of net is uniformly provided on silk screen
Hole;
Step 3: the brush diamond powder on the silk screen of step 2, makes diamond powder pass through silk screen and is uniformly layed in ball
On the glue of piece body upper surface;
Step 4: upper brazing solder is gone forward side by side, stove is sintered, and forms diamond pellet;
Step 5: carrying out brushing flat operation to the upper surface of diamond pellet;
Step 6: taking a metal fluted disc, it is provided with frosted layer on the tooth of metal fluted disc periphery, one is offered on metal fluted disc
Mounting hole is enclosed, brushes flat the diamond pellet of operation by passing through in anaerobic adhesive installation steps five in each mounting hole, and 200
So that diamond pellet is adhesively fixed with metal fluted disc at DEG C, forms medal polish disk;
Step 7: carrying out dressing operation to the medal polish disk obtained in step 6 obtains final product.
In addition to the implementation, all to use equivalent transformation or equivalent replacement the invention also includes there is an other embodiment
The technical solution that mode is formed should all be fallen within the scope of the hereto appended claims.
Claims (4)
1. a kind of medal polish disk, it is characterised in that:It includes metal fluted disc (1), and the metal fluted disc (1), which is provided centrally with, to be turned
Axis hole (4), shaft hole (4) periphery are provided with a circle mounting hole (2), diamond pellet are provided in the mounting hole (2)
(3), the diamond pellet (3) includes the pellet ontology (3.1) of T shapes, and the pellet ontology (3.1) of the T shapes is plugged in installation
In hole (2), the leading flank of the pellet ontology (3.1) of the T shapes is provided with diamond abrasive layer (3.2) by soldering.
2. a kind of medal polish disk according to claim 1, it is characterised in that:The diamond pellet (3) passes through anaerobism
Glue and metal fluted disc (1) are bonding.
3. a kind of medal polish disk according to claim 1, it is characterised in that:Metal fluted disc (1) periphery is provided with
One circle tooth (5), the outer surface of the tooth (5) is provided with frosted layer (6).
4. a kind of manufacturing method of medal polish disk, it is characterised in that the described method comprises the following steps:
Step 1: the pellet ontology of batch making T shapes, gluing operation is carried out in the pellet body upper surface of T shapes;
Step 2: being laid with one layer of silk screen above the pellet ontology of T shapes, 400~600 μm of mesh is uniformly provided on silk screen;
Step 3: the brush diamond powder on the silk screen of step 2, makes diamond powder pass through silk screen and is uniformly layed in pellet sheet
On the glue of body upper surface;
Step 4: upper brazing solder is gone forward side by side, stove is sintered, and forms diamond pellet;
Step 5: carrying out brushing flat operation to the upper surface of diamond pellet;
Step 6: taking a metal fluted disc, it is provided with frosted layer on the tooth of metal fluted disc periphery, circle peace is offered on metal fluted disc
Hole is filled, brushes flat the diamond pellet of operation by passing through in anaerobic adhesive installation steps five in each mounting hole, and at 200 DEG C
So that diamond pellet is adhesively fixed with metal fluted disc, forms medal polish disk;
Step 7: carrying out dressing operation to the medal polish disk obtained in step 6 obtains final product.