CN108298945A - It is a kind of to prepare acoustic material, the method for sound panel and acoustic material, sound panel using Industry Waste ash - Google Patents
It is a kind of to prepare acoustic material, the method for sound panel and acoustic material, sound panel using Industry Waste ash Download PDFInfo
- Publication number
- CN108298945A CN108298945A CN201710833592.9A CN201710833592A CN108298945A CN 108298945 A CN108298945 A CN 108298945A CN 201710833592 A CN201710833592 A CN 201710833592A CN 108298945 A CN108298945 A CN 108298945A
- Authority
- CN
- China
- Prior art keywords
- acoustic material
- sound panel
- industry waste
- waste ash
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method for preparing acoustic material using Industry Waste ash and preparing sound panel using the acoustic material, raw material is made of following components by weight percent:100 200 parts of Industry Waste ash, 60 80 parts of silica, 80 120 parts of Iron-ore Slag, 10 15 parts of carbon black, 40 60 parts of clay, 100 150 parts of water.The preparation method of acoustic material includes the processing of Industry Waste ash, the processing of Iron-ore Slag, the mixing of raw material, compression molding and drying and processing;The preparation method of sound panel includes the preparation of acoustic material, the preparation of sound panel.The acoustic material grade sound panel prepared through the invention, mechanical property are improved, and have excellent weatherable, and for a long time using being unlikely to deform, and intensity improves, and effect of vibration and noise reduction is apparent.Meanwhile the acoustic material and sound panel safety and environmental protection, its own is degradable, will not cause white pollution to environment, and can be re-utilized after its own degradation, reduce production cost.
Description
Technical field
The invention belongs to building material technical field, relate particularly to a kind of preparing acoustic material using Industry Waste ash
Method, the acoustic material being prepared by this method, and the system of sound panel and sound panel that is prepared using the acoustic material
Preparation Method.
Background technology
Now, with the continuous acceleration of urbanization, noise pollution also becomes increasingly severe.It makes an uproar to effectively separate
Sound, common settling mode are to use acoustic material.Existing acoustic material is generally cement concrete, glass plate etc., these
The soundproof effect of acoustic material is not fine, therefore common solution is to increase the thickness of acoustic material, is caused in this way
The problem of be that acoustic material quality is overweight, cost is excessively high, and installation process is inconvenient.
Containing components such as a large amount of sulphur, lime in Industry Waste ash, giving up to this part, there are as below methods for grey processing --- and it is straight
Connect exhaust method, terminal processes method, cycling and reutilization method etc..Wherein, direct emission method, give up ash in untreated sulphur and lime etc.
It would seriously pollute the environment;Terminal processes method, needs to collect all useless ashes and focuses on again, and investment is big;And cycling and reutilization method is
One more effective processing method.
Iron-ore Slag is iron ore exploitation or the impurity that is detached after being produced using iron ore as raw material, mainization of Iron-ore Slag
Studying point has:Iron, iron oxide, silica and ferrous oxide etc. can recycle metal therein with high-temperature chlorination, reduce pollution
Object discharges.Iron-ore Slag stores up land occupation, builds stockyard and expends a large amount of human and material resources.Ground-slag is flown upward, and pollutes air and peripheral ring
Border.Iron-ore Slag quality is loose, and is porous shot-like particle, is suitable for making acoustic material.
Sound panel is a kind of plank acting on soundproof effect, and present sound panel majority is to install rubber between the two plates
What glue-line, damping material or deadening felt etc. were made, the material one side service life is short, and soundproof effect declines with service life,
On the other hand with high costs, bad practicality.
Invention content
The purpose of the present invention one is to provide a kind of method preparing acoustic material and sound panel using Industry Waste ash.
To achieve the above object, the technical scheme is that:
A method of acoustic material being prepared using Industry Waste ash, is included the following steps:
(1) processing of Industry Waste ash:
Industry Waste ash is crushed, is ground, grinds after taking Industry Waste ash powder and the silica mixing after crushing
Mixture A is obtained after mill;
(2) processing of Iron-ore Slag:
Iron-ore Slag is crushed, is ground after taking Iron-ore Slag powder and the carbon black mixing after crushing, is obtained after grinding
Mixture B;
(3) mixing of raw material:
Mixture A, mixture B, clay, water are mixed, obtain mixture C after mixing;
(4) compression molding:Mixture C is added in mold and carries out compression molding, obtains acoustic material semi-finished product;
(5) drying and processing:Acoustic material semi-finished product are positioned in drying chamber and are dried, acoustic material is obtained after drying.
Preferably, the parts by weight of the raw material of mixture C are:
100-200 parts of Industry Waste ash, 60-80 parts of silica, 80-120 parts of Iron-ore Slag, 10-15 parts of carbon black, clay 40-
60 parts, 100-150 parts of water.
Preferably, the grain size of Industry Waste ash be 200-500 mesh, silica grain size be the grain of 300-600 mesh, Iron-ore Slag
Diameter be 100-400 mesh, carbon black grain size be 600-800 mesh, clay grain size be 200-300 mesh.
Preferably, the grain size of mixture A is 1000-2000 mesh, and the grain size of mixture B is 1000-2000 mesh.
Further, in step (4), a length of 40-80cm, width 20-40cm, the thickness 1-5cm of mold.
Further, in step (5), the temperature in drying chamber is 100-200 DEG C.
Compared with prior art, it is an advantage of the invention that:
Acoustic material is prepared for primary raw material using Industry Waste ash in the present invention, the Industry Waste of package silica is utilized
The big substance of ash, Iron-ore Slag, carbon black, clay density carries out compression molding, then carries out drying and processing, and highdensity sound insulation is made
Material.The present invention utilizes component in Industry Waste ash to have the characteristics that lime and Iron-ore Slag quality are loose, porous well, is reducing
Environmental pollution is also reduced while production cost.And by adding clay, make acoustic material entire body obtained rich in a large amount of equal
Even and fine close open stomata, therefore sound wave can completely or partially reflect away, play outdoor noise reduction, interior elimination echo effect
Fruit.So that the acoustic material prepared has good attraction effect.
The purpose of the present invention two is to provide a kind of acoustic material, to achieve the above object, the technical scheme is that:
A kind of acoustic material is made by the method for preparing acoustic material using Industry Waste ash in the object of the invention one.
Compared with prior art, it is an advantage of the invention that:
The acoustic material prepared by the above method, mechanical property are improved, and have excellent weatherable, long
Time use is unlikely to deform, and intensity improves, and effect of vibration and noise reduction is apparent.Meanwhile the acoustic material safety and environmental protection, its own can
Degradation will not cause white pollution to environment, and can be re-utilized after its own degradation, reduce production cost.
The purpose of the present invention three is to provide a kind of sound panel, to achieve the above object, the technical scheme is that:
A kind of sound panel, the sound panel prepared with above-mentioned acoustic material.
Compared with prior art, it is an advantage of the invention that:
Sound panel stability prepared by the present invention is good, while non-aging and sound insulation value greatly improves, substantially reduces
The costs of raw material.Meanwhile the used prices of raw materials are cheap, safety and environmental protection, its own is degradable, will not be caused to environment
White pollution, and can be re-utilized after its own degradation.
The purpose of the present invention four is to provide a kind of preparation method of sound panel, to achieve the above object, technology of the invention
Scheme is:
A kind of preparation method of sound panel, includes the following steps:
(1) preparation of acoustic material:
Acoustic material is prepared with the method for preparing acoustic material using Industry Waste ash in the object of the invention one;
(2) preparation of sound panel:
Acoustic material is put into high temperature kiln and is fired at 1300-1800 DEG C, is fired 2-3 days;Then it anneals, certainly
Under right cooling condition it is 4-5 days cooling after, then be warming up to 1300-1800 DEG C, then at this temperature with the speed of 10 DEG C/min into
The rapid cooling of row, can be made sound panel when temperature is cooled to room temperature.
Further, the preparation method of sound panel further includes the polishing to sound panel and cleaning treatment, i.e.,:By sound panel
It polishes, polishing thickness is 1-5mm;It is washed 2-3 times with clear water after polishing, removes the dust on its surface.
Compared with prior art, it is an advantage of the invention that:
In the preparation method of sound panel of the present invention, protect when acoustic material is heated to certain temperature and at this temperature
Temperature, then Slow cooling reduction room temperature, is then heated to certain temperature by acoustic material again, is dropped rapidly with speed appropriate
Temperature, this method increase the hardness of sound panel and its abrasion resistances, for a long time using being unlikely to deform.
Specific implementation mode
Technical solution in the embodiment of the present invention is subjected to clear, complete description below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
All other embodiment for being obtained without making creative work of technical staff, belong to the guarantor of the present invention
Protect range.
Embodiment 1
1, the preparation of acoustic material:
(1) processing of Industry Waste ash:
The Industry Waste ash of 200 mesh is crushed, Industry Waste ash powder and 60 part of 300 purpose two after 100 parts of crushing are taken
It is ground after silica mixing, the mixture A of 1000 mesh is obtained after grinding;
(2) processing of Iron-ore Slag:
The Iron-ore Slag of 100 mesh is crushed, the carbon black mixing of the Iron-ore Slag powder after 80 parts of crushing and 10 part of 600 mesh is taken
After be ground, the mixture B of 1000 mesh is obtained after grinding;
(3) mixing of raw material:
Clay, the 100 parts of water of mixture A, mixture B, 40 part of 200 mesh are mixed, are mixed after mixing
Object C;
(4) compression molding:Mixture C is added in the mold that long * wide * thickness is 40cm*20cm*1cm and carries out compression molding,
Obtain acoustic material semi-finished product;
(5) drying and processing:Acoustic material semi-finished product are positioned in 100 DEG C of drying chamber and are dried, obtained after drying every
Sound material.
2, the preparation of sound panel:
Acoustic material is put into high temperature kiln and is fired at 1300 DEG C, is fired 3 days;Then under the conditions of natural cooling
After 4 days cooling, then 1300 DEG C are warming up to, are then cooled down rapidly with the speed of 10 DEG C/min at this temperature, wait for that temperature is cold
Sound panel can be made when but arriving room temperature.
Preferably, obtained sound panel is polished, polishing thickness is 1mm;It is washed 2 times, is removed with clear water after polishing
The dust on its surface.
Embodiment 2
1, the preparation of acoustic material:
(1) processing of Industry Waste ash:
The Industry Waste ash of 350 mesh is crushed, Industry Waste ash powder and 70 part of 450 purpose two after 150 parts of crushing are taken
It is ground after silica mixing, the mixture A of 1500 mesh is obtained after grinding;
(2) processing of Iron-ore Slag:
The Iron-ore Slag of 250 mesh is crushed, takes the carbon black of Iron-ore Slag powder and 12 part of 700 mesh after 100 parts of crushing mixed
It is ground after conjunction, the mixture B of 1500 mesh is obtained after grinding;
(3) mixing of raw material:
Clay, the 110 parts of water of mixture A, mixture B, 50 part of 250 mesh are mixed, are mixed after mixing
Object C;
(4) compression molding:Mixture C is added in the mold that long * wide * thickness is 60cm*30cm*3cm and carries out compression molding,
Obtain acoustic material semi-finished product;
(5) drying and processing:Acoustic material semi-finished product are positioned in 150 DEG C of drying chamber and are dried, obtained after drying every
Sound material.
2, the preparation of sound panel:
Acoustic material is put into high temperature kiln and is fired at 1500 DEG C, is fired 2.5 days;Then in natural cooling condition
After lower cooling 4.5 days, then 1500 DEG C are warming up to, are then cooled down rapidly with the speed of 10 DEG C/min at this temperature, wait for temperature
Sound panel can be made when being cooled to room temperature in degree.
Preferably, obtained sound panel is polished, polishing thickness is 3mm;It is washed 2 times, is removed with clear water after polishing
The dust on its surface.
Embodiment 3
1, the preparation of acoustic material:
(1) processing of Industry Waste ash:
The Industry Waste ash of 500 mesh is crushed, Industry Waste ash powder and 80 part of 600 purpose two after 200 parts of crushing are taken
It is ground after silica mixing, the mixture A of 2000 mesh is obtained after grinding;
(2) processing of Iron-ore Slag:
The Iron-ore Slag of 400 mesh is crushed, takes the carbon black of Iron-ore Slag powder and 15 part of 800 mesh after 120 parts of crushing mixed
It is ground after conjunction, the mixture B of 2000 mesh is obtained after grinding;
(3) mixing of raw material:
Clay, the 150 parts of water of mixture A, mixture B, 60 part of 300 mesh are mixed, are mixed after mixing
Object C;
(4) compression molding:Mixture C is added in the mold that long * wide * thickness is 80cm*40cm*5cm and carries out compression molding,
Obtain acoustic material semi-finished product;
(5) drying and processing:Acoustic material semi-finished product are positioned in 200 DEG C of drying chamber and are dried, obtained after drying every
Sound material.
2, the preparation of sound panel:
Acoustic material is put into high temperature kiln and is fired at 1800 DEG C, is fired 2 days;Then under the conditions of natural cooling
After 5 days cooling, then 1800 DEG C are warming up to, are then cooled down rapidly with the speed of 10 DEG C/min at this temperature, wait for that temperature is cold
Sound panel can be made when but arriving room temperature.
Preferably, obtained sound panel is polished, polishing thickness is 5mm;It is washed 3 times, is removed with clear water after polishing
The dust on its surface.
Embodiment 4
1, the preparation of acoustic material:
(1) processing of Industry Waste ash:
The Industry Waste ash of 400 mesh is crushed, Industry Waste ash powder and 75 part of 500 purpose two after 170 parts of crushing are taken
It is ground after silica mixing, the mixture A of 1700 mesh is obtained after grinding;
(2) processing of Iron-ore Slag:
The Iron-ore Slag of 360 mesh is crushed, takes the carbon black of Iron-ore Slag powder and 13 part of 550 mesh after 110 parts of crushing mixed
It is ground after conjunction, the mixture B of 1700 mesh is obtained after grinding;
(3) mixing of raw material:
Clay, the 120 parts of water of mixture A, mixture B, 45 part of 270 mesh are mixed, are mixed after mixing
Object C;
(4) compression molding:Mixture C is added in the mold that long * wide * thickness is 70cm*35cm*2.5cm and is molded into
Type obtains acoustic material semi-finished product;
(5) drying and processing:Acoustic material semi-finished product are positioned in 180 DEG C of drying chamber and are dried, obtained after drying every
Sound material.
2, the preparation of sound panel:
Acoustic material is put into high temperature kiln and is fired at 1650 DEG C, is fired 2.5 days;Then in natural cooling condition
After lower cooling 4.5 days, then 1650 DEG C are warming up to, are then cooled down rapidly with the speed of 10 DEG C/min at this temperature, wait for temperature
Sound panel can be made when being cooled to room temperature in degree.
Preferably, obtained sound panel is polished, polishing thickness is 4mm;It is washed 3 times, is removed with clear water after polishing
The dust on its surface.
Comparative example 1
Commercially available sound panel is made from the following raw materials in parts by weight:42-56 parts of thermoplastic phenol resin, expanded vermiculite 20-25
Part, 4-6 parts of polystyrene foam plastics, 2-3 parts of silane coupling agent, 8-10 parts of polymethyl methacrylate, antioxidant 0.1-0.2
Part, 0.1-0.2 parts of foaming agent, aqueous 10-12 parts of poly- ammonia lotion, 10-20 parts of collagenous fibres, 20-30 parts of waste wool felt and auxiliary agent 2-5
Part.
Commercially available sound panel in the sound panel being prepared by embodiment 1-4 and comparative example 1 is done into performance survey respectively
Examination, obtains following test result:
1, abrasion resistance is tested
Sound panel prepared by embodiment 1-4 carries out abrasion resistance test respectively with the commercially available sound panel in comparative example 1.
Examination is produced according to the requirement of the GB/T 15036.2-2001 in standard GB/T/5036.1~15036.2-2001 of T and regulation
Part:Test specimen paint is mounted on abrasiometer upwardly, and abrasive wheel is rack-mount, in each contact
100r is worn away under the conditions of 4.9N ± 0.2N.This performance test is tested using BN706 type paint film abrasion performance instrument, and test result is such as
Shown in following table:
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Commercially available sound panel | |
Wearing valve/mg | 18 | 17 | 15 | 10 | 22 |
As seen from the above table, the sound panel that 1-4 of the embodiment of the present invention is prepared is superior to commercially available sound panel in terms of abrasion,
Illustrate acoustic material prepared by method and dispensing through the invention, and the sound panel prepared using the acoustic material is with excellent
Weatherable, for a long time using being unlikely to deform, and intensity is higher.
2, soundproof effect performance test
Commercially available sound panel in the embodiment 1-4 sound panels prepared and comparative example 1 is subjected to soundproof effect test respectively.It presses
According to national standard GB/T19899.3-2005 (ISO140-3:1995) it is carried out with the examination criteria of GB-T501212005 (ISO717-1)
Sound insulation volume is evaluated, and in the case where generating frequency noise and being 2000 hertz, testing result is as follows:
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Commercially available sound panel | |
Sound transmission loss/dB | 32 | 34 | 30 | 31 | 52 |
As seen from the above table, the sound panel that 1-4 of the embodiment of the present invention is prepared be superior in terms of soundproof effect it is commercially available every
Soundboard illustrates that sound panel prepared by method and dispensing through the invention has good soundproof effect, effect of vibration and noise reduction bright
It is aobvious.
3, cost compares
Cost by the embodiment 1-4 sound panels being prepared be respectively 120 yuan/square meter, 135 yuan/square meter, 130 yuan/
Square meter, 126 yuan/square meter, and the commercially available sound panel in comparative example 1 be 185 yuan/square meter, therefore, prepare through the invention every
Soundboard is cheap, can be used for large-scale mass production.
Preferably, preferred embodiment of the invention is:
1, the preparation of acoustic material:
(1) processing of Industry Waste ash:
The Industry Waste ash of 400 mesh is crushed, Industry Waste ash powder and 75 part of 500 purpose two after 170 parts of crushing are taken
It is ground after silica mixing, the mixture A of 1700 mesh is obtained after grinding;
(2) processing of Iron-ore Slag:
The Iron-ore Slag of 360 mesh is crushed, takes the carbon black of Iron-ore Slag powder and 13 part of 550 mesh after 110 parts of crushing mixed
It is ground after conjunction, the mixture B of 1700 mesh is obtained after grinding;
(3) mixing of raw material:
Clay, the 120 parts of water of mixture A, mixture B, 45 part of 270 mesh are mixed, are mixed after mixing
Object C;
(4) compression molding:Mixture C is added in the mold that long * wide * thickness is 70cm*35cm*2.5cm and is molded into
Type obtains acoustic material semi-finished product;
(5) drying and processing:Acoustic material semi-finished product are positioned in 180 DEG C of drying chamber and are dried, obtained after drying every
Sound material.
2, the preparation of sound panel:
Acoustic material is put into high temperature kiln and is fired at 1650 DEG C, is fired 2.5 days;Then in natural cooling condition
After lower cooling 4.5 days, then 1650 DEG C are warming up to, are then cooled down rapidly with the speed of 10 DEG C/min at this temperature, wait for temperature
Sound panel can be made when being cooled to room temperature in degree.
Preferably, obtained sound panel is polished, polishing thickness is 4mm;It is washed 3 times, is removed with clear water after polishing
The dust on its surface.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (10)
1. a kind of method preparing acoustic material using Industry Waste ash, which is characterized in that include the following steps:
(1) processing of Industry Waste ash:
Industry Waste ash is crushed, is ground after taking Industry Waste ash powder and the silica mixing after crushing, after grinding
Obtain mixture A;
(2) processing of Iron-ore Slag:
Iron-ore Slag is crushed, is ground after taking Iron-ore Slag powder and the carbon black mixing after crushing, is mixed after grinding
Object B;
(3) mixing of raw material:
The mixture A, the mixture B, clay, water are mixed, obtain mixture C after mixing;
(4) compression molding:The mixture C is added in mold and carries out compression molding, obtains acoustic material semi-finished product;
(5) drying and processing:The acoustic material semi-finished product are positioned in drying chamber and are dried, acoustic material is obtained after drying.
2. the method according to claim 1 for preparing acoustic material using Industry Waste ash, which is characterized in that the mixture
The parts by weight of the raw material of C are:
100-200 parts of Industry Waste ash, 60-80 parts of silica, 80-120 parts of Iron-ore Slag, 10-15 parts of carbon black, 40-60 parts of clay,
100-150 parts of water.
3. the method according to claim 2 for preparing acoustic material using Industry Waste ash, which is characterized in that the Industry Waste
Ash grain size be 200-500 mesh, silica grain size be 300-600 mesh, Iron-ore Slag grain size be 100-400 mesh, carbon black
Grain size be 600-800 mesh, clay grain size be 200-300 mesh.
4. the method according to claim 1 for preparing acoustic material using Industry Waste ash, which is characterized in that the mixture
The grain size of A is 1000-2000 mesh, and the grain size of the mixture B is 1000-2000 mesh.
5. the method according to claim 1 for preparing acoustic material using Industry Waste ash, which is characterized in that the step
(4) in, a length of 40-80cm, width 20-40cm, the thickness 1-5cm of mold.
6. the method according to claim 1 for preparing acoustic material using Industry Waste ash, which is characterized in that the step
(5) in, the temperature in drying chamber is 100-200 DEG C.
7. a kind of acoustic material, which is characterized in that by utilizing Industry Waste ash described in any one of claim 1-6 claims
The method for preparing acoustic material is made.
8. a kind of sound panel, which is characterized in that the sound panel prepared with the acoustic material described in claim 7.
9. a kind of preparation method of sound panel according to any one of claims 8, which is characterized in that include the following steps:
(1) preparation of acoustic material:
Acoustic material is prepared with the method described in claim 1 for preparing acoustic material using Industry Waste ash;
(2) preparation of sound panel:
The acoustic material is put into high temperature kiln and is fired at 1300-1800 DEG C, is fired 2-3 days;Then it anneals, certainly
Under right cooling condition it is 4-5 days cooling after, then be warming up to 1300-1800 DEG C, then at this temperature with the speed of 10 DEG C/min into
The rapid cooling of row, can be made the sound panel when temperature is cooled to room temperature.
10. the preparation method of sound panel according to claim 9, which is characterized in that further include beating the sound panel
Mill and cleaning treatment, i.e.,:The sound panel is polished, polishing thickness is 1-5mm;It is washed 2-3 times, is removed with clear water after polishing
Remove the dust on its surface.