CN108285289A - A kind of concrete corrosion-prevention rust-resistance agent - Google Patents
A kind of concrete corrosion-prevention rust-resistance agent Download PDFInfo
- Publication number
- CN108285289A CN108285289A CN201810228372.8A CN201810228372A CN108285289A CN 108285289 A CN108285289 A CN 108285289A CN 201810228372 A CN201810228372 A CN 201810228372A CN 108285289 A CN108285289 A CN 108285289A
- Authority
- CN
- China
- Prior art keywords
- parts
- concrete
- sodium
- water
- resistance agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of concrete corrosion-prevention rust-resistance agent, it is characterised in that:It is by the component of following parts by weight:10 15 parts of reinforcing bar passivator, 5 10 parts of amino alcohol, 15 30 parts of polycarboxylate water-reducer, 15 parts of sodium tripolyphosphate, 15 parts of borax, 15 parts of sodium gluconate, 12 parts of methyl cellulose ether, 0.5 1 parts of rosin, 0.1 0.5 parts of dodecyl sodium sulfate, 0.1 0.3 parts of sodium molybdate, 40 60 parts of water.The invention has the advantages that:The pore in concrete can be blocked, improve the Anti-Chloride Ion Penetration of concrete, brokenization of the chlorion to rebar passivation film can significantly be alleviated, enhance the ability of concrete sulfate-resistant corrosion, with excellent anticorrosion performance, repairing performance is good, and the endurance quality and concrete that can promote concrete integrate erosion-resisting ability, significantly improve building durability.
Description
Technical field
The present invention relates to corrosion inhibitor technical fields, and in particular to a kind of concrete corrosion-prevention rust-resistance agent.
Background technology
Reinforcing steel bar corrosion inhibitor mixes in concrete to prevent or slow down the additive of steel bar corrosion.Reinforcing steel bar corrosion inhibitor refers to adding
Enter in concrete or brush in concrete surface, can prevent or slow down the chemical substance of reinforcement corrosion.Some can improve concrete
Additive or outer coating protectant (such as silicon ash, impregnating with silane agent) to reinforcing bar barrier propterty are not belonging to reinforcing steel bar corrosion inhibitor scope,
Reinforcing steel bar corrosion inhibitor must be able to directly prevent or delay steel bar corrosion.Traditional corrosion inhibitor can be divided into Anodic Type and cathode type.Using
Extensive nitrite is Anodic Type corrosion inhibitor, and this kind of corrosion inhibitor has larger murder by poisoning to human body and environment, the meeting when dosage deficiency
Accelerate steel bar corrosion, there are prodigious application risk, current many developed countries have been forbidden to use.Cathode type corrosion inhibitor is such as:Phosphorus
The dosage of hydrochlorate, carbonate, aliphatic ester etc., this kind of corrosion inhibitor is often larger, and Cost of Concrete is made to improve, and inconvenience is promoted.
Invention content
In order to solve the above technical problems, technical solution provided by the invention is:A kind of concrete corrosion-prevention rust-resistance agent, feature
It is:It is by the component of following parts by weight:10-15 parts of reinforcing bar passivator, 5-10 parts of amino alcohol, polycarboxylate water-reducer 15-30
Part, 1-5 parts of sodium tripolyphosphate, 1-5 parts of borax, 1-5 parts of sodium gluconate, 1-2 parts of methyl cellulose ether, 0.5-1 parts of rosin, ten
0.1-0.5 parts of dialkyl sulfonates, 0.1-0.3 parts of sodium molybdate, 40-60 parts of water.
Preferably, it is by the component of following parts by weight:12 parts of reinforcing bar passivator, 8 parts of amino alcohol, polycarboxylate water-reducer 20
Part, 3 parts of sodium tripolyphosphate, 3 parts of borax, 4 parts of sodium gluconate, 1 part of methyl cellulose ether, 0.6 part of rosin, dodecyl sodium sulfonate
0.2 part of sodium, 0.2 part of sodium molybdate, 50 parts of water.
Preferably, it is by the component of following parts by weight:10 parts of reinforcing bar passivator, 5 parts of amino alcohol, polycarboxylate water-reducer 15
Part, 1 part of sodium tripolyphosphate, 1 part of borax, 1 part of sodium gluconate, 1 part of methyl cellulose ether, 0.5 part of rosin, dodecyl sodium sulfonate
0.1 part of sodium, 0.1 part of sodium molybdate, 40 parts of water.
Preferably, it is by the component of following parts by weight:15 parts of reinforcing bar passivator, 10 parts of amino alcohol, polycarboxylate water-reducer
30 parts, 5 parts of sodium tripolyphosphate, 5 parts of borax, 5 parts of sodium gluconate, 2 parts of methyl cellulose ether, 1 part of rosin, dodecyl sodium sulfonate
0.5 part of sodium, 0.3 part of sodium molybdate, 60 parts of water.
The invention has the advantages that:The pore in concrete can be blocked, the resistance of chloride ion penetration of concrete is improved
Can, it can significantly alleviate brokenization of the chlorion to rebar passivation film, enhance the ability of concrete sulfate-resistant corrosion, have excellent
Anticorrosion performance, repairing performance is good, and the endurance quality and concrete that can promote concrete integrate erosion-resisting ability, significantly improve
Building durability.
Specific implementation mode
Embodiment one
A kind of concrete corrosion-prevention rust-resistance agent, it is characterised in that:It is by the component of following parts by weight:Reinforcing bar passivator 12
Part, 8 parts of amino alcohol, 20 parts of polycarboxylate water-reducer, 3 parts of sodium tripolyphosphate, 3 parts of borax, 4 parts of sodium gluconate, methylcellulose
1 part of ether, 0.6 part of rosin, 0.2 part of dodecyl sodium sulfate, 0.2 part of sodium molybdate, 50 parts of water.
Water-cement ratio:0.371, cement:412kg/m3;Sand:798kg/m3;Stone:1015kg/m3;Additive:AMCI-
C16.48;Water:153kg/m3.
The slump:It is initially 180mm, 1h 135mm;Air content is 4.6%;3d, 7d, 28d, 56d compression strength are distinguished
For 21.9MPa, 42.5MPa, 50.8MPa, 56.2MPa.
Embodiment two
A kind of concrete corrosion-prevention rust-resistance agent, it is characterised in that:It is by the component of following parts by weight:Reinforcing bar passivator 10
Part, 5 parts of amino alcohol, 15 parts of polycarboxylate water-reducer, 1 part of sodium tripolyphosphate, 1 part of borax, 1 part of sodium gluconate, methylcellulose
1 part of ether, 0.5 part of rosin, 0.1 part of dodecyl sodium sulfate, 0.1 part of sodium molybdate, 40 parts of water.
Water-cement ratio:0.371, cement:252kg/m3;Sand:798kg/m3;Stone:1015kg/m3;Slag powders:80kg/
m3;Flyash:80kg/m3;Additive:AMCI-C16.48;Water:153kg/m3.
The slump:It is initially 210mm, 1h 175mm;Air content is 5.0%;3d, 7d, 28d, 56d compression strength are distinguished
For 16.3MPa, 36.8MPa, 50.9MPa, 55.3MPa.
Embodiment three
A kind of concrete corrosion-prevention rust-resistance agent, it is characterised in that:It is by the component of following parts by weight:Reinforcing bar passivator 15
Part, 10 parts of amino alcohol, 30 parts of polycarboxylate water-reducer, 5 parts of sodium tripolyphosphate, 5 parts of borax, 5 parts of sodium gluconate, methylcellulose
2 parts of ether, 1 part of rosin, 0.5 part of dodecyl sodium sulfate, 0.3 part of sodium molybdate, 60 parts of water.
Water-cement ratio:0.371, cement:252kg/m3;Sand:798kg/m3;Stone:1015kg/m3;Slag powders:80kg/
m3;Flyash:80kg/m3;Additive:YJ-50419.36;Water:153kg/m3.
The slump:It is initially 225mm, 1h 195mm;Air content is 4.8%;3d, 7d, 28d, 56d compression strength are distinguished
For 21.0MPa, 35.5MPa, 53.9MPa, 57.2MPa.
Claims (4)
1. a kind of concrete corrosion-prevention rust-resistance agent, it is characterised in that:It is by the component of following parts by weight:Reinforcing bar passivator 10-15
Part, 5-10 parts of amino alcohol, 15-30 parts of polycarboxylate water-reducer, 1-5 parts of sodium tripolyphosphate, 1-5 parts of borax, sodium gluconate 1-5
Part, 1-2 parts of methyl cellulose ether, 0.5-1 parts of rosin, 0.1-0.5 parts of dodecyl sodium sulfate, 0.1-0.3 parts of sodium molybdate, water
40-60 parts.
2. a kind of concrete corrosion-prevention rust-resistance agent according to claim 1, it is characterised in that:It is by the group of following parts by weight
Point:12 parts of reinforcing bar passivator, 8 parts of amino alcohol, 20 parts of polycarboxylate water-reducer, 3 parts of sodium tripolyphosphate, 3 parts of borax, sodium gluconate
4 parts, 1 part of methyl cellulose ether, 0.6 part of rosin, 0.2 part of dodecyl sodium sulfate, 0.2 part of sodium molybdate, 50 parts of water.
3. a kind of concrete corrosion-prevention rust-resistance agent according to claim 1, it is characterised in that:It is by the group of following parts by weight
Point:10 parts of reinforcing bar passivator, 5 parts of amino alcohol, 15 parts of polycarboxylate water-reducer, 1 part of sodium tripolyphosphate, 1 part of borax, sodium gluconate
1 part, 1 part of methyl cellulose ether, 0.5 part of rosin, 0.1 part of dodecyl sodium sulfate, 0.1 part of sodium molybdate, 40 parts of water.
4. a kind of concrete corrosion-prevention rust-resistance agent according to claim 1, it is characterised in that:It is by the group of following parts by weight
Point:15 parts of reinforcing bar passivator, 10 parts of amino alcohol, 30 parts of polycarboxylate water-reducer, 5 parts of sodium tripolyphosphate, 5 parts of borax, gluconic acid
5 parts of sodium, 2 parts of methyl cellulose ether, 1 part of rosin, 0.5 part of dodecyl sodium sulfate, 0.3 part of sodium molybdate, 60 parts of water.