CN108274099A - A kind of welding procedure of switchgear - Google Patents
A kind of welding procedure of switchgear Download PDFInfo
- Publication number
- CN108274099A CN108274099A CN201711419874.0A CN201711419874A CN108274099A CN 108274099 A CN108274099 A CN 108274099A CN 201711419874 A CN201711419874 A CN 201711419874A CN 108274099 A CN108274099 A CN 108274099A
- Authority
- CN
- China
- Prior art keywords
- welding
- switchgear
- heat treatment
- control
- soldering opening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a kind of welding procedure of switchgear, is included the following steps：By the soldering opening wiped clean to be processed on weldment surface；The pre-heat treatment is carried out after the completion of cleaning；It is welded using tungsten electrode butt-welding fitting；It is heat-treated after being carried out to the switchgear after welding fabrication；After reaching constant temperature time, room temperature is down to the switchgear of welding fabrication and takes out weldment, that is, completes welding procedure.The present invention provides a kind of welding procedure of switchgear, by to soldering opening handle and be welded using tungsten electrode butt-welding fitting, control the welding parameter of welding gun and rear heat treatment, switchgear is effectively reduced the case where the face of weld in welding quality is recessed and solder joint deviates, improve the exterior quality of switchgear, reduce number of doing over again simultaneously, substantially increases production efficiency.
Description
Technical field
The present invention relates to welding technology field more particularly to a kind of welding procedures of switchgear.
Background technology
Switchgear is a kind of electrical equipment, and main function is to be generated electricity in electric system, transmitted electricity, the conversion of distribution and electric energy
During, electrical equipment is opened and closed, controlled and protected, is widely used in power plant, substation, petrochemical industry, metallurgy roll
The various different occasions such as steel, industry light industry textile industry, industrial enterprise and residential quarters, skyscraper.The process of switchgear exists at present
There are face of weld recess, the defect of solder joint offset to seriously affect the exterior quality of switchgear in welding quality, while it is secondary to do over again
Number is more, wastes manpower and materials, greatly reduces production efficiency.
Invention content
Present invention seek to address that the deficiencies in the prior art, and a kind of welding procedure of switchgear is provided.
The present invention to achieve the above object, using following technical scheme：
A kind of welding procedure of switchgear, which is characterized in that include the following steps：
(1) by the soldering opening wiped clean to be processed on weldment surface, ensure clean free from admixture；
(2) it polishes and disposes the metal oxide film for processing 20-30mm ranges around soldering opening on weldment surface, between weld seam
Gap control is 0.3-0.6mm, and the pre-heat treatment is carried out after the completion of cleaning, and preheating temperature control is 400-450 DEG C；
(3) it after preheating, is welded using tungsten electrode butt-welding fitting, control resistance welding gun electric conducting nozzle is at a distance from soldering opening
0.6-0.9mm, the speed of welding for controlling welding gun are 25-35cm/min；
(4) it is heat-treated after being carried out to the switchgear after welding fabrication, cabinet is placed in electrical heating case, control electrical heating case
Ranging from 6-10 DEG C/min of heating rate, temperature rises to 400-450 DEG C, and it is 30-45min to control constant temperature time；
(5) after reaching constant temperature time, room temperature is down to the switchgear of welding fabrication and takes out weldment, that is, completes welding procedure.
Particularly, the pre-heat treatment in the step (2) carries out the pre-heat treatment using manual grilled gun.
The beneficial effects of the invention are as follows：The present invention provides a kind of welding procedure of switchgear, to soldering opening
It manages and tungsten electrode butt-welding fitting is used to be welded, control the welding parameter of welding gun and rear heat treatment, effectively reduce switchgear and exist
The case where face of weld recess and solder joint in welding quality deviate, improves the exterior quality of switchgear, reduces simultaneously
It does over again number, substantially increases production efficiency.
Specific implementation mode
With reference to embodiment, the invention will be further described：
Embodiment 1
A kind of welding procedure of switchgear, includes the following steps：
(1) by the soldering opening wiped clean to be processed on weldment surface, ensure clean free from admixture；
(2) it polishes and disposes the metal oxide film for processing 20mm ranges around soldering opening on weldment surface, weld gap
For 0.3mm, the pre-heat treatment is carried out after the completion of cleaning, the pre-heat treatment is carried out using manual grilled gun, preheating temperature is 400 DEG C；
(3) it after preheating, is welded using tungsten electrode butt-welding fitting, control resistance welding gun electric conducting nozzle is at a distance from soldering opening
0.6mm, the speed of welding for controlling welding gun are 25cm/min；
(4) it is heat-treated after being carried out to the switchgear after welding fabrication, cabinet is placed in electrical heating case, control electrical heating case
Heating rate be 6 DEG C/min, temperature rises to 400 DEG C, and it is 45min to control constant temperature time；
(5) after reaching constant temperature time, room temperature is down to the switchgear of welding fabrication and takes out weldment, that is, completes welding procedure.
Embodiment 2
A kind of welding procedure of switchgear, includes the following steps：
(1) by the soldering opening wiped clean to be processed on weldment surface, ensure clean free from admixture；
(2) it polishes and disposes the metal oxide film for processing 30mm ranges around soldering opening on weldment surface, weld gap
For 0.6mm, the pre-heat treatment is carried out after the completion of cleaning, the pre-heat treatment is carried out using manual grilled gun, preheating temperature is 450 DEG C；
(3) it after preheating, is welded using tungsten electrode butt-welding fitting, control resistance welding gun electric conducting nozzle is at a distance from soldering opening
0.9mm, the speed of welding for controlling welding gun are 35cm/min；
(4) it is heat-treated after being carried out to the switchgear after welding fabrication, cabinet is placed in electrical heating case, control electrical heating case
Heating rate ranging from 10 DEG C/min, temperature rises to 450 DEG C, and it is 30min to control constant temperature time；
(5) after reaching constant temperature time, room temperature is down to the switchgear of welding fabrication and takes out weldment, that is, completes welding procedure.
The present invention is exemplarily described above, it is clear that present invention specific implementation is not subject to the restrictions described above,
As long as using the various improvement of inventive concept and technical scheme of the present invention progress, or not improved directly apply to other fields
It closes, within protection scope of the present invention.
Claims (2)
1. a kind of welding procedure of switchgear, which is characterized in that include the following steps：
(1) by the soldering opening wiped clean to be processed on weldment surface, ensure clean free from admixture；
(2) it polishes and disposes the metal oxide film for processing 20-30mm ranges around soldering opening on weldment surface, weld gap control
It is made as 0.3-0.6mm, the pre-heat treatment is carried out after the completion of cleaning, preheating temperature control is 400-450 DEG C；
(3) it after preheating, is welded using tungsten electrode butt-welding fitting, control resistance welding gun electric conducting nozzle is 0.6- at a distance from soldering opening
0.9mm, the speed of welding for controlling welding gun are 25-35cm/min；
(4) it is heat-treated after being carried out to the switchgear after welding fabrication, cabinet is placed in electrical heating case, control the liter of electrical heating case
Warm velocity interval is 6-10 DEG C/min, and temperature rises to 400-450 DEG C, and it is 30-45min to control constant temperature time；
(5) after reaching constant temperature time, room temperature is down to the switchgear of welding fabrication and takes out weldment, that is, completes welding procedure.
2. a kind of welding procedure of switchgear according to claim 1, which is characterized in that pre- in the step (2)
Heat treatment carries out the pre-heat treatment using manual grilled gun.