CN108272324A - A kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain - Google Patents
A kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain Download PDFInfo
- Publication number
- CN108272324A CN108272324A CN201810248997.0A CN201810248997A CN108272324A CN 108272324 A CN108272324 A CN 108272324A CN 201810248997 A CN201810248997 A CN 201810248997A CN 108272324 A CN108272324 A CN 108272324A
- Authority
- CN
- China
- Prior art keywords
- magnetic stripe
- magnetic
- preparation
- thickness
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of self-priming closure magnetic stripes for flexible door curtain and preparation method thereof and preparation method thereof, it is coated on the consistent flexible magnetic strips of the intramarginal adjacent material of flexible door curtain including at least a pair of, the magnetic stripe includes the closely coupled magnetic layer and soft magnetosphere connect, and a pair of of magnetic stripe that the side that front-back is south poles inequality is mutually inhaled, magnetic stripe lateral thickness is not more than 5mm, and front-back width is not less than thickness.The preparation method of the magnetic stripe includes the following steps:Magnetic layer and soft magnetosphere distinguish calendering formation, and by lamination or gluing, soft magnetosphere is close-coupled on the front-back of magnetic layer, splitting winding, and magnetic stripe through-thickness magnetizes.The present invention realizes door and closes magnetic stripe side uniform adsorption, and door closes that effect is good, and more preferably, magnetic stripe thickness can be thinner for user experience, and product is easy slitting, upper amount, realizes higher productivity and yield rate, reaches lower production cost.
Description
Technical field
The self-priming closure magnetic stripe and preparation method thereof that the present invention relates to a kind of for flexible door curtain.
Background technology
The utilization of magnetic self-suction flexible door curtain is more and more extensive, is chiefly used in the public arenas such as market, dining room, workshop, also uses
In household, have the functions such as windproof, dust-proof, mosquito-proof, transparent, decoration, self-priming closure, increasingly by the blueness of ornament materials circle
It looks at.
Since the difference of magnetic mode exists, all various deficiencies need the magnetic self-suction flexible door curtain of the prior art
It improves.
Authorization Notice No. 2802053Y discloses a kind of rubber magnetic strip type whole closed soft screen door, the overlapping on two width door sides
Place is equipped with rubber magnet strip of paper used for sealing, and the ferrite sintered magnetic patch of relatively high magnetism is equipped in the lower end of strip of paper used for sealing.Its shortcoming is door seal
Overlapping, screen door thickness can be increased, influence decorative effect, ferrite sintered piece, local suction is strong, brings the endless of usage experience
Security risk at beautiful and strong suction.The obvious patent is adsorbed using the front-back overlapping of rubber seal strip, to ensure enough suctions
Power but brings thickness increase, the drawbacks such as too fat to move.
Authorization Notice No. 101731928B, magnetic catch type transparent film curtain disclose commissure device number row's magnetic and touch dress
It sets, there is stripe shape magnetic patch, outside to use cushion compound bound edge in crash device.The shortcoming of this patent is inhaled by local magnetic force
Attached, the magnetic block for generating local suction certainly exists security risk, and suction is unevenly distributed, and user experience uses inevitable not complete enough
U.S., sealing effect can not also ensure.
Authorization Notice No. 2272713Y, a kind of door curtain, the strip soft material that it is vertically hung by several are constituted, special
Sign is that the transverse sides in strip soft material are respectively equipped with vertical tubule, and two tubules are respectively filled with silicon materials and magnetic material
Material can not therefrom be obtained and magnetic suck may be implemented, can not also be obtained other suction types due to two tube materials difference, it is seen that
The firmness of self-priming is no collateral security, and this patent does not carry out the disclosure of related suction.
The final effect parameter that suction F can intuitively embody when being magnet use, F ∝ Bg*Bg*S, suction are proportional to
Square of the magnetic flux density Bg in the magnetic circuit gap that magnet and absorbate matter are formed, suction size is directly proportional to adsorption area, conventional
The working face of magnetic stripe all designs the one side larger in magnetic stripe area, and the small side of area is not usually in the range of consideration.This
Applicant's Authorization Notice No. 104945754B discloses a kind of manufacturing method for the rubber extruding magnetic stripe improving suction:Magnetic stripe passes through
Co-extrusion is integrally formed, at least double-layer structure, and one layer is conventional magnetic layer, and in addition one layer is soft magnetosphere, and suction improves 15-
30%, but the patent does not disclose the selection of the working face of magnetic stripe further, the matching to the mode of magnetizing and working face
Also it does not disclose further.
The big working face of area is abandoned, the small side of conversion suction is perverse, moreover must increase the thickness of side,
This brings the difficulty for being difficult to overcome to magnetic stripe production technology, and magnetic stripe is too thick to be difficult to cut, and yield rate is low, and the production of magnetic stripe can not
Upper amount, production cost are high.
The present invention program will solve deficiency in the prior art:To ensure that side has enough suction, magnetic stripe thickness that need to reach
To 5mm, slitting is difficult, and yield rate is low, it is difficult to upper amount;Suction is by the offer of magnetic stripe part, edge seal discontinuity, part
There are security risks at strong suction;Magnetic attracting device front-back overlapping absorption, adsorption plane are far longer than side, too fat to move, influence door curtain
Utility function and decoration functions.
Invention content
The self-priming closure magnetic stripe and preparation method thereof that the purpose of the present invention is to provide a kind of for flexible door curtain.
A kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain, including at least a pair is coated on flexibility
The consistent flexible magnetic strips of adjacent material in door curtain edge, it is characterized in that the magnetic stripe includes the closely coupled magnetic layer b connect
With soft magnetosphere a, and the side that front-back is south poles inequality, to a pair of of magnetic stripe of suction, magnetic stripe lateral thickness 3 is not more than 5mm, magnetic
Width 2 is not less than thickness 3.
The soft magnetism layer thickness is not more than 1mm, and the permanent magnetism layer thickness is not more than 4mm.
The soft magnetosphere is tightly disposed on the front-back of magnetic layer respectively.
It is lamination, gluing that the soft magnetosphere is tightly disposed in the mode on the front-back of magnetic layer respectively.
The pattern of the permanent magnetism magnetic material is sheet.
The soft magnetosphere is modified high-molecular polymeric layer of the soft magnetic property substance as filler.
The magnetic layer is modified high-molecular polymeric layer of the permanent magnetism magnetisable material as filler.
The magnetic stripe cross sectional shape is rectangle or its equivalent abnormity.
The preparation method of the magnetic stripe includes the following steps:Magnetic layer and soft magnetosphere distinguish calendering formation, by lamination or
Person's gluing, soft magnetosphere are close-coupled on the front-back of magnetic layer, splitting winding, and magnetic stripe through-thickness magnetizes.
The beneficial effects of the invention are as follows:
1. magnetic stripe suction foot, side suction can be improved to year-on-year 2 times, and thickness is thinner than 5mm, and cutting is easy, high yield rate,
Productivity is high, at low cost, solve in puzzlement reality production can not the amount of going up urgent bottleneck problem.
2. the suction of magnetic stripe front-back is greatly reduced, it is year-on-year 0.28 to 0.65, avoids conventional front and back larger face
The long-pending absorption that forward laps, does not increase door curtain thickness, does not influence the decorative effect of door curtain.
3. suction covers adjacent all contact surfaces of door curtain from top to bottom, because magnetic stripe front-back is the south poles of inequality,
That is north and south thickness magnetizes, and suction is uniform, and it is good that door closes effect.
4. the width of the front-back of magnetic stripe is much larger than thickness, magnetic stripe does not reverse.
5. suction is uniform from top to bottom for magnetic stripe, user experience is more perfect, eliminates the security risk of the strong magnetic in part.
6. improvement of the present invention is notable, versatile, it can be used for various plane formula self-priming closed curtain.
With reference to specific embodiments and the drawings explanation, the present invention is described further, but should not be understood as to the present invention's
Further limitation:
Description of the drawings
Fig. 1 is the structural schematic diagram of face view of the present invention;
Fig. 2 is vertical view face of the present invention structural schematic diagram;
Fig. 3 is that the adjacent side right side of the present invention regards and left view structural representation;
Fig. 4 is the structural schematic diagram in the vertical view face of the prior art;
Fig. 5 is that the adjacent side right side of the prior art regards and left view structural representation.
In Fig. 1 to Fig. 5:1 is magnetic stripe length L, and 2 be magnetic stripe width W, and 3 magnetic stripe thickness T, a are soft magnetosphere, and b is permanent magnetism
Layer.
Specific implementation mode:
A kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain, including at least a pair is coated on flexible door curtain
The consistent flexible magnetic strips of intramarginal adjacent material, it is characterized in that the magnetic stripe includes the closely coupled magnetic layer b connect and soft
Magnetosphere a, and the side that front-back is south poles inequality, to a pair of of magnetic stripe of suction, magnetic stripe lateral thickness 3 is not more than 5mm, and magnetic stripe is wide
Degree 2 is not less than thickness 3.
Further, magnetic stripe is that the north and south of thickness direction is magnetized.
Further, the front-back is the front-back that door shown in FIG. 1 closes magnetic stripe front view.
The soft magnetism layer thickness is not more than 1mm, and the permanent magnetism layer thickness is not more than 4mm.
The soft magnetosphere is tightly disposed on the front-back of magnetic layer respectively.
Further, soft magnetosphere and magnetic layer are closely connected by lamination, gluing.
The pattern of the permanent magnetism magnetic material is sheet.
The soft magnetosphere is modified high-molecular polymeric layer of the soft magnetic property substance as filler.
Further, soft magnetic property substance be publicly-owned knowledge in pure iron and mild steel, iron Si system alloy, iron aluminum series alloy,
In iron silicon aluminum series alloy, nickel iron-based alloy, iron Co-based alloy, soft magnetic ferrite, amorphous soft magnetic alloy, super-microcrystalline soft magnetic alloy
At least one.
The magnetic layer is modified high-molecular polymeric layer of the permanent magnetism magnetisable material as filler.
Further, permanent magnetism magnetisable material is Al-Ni-Co series permanent-magnet alloy, siderochrome cobalt system permanent magnetism gold, the permanent magnetism in publicly-owned knowledge
At least one of ferrite, rare earth permanent-magnetic material and composite permanent-magnetic material.
The magnetic stripe cross sectional shape(Vertical view face)For rectangle or its equivalent abnormity.
Further, its described equivalent abnormity is the similar rectangular figure that section rectangle outline of straight line has made special-shaped adjustment
Shape.
The preparation method of the magnetic stripe includes the following steps:Magnetic layer and soft magnetosphere distinguish calendering formation, by lamination or
Person's adhesive means, soft magnetosphere are close-coupled on the front-back of magnetic layer, splitting winding, and magnetic stripe through-thickness magnetizes.
Embodiment 1
Shown referring to Fig.1 for magnetic stripe of the present invention, a pair is coated on the consistent flexible magnetic of the intramarginal adjacent materials of flexible door curtain
Item, interception magnetic stripe length L is 10cm, and with reference to Fig. 2, the magnetic stripe contains magnetic layer b and is tightly disposed in magnetic layer front-back
On soft magnetosphere a, the magnetic stripe front-back is the south poles of inequality, i.e. magnetic stripe thickness direction north and south magnetizes, and magnetic stripe overlooks face
Dimension width W is 8mm, and magnetic stripe thickness T is 5mm, and the magnetic stripe magnetic layer b thickness is 4mm, and the magnetic stripe soft magnetosphere a thickness is
0.5mm, the magnetic layer are sheet permanent-magnet ferrite powder(NF11 expects)For the macromolecule modified polymeric layer of filler material, permanent magnetism
The maximum magnetic energy product of layer(BH)Max is 1.4 ~ 1.5MGOe, and the soft magnetosphere is that soft magnetism fine iron breeze (oxide of iron) is
The macromolecule modified polymeric layer of filler material, soft magnetosphere are fitted tightly over by stickup or lamination on the front-back of magnetic layer, phase
The adsorption plane of adjacent door curtain is in the side of magnetic stripe, and with reference to Fig. 3, respectively this mutually inhales the right side view of side to magnetic stripe and left side regards
Figure.The preparation method of the magnetic stripe includes the following steps:Magnetic layer and soft magnetosphere distinguish calendering formation, pass through lamination or glue
Viscous, soft magnetosphere is close-coupled on the front-back of magnetic layer, splitting winding, and magnetic stripe through-thickness magnetizes.
Embodiment 2
For magnetic stripe of the present invention, in addition to magnetic layer b thickness is 3mm, soft magnetosphere a thickness is outside 1mm, other are all consistent with embodiment 1.
Comparative example 1
Comparative example is prior art magnetic stripe, shown referring to Fig.1, and a pair is coated on the intramarginal adjacent material one of flexible door curtain
The flexible magnetic strips of cause, magnetic stripe intercepted length L is 10cm, with reference to Fig. 4, it is characterized in that the magnetic stripe contains only magnetic layer, it is described
Magnetic stripe permanent magnetism layer thickness b is 5mm, it is described this to the south poles that magnetic stripe front-back is inequality, i.e. magnetic stripe north and south thickness magnetizes, and overlooks
The size in face is that magnetic stripe width W is 8mm, and magnetic stripe thickness T is 5mm, and the magnetic layer is sheet permanent-magnet ferrite powder(NF12
Material)For the macromolecule modified polymeric layer of filler material, the maximum magnetic energy product of magnetic layer(BH)Max is 1.6 ~ 1.7MGOe, is inhaled
Attached face is in side, with reference to Fig. 5, respectively this right side view and left side view for mutually inhaling side to magnetic stripe.The preparation of the magnetic stripe
Method includes the following steps:Magnetic layer calendering formation, splitting winding, magnetic stripe through-thickness magnetize.
It is the embodiment of the present invention 1,2, comparative examples, market conventional example side 5mm × 10mm and front-back below
8mm × 10mm is to inhaling tensile test, record such as the following table 1
Remarks:The magnetic layer of NF12 material(BH)Max be 1.6 ~ 1.7MGOe, the magnetic layer of NF11 material(BH)Max is
1.4~1.5MGOe。
Conclusion 1, compare from the above suction it is found that when magnetic stripe grow generous size it is identical when, 1.1, the embodiment of the present invention 1 and real
Although the lateralarea for applying example 2 is much smaller than front-back area, side suction is far longer than front-back suction, so that door curtain
Self-priming avoids the overlapping absorption of front-back when being closed, side automatic absorbing is closed guarantee;1.2, comparative example and market
Conventional example is the magnetic stripe of thickness 5mm, and magnetic stripe thickness can not reduce, and there are slitting difficulties, and efficiency is low, and yield rate is low, it is difficult to
The drawbacks of upper amount;And front-back suction is suitable with side suction, and when absorption, necessarily leads to confusion, influences door and closes effect.1.3
On the market 6.45N met door curtain suction requirement under conditions of, the side adsorption capacity 12.99N of embodiment 1, most by force, it is seen that
This structure is that the thickness of magnetic stripe leaves prodigious reduction space, and the structure of embodiment 1 can be adjusted to minimum thickness, right
Answer minimum cost and best decorative effect and user experience effect.
Embodiment 3:
For magnetic stripe of the present invention, in addition to magnetic layer b thickness is 2.5mm, soft magnetosphere a thickness is 0.5mm, and the width W of magnetic stripe is 6mm,
The magnetic layer is sheet permanent-magnet ferrite powder(NF12 expects)For the macromolecule modified polymeric layer of filler material, magnetic layer
Maximum magnetic energy product(BH)Max is 1.6 ~ 1.7MGOe, other are all consistent with embodiment 1.
Embodiment 4:
For magnetic stripe of the present invention, in addition to the width W of magnetic stripe is 8mm, other are all consistent with embodiment 3.
Embodiment 5:
For magnetic stripe of the present invention, in addition to the width W of magnetic stripe is 10mm, other are all consistent with embodiment 3.
Embodiment 6:
For magnetic stripe of the present invention, in addition to the width W of magnetic stripe is 12mm, other are all consistent with embodiment 3.
Be below the embodiment of the present invention 3,4,5,6, market conventional example side is to pulling power and front-back to pulling power
Test, record such as the following table 2
Remarks:Big press proof is volume production sample in table.
Conclusion 2
From the above suction measurement Comparative result it is found that product volume production sample of the present invention is although thickness is less than market sample, same widths
With the suction of length still will greater than market sample, when magnetic stripe side adsorption area all, and the thickness of soft magnetosphere and magnetic layer
When being all unanimously 0.5mm and 2.5mm, side suction is increased with the increasing of magnetic stripe width, this is also the different occasions of door curtain
Using enough adjustment spaces are left, front-back suction is much smaller than side suction, and overlapping is avoided to adsorb.
Embodiment 7
For magnetic stripe of the present invention, in addition to magnetic layer b thickness is 2.0mm, soft magnetosphere a thickness is 0.7mm, and magnetic stripe thickness T is 3.4mm,
The magnetic layer is sheet permanent-magnet ferrite powder(NF12 expects)For the macromolecule modified polymeric layer of filler material, magnetic layer
Maximum magnetic energy product(BH)Max is outside 1.6 ~ 1.7MGOe, other are all consistent with embodiment 1.
Embodiment 8
For magnetic stripe of the present invention, other than magnetic layer b thickness is 2.5mm, soft magnetosphere a thickness is 0.5mm, and magnetic stripe thickness T is 3.5mm
Outside, other all consistent with embodiment 7.
Embodiment 9
For magnetic stripe of the present invention, other than magnetic layer b thickness is 2.5mm, soft magnetosphere a thickness is 0.7mm, and magnetic stripe thickness T is 3.9mm
Outside, other all consistent with embodiment 7.
Embodiment 10
For magnetic stripe of the present invention, in addition to magnetic layer b thickness is 3.0mm, soft magnetosphere a thickness is outside 0.5mm, and magnetic stripe thickness T is
4.0mm, the magnetic layer are sheet permanent-magnet ferrite powder(NF11 expects)For the macromolecule modified polymeric layer of filler material, permanent magnetism
The maximum magnetic energy product of layer(BH)Max is 1.4 ~ 1.5MGOe, other are all consistent with embodiment 7.
Below be inventive embodiments 7,8,9,10, market conventional example side to pull power and front-back to pull power survey
Examination, record such as the following table 3
Conclusion 3, from the above suction measurement Comparative result it is found that the side suction of comparison market 6.45N, magnetic stripe width W is consistent
In the case of, the magnetic stripe thickness of the embodiment of the present invention 7,8,9,10 is all thinner than market, and thickness still remains the space turned down,
Although year-on-year front-back area is far longer than lateralarea, to be but far smaller than side pulling force to pulling power, ensure that side
The self-priming in face avoids the overlapping absorption of door curtain.
Embodiments of the present invention are explained in detail above in conjunction with attached drawing, but the present invention is not limited to the above embodiment,
The technical field those of ordinary skill within the scope of knowledge, can also be without departing from the purpose of the present invention
Various changes can be made.
Claims (9)
1. a kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain, including at least a pair is coated on flexible door
The consistent flexible magnetic strips of the intramarginal adjacent material of curtain, it is characterized in that the magnetic stripe includes the closely coupled magnetic layer connect(b)
And soft magnetosphere(a), and the side that front-back is south poles inequality is to a pair of of magnetic stripe of suction, magnetic stripe lateral thickness(3)It is not more than
5mm, magnetic stripe width(2)Not less than thickness(3).
2. a kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain described in claim 1, it is characterized in that:It is described
Soft magnetism layer thickness is not more than 1mm, and the permanent magnetism layer thickness is not more than 4mm.
3. a kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain described in claim 2, it is characterized in that:It is described
Soft magnetosphere is tightly disposed on the front-back of magnetic layer respectively.
4. a kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain described in claim 3, it is characterized in that:It is described
It is lamination or gluing that soft magnetosphere is tightly disposed in the mode on the front-back of magnetic layer respectively.
5. a kind of claim 2 to 4 self-priming closure magnetic stripe and preparation method thereof for flexible door curtain, it is characterized in that:
The pattern of the permanent magnetism magnetic material is sheet.
6. a kind of claim 2 to 4 self-priming closure magnetic stripe and preparation method thereof for flexible door curtain, it is characterized in that:
The soft magnetosphere is modified high-molecular polymeric layer of the soft magnetic property substance as filler.
7. a kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain described in claim 5, it is characterized in that:It is described
Magnetic layer is modified high-molecular polymeric layer of the permanent magnetism magnetisable material as filler.
8. a kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain described in claim 1, it is characterized in that:It is described
Magnetic stripe cross sectional shape is rectangle or its equivalent abnormity.
9. a kind of self-priming closure magnetic stripe and preparation method thereof for flexible door curtain described in claim 1, it is characterized in that:It is described
The preparation method of magnetic stripe includes the following steps:Magnetic layer and soft magnetosphere distinguish calendering formation, soft by lamination or adhesive means
Magnetosphere is close-coupled on the front-back of magnetic layer, splitting winding, and magnetic stripe through-thickness magnetizes.