CN108220849A - A kind of surface treatment method for the fission of titanium article titanium molecule - Google Patents
A kind of surface treatment method for the fission of titanium article titanium molecule Download PDFInfo
- Publication number
- CN108220849A CN108220849A CN201810015450.6A CN201810015450A CN108220849A CN 108220849 A CN108220849 A CN 108220849A CN 201810015450 A CN201810015450 A CN 201810015450A CN 108220849 A CN108220849 A CN 108220849A
- Authority
- CN
- China
- Prior art keywords
- titanium
- article
- fission
- surface treatment
- titanium article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of surface treatment methods for the fission of titanium article titanium molecule, include the following steps:(1) titanium article is polished and degreased;(2) it puts the titanium article after polishing into vacuum heat stove, and keeps 8 10Pa of negative pressure;(3) temperature in vacuum heat stove is warming up to 1,000 1500 DEG C, and 1 5h of constant temperature;Again from high temperature 1,000 1500 DEG C be down to 100 500 DEG C, and add in air, then 0.5 4h of constant temperature, blow-on.Provided by the present invention for the surface treatment method of titanium article titanium molecule fission, impurity in titanium products is disposed by high temperature, meet the requirement of environmental protection is safe to use;Meanwhile phenomena such as affixing the lines of the hand, product scratch, breaking is prevented, color unifies no color differnece, and smooth surface is beautiful, enhances titanium article case hardness, improves its overall performance without polishing line and weld line phenomenon after processing.
Description
Technical field
The present invention relates to a kind of process for treating surface more particularly to a kind of surface treatments for the fission of titanium article titanium molecule
Method.
Background technology
In general, after titanium article is made, need to handle its surface, and after traditional surface treatment method processing,
Surface has the disadvantages that:There is apparent polishing line and weld line, and the lines of the hand are easily affixed after sandblasting, sandblasting is uneven to be caused
Color disunity, there are aberration etc..
Invention content
Against the above deficiency, the purpose of the present invention is to provide a kind of surface treatment sides for the fission of titanium article titanium molecule
Method disposes impurity in titanium products by high temperature, and meet the requirement of environmental protection is safe to use;Meanwhile after processing without polishing line with
Weld line phenomenon prevents phenomena such as affixing the lines of the hand, product scratch, breaking, and color unifies no color differnece, and smooth surface is beautiful,
Enhance titanium article case hardness, improve its overall performance.
The used in order to achieve the above objectives technical solution of the present invention is:
A kind of surface treatment method for the fission of titanium article titanium molecule, which is characterized in that include the following steps:
(1) titanium article is polished and degreased;
(2) it puts the titanium article after polishing into vacuum heat stove, and keeps negative pressure 8-10Pa;
(3) temperature in vacuum heat stove is warming up to 1000-1500 DEG C, and constant temperature 1-5h;Again from high temperature 1000-
1500 DEG C are down to 100-500 DEG C, and add in air, then constant temperature 0.5-4h, blow-on.
As a further improvement on the present invention, it is further comprising the steps of:
(4) liquid gas is passed through to cool down titanium article.
As a further improvement on the present invention, the liquid gas is liquid nitrogen.
As a further improvement on the present invention, in the step (3), the time required to temperature is warming up to 1000-1500 DEG C
For 1-4h.
As a further improvement on the present invention, in the step (3), temperature is down to 100-500 DEG C from 1000-1500 DEG C
Required time is 20-60min.
Beneficial effects of the present invention are:Using novel process of surface treatment, by being surface-treated to titanium article, titanium
Impurity after high temperature by being disposed of in product, and meet the requirement of environmental protection is safe to use;Meanwhile after processing without polishing line with
Weld line phenomenon prevents phenomena such as affixing the lines of the hand, product scratch, breaking, and color unifies no color differnece, and smooth surface is beautiful,
Enhance titanium article case hardness, improve its overall performance.
Above-mentioned is the general introduction of inventive technique scheme, and below in conjunction with specific embodiment, the present invention will be further described.
Specific embodiment
The technological means and effect taken further to illustrate the present invention to reach predetermined purpose, below in conjunction with preferable
The specific embodiment of the present invention is described in detail in embodiment.
Embodiment one:
The present embodiment provides a kind of surface treatment methods for the fission of titanium article titanium molecule, include the following steps:
(1) titanium article is polished and degreased;
(2) it puts the titanium article after polishing into vacuum heat stove, and keeps negative pressure 8Pa;
(3) temperature in vacuum heat stove is warming up to 100 DEG C, and constant temperature 1h;Again from high temperature 1000 DEG C be down to 100
DEG C, and air is added in, then constant temperature 0.5h, blow-on;
(4) liquid gas is passed through to cool down titanium article.
In the present embodiment step (4), the liquid gas is liquid nitrogen.
In the step (3), it is 1h that temperature, which is warming up to 1000 DEG C of required times,.
In the step (3), it is 20min that temperature, which is down to 100 DEG C of required times from 1000 DEG C,.
Embodiment two:
The present embodiment provides a kind of surface treatment methods for the fission of titanium article titanium molecule, include the following steps:
(1) titanium article is polished and degreased;
(2) it puts the titanium article after polishing into vacuum heat stove, and keeps negative pressure 10Pa;
(3) temperature in vacuum heat stove is warming up to 1500 DEG C, and constant temperature 5h;Again from high temperature 1500 DEG C be down to 500
DEG C, and air is added in, then constant temperature 4h, blow-on;
(4) liquid gas is passed through to cool down titanium article.
In the present embodiment step (4), the liquid gas is liquid nitrogen.
In the step (3), it is 4h that temperature, which is warming up to 1500 DEG C of required times,.
In the step (3), it is 60min that temperature, which is down to 500 DEG C of required times from 1500 DEG C,.
Embodiment three:
The present embodiment provides a kind of surface treatment methods for the fission of titanium article titanium molecule, include the following steps:
(1) titanium article is polished and degreased;
(2) it puts the titanium article after polishing into vacuum heat stove, and keeps negative pressure 9Pa;
(3) temperature in vacuum heat stove is warming up to 1250 DEG C, and constant temperature 3h;Again from high temperature 1250 DEG C be down to 300
DEG C, and air is added in, then constant temperature 2.5h, blow-on;
(4) liquid gas is passed through to cool down titanium article.
In the present embodiment step (4), the liquid gas is liquid nitrogen.
In the step (3), it is 1-4h that temperature, which is warming up to 1250 DEG C of required times,.
In the step (3), it is 40min that temperature, which is down to 300 DEG C of required times from 1250 DEG C,.
Surface treatment method provided in an embodiment of the present invention for the fission of titanium article titanium molecule, titanium article are in high temperature
Time length directly determine titanium article fission decorative pattern size, the time length fission decorative pattern it is big, the time it is short fission decorative pattern it is small, so as to
Increase perception degree.
The emphasis of the present invention essentially consists in, using novel process of surface treatment, by being surface-treated to titanium article,
Impurity after high temperature by being disposed of in titanium products, and meet the requirement of environmental protection is safe to use;Meanwhile without polishing line after processing
With weld line phenomenon, phenomena such as affixing the lines of the hand, product scratch, breaking is prevented, color unifies no color differnece, and smooth surface is beautiful
It sees, enhances titanium article case hardness, improve its overall performance.
The above described is only a preferred embodiment of the present invention, be not intended to limit the scope of the present invention,
Therefore identical with the above embodiment of the present invention or approximate technical characteristic is used, and obtained other structures, the guarantor in the present invention
Within the scope of shield.
Claims (5)
1. a kind of surface treatment method for the fission of titanium article titanium molecule, which is characterized in that include the following steps:
(1) titanium article is polished and degreased;
(2) it puts the titanium article after polishing into vacuum heat stove, and keeps negative pressure 8-10Pa;
(3) temperature in vacuum heat stove is warming up to 1000-1500 DEG C, and constant temperature 1-5h;Again from 1000-1500 DEG C of high temperature
100-500 DEG C is down to, and adds in air, then constant temperature 0.5-4h, blow-on.
2. the surface treatment method according to claim 1 for the fission of titanium article titanium molecule, which is characterized in that further include
Following steps:
(4) liquid gas is passed through to cool down titanium article.
3. the surface treatment method according to claim 2 for the fission of titanium article titanium molecule, which is characterized in that the liquid
State gas is liquid nitrogen.
4. the surface treatment method according to claim 1 for the fission of titanium article titanium molecule, which is characterized in that described
In step (3), it is 1-4h that temperature, which is warming up to 1000-1500 DEG C of required time,.
5. the surface treatment method according to claim 1 for the fission of titanium article titanium molecule, which is characterized in that described
In step (3), it is 20-60min that temperature, which is down to 100-500 DEG C of required time from 1000-1500 DEG C,.