CN108220669A - A kind of pltine band and its manufacture craft - Google Patents
A kind of pltine band and its manufacture craft Download PDFInfo
- Publication number
- CN108220669A CN108220669A CN201810110863.2A CN201810110863A CN108220669A CN 108220669 A CN108220669 A CN 108220669A CN 201810110863 A CN201810110863 A CN 201810110863A CN 108220669 A CN108220669 A CN 108220669A
- Authority
- CN
- China
- Prior art keywords
- pltine
- band
- zinc
- manufacture craft
- melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to pltine technical fields, disclose a kind of manufacture craft of pltine band, include the raw material of following parts by weight proportioning：Zinc 10 25%, aluminium 5 10%, phosphorus 0.1 0.5%, lead 0.5 1%, tin 1 2%, copper are surplus.Include the following steps：1) by zinc in melting furnace, argon gas protection environment, fusion temperature is 420 450 DEG C, obtains zinc melt；2) melting will be carried out in raw material input vaccum sensitive stove besides zinc, obtains molten metal liquid；3) zinc melt is warming up to 650 700 DEG C, adds in the molten metal in step 2) in batches, is configured to pltine melt；4) the pltine melt in step 3) is poured into continuous casting installation for casting, pltine band line base is made.The pltine band and its manufacture craft by the way that zinc raw material is individually carried out melting, not only increase the utilization rate and Melting Quality of zinc raw material, while also simplify technological process, also ensure the outgoing of the pltine band, have a good application prospect.
Description
Technical field
The present invention relates to pltine technical field, specially a kind of pltine band and its manufacture craft.
Background technology
Using copper as the kirsite of main alloy element, it is silvery white in color, it is oxidizable.The main trade mark have ZnCu1.5,
ZnCu1.2, ZnCu1, ZnCu0.3 etc..Intensity, hardness and impact flexibility can be improved, but when reduction plasticity and casting by adding in copper
Mobility, should generally control in 1%~7% range.It is prepared by fusion method.It is mainly used to manufacture rolling and extruded product, can uses
Make the substitute of the brass such as H68, H70, alloy strip obtained may be utilized in fabricating slide fastener, laminated padlock and other haberdashery and hardware etc.,
But current preparation process is cumbersome, product quality is relatively low, for this purpose, we have proposed a kind of pltine band and its making
Technique solves the above problems.
Invention content
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of pltine band and its manufacture crafts, have flow letter
The advantages that single.
(2) technical solution
To achieve the above object, the present invention provides following technical solution：
A kind of manufacture craft of pltine band includes the raw material of following parts by weight proportioning：Zinc 10-25%, aluminium 5-
10%th, phosphorus 0.1-0.5%, lead 0.5-1%, tin 1-2%, copper are surplus.
Preferably, a kind of manufacture craft of pltine band, includes the following steps：
1) by zinc in melting furnace, argon gas protection environment, fusion temperature is 420-450 DEG C, obtains zinc melt；
2) melting will be carried out in raw material input vaccum sensitive stove besides zinc, obtains molten metal liquid；
3) zinc melt is warming up to 650-700 DEG C, adds in the molten metal in step 2) in batches, is configured to pltine and melts
Body；
4) the pltine melt in step 3) is poured into continuous casting installation for casting, pltine band line base is made；
5) online annealing is carried out after pltine band line base cooling is stretched, completes the making of pltine band.
Preferably, the fusing time in the step 3) is 1-2 hours.
Preferably, the casting temperature in the step 4) is 1300-1500 DEG C, hydraulic pressure 1-3MPa.
Preferably, the annealing temperature in the step 5) is 600-700 DEG C, and annealing time is 15-60 seconds.
A kind of pltine band, including any one manufacture craft.
(3) advantageous effect
Compared with prior art, the present invention provides a kind of pltine band and its manufacture crafts, have following beneficial to effect
Fruit：
The pltine band and its manufacture craft by the way that zinc raw material is individually carried out melting, not only increase zinc raw material
Utilization rate and Melting Quality, while technological process is also simplified, it also ensures the outgoing of the pltine band, has
Good application prospect.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained without making creative work
Example, shall fall within the protection scope of the present invention.
Embodiment one：
A kind of manufacture craft of pltine band includes the raw material of following parts by weight proportioning：Zinc 10-25%, aluminium 5-
10%th, phosphorus 0.1-0.5%, lead 0.5-1%, tin 1-2%, copper are surplus.
A kind of manufacture craft of pltine band, includes the following steps：
1) by zinc in melting furnace, argon gas protection environment, fusion temperature is 420-450 DEG C, obtains zinc melt；
2) melting will be carried out in raw material input vaccum sensitive stove besides zinc, obtains molten metal liquid；
3) zinc melt is warming up to 650-700 DEG C, adds in the molten metal in step 2) in batches, fusing time is small for 1-2
When, it is configured to pltine melt；
4) the pltine melt in step 3) is poured into continuous casting installation for casting, casting temperature is 1300-1500 DEG C, and hydraulic pressure is
Pltine band line base is made in 1-3MPa；
5) online annealing is carried out after pltine band line base cooling is stretched, annealing temperature is 600-700 DEG C, annealing time
It is 15-60 seconds, completes the making of pltine band.
A kind of pltine band, the manufacture craft including any of the above-described.
Embodiment two：
A kind of manufacture craft of pltine band includes the raw material of following parts by weight proportioning：Zinc 10-25%, aluminium 5-
10%th, phosphorus 0.1-0.5%, lead 0.5-1%, tin 1-2%, copper are surplus.
A kind of manufacture craft of pltine band, includes the following steps：
1) by zinc in melting furnace, argon gas protection environment, fusion temperature is 420-450 DEG C, obtains zinc melt；
2) melting will be carried out in raw material input vaccum sensitive stove besides zinc, obtains molten metal liquid；
3) zinc melt is warming up to 650-680 DEG C, adds in the molten metal in step 2) in batches, fusing time is small for 1-2
When, it is configured to pltine melt；
4) the pltine melt in step 3) is poured into continuous casting installation for casting, casting temperature is 1300-1500 DEG C, and hydraulic pressure is
Pltine band line base is made in 1-3MPa；
5) online annealing is carried out after pltine band line base cooling is stretched, annealing temperature is 600-650 DEG C, annealing time
It is 15-60 seconds, completes the making of pltine band.
A kind of pltine band, the manufacture craft including any of the above-described.
The beneficial effects of the invention are as follows：The pltine band and its manufacture craft, by the way that zinc raw material is individually carried out melting,
The utilization rate and Melting Quality of zinc raw material are not only increased, while also simplifies technological process, also ensures that the zinc-copper closes
The outgoing of gold ribbon, has a good application prospect.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of manufacture craft of pltine band, which is characterized in that include the raw material of following parts by weight proportioning：Zinc 10-
25%th, aluminium 5-10%, phosphorus 0.1-0.5%, lead 0.5-1%, tin 1-2%, copper are surplus.
2. the manufacture craft of a kind of pltine band according to claim 1, which is characterized in that include the following steps：
1) by zinc in melting furnace, argon gas protection environment, fusion temperature is 420-450 DEG C, obtains zinc melt；
2) melting will be carried out in raw material input vaccum sensitive stove besides zinc, obtains molten metal liquid；
3) zinc melt is warming up to 650-700 DEG C, adds in the molten metal in step 2) in batches, is configured to pltine melt；
4) the pltine melt in step 3) is poured into continuous casting installation for casting, pltine band line base is made；
5) online annealing is carried out after pltine band line base cooling is stretched, completes the making of pltine band.
3. the manufacture craft of a kind of pltine band according to claim 1, which is characterized in that molten in the step 3)
It is 1-2 hours to change the time.
A kind of 4. manufacture craft of pltine band according to claim 1, which is characterized in that the company in the step 4)
It is 1300-1500 DEG C to cast temperature, hydraulic pressure 1-3MPa.
A kind of 5. manufacture craft of pltine band according to claim 1, which is characterized in that moving back in the step 5)
Fiery temperature is 600-700 DEG C, and annealing time is 15-60 seconds.
6. a kind of pltine band, which is characterized in that including manufacture craft described in any one of claim 1 to 5.