CN108219548A - A kind of antiultraviolet mobile phone tempered glass film - Google Patents
A kind of antiultraviolet mobile phone tempered glass film Download PDFInfo
- Publication number
- CN108219548A CN108219548A CN201711396492.0A CN201711396492A CN108219548A CN 108219548 A CN108219548 A CN 108219548A CN 201711396492 A CN201711396492 A CN 201711396492A CN 108219548 A CN108219548 A CN 108219548A
- Authority
- CN
- China
- Prior art keywords
- parts
- antiultraviolet
- mobile phone
- tempered glass
- glass film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of antiultraviolet mobile phone tempered glass film, tempered glass film includes glass-base and applies the ultraviolet-proof being covered on glass-base, and ultraviolet-proof is made of following raw material:Base polyurethane prepolymer for use as;2,4 dihydroxy benaophenonels;Octrizole;Salicylic acid isooctyl ester;Dimethicone;Octadecyl acrylate;Vinyl chloroacetate;Anhydrous Aluminum chloride;2,4,7,9 tetramethyl, 5 decine, 4,7 glycol;N-nonyl alcohol;Nano-calcium carbonate.The present invention is coated with ultraviolet-proof in glass basal plane, can absorb ultraviolet light in the sun so that the content that mobile phone screen is shown is more bright, convenient for checking.
Description
Technical field
A kind of antiultraviolet mobile phone tempered glass film of the present invention.
Background technology
Mobile phone tempered glass film is that original screen cover is completely covered, and prevents from being damaged by external force, scratches, more increases
Impact absorbency, and does not interfere with the video effect of screen by higher than the standard of PET film 5 times.
Invention content
The present invention provides a kind of antiultraviolet mobile phone tempered glass film, and ultraviolet-proof is coated on its surface, can be with
Ultraviolet light is absorbed in the sun so that the content that mobile phone screen is shown is more bright, convenient for checking.
A kind of antiultraviolet mobile phone tempered glass film, the tempered glass film includes glass-base and painting is covered in glass
Ultraviolet-proof in base, the ultraviolet-proof are made of following raw material:
Base polyurethane prepolymer for use as:60-70 parts;
2-5 parts of 2,4 dihydroxyl benzophenone;
1-3 parts of Octrizole;
0.6-1.5 parts of salicylic acid isooctyl ester;
Dimethicone 4-9;
1-2 parts of octadecyl acrylate;
0.6-0.9 parts of vinyl chloroacetate;
0.1-0.4 parts of anhydrous Aluminum chloride;
1-2 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
1-3 parts of n-nonyl alcohol;
0.6-0.9 parts of nano-calcium carbonate.
Further, the ultraviolet-proof is made of following raw material:
Base polyurethane prepolymer for use as:66 parts;
3 parts of 2,4 dihydroxyl benzophenone;
1.8 parts of Octrizole;
0.8 part of salicylic acid isooctyl ester;
6 parts of dimethicone;
1.2 parts of octadecyl acrylate;
0.72 part of vinyl chloroacetate;
0.3 part of anhydrous Aluminum chloride;
1.6 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
2.2 parts of n-nonyl alcohol;
0.8 part of nano-calcium carbonate.
Further, the ultraviolet-proof is made of following raw material:
Base polyurethane prepolymer for use as:63 parts;
4 parts of 2,4 dihydroxyl benzophenone;
1.6 parts of Octrizole;
0.7 part of salicylic acid isooctyl ester;
8 parts of dimethicone;
1.5 parts of octadecyl acrylate;
0.63 part of vinyl chloroacetate;
0.23 part of anhydrous Aluminum chloride;
1.7 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
2.1 parts of n-nonyl alcohol;
0.9 part of nano-calcium carbonate.
Further, the ultraviolet-proof is made of following raw material:
Base polyurethane prepolymer for use as:69 parts;
4 parts of 2,4 dihydroxyl benzophenone;
3 parts of Octrizole;
1.4 parts of salicylic acid isooctyl ester;
9 parts of dimethicone;
1.3 parts of octadecyl acrylate;
0.84 part of vinyl chloroacetate;
0.23 part of anhydrous Aluminum chloride;
1.4 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
2.1 parts of n-nonyl alcohol;
0.65 part of nano-calcium carbonate.
The present invention is coated with ultraviolet-proof in glass basal plane, can absorb ultraviolet light in the sun so that Mobile phone screen
The content of curtain display is more bright, convenient for checking.
Specific embodiment
Embodiment 1
A kind of antiultraviolet mobile phone tempered glass film, the tempered glass film includes glass-base and painting is covered in glass-base
On ultraviolet-proof, the ultraviolet-proof is made of following raw material:
Base polyurethane prepolymer for use as:66 parts;
3 parts of 2,4 dihydroxyl benzophenone;
1.8 parts of Octrizole;
0.8 part of salicylic acid isooctyl ester;
6 parts of dimethicone;
1.2 parts of octadecyl acrylate;
0.72 part of vinyl chloroacetate;
0.3 part of anhydrous Aluminum chloride;
1.6 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
2.2 parts of n-nonyl alcohol;
0.8 part of nano-calcium carbonate.
Embodiment 2
A kind of antiultraviolet mobile phone tempered glass film, the tempered glass film includes glass-base and painting is covered in glass-base
On ultraviolet-proof, the ultraviolet-proof is made of following raw material:
Base polyurethane prepolymer for use as:63 parts;
4 parts of 2,4 dihydroxyl benzophenone;
1.6 parts of Octrizole;
0.7 part of salicylic acid isooctyl ester;
8 parts of dimethicone;
1.5 parts of octadecyl acrylate;
0.63 part of vinyl chloroacetate;
0.23 part of anhydrous Aluminum chloride;
1.7 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
2.1 parts of n-nonyl alcohol;
0.9 part of nano-calcium carbonate.
Embodiment 3
A kind of antiultraviolet mobile phone tempered glass film, the tempered glass film includes glass-base and painting is covered in glass-base
On ultraviolet-proof, the ultraviolet-proof is made of following raw material:
Base polyurethane prepolymer for use as:69 parts;
4 parts of 2,4 dihydroxyl benzophenone;
3 parts of Octrizole;
1.4 parts of salicylic acid isooctyl ester;
9 parts of dimethicone;
1.3 parts of octadecyl acrylate;
0.84 part of vinyl chloroacetate;
0.23 part of anhydrous Aluminum chloride;
1.4 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
2.1 parts of n-nonyl alcohol;
0.65 part of nano-calcium carbonate.
It is dehydrated after base polyurethane prepolymer for use as being heated to 130 DEG C in embodiment 3, is cooled to 65 DEG C of addition clouts, then
1 hour is stirred to get coating of the present invention.
The above described is only a preferred embodiment of the present invention, being not that the invention has other forms of limitations, appoint
What those skilled in the art changed or be modified as possibly also with the technology contents of the disclosure above equivalent variations etc.
Imitate embodiment.But it is every without departing from technical solution of the present invention content, technical spirit according to the present invention is to above example institute
Any simple modification, equivalent variations and the remodeling made still fall within the protection domain of technical solution of the present invention.
Claims (4)
1. a kind of antiultraviolet mobile phone tempered glass film, the tempered glass film includes glass-base and painting is covered in glass base
Ultraviolet-proof on layer, which is characterized in that the ultraviolet-proof is made of following raw material:
Base polyurethane prepolymer for use as:60-70 parts;
2-5 parts of 2,4 dihydroxyl benzophenone;
1-3 parts of Octrizole;
0.6-1.5 parts of salicylic acid isooctyl ester;
Dimethicone 4-9;
1-2 parts of octadecyl acrylate;
0.6-0.9 parts of vinyl chloroacetate;
0.1-0.4 parts of anhydrous Aluminum chloride;
1-2 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
1-3 parts of n-nonyl alcohol;
0.6-0.9 parts of nano-calcium carbonate.
A kind of 2. antiultraviolet mobile phone tempered glass film according to claim 1, which is characterized in that the antiultraviolet
Coating is made of following raw material:
Base polyurethane prepolymer for use as:66 parts;
3 parts of 2,4 dihydroxyl benzophenone;
1.8 parts of Octrizole;
0.8 part of salicylic acid isooctyl ester;
6 parts of dimethicone;
1.2 parts of octadecyl acrylate;
0.72 part of vinyl chloroacetate;
0.3 part of anhydrous Aluminum chloride;
1.6 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
2.2 parts of n-nonyl alcohol;
0.8 part of nano-calcium carbonate.
A kind of 3. antiultraviolet mobile phone tempered glass film according to claim 1, which is characterized in that the antiultraviolet
Coating is made of following raw material:
Base polyurethane prepolymer for use as:63 parts;
4 parts of 2,4 dihydroxyl benzophenone;
1.6 parts of Octrizole;
0.7 part of salicylic acid isooctyl ester;
8 parts of dimethicone;
1.5 parts of octadecyl acrylate;
0.63 part of vinyl chloroacetate;
0.23 part of anhydrous Aluminum chloride;
1.7 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
2.1 parts of n-nonyl alcohol;
0.9 part of nano-calcium carbonate.
A kind of 4. antiultraviolet mobile phone tempered glass film according to claim 1, which is characterized in that the antiultraviolet
Coating is made of following raw material:
Base polyurethane prepolymer for use as:69 parts;
4 parts of 2,4 dihydroxyl benzophenone;
3 parts of Octrizole;
1.4 parts of salicylic acid isooctyl ester;
9 parts of dimethicone;
1.3 parts of octadecyl acrylate;
0.84 part of vinyl chloroacetate;
0.23 part of anhydrous Aluminum chloride;
1.4 parts of 2,4,7,9- tetramethyl -5- decine -4,7- glycol;
2.1 parts of n-nonyl alcohol;
0.65 part of nano-calcium carbonate.