CN108219219A - A kind of mildewproof rubber and preparation method thereof - Google Patents
A kind of mildewproof rubber and preparation method thereof Download PDFInfo
- Publication number
- CN108219219A CN108219219A CN201810054370.1A CN201810054370A CN108219219A CN 108219219 A CN108219219 A CN 108219219A CN 201810054370 A CN201810054370 A CN 201810054370A CN 108219219 A CN108219219 A CN 108219219A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- rubber
- preparation
- biotite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of mildewproof rubbers, are prepared using the following raw material：50 75 parts by weight of natural rubber, 15 25 parts by weight of silicone rubber, 28 parts by weight of titanium dioxide, 14 parts by weight odium stearate, 5 15 parts by weight precipitated calcium carbonates, 36 parts by weight diatomite, 13 parts by weight propylene amides, 13 parts by weight biotite, 12 parts by weight anti-aging agents.Using natural rubber, silicon rubber, titanium dioxide, odium stearate, precipitated calcium carbonate, diatomite, acrylamide, biotite, anti-aging agent as raw material, each ingredient influences each other, interacts the present invention, improves antibacterial, the fungicidal properties of the rubber of preparation.
Description
Technical field
The present invention relates to technical field of rubber material, and in particular to a kind of mildewproof rubber and preparation method thereof.
Background technology
Rubber is the important component of chemical industry, tire, sebific duct, adhesive tape, rubber roller, rubber seal, spread goods
Rubbers is waited to be widely used in the national economy such as automobile production, aircraft manufacturing, Crude Oil Transportation, telecommunications, hospital
Industry-by-industry, it has also become one of important basic industry.In the prior art, rubber and preparation method thereof has been obtained for widely
Report, but rubber mildew resistance is poor mostly.
Invention content
For above-mentioned, the object of the present invention is to provide a kind of mildewproof rubber and preparation method thereof, with good antibacterial, anti-
Mouldiness.
In view of this, it the present invention provides a kind of mildewproof rubber, is prepared using the following raw material：The natural rubber of 50-75 parts by weight
Glue, 15-25 parts by weight of silicone rubber, 2-8 parts by weight of titanium dioxide, 1-4 parts by weight odium stearate, 5-15 parts by weight lightweight carbonic acid
Calcium, 3-6 parts by weight diatomite, 1-3 parts by weight propylene amide, 1-3 parts by weight biotite, 1-2 parts by weight anti-aging agents.
Correspondingly, the present invention also provides a kind of preparation method of mildewproof rubber, include the following steps：By 50-75 weight
Part natural rubber, 15-25 parts by weight of silicone rubber, 2-8 parts by weight of titanium dioxide, 1-4 parts by weight odium stearate, 5-15 parts by weight are light
Matter calcium carbonate, 3-6 parts by weight diatomite, 1-3 parts by weight propylene amide, the mixing of 1-3 parts by weight biotite stir evenly, and are kneaded 120-
Then 150min adds in 1-2 parts by weight anti-aging agent and is kneaded 10-20min to get mildewproof rubber.
Preferably, the natural rubber is 55-70 parts by weight.
Preferably, the silicon rubber is 18-22 parts by weight.
Preferably, the titanium dioxide is 4-6 parts by weight.
Preferably, the odium stearate is 2-3 parts by weight.
Preferably, the precipitated calcium carbonate is 8-12 parts by weight.
Preferably, diatomite is 4-5 parts by weight.
Preferably, the acrylamide is 1.5-2.5 parts by weight.
Preferably, the biotite is 1.5-2.5 parts by weight.
It is an advantage of the invention that：The present invention with natural rubber, silicon rubber, titanium dioxide, odium stearate, precipitated calcium carbonate,
Diatomite, acrylamide, biotite, anti-aging agent are raw material, and each ingredient influences each other, interacts, and improves the rubber of preparation
The antibacterial of glue, fungicidal properties.
Specific embodiment
For a further understanding of the present invention, the preferred embodiment of the invention is described with reference to embodiment, still
It should be appreciated that these descriptions are only for the feature and advantage that further illustrate the present invention rather than to the claims in the present invention
Limitation.
The embodiment of the invention discloses a kind of mildewproof rubbers, are prepared using the following raw material：50-75 parts by weight of natural rubber,
15-25 parts by weight of silicone rubber, 2-8 parts by weight of titanium dioxide, 1-4 parts by weight odium stearate, 5-15 parts by weight precipitated calcium carbonate, 3-
6 parts by weight diatomite, 1-3 parts by weight propylene amide, 1-3 parts by weight biotite, 1-2 parts by weight anti-aging agents.
Correspondingly, the embodiment of the present invention additionally provides a kind of preparation method of mildewproof rubber, includes the following steps：By 50-
75 parts by weight of natural rubber, 15-25 parts by weight of silicone rubber, 2-8 parts by weight of titanium dioxide, 1-4 parts by weight odium stearate, 5-15 weights
Amount part precipitated calcium carbonate, 3-6 parts by weight diatomite, 1-3 parts by weight propylene amide, the mixing of 1-3 parts by weight biotite stir evenly, and are kneaded
Then 120-150min adds in 1-2 parts by weight anti-aging agent and is kneaded 10-20min to get mildewproof rubber.
From above scheme as can be seen that the present invention is with natural rubber, silicon rubber, titanium dioxide, odium stearate, lightweight carbonic acid
Calcium, diatomite, acrylamide, biotite, anti-aging agent are raw material, and each ingredient influences each other, interacts, and improves preparation
The antibacterial of rubber, fungicidal properties.
Embodiment 1
A kind of preparation method of mildewproof rubber, includes the following steps：By 50 parts by weight of natural rubber, 15 parts by weight silicon rubbers
Glue, 2 parts by weight of titanium dioxide, 1 parts by weight odium stearate, 5 parts by weight precipitated calcium carbonates, 3 parts by weight diatomite, 1 parts by weight third
Acrylamide, the mixing of 1 parts by weight biotite stir evenly, and are kneaded 120min, then add in 1 parts by weight anti-aging agent and are kneaded 10min to get anti-
Mould rubber.
Embodiment 2
A kind of preparation method of mildewproof rubber, includes the following steps：By 55 parts by weight of natural rubber, 18 parts by weight silicon rubbers
Glue, 4 parts by weight of titanium dioxide, 2 parts by weight odium stearate, 8 parts by weight precipitated calcium carbonates, 4 parts by weight diatomite, 1.5 parts by weight
Acrylamide, the mixing of 1.5 parts by weight biotite stir evenly, and are kneaded 120min, then add in 1 parts by weight anti-aging agent and are kneaded 10min, i.e.,
Obtain mildewproof rubber.
Embodiment 3
A kind of preparation method of mildewproof rubber, includes the following steps：By 62.5 parts by weight of natural rubber, 20 parts by weight silicon rubbers
Glue, 5 parts by weight of titanium dioxide, 2.5 parts by weight odium stearate, 10 parts by weight precipitated calcium carbonates, 4.5 parts by weight diatomite, 2 weight
Part acrylamide, the mixing of 2 parts by weight biotite stir evenly, and are kneaded 135min, then add in 1.5 parts by weight anti-aging agents and are kneaded 15min,
Up to mildewproof rubber.
Embodiment 4
A kind of preparation method of mildewproof rubber, includes the following steps：By 70 parts by weight of natural rubber, 22 parts by weight silicon rubbers
Glue, 6 parts by weight of titanium dioxide, 3 parts by weight odium stearate, 12 parts by weight precipitated calcium carbonates, 5 parts by weight diatomite, 2.5 parts by weight
Acrylamide, the mixing of 2.5 parts by weight biotite stir evenly, and are kneaded 140min, then add in 2 parts by weight anti-aging agents and are kneaded 20min, i.e.,
Obtain mildewproof rubber.
Embodiment 5
A kind of preparation method of mildewproof rubber, includes the following steps：By 75 parts by weight of natural rubber, 25 parts by weight silicon rubbers
Glue, 8 parts by weight of titanium dioxide, 4 parts by weight odium stearate, 15 parts by weight precipitated calcium carbonates, 6 parts by weight diatomite, 3 parts by weight third
Acrylamide, the mixing of 3 parts by weight biotite stir evenly, and are kneaded 150min, then add in 2 parts by weight anti-aging agents and are kneaded 20min to get anti-
Mould rubber.
Claims (10)
1. a kind of mildewproof rubber, it is characterised in that prepared using the following raw material：50-75 parts by weight of natural rubber, 15-25 parts by weight
Silicon rubber, 2-8 parts by weight of titanium dioxide, 1-4 parts by weight odium stearate, 5-15 parts by weight precipitated calcium carbonate, 3-6 parts by weight diatoms
Soil, 1-3 parts by weight propylene amide, 1-3 parts by weight biotite, 1-2 parts by weight anti-aging agents.
2. a kind of preparation method of mildewproof rubber, it is characterised in that include the following steps：By 50-75 parts by weight of natural rubber, 15-
25 parts by weight of silicone rubber, 2-8 parts by weight of titanium dioxide, 1-4 parts by weight odium stearate, 5-15 parts by weight precipitated calcium carbonate, 3-6 weights
Amount part diatomite, 1-3 parts by weight propylene amide, the mixing of 1-3 parts by weight biotite stir evenly, and are kneaded 120-150min, then add in
1-2 parts by weight anti-aging agent is kneaded 10-20min to get mildewproof rubber.
3. preparation method according to claim 2, it is characterised in that the natural rubber is 55-70 parts by weight.
4. preparation method according to claim 2, it is characterised in that the silicon rubber is 18-22 parts by weight.
5. preparation method according to claim 2, it is characterised in that the titanium dioxide is 4-6 parts by weight.
6. preparation method according to claim 2, it is characterised in that the odium stearate is 2-3 parts by weight.
7. preparation method according to claim 2, it is characterised in that the precipitated calcium carbonate is 8-12 parts by weight.
8. preparation method according to claim 2, it is characterised in that diatomite is 4-5 parts by weight.
9. preparation method according to claim 2, it is characterised in that the acrylamide is 1.5-2.5 parts by weight.
10. preparation method according to claim 2, it is characterised in that the biotite is 1.5-2.5 parts by weight.