CN108215426A - A kind of production line and its production technology of fire resistant epoxy glass cloth laminated board - Google Patents
A kind of production line and its production technology of fire resistant epoxy glass cloth laminated board Download PDFInfo
- Publication number
- CN108215426A CN108215426A CN201711456420.0A CN201711456420A CN108215426A CN 108215426 A CN108215426 A CN 108215426A CN 201711456420 A CN201711456420 A CN 201711456420A CN 108215426 A CN108215426 A CN 108215426A
- Authority
- CN
- China
- Prior art keywords
- glass cloth
- tank
- cloth prepreg
- laminated board
- prepreg
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of production lines of fire resistant epoxy glass cloth laminated board, it is characterized by comprising the glass cloth feeding devices of arranged in series, gumming device, glass cloth prepreg drying device, glass cloth prepreg blanking device, glass cloth prepreg laminater, cutting means and final finishing device, the side of the gumming device is provided with glue configuration reaction kettle, the side oblique upper of the glue configuration reaction kettle is disposed with bisphenol A type epoxy resin tank, Study On O-cresol Epoxy Resin tank, diamino diphenyl sulfone tank, linear phenolic resin tank, methylimidazole tank, dimethylformamide tank and hydroxide aluminium pot.The production line of the fire resistant epoxy glass cloth laminated board of the present invention has the advantages of production efficiency is high, good product quality.
Description
Technical field
The invention belongs to epoxy glass cloth laminated board correlative technology fields, and in particular to a kind of fire resistant epoxy glass fabric layer
The production line and its production technology of pressing plate.
Background technology
It by chemically treated electrician with alkali-free glass fiber cloth is base material that epoxy glass cloth laminated board, which is, with epoxy resin
As the laminated product that adhesive is formed through hot pressing, high mechanical strength under high temperature, electric property stability is good under high humidity, epoxy glass
Glass cloth laminated board abbreviation epoxy plate, definition and purposes, epoxy glass cloth laminated board are by chemically treated electrician alkali-free glass
Glass fiber cloth is base material, the laminated product formed using epoxy resin as adhesive through hot pressing, high mechanical strength under high temperature, high humidity
Lower electric property stability is good.Suitable for fields such as machinery, electrical and electronics, laminate surface is smooth, bubble-free, pockmark and wrinkle
Line allows to have the other defect for not influencing to use, such as：Scratch, impression, stain and a small amount of spot.Edge should be cut neatly, end
Face must not have layering and crackle.
Existing epoxy glass cloth laminated board technology has the following problems：Present epoxy glass cloth laminated board is in installation
When, hole is all fixed size, does not adapt to the installation under different situations thus, so as to epoxy glass cloth laminated board
Installation brings big inconvenience.
Invention content
It is above-mentioned to solve the purpose of the present invention is to provide a kind of production line of fire resistant epoxy glass cloth laminated board
Itd is proposed in background technology the size in hole it is immutable bring installation it is inconvenient the problem of.
To achieve the above object, the present invention provides following technical solution：
A kind of production line of fire resistant epoxy glass cloth laminated board, for producing a kind of fire resistant epoxy glass fabric layer
Pressing plate, the fire resistant epoxy glass cloth laminated board include adjustable mounting hole, and it is solid that the interstitial hole is mounted on compound glass cloth half
Change the center position of piece, the inside of the compound glass cloth prepreg and be provided with adjustable installation at the corner location
Hole, protection connector is provided at the quadrangle outer fix of the compound glass cloth prepreg, and the compound glass cloth half is solid
Change on the outside of four sides of piece and be provided with protection frame between two protection connectors.
The production line of the fire resistant epoxy glass cloth laminated board includes glass cloth feeding device, gumming device, glass
Glass cloth prepreg drying device, glass cloth prepreg blanking device, glass cloth prepreg laminater, cutting means with
And final finishing device, the glass cloth feeding device, gumming device, glass cloth prepreg drying device, glass cloth semi-solid preparation
Slice baiting apparatus, glass cloth prepreg laminater, cutting means and final finishing device arranged in series, the gumming device
Side be provided with glue configuration reaction kettle, the side oblique upper of glue configuration reaction kettle is disposed with bisphenol-A type ring
Oxygen resin container, Study On O-cresol Epoxy Resin tank, diamino diphenyl sulfone tank, linear phenolic resin tank, methylimidazole tank, two
Methylformamide tank and hydroxide aluminium pot；Bisphenol A type epoxy resin tank, Study On O-cresol Epoxy Resin tank, diamino hexichol
Base sulfone tank, linear phenolic resin tank, methylimidazole tank, dimethylformamide tank and hydroxide aluminium pot discharge port lead to respectively
Cross the feed inlet of a pipeline connection glue configuration reaction kettle, the charging of the discharge port connection gumming device of glue configuration reaction kettle
Mouthful；Final finishing device is for opening up adjustable mounting hole, connector is protected in installation and installation protection frame.
Preferably, the compound glass cloth prepreg includes third layer glass cloth prepreg, lower extruded layer, the second layer
Glass cloth prepreg, upper extruded layer and first layer glass cloth prepreg, the first layer glass cloth prepreg are mounted on
The lower end of upper extruded layer, the lower end of the upper extruded layer are provided with second layer glass cloth prepreg, the second layer glass cloth
The lower end of prepreg is provided with lower extruded layer, and the lower end of the lower extruded layer is provided with third layer glass cloth prepreg, institute
State third layer glass cloth prepreg, lower extruded layer, second layer glass cloth prepreg, upper extruded layer and first layer glass cloth half
Cured sheets are laminated.
Preferably, the adjustable mounting hole includes intermediate seam, endoporus, upper baffle ring, outer shroud and lower baffle ring, the endoporus installation
In the center position of outer shroud, the upper end of the outer shroud is provided with baffle ring, lower baffle ring is provided with below the outer shroud, described
The centre of upper baffle ring, outer shroud and lower baffle ring is provided with intermediate seam.
Preferably, the protection frame includes framework, link slot and card slot, the inside of the framework and is set positioned at positive front end
Card slot is equipped with, link slot is provided at left and right sides of the framework.
Preferably, it is described protection connector include upper connection bump, lower connection bump and connector, the connector it is upper
End is provided with connection bump, and the lower right of the connector is provided with lower connection bump.
The configuration technique of glue configuration reaction kettle is as follows：
70 parts of bisphenol A type epoxy resin, 30 parts of Study On O-cresol Epoxy Resin, diamino diphenyl sulfone 20 are provided first
Then part, 20 parts of linear phenolic resin, 0.1 part of methylimidazole, 30 parts of dimethylformamide, 20 parts of aluminium hydroxide are reacting
Dimethylformamide is added in kettle and adds diamino diphenyl sulfone and methylimidazole normal-temperature dissolution 30 minutes, adds bis-phenol
A types epoxy resin, Study On O-cresol Epoxy Resin and linear phenolic resin fully dissolve 4 hours, and it is molten to be eventually adding aluminium hydroxide
Solution 60 minutes, such high-temperature-resistant epoxy resin glue, which can be configured, to be completed.
Compared with prior art, the beneficial effects of the invention are as follows：
1st, the present invention is mounted with adjustable mounting hole on epoxy glass cloth laminated board, and adjustable mounting hole is to be stitched by centre, is interior
What hole, upper baffle ring, outer shroud and lower baffle ring formed, adjustable mounting hole is placed at epoxy glass cloth laminated board corner location and is shifted to an earlier date
Inside the hole opened, and the hole opened in advance is bigger than normal, in this way when epoxy glass cloth laminated board is installed, it is possible to use
Adjustable mounting hole is installed, in this way when installing pillar either nut is bigger than normal or less than normal, it is possible to baffle ring in movement,
The intermediate size stitched of outer shroud and lower baffle ring, it is possible to the size of endoporus is adjusted, so as to adjust the size of adjustable mounting hole,
Installation can adapt to different size of installation pillar or nut in this way, so that the peace of epoxy glass cloth laminated board
Dress is more diversified.
2nd, the present invention is mounted with protection frame and protection connector on epoxy glass cloth laminated board, and protection frame is by frame
Body, link slot and card slot composition, protection connector be by upper connection bump, lower connection bump and connector, thus can be with
Protection frame is placed at four side positions of epoxy glass cloth laminated board, the card slot inside protection frame is stuck in epoxy glass fabric
Then upper connection bump on protection connector and lower connection bump are inserted respectively into protection frame both ends by four sides of laminate
Inside the link slot of the inside, so that protection frame is mounted on four sides of epoxy glass cloth laminated board, such protection frame and anti-
Shield connector can protect epoxy glass cloth laminated board, it is therefore prevented that other sundries hit epoxy glass cloth laminated board pair
Epoxy glass cloth laminated board damages, and improves the performance of epoxy glass cloth laminated board.
3rd, the production line of fire resistant epoxy glass cloth laminated board of the invention has production efficiency height, good product quality
The advantages of.
Description of the drawings
Fig. 1 is the structure diagram of the fire resistant epoxy glass cloth laminated board of the present invention；
Fig. 2 is the compound glass cloth prepreg structure diagram of the present invention；
Fig. 3 is the adjustable structure of mounting hole schematic diagram of the present invention；
Fig. 4 is the protection frame structure diagram of the present invention；
Fig. 5 is the protection connector structure diagram of the present invention；
Fig. 6 is the floor plan of the production line of the fire resistant epoxy glass cloth laminated board of the present invention.
In figure：1st, adjustable mounting hole；11st, intermediate seam；12nd, endoporus；13rd, upper baffle ring；14th, outer shroud；15th, lower baffle ring；2nd, in
Between hole；3rd, compound glass cloth prepreg；31st, third layer glass cloth prepreg；32nd, lower extruded layer；33rd, second layer glass cloth
Prepreg；34th, upper extruded layer；35th, first layer glass cloth prepreg；4th, protection frame；41st, framework；42nd, link slot；43、
Card slot；5th, connector is protected；51st, upper connection bump；52nd, lower connection bump；53rd, connector.
Specific embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment shall fall within the protection scope of the present invention.
- 6 are please referred to Fig.1, the present invention provides a kind of technical solution：A kind of fire resistant epoxy glass cloth laminated board, including can
Mounting hole 1 is adjusted, interstitial hole 2 is mounted on the center position of compound glass cloth prepreg 3, compound glass cloth prepreg 3
It is internal and adjustable mounting hole 1 is provided at corner location, it is set at the quadrangle outer fix of compound glass cloth prepreg 3
Have and protect connector 5, be provided on the outside of four sides of compound glass cloth prepreg 3 and between two protection connectors 5 anti-
Safe edge frame 4.
In order to which working performance is more preferable, in the present invention, it is preferred that compound glass cloth prepreg 3 includes third layer glass cloth
Prepreg 31, lower extruded layer 32, second layer glass cloth prepreg 33, upper extruded layer 34 and first layer glass cloth prepreg
35, first layer glass cloth prepreg 35 is mounted on the lower end of upper extruded layer 34, and the lower end of upper extruded layer 34 is provided with the second layer
Glass cloth prepreg 33, the lower end of second layer glass cloth prepreg 33 are provided with lower extruded layer 32, under lower extruded layer 32
End is provided with third layer glass cloth prepreg 31, third layer glass cloth prepreg 31, lower extruded layer 32, second layer glass cloth
Prepreg 33, upper extruded layer 34 and the lamination of 35 laminater of first layer glass cloth prepreg produce.
In order to install enhanced convenience, in the present invention, it is preferred that adjustable mounting hole 1 include intermediate seam 11, endoporus 12, on
Baffle ring 13, outer shroud 14 and lower baffle ring 15, endoporus 12 are mounted on the center position of outer shroud 14, and the upper end of outer shroud 14 is provided with gear
Circle 13, the lower section of outer shroud 14 is provided with lower baffle ring 15, and the centre of upper baffle ring 13, outer shroud 14 and lower baffle ring 15 is provided with intermediate seam
11。
In order to preferably protect, in the present invention, it is preferred that protection frame 4 includes framework 41, link slot 42 and card slot
43, the inside of framework 41 and positive front end is provided with card slot 43, the left and right sides of framework 41 is provided with link slot 42.
In order to preferably protect, in the present invention, it is preferred that protection connector 5 includes upper connection bump 51, lower connection
Protrusion 52 and connector 53, the upper end of connector 53 are provided with connection bump 51, and the lower right of connector 53 is provided with lower company
Connect protrusion 52.
The operation principle and process for using of the present invention：70 parts of bisphenol A type epoxy resin, o-cresol epoxy novolac are provided first
30 parts of resin, 20 parts of diamino diphenyl sulfone, 20 parts of linear phenolic resin, 0.1 part of methylimidazole, dimethylformamide 30
Part, then 20 parts of aluminium hydroxide adds in dimethylformamide and adds diamino diphenyl sulfone and dimethyl miaow in a kettle
Azoles normal-temperature dissolution 30 minutes, it is fully molten to add bisphenol A type epoxy resin, Study On O-cresol Epoxy Resin and linear phenolic resin
Solution 4 hours is eventually adding aluminium hydroxide and dissolves 60 minutes, and such high-temperature-resistant epoxy resin glue, which can be configured, to be completed.
Original technique：Bisphenol A type epoxy resin and the mixing gelatinization 300 seconds of 20 parts of Boron Trifluoride Ethylamine, solidification temperature 180
℃。
Present technique：Diamino diphenyl sulfone, linear phenolic resin and methylimidazole mixing gelatinization 200 seconds, curing temperature
170 DEG C of degree.
Then glass cloth is immersed in inside the high-temperature-resistant epoxy resin glue of configuration, such glass cloth prepreg can
With production complete, then third layer glass cloth prepreg 31, lower extruded layer 32, second layer glass cloth prepreg 33,
Upper extruded layer 34 and first layer glass cloth prepreg 35 are squeezed into compound glass cloth prepreg 3 by pressue device, then
Compound glass cloth prepreg 3 can be applied to normal work life and suffer, and installed on epoxy glass cloth laminated board
Adjustable mounting hole 1, adjustable mounting hole 1 are made of centre seam 11, endoporus 12, upper baffle ring 13, outer shroud 14 and lower baffle ring 15,
Adjustable mounting hole 1 is placed into inside the hole opened in advance at epoxy glass cloth laminated board corner location, and the hole opened in advance will
It is bigger than normal, in this way when epoxy glass cloth laminated board is installed, it is possible to installed using adjustable mounting hole 1, in this way when
Pillar is installed when either nut is bigger than normal or less than normal, it is possible to the centre of baffle ring 13, outer shroud 14 and lower baffle ring 15 in movement
The size of seam 11, it is possible to adjust the size of endoporus 12, so as to adjust the size of adjustable mounting hole 1, installation can in this way
To adapt to different size of installation pillar or nut, so that the installation of epoxy glass cloth laminated board is more various
Change, be even more mounted on epoxy glass cloth laminated board protection frame 4 and protection connector 5, protection frame 4 be by framework 41,
What link slot 42 and card slot 43 formed, protection connector 5 be by upper connection bump 51, lower connection bump 52 and connector 53, this
Sample can be placed on protection frame 4 at four side positions of epoxy glass cloth laminated board, and the card slot 43 of 4 the inside of protection frame is blocked
On four sides of epoxy glass cloth laminated board, then the upper connection bump 51 on protection connector 5 and lower connection bump 52 are distinguished
42 the inside of link slot inside 4 both ends of protection frame is inserted into, so as to which protection frame 4 is mounted on epoxy glass cloth laminated board
Four sides, such protection frame 4 and protection connector 5 can protect epoxy glass cloth laminated board, it is therefore prevented that other are miscellaneous
Object hits epoxy glass cloth laminated board and epoxy glass cloth laminated board is damaged, and improves the use of epoxy glass cloth laminated board
Performance.
A kind of production line of fire resistant epoxy glass cloth laminated board, it includes glass cloth feeding device 601, impregnation fills
Put 602, glass cloth prepreg drying device 603, glass cloth prepreg blanking device 604, the lamination of glass cloth prepreg
Device 605, cutting means 606 and final finishing device 607, the glass cloth feeding device 601, gumming device 602, glass cloth
Prepreg drying device 603, glass cloth prepreg laminater 605, is cut glass cloth prepreg blanking device 604
607 arranged in series of device 606 and final finishing device, the side of the gumming device 602 are provided with glue configuration reaction kettle
600, the side oblique upper of the glue configuration reaction kettle 600 is disposed with bisphenol A type epoxy resin tank 600.1, o-cresol
Novolac epoxy resin tank 600.2, diamino diphenyl sulfone tank 600.3, linear phenolic resin tank 600.3, methylimidazole tank
600.4th, dimethylformamide tank 600.5 and hydroxide aluminium pot 600.6；Bisphenol A type epoxy resin tank 600.1, o-Hydroxytoluene
Formaldehyde epoxy resin tank 600.2, diamino diphenyl sulfone tank 600.3, linear phenolic resin tank 600.3, methylimidazole tank
600.4th, the discharge port of dimethylformamide tank 600.5 and hydroxide aluminium pot 600.6 connects glue by a pipeline respectively
The feed inlet of reaction kettle 600, the feed inlet of the discharge port connection gumming device 602 of glue configuration reaction kettle 600 is configured；Final finishing
Device 607 is for opening up adjustable mounting hole 1, connector 5 is protected in installation and installation protection frame 4.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of production line of fire resistant epoxy glass cloth laminated board, it is characterised in that for producing a kind of fire resistant epoxy
Glass cloth laminated board, the fire resistant epoxy glass cloth laminated board include adjustable mounting hole (1), it is characterised in that：The centre
Hole (2) is mounted on the center position of compound glass cloth prepreg (3), the inside of the compound glass cloth prepreg (3)
And adjustable mounting hole (1) is provided at corner location, at the quadrangle outer fix of the compound glass cloth prepreg (3)
It is provided with and protects connector (5), on the outside of four sides of the compound glass cloth prepreg (3) and positioned at two protection connectors
(5) protection frame (4) is provided between；
The production line of the fire resistant epoxy glass cloth laminated board includes glass cloth feeding device, gumming device, glass cloth
Prepreg drying device, glass cloth prepreg blanking device, glass cloth prepreg laminater, cutting means and after
Collating unit, under the glass cloth feeding device, gumming device, glass cloth prepreg drying device, glass cloth prepreg
Material device, glass cloth prepreg laminater, cutting means and final finishing device arranged in series, the one of the gumming device
Side is provided with glue configuration reaction kettle, and the side oblique upper of the glue configuration reaction kettle is disposed with bisphenol type epoxy tree
Fat tank, Study On O-cresol Epoxy Resin tank, diamino diphenyl sulfone tank, linear phenolic resin tank, methylimidazole tank, dimethyl
Formamide tank and hydroxide aluminium pot；Bisphenol A type epoxy resin tank, Study On O-cresol Epoxy Resin tank, diamino diphenyl sulfone
Tank, linear phenolic resin tank, methylimidazole tank, dimethylformamide tank and hydroxide aluminium pot discharge port pass through one respectively
The feed inlet of root pipeline connection glue configuration reaction kettle, the feed inlet of the discharge port connection gumming device of glue configuration reaction kettle；
Final finishing device is for opening up adjustable mounting hole, connector is protected in installation and installation protection frame.
2. a kind of production line of fire resistant epoxy glass cloth laminated board according to claim 1, it is characterised in that：Institute
It states compound glass cloth prepreg (3) and includes third layer glass cloth prepreg (31), lower extruded layer (32), second layer glass cloth
Prepreg (33), upper extruded layer (34) and first layer glass cloth prepreg (35), the first layer glass cloth prepreg
(35) mounted on the lower end of upper extruded layer (34), the lower end of the upper extruded layer (34) is provided with second layer glass cloth prepreg
(33), the lower end of the second layer glass cloth prepreg (33) is provided with lower extruded layer (32), the lower extruded layer (32)
Lower end is provided with third layer glass cloth prepreg (31), the third layer glass cloth prepreg (31), lower extruded layer (32),
Second layer glass cloth prepreg (33), upper extruded layer (34) and first layer glass cloth prepreg (35) are laminated.
3. a kind of production line of fire resistant epoxy glass cloth laminated board according to claim 1, it is characterised in that：Institute
It states adjustable mounting hole (1) and includes centre seam (11), endoporus (12), upper baffle ring (13), outer shroud (14) and lower baffle ring (15), it is described interior
Mounted on the center position of outer shroud (14), the upper end of the outer shroud (14) is provided with baffle ring (13), the outer shroud in hole (12)
(14) lower baffle ring (15) is provided with below, during the centre of the upper baffle ring (13), outer shroud (14) and lower baffle ring (15) is provided with
Between stitch (11).
4. a kind of production line of fire resistant epoxy glass cloth laminated board according to claim 1, it is characterised in that：Institute
It states protection frame (4) and includes framework (41), link slot (42) and card slot (43), the inside of the framework (41) and positioned at positive front end
Card slot (43) is provided with, link slot (42) is provided at left and right sides of the framework (41).
5. a kind of production line of fire resistant epoxy glass cloth laminated board according to claim 1, it is characterised in that：Institute
It states protection connector (5) and includes upper connection bump (51), lower connection bump (52) and connector (53), the connector (53)
Upper end is provided with connection bump (51), and the lower right of the connector (53) is provided with lower connection bump (52).
A kind of 6. production line of fire resistant epoxy glass cloth laminated board according to claim 1, it is characterised in that glue
The configuration technique of water configuration reaction kettle is as follows：
70 parts of bisphenol A type epoxy resin, 30 parts of Study On O-cresol Epoxy Resin, 20 parts of diamino diphenyl sulfone, line are provided first
Property 20 parts of phenolic resin, 0.1 part of methylimidazole, 30 parts of dimethylformamide, 20 parts of aluminium hydroxide, then in a kettle plus
Enter dimethylformamide and add diamino diphenyl sulfone and methylimidazole normal-temperature dissolution 30 minutes, add bisphenol-A type ring
Oxygen resin, Study On O-cresol Epoxy Resin and linear phenolic resin fully dissolve 4 hours, are eventually adding aluminium hydroxide and dissolve 60 points
Clock, such high-temperature-resistant epoxy resin glue, which can be configured, to be completed.